Effects of dipolar interactions on the magnetic hyperthermia of Zn0.3Fe2.7O4 nanoparticles with different sizes

Tumor-targeted magnetic hyperthermia has recently attracted much attention.Magnetic nanoparticles(NPs) are heat mediator nanoprobes in magnetic hyperthermia for cancer treatment.In this paper,single cubic spinel structural Zn_0.3Fe_2.7O₄ magnetic NPs with sizes of 14 nm-20 nm were synthesized,followed by coating with SiO₂ shell.The SLP value of Zn_0.3Fe_2.7O₄/SiO₂ NPs below 20 nm changes non-monotonically with the concentration of solution under the alternating current(AC) magnetic field of 430 kHz and 27 kA/m.SLP values of all Zn_0.3Fe_2.7O₄/SiO₂ NPs appear a peak value with change of solution concentration.The solution concentrations with optimal SLP value decrease with increasing magnetic core size.This work can give guidance to the better prediction and control of the magnetic hyperthermia performance of materials in clinical applications.     

Effect of Magnetic Anisotropy on Magnetic Thermal Induction of Mn_(0.3)Zn_(0.3)Co_xFe_(2.4-x)O_4 Nanoparticles

Mn_(0.3)Zn_(0.3)Co_xFe_(2.4-x)O_4 series magnetic nanoparticles are prepared by the high-temperature organic solvent method, and Mn_(0.3)Zn_(0.3)Co_xFe_(2.4-x)O_4@SiO_2 composite nanoparticles are prepared by the reverse microemulsion method. The as-prepared samples are characterized, and the results show that the magnetic anisotropy constant of nanoparticles increases with the cobalt content, and the magnetic thermal induction shows a trend of increasing first and then decreasing. The optimal magnetic thermal induction is obtained at x = 0.12 with a specific loss power of 2086 w/gmetal, which is a bright prospect in clinical magnetic hyperthermia.     

Table-Like Large Magnetocaloric Effect in the Misch Metal RSi Compound

Magnetic properties and the magnetocaloric effect(MCE)of the RSi(R=Ce,Pr,Nd)compounds made of Misch metal(MM)are investigated.Two transitions are found at 12K and 38K.Field variation generated large MCE and two peaks are found in the magnetic entropy change(△S)curves,which correspond to the two transition temperatures.The maximum values of the magnetic entropy changes(△S)are found to be-5.1 J/(kg·K)and-9.3 J/(kg·K)for the field ranges of 0-2 T and 0-5 T,respectively.The large AS as well as ultra-low price of MM make(MM)Si a competitive magnetic refrigerant candidate for low temperature in Eriksson cycle.