超高温焙烧的Ni/Al2O3对甲烷部分氧化反应的催化活性

考察了超高温焙烧的Ni/Al2O3对甲烷部分氧化反应的催化性能,发现该催化剂经还原后对甲烷部分氧化反应表现出较高的催化活性.X射线衍射结果显示,Ni/Al2O3催化剂在超高温(1200~1400℃)下焙烧后生成了NiAl2O4,且无相转移,进一步经950℃还原后催化剂中绝大部分Ni以单质Ni0形式存在.透射电子显微镜测试结果表明,不同超高温焙烧的催化剂经950℃还原后Ni晶粒的大小无明显差异.这说明超高温焙烧的Ni/Al2O3对甲烷部分氧化反应的高活性可归结为NiAl2O4的可还原性以及还原后Ni0相似的晶粒尺寸.同时还发现,焙烧温度越高,生成的NiAl2O4的还原温度越高.     

制备方法对镧钡共改性氧化铝性能的影响

The effect of preparation method on the properties of alumina modified by La₂O₃ and BaO was investigated by means of Low temperature nitrogen adsorption-desorption, NH₃-TPD, NO-TPD and XRD. The results show that alumina prepared by peptizing method exhibits the best textural properties, alumina obtained by co-precipitation method presents the strongest surface acidity and alumina derived from impregnation method shows the best ability of NO adsorption. After calcination at 1 100 ℃, all alumina except that from impregnation method have excellent thermal stability. When the specific surface area and pore volume of alumina are large enough, the activity of catalyst Pd/alumina is affected primarily by the surface acidity of alumina.     

胶溶法制备镧-钡共稳定氧化铝的性能

以硝酸为胶溶剂, 两种拟薄水铝石为前驱体, 用胶溶法制备了镧-钡共稳定的氧化铝. 采用X 射线衍射(XRD)、表面分析仪(BET)、氨气程序升温脱附(NH3-TPD)和NO2程序升温脱附(NO2-TPD)技术对所制备的镧改性和镧钡共改性氧化铝的结构特性和表面性能进行了表征. XRD结果表明, 改性氧化铝在1273 K焙烧后均以γ-Al2O3相存在. 当BaO添加量达到14%(w)时, 有少量BaCO3生成. BET结果表明, 在1273 K下焙烧5 h后, 5%(w)La2O3稳定的氧化铝(Ba-0)和5%La2O3与8%BaO共同稳定的氧化铝(Ba-8)均具有较大的比表面积, 各种氧化铝的吸附等温线表明它们的孔形状均为狭缝型孔和瓶型孔, 孔径分布曲线表明, 仅有样品Ba-8的孔径分布较宽, 孔径为6-10 nm, 其它三种样品的孔径均集中在10 nm; NH3-TPD结果表明, 随着氧化钡添加量的逐渐增多, 氧化铝表面的酸量、酸强度逐步减少. NO2-TPD结果表明, 添加BaO后载体对NO2的吸附量增多, 随着BaO含量的增多, 体相Ba(NO3)2增多. 由于样品Ba-8同时具有很好的织构性质、适中的表面酸量和酸强度分布及NO2吸附脱附能力, 使得以它为载体的催化剂具有最好的催化性能,丙烷的起燃温度和完全转化温度分别为526 K和593 K.     

胶溶法制备改性氧化铝的结构及织构特点

对胶溶法制备的镧和聚乙二醇(PEG)改性的氧化铝载体进行了深入研究.