TFA-MOD方法制备YBCO超导薄膜研究

采用TFA-MOD方法在LaAlO3(001)单晶基片上制备了性能良好的YBCO超导薄膜:临界电流密度(Jc)可达3MA/cm2(77K,0T),超导转变温度Tc≈90K,转变宽度ΔTc=0.5K,其一次涂层厚度达338nm.通过X射线衍射(XRD)分析表明YBCO具有纯c-轴取向、无a-轴取向的晶粒存在.ω扫描分析表明该YBCO薄膜具有很好的面外外延性,其摇摆曲线的半高宽(FWHM)为0.653°. 用SEM分析也表明膜的表面无裂纹存在,表面平整,没有a轴晶粒生长.     

Sodium beta-alumina thin films as gate dielectrics for A1GaN/GaN metal-insulator-semiconductor high-electron-mobility transistors

<正>Sodium beta-alumina（SBA） is deposited on AlGaN/GaN by using a co-deposition process with sodium and Al₂O₃ as the precursors.The X-ray diffraction（XRD） spectrum reveals that the deposited thin film is amorphous.The binding energy and composition of the deposited thin film,obtained from the X-ray photoelectron spectroscopy（XPS） measurement,are consistent with those of SBA.The dielectric constant of the SBA thin film is about 50.Each of the capacitance-voltage characteristics obtained at five different frequencies shows a high-quality interface between SBA and AlGaN.The interface trap density of metal-insulator-semiconductor high-electron-mobility transistor（MISHEMT） is measured to be（3.5～9.5）×10¹⁰ cm^-2·eV^-1 by the conductance method.The fixed charge density of SBA dielectric is on the order of 2.7×10¹² cm^-2.Compared with the AlGaN/GaN metal-semiconductor heterostructure high-electronmobility transistor（MESHEMT）,the AlGaN/GaN MISHEMT usually has a threshold voltage that shifts negatively. However,the threshold voltage of the AlGaN/GaN MISHEMT using SBA as the gate dielectric shifts positively from—5.5 V to—3.5 V.From XPS results,the surface valence-band maximum（VBM-E_F） of AlGaN is found to decrease from 2.56 eV to 2.25 eV after the SBA thin film deposition.The possible reasons why the threshold voltage of AlGaN/GaN MISHEMT with the SBA gate dielectric shifts positively are the influence of SBA on surface valence-band maximum （VBM-E_F）,the reduction of interface traps and the effects of sodium ions,and/or the fixed charges in SBA on the two-dimensional electron gas（2DEG）.     

Characterization of vertical Au/β-Ga_2O_3 single-crystal Schottky photodiodes with MBE-grown high-resistivity epitaxial layer

High-resistivity β-Ga_2O_3 thin films were grown on Si-doped n-type conductive β-Ga_2O_3 single crystals by molecular beam epitaxy(MBE).Vertical-type Schottky diodes were fabricated,and the electrical properties of the Schottky diodes were studied in this letter.The ideality factor and the series resistance of the Schottky diodes were estimated to be about1.4 and 4.6×10~6 Ω.The ionized donor concentration and the spreading voltage in the Schottky diodes region are about4×10~(18)cm~(-3) and 7.6 V,respectively.The ultra-violet(UV) photo-sensitivity of the Schottky diodes was demonstrated by a low-pressure mercury lamp illumination.A photoresponsivity of 1.8 A/W and an external quantum efficiency of8.7 ×10~2%were observed at forward bias voltage of 3.8 V,the proper driving voltage of read-out integrated circuit for UV camera.The gain of the Schottky diode was attributed to the existence of a potential barrier in the i-n junction between the MBE-grown highly resistive β-Ga_2O_3 thin films and the n-type conductive β-Ga_2O_3 single-crystal substrate.