Depth-dependent mosaic tilt and twist in GaN epilayer:An approximate evaluation

An approach based on depth-sensitive skew-angle x-ray diffraction （SAXRD） is presented for approximately evalu- ating the depth-dependent mosaic tilt and twist in wurtzite c-plane GaN epilayers. It is found that （103） plane and （101） plane, among the lattice planes not perpendicular to the sample surface, are the best choices to measure the depth profiles of tilt and twist for a GaN epilayer with a thickness of less than 2 μm according to the diffraction geometry of SAXRD. As an illustration, the depth-sensitive （103）/（101） ω-scans of a 1.4-μm GaN film grown by metal-organic chemical vapor deposition on sapphire substrate are measured and analyzed to show the feasibility of this approach.     

晶格匹配InAlN/GaN和InAlN/AlN/GaN材料二维电子气输运特性研究

文章研究了InAlN/GaN和引入AlN界面插入层形成的InAlN/AlN/GaN材料的输运性质. 样品均在蓝宝石上以脉冲金属有机物化学气相淀积法生长,霍尔迁移率变温特性具有典型的二维电子气(2DEG)特征. 综合各种散射机理包括声学形变势散射、压电散射、极性光学声子散射、位错散射、合金无序散射和界面粗糙度散射,理论分析了温度对迁移率的影响,发现室温下两种材料中2DEG支配性的散射机理都是极性光学波散射和界面粗糙度散射;AlN插入层对InAlN/GaN材料迁移率的改善作用一方面是免除2DEG的合金无序散射,另外还显著改善异质界面,抑制了界面粗糙度散射. 考虑到2DEG密度也是影响其迁移率的重要因素,结合实验数据给出了晶格匹配InAlN/GaN和InAlN/AlN/GaN材料的2DEG迁移率随电子密度变化的理论上限. 关键词： InAlN/GaN 二维电子气 迁移率     

高电子迁移率晶格匹配InAlN/GaN材料研究

文章基于蓝宝石衬底采用脉冲金属有机物化学气相淀积(MOCVD)法生长的高迁移率InAlN/GaN材料,其霍尔迁移率在室温和77 K下分别达到949和2032 cm²/Vs,材料中形成了二维电子气(2DEG). 进一步引入1.2 nm的AlN界面插入层形成InAlN/AlN/GaN结构,则霍尔迁移率在室温和77 K下分别上升到1437和5308 cm²/Vs. 分析样品的X射线衍射、原子力显微镜测试结果以及脉冲MOCVD生长方法的特点,发现InAlN/GaN材料的结晶质量较高,与GaN晶格匹配的InAlN材料具有平滑的表面和界面. InAlN/GaN和InAlN/AlN/GaN材料形成高迁移率特性的主要原因归结为形成了密度相对较低(1.6×10¹³-1.8×10¹³ cm^-2)的2DEG,高质量的InAlN晶体降低了组分不均匀分布引起的合金无序散射,以及2DEG所在界面的粗糙度较小,削弱了界面粗糙度散射. 关键词： InAlN/GaN 脉冲金属有机物化学气相淀积 二维电子气 迁移率