Ba1-xSrxTi1-yMyO3固溶体的湿化学法合成与介电特性

A series of Ba_1-xSr_xTi_1-yM_yO₃ (M=Zr,Sn, 0≤ x≤ 0.5,0≤ y≤ 0.3) solid solutions were synthesized by chemical method at below 100℃ . XRD and cell parameters component figures of the series of the solid solutions powder demonstrated that the compounds are mutually miscible in the solid solutions. The particls size is about 70nm with spherical shape and uniform distribution. The result of preparing ceramics showed that after adulterating with Sr²⁺ and Zr⁴⁺ or Sn⁴⁺ in pure BaTiO₃ phase, the dielectric constant increased eight times while the dielectric loss decreased three times at room temperature.     

Ba1-xSrxTi1-yMyO3固溶体的湿化学法合成与介电特性

为了提高 BaTiO3的室温介电常数和减少介电损失，目前工业上在电子元器件的制造过程中，采用固相掺杂方法，于 BaTiO3粉体中掺入适量锶、锆、锡和一些稀土元素的氧化物，以改善其性能。但由于固相掺杂的不均匀性，使得元器件的各项参数改善并不理想 [1]。近几年国外虽有用 Sol Gel法对 BaTiO3进行掺杂改性的研究 [2]，但却因为原材料价格昂贵而无法在我国生产。为此，本文率先用湿化学合成方法，在 100℃以下水溶液中对 BaTiO3进行了掺杂改性，使掺杂离子均匀进入母体晶格，合成了一系列 BaTiO3基固溶体纳米粉末，并对其介电特性进…     

中学物理中的理想化方法

物理现象和物理过程都是很复杂的,如果我们把所有的因素都毫不遗漏地考虑进去,实际问题就很难,甚至无法解决。因此,理想化方法就成为物理学研究和教学中的一种重要方法。所谓理想化方法,就是通过逻辑思维,在复杂问题中忽略次要因素,抓住主要因素,将实际问题简化处理,从而得出结论的方法,它是一种科学抽象的方法。理想化方法不仅在中学物理教学中经常被采用,而且对于培养中学生分析、解决问题的能力起着很大的作用。在中学物理中,理想化方法主要包括以下三种形式:物理条件的理想化、建立理想模型、进行理想实验。 一、物理条件的理想化 中学物理中遇到的物体,实际上都是处在多种外界条件之中的,但并不是所有的条件都具有同样重要的作用,在这些条件中,有一些对物体的运动规律起着主导作用,而另一些条件却对所研究的问题影响很小、甚至根本就没有影响。这时,就需要我们帮助学生分析哪些条件是主要的,必须考虑,哪些条件可以忽略。然后在此基础上做进一步的分析,最后解决这个问题。 在中学物理习题中,最常见的是忽略摩擦力。比如:“两物体接触面光滑”、“忽略一切摩擦阻力”、“不计空气阻力”等等,这些都说明忽略摩擦力是中学生解题时经常要注意的。特别是中学物理课本中的“自由     

Ba1-xSrxMyTi1-yO3(M=Zr, Sn)纳米材料的软化学合成、结构与介电特性

用软化学方法,在１００℃以下合成了一系列Ｂａ_(１－ｘ)Ｓｒ_ｘＭ_ｙＴｉ_(１－ｙ)Ｏ_３固溶体纳米粉末（Ｍ＝Ｚｒ,Ｓｎ,０ ≤ｘ≤０．４,０≤ｙ≤０．３）,经ＸＲＤ物相分析和ｄ－间距－组成图证明,产品为立方晶系的完全互溶取代固溶体,结果符合Ｖｅｇａｒｄ定律．ＴＥＭ形貌观察,粒子为均匀球形,平均粒径７０ｎｍ．通过制陶实验,分别测定了该系列固溶体的室温介电常数以及介电常数随温度的变化．结果发现,用软化学方法在ＢａＴｉＯ_３中掺入适量锶和锆或锡,由于掺杂离子均匀进入母体晶格,引起Ｔｃ降低,介电性能改善显著．当ｘ＝０．２,ｙ＝０．１时,室温介电常数达 １１ ０００,比 ＢａＴｉＯ_３纯相提高 ８倍,而介电损失却下降 ３倍．     

Synthesis, structure and dielectric properties of Ba1-xSrx My Ti1-yO3 (M = Zr, Sn)

A series of Ba1-xSrxMyTi1-yO3 (M = Zr, Sn, 0≤x≤0.4, 0≤y≤0.3) solid solutions were synthesized with the soft chemical method below 100 ℃. XRD pattern and cell parameters-composition figures of the prepared powder demonstrate that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM shows that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of the powder doped with Sr2 and Zr4 or Sn4 have dielectric constant eight times higher and dielectric loss thirty per cent lower than those of pure BaTiO3 phase at room temperature.     

Ba~1~-~xCa~xSn~yTi~1~-~yO~3纳米材料的、合成结构与性能

采用常压水相法,在100℃以下制备了一系列Ba~1~-~xCa~xSn~yTi~1~-~yO~3固溶体纳米粉末(0≤x≤0.5,0≤y≤0.3),经XRD物相分析和d-间距-组成图证明,产品为立方晶系的完全互溶取代固溶体,结果符合Vegard定律。TEM形貌观察,粒子为均匀球形,平均粒径70nm。通过制陶实验,分别测定了该系列固溶体的室温介电常数以及介电常数随温度的变化,结果发现,用软化学方法在BaTiO~3中掺入适量钙和锡,由于掺杂离子均匀进入母体晶格,引起T~c降低,室温介电常数达9800,经BaTiO~3纯相提高6倍,而介电损失却降低50%。     

低温-低压水热合成Ba1-xSrxTi1-ySnyO3纳米材料及其 结构与性能研究

采用低温-低压水热法,在150℃,0.5MPa以下合成了一系列Ba1-xSrxTi1-ySnyO3固溶体纳米粉末(0≤x≤0.5≤y≤0.4),经XRD物相分析和d-间距-组成图证明,产品为立方晶系的完全互溶取代固溶体,结果符合Vegard定律,TEM形貌观察,粒子为均匀球形,平均粒径80nm。通过制陶实验,分别测定了该系列固溶体的室温介电常数、介电损失以及介电常数随温度的变化。结果发现,用该方法在BaTiO3中掺入适量锶和锡,由于掺杂离子均匀进入母体晶格,引起Tc降低,介电性能改善显著,当x=0.1,y=0.08时,室温介电常数达17000,比BaTiO3纯相提高10倍,而介电损失却降低88%。