碳纳米管在药物载体领域的进展

基于其独特的结构、电子及机械性能,碳纳米管自被发现以来就是极具吸引力的材料,被广泛研究。在药物化学领域,碳纳米管成为载运治疗药物实现靶向治疗、控制释放等的热点,研究日益深入。本文概述了近年来碳纳米管在药物载体领域的研究进展情况,评述了其未来发展趋势,认为深入考察修饰碳纳米管的毒性,探索其载药释药机制,并逐步应用于临床,...     

表面活性剂碳化法合成Fe3O4/C复合物及其电化学性能

以水热法合成的包覆油酸的α-Fe₂O₃粒子为前驱体, 在氩气下500 °C煅烧1 h, 得到Fe₃O₄/C纳米复合物. 用傅里叶变换红外(FTIR)光谱, X射线衍射(XRD), 扫描电镜(SEM), X射线能量散射(EDX)谱, 高分辨透射电镜(HRTEM), 元素分析, 循环伏安(CV)和恒流充放电测试等方法对材料的结构、形貌、成分及电化学性能进行了表征. 结果表明: 所制备的Fe₃O₄/C复合物呈长约200 nm, 粗约100 nm的纺锤形, 表面碳层厚约1-2 nm, 碳含量为1.956%(质量分数); 这种复合物作为锂离子电池负极材料具有很好的循环稳定性(在0.2C (1C=928 mA·g^-1)循环80次后具有691.7 mAh·g^-1比容量)和倍率性能(在2C循环20次后依然有520 mAh·g^-1比容量). 相对于未包覆的商业Fe₃O₄粒子, 复合物显著提高的电化学性能是由于碳包覆能防止粒子聚集, 提高导电性以及稳定固体电解质界面(SEI)膜.     

功能添加剂对锂离子电池的防过充电化学行为研究

研究了功能添加剂3-氯苯甲醚(3CA)和联苯(BP)联合使用在锂离子电池电解液中的防过充行为。通过采用微电极循环伏安法、动电位扫描分析、扫描电镜法和充放电法等手段研究表明：联苯和3-氯苯甲醚混合添加剂的聚合电位随3-氯苯甲醚含量的增加由4.7V前移至4.6V (vs. Li/Li+);电池在正常工作电压(2.75V~4.2V)下,添加剂不参与电池反应过程;当电压高于4.2V电池发生过充时,3-氯苯甲醚在电极表面首先发生氧化还原飞梭分流限压对电池进行过充保护;电压继续升高时,联苯在电极表面发生电聚合反应,生成的聚合膜表面光滑致密是电子的良导体能有效的阻止Li+的嵌入与脱出,并通过自放电使电池处于安全状态,防止电池过充发生爆炸。两种防过充机制共同作用,对电池实施多重护防,提高了电池的安全性能。     

电子功能外延薄膜的电沉积

电沉积作为一种在温和条件下从溶液中合成材料的技术已被广泛应用于在导体和半导体基底表面合成各种功能材料。电沉积一般由人为施加于基底的电刺激（如：施加电位/电流）来触发。这种电刺激通过氧化或还原靠近基底表面的溶液层内部的离子、 分子或配合物从而使该溶液层偏离其热力学平衡状态,随后引起目标产物在基底表面的沉积。在电沉积过程中, 许多实验参数都可能从不同的方面对沉积物的物化性质造成影响。迄今为止,已通过电沉积制备出多种单质（包括金属和非金属单质）、 化合物（例如：金属氧化物、金属氢氧化物、 金属硫化物等）以及复合材料。电沉积制备的这些材料大多为多晶、 织构或外延薄膜的形式。其中, 外延薄膜是一种具有特定的面外和面内晶体生长取向且其晶体取向受基底控制的类单晶薄膜。由于外延薄膜中高度有序的原子排列,它们常呈现出独特的电磁性质。本文总结了常见的电沉积合成路线及影响沉积物外延生长的关键实验因素。此外, 本文简要介绍了用于表征外延薄膜的技术。最后, 本文还讨论了一些采用电沉积制备的具有特殊电子、 电磁及光电特性的功能外延薄膜。     

二氧化碳/环氧丙烷/γ-丁内酯三元共聚物微球降解性的研究

动物体内的体液和肠胃等器官的环境各不相同，这就要求各种不同用途的载药体的降解性能必须满足特定环境的要求。同时，可降解材料在不同的降解介质中通常有着不同的降解表现，这也决定着可降解材料的运用环境。因此，有必要对降解性材料在不同降解介质中的降解性进行专门的研究，由CO2和环氧化物合成的脂肪族聚碳酸酯具有良好的生物降解性能。     

碱土金属掺杂纳米TiO2催化剂的制备与光催化活性的评价

The nanometer TiO₂ were prepared by the hydrolyze-gel method and fellowed by doping alkaline-earth metals (Mg, Ca, Sr, Ba). XRD, SEM, diffuse reflection spectra were used to investigate their characteristices. The result indicates that the average particles size of the TiO₂ is about 80 nm and keep uniformity in distributing. The product was mainly anatase in 300～400 ℃ calcinations, the einstein shift of absorption spectrum was observed after doping the alkaline-earth metals. The best mole percentages of Mg, Ca, Sr and Ba are 0.5%, 1.0%, 1.5%, 1.5% respectively. Under the same reaction conditions, it is more effective to the UV-catalyed degradation reaction that the catalysts containing Mg and Ca were calcined at 300 ℃ for 1h or containing Sr and Ba were calcined at 400 ℃ for 1 h. The photocatalystic activity is considerably depondent on pH and the concentration of the oxidant. Using the sunlight to do the degradation experimental, the result also show that the doping catalysts has higher degradation efficiency than that of pure TiO₂.     

添加剂对SiO电性能的影响及其机理分析

SiO_x/CoO and SiO/Li₂CO₃ composite materials were prepared by mechanical ball-milling. The structures of the obtained materials were characterized by X-ray diffraction (XRD). And scanning electron microscopes (SEM) of three samples after 20 cycles were also given. In addition， the electrochemical performances of three materials with galvanostatic charge-discharge cycling were investigated. The results show that the composite samples have larger initial reversible capacities and better cycle performance than pure SiO. Also，a schematic diagram showing the buffer effects of Li₂CO₃ addition and the mechanism of improving electrochemical performance by adding Li₂CO₃ are suggested.     

聚[碳酸(亚丁酯-co-ε-己内酯)酯]的制备及其载药微球性能的研究

采用阴离子配位聚合方法, 合成了二氧化碳、1,2-环氧丁烷与ε-己内酯的三元共聚物: 聚[碳酸(亚丁酯-co-ε-己内酯)酯](PBCL). 并采用复相乳液(W/O/W)溶剂挥发法制备了包裹抗菌药物甲磺酸帕珠沙星的可降解微球. 对聚合物进行了FTIR, ¹H NMR, ¹³C NMR, DSC, TGA和WAXD等表征, 以及降解性能和载药微球特性的研究. 结果表明, PBCL热稳定性及降解性能优于聚碳酸亚丁酯(PBC). 所得PBCL微球球形规整、表面光滑. 大部分微球粒径在0.5～1 μm的范围内, 载药量和包封率分别达到38.21%和87.9%. 微球的体外释药性能研究在pH 7.4的磷酸缓冲溶液中进行, 释放21 d后, PBCL微球的累积释药量为84.74%, PBC微球的释药量仅为17.29%. 药物的体外释放行为符合Higuchi方程. PBCL载药微球具有长效缓释作用.     

溶剂热法合成不同形貌的Co3O4及其电容特性

采用溶剂热法以不同的钴盐在水-正丁醇体系中合成了不同形貌及尺寸的纳米Co3O4. 采用XRD和TEM对产物的物相和形貌进行表征. 结果表明, 通过改变反应体系中阴离子的种类, 可以控制产物Co3O4的形貌与晶粒尺寸. 通过循环伏安法、恒流充放电和交流阻抗法对Co3O4电极材料的电化学性能进行表征. 结果表明, Co3O4的形貌与晶粒尺寸对其电化学性能有显著影响. 在2 mol·L-1 KOH溶液中, 在-0.40 - 0.55 V (vs SCE)电位范围内, 由Co(NO3)2制备的球形Co3O4表现出更好的电容特性,单电极初始比容量达362.0 F·g-1, 经过400 次循环后比容量仍保持90%.     

反相微乳液法制备纳米Al2O3颗粒及其形成反应机理的研究

通过聚乙二醇辛基苯基醚(曲拉通X-100)/正丁醇/环己烷/水溶液形成的体系, 采用反相微乳液法合成了Al₂O₃纳米粒子. 对前驱体进行热分析(TG-DTG-DTA), 确定了合适的煅烧温度为1150 ℃. 采用X射线衍射(XRD)、透射电镜(TEM)、紫外可见分光光度法(UV-vis)分别对产物的结构、粒度和形貌进行了表征, 考察了微乳液中水与表面活性剂的物质的量之比(ω_o)、煅烧温度和煅烧时升温速率等关键因素对产物形貌和晶相的影响, 并通过分析进一步揭示了Al₂O₃纳米粒子的形成机理. 结果表明, 控制ω_o为10、煅烧温度为1150 ℃可得到分散性好、粒径分布均匀的Al₂O₃纳米粒子, 且2 ℃/min的升温速率更有利于产物向稳定的α晶相转变.