半化学法制备0.5Pb(Mg1/2W1/2)O3-0.5PbTiO3粉体的反应机理探讨

半化学法制备0.5Pb(Mg1/2W1/2)O3-0.5PbTiO3粉体的反应机理探讨;钨镁酸铅;钙钛矿相;半化学法;反应机理     

半化学法制备PMW-PNN-PT粉体的反应机理研究

The mechanism of perovskite 0.1Pb(Mg_1/2W_1/2)O₃-0.6Pb(Ni_1/3Nb_2/3)O₃-0.3PbTiO₃ (abbreviated PMW-PNN-PT) phase formation by Semichemical Method has been studied. The precursors were prepared by adding aqueous solution of Mg(Ac)₂ and Ni(AC)₂ rather than solid MgO and NiO to the alcoholic slurry of PbO, WO₃, Nb₂O₅ and TiO₂. The TG-DTG and DSC of the precursors and XRD analysis of the powders at various calcination temperature showed that the mechanism of this method was different from that of the conventional mixed oxide method. The aqueous Mg(Ac)₂ and Ni(Ac)₂ reacted with PbO to form basic lead acetate, basic magnesium acetate and basic nickel acetate and so on. With the increase of calcination temperature these basic salt decomposed to form nascent PbO, MgO and NiO, which improved the reactivity and distribution of PbO, MgO and NiO. In addition, the formation of PbWO₄ and pyrochlore phase Pb₃Nb₂O₈ in the process was in favor of the pervoskite PMW-PNN-PT phase formation. At the calcining temperature of 850 ℃, the perovskite phase reached 98%.     

PMW-PNN-PT陶瓷的制备及介电性能研究

0.29Pb(Mg_1/2W_1/2)O₃-0.41Pb(Ni_1/3Nb_2/3)O₃-0.30PbTiO₃ ＋ 0.002 5MnO₂＋xWO₃(PMW-PNN-PT) ceramics were prepared by Semichemical Method. The Mg(Ac)₂, Ni(Ac)₂, and Mn(NO)₃ solution rather than MgO, NiO and MnO₂ were added to the slurry of PbO, WO₃, Nb₂O₅ and TiO₂ and then calcined at 850 ℃ for 2 h. Then the sample was sintered at 1 100～1 200 ℃ for 2 h. The effect of sintering temperature and WO₃-excess amounts on the phase constitute, microstructure and the dielectric characteristics was investigated. The result showed that the PMW-PNN-PT powders with pure pervoskite phase were prepared by single-step calcination. The development of sintered temperature contributes to the increase of dielectric constant and the flatness of dielectric temperature dependence. But the dielectric properties will be worse if the sintered temperature is too high. The increase of WO₃-excess level lead to an increase of Pb₂WO₅ phase and the flatness of dielectric curves, but the dielectric constant will be decreased. The proper WO₃-excess amount of X7R type PMW-PNN-PT ceramics is 5mol% and the proper sintering condition is 1 150 ℃ for 2 h, the maximum dielectric constant is 5 395.