三维有序大孔WO3的制备及其对丙酮的气敏响应

三维有序大孔(3DOM)材料具有高度有序的孔结构和较大的比表面积,这些特点有利于气体在材料表面的传输与扩散,可以作为良好的气敏材料.本文通过聚苯乙烯模板结合煅烧处理的方法制备了3DOM WO3气敏材料,并运用XRD、SEM、BET、XPS等手段对其物相、形貌、比表面积和表面成分等进行了表征.气敏测试结果表明,所制备的3DOM材料对丙酮灵敏度高(在丙酮浓度10 ppm时,S=10),检测限可低至0.2 ppm.此外,3DOM WO3材料对丙酮还具有良好的选择性和长期稳定性.最后,对所制备的3DOM WO3材料进行了气敏机理解释.     

新型三维间排层状钴磷酸盐配合物Co3(PO4)2·6H2O的合成与晶体结构

A new three dimensional layered cobalt phosphate complex Co₃(PO₄)₂·6H₂O, was prepared by hydro-thermal reaction of Co(CH₃COO)₂·4H₂O and H₃PO₄, NH₄VO₃. The crystal structure of the complex was deter-mined by single-crystal X-ray diffraction. The result indicates that it crystallizes in the tetragonal space group I4/m. It rarely occurs in cobalt phosphate complex to form two kinds of coordinate geometry of Co(Ⅱ), six water molecular oxygen atoms surround Co(Ⅰ) and form an octahedron geometry, Co(2) bond to four oxygen atoms from 4PO₄^3- and one water molecular oxygen and build a tetragonal pyramid. The kinetic study shows that the first decomposition stage is governed by A(?)B(?)C mode. CSD: 414600.     

喷雾-胶凝法制备超细莫来石粉末

以水玻璃和硝酸铝为原料 ,通过喷雾 -胶凝法和共沸蒸馏技术制备莫来石前驱粉体 ,然后煅烧得到超细莫来石粉末 .用TG -DTA、XRD、TEM及BET研究了莫来石前驱粉体在煅烧过程中的热学性质、物相与比表面变化及颗粒大小与形貌变化 ,并对所制得的莫来石粉进行了表征 .结果表明 ,莫来石前驱粉体经 130 0℃煅烧 1h可制得粒径为 2 5nm～ 4 0nm ,比表面积为 4 2 5m2 /g的莫来石超细粉 ;煅烧过程中的物相变化次序为 :勃姆石 +非晶态SiO2 →非晶态Al2 O3 +非晶态SiO2 →γ -Al2 O3 +非晶态SiO2 → 3Al2 O3 ·2SiO2 .     

Cu掺杂WO3纳米棒的制备及其对正丁醇的气敏响应

通过水热法简易的制备出Cu掺杂WO3纳米棒材料,并运用XRD、SEM、BET等手段对其物相、形貌和比表面积等进行了表征,并研究了其对正丁醇的气敏性能.气敏测试结果表明,所制备的Cu掺杂WO3纳米棒材料对正丁醇具有良好气敏性能.当工作温度为400 ℃时,Cu掺杂WO3材料对100ppm的正丁醇的响应达到了29,约为纯WO3的3倍.同时,Cu掺杂WO3材料对正丁醇的检测限可低至0.1ppm,并且对正丁醇还具有良好的选择性.最后对所制备的Cu掺杂WO3材料进行了气敏机理解释.     

温度和pH敏感P(NIPA-co-AA)/粘土复合水凝胶的辐射制备与表征

以N-异丙基丙烯酰胺(NIPA)作为温敏性聚合单体,丙烯酸(AA)为pH敏感性单体,有机粘土为改性剂,采用~(60)Co-γ射线为辐射源,辐射合成了P(NIPA-co-AA),粘土复合水凝胶,研究了粘土的加入对水凝胶溶胀率、温度及pH敏感性和压缩性能的影响.结果表明,P(NIPA-co-AA)/粘土复合水凝胶的溶胀性能优于P(NIPA-co-AA)水凝胶,平衡溶胀率(SR)明显提高;且复合水凝胶仍表现出明显的温度和pH敏感性;粘土的加入提高了水凝胶的压缩强度、最大压缩力和压缩屈服力等力学性能,当粘土含量为15%时,P(NIPA-co-AA)/粘土复合水凝胶的压缩强度为P(NIPA-co-AA)共聚水凝胶的2.4倍,最大压缩力为P(NIPA-co-AA)的2.1倍.     

碳酸铝铵热分解制备纳米氧化铝粉体

Nanosized alumina powders were prepared from Al(NO₃)₃·9H₂O and (NH₄)₂CO₃ through the synthesis of ammonium aluminium carbonate hydroxide (AACH) and followed by calcination. TG-DTA， XRD， TEM and BET were employed to study the process of AACH thermal decomposition and to characterize the products obtained. The results show that high purity (99.97%) and nanosized spherical α-Al₂O₃ powders with the diameter of 40～50nm and BET surface area 32.5m²·g^-1 can be obtained by calcining AACH at 1150℃ for 1.5h， the sequence of phase transformation during calcination was AACH → amorphous Al₂O₃ → γ-Al₂O₃ → α-Al₂O₃， and the activation energy of AACH decomposition is (115±5)kJ·mol^-1.     

新型三维间排层状钴磷酸盐配合物Co_3(PO_4)_2·6H_2O的合成与晶体结构

0引言 60年代初,Weisz提出规整结构分子筛"择形催化"概念,继而发现它对催化裂化反应的惊人活性[1].金属有机膦酸化学因其在自组装化学、超分子化学、软化学和纳米化学等前沿领域的广泛研究而倍受广大化学工作者的关注[2],尤其是在吸附、催化、离子交换、非线性光学材料方面潜在极大的应用前景[3,4],因而设计和合成新型的有机膦酸及其金属化合物,并进一步探索其结构和性能之间的关系,对筛选出具有实际应用价值的新型结构材料具有重要的意义.     

Na~+浓度对反应体系成胶特性及SiO_2凝胶粉末性能的影响

以水玻璃为原料，乙酸乙酯为潜伏酸试剂，采用溶胶—凝胶法制备超细二氧化硅凝胶粉末。研究了成胶反应过程中Ｎａ＋ 浓度对反应体系成胶特性及最终所得二氧化硅凝胶粉末性能的影响，并用透射电镜和氮气物理吸附实验手段对粉末的有关性能进行了测试表征