Two localized CO2 laser treatment methods for mitigation of UV damage growth in fused silica

Two methods：high-power,short-time,single-shot irradiation（Method A） and low-power,long-time,multi-shot irradiation（Method B） are investigated to mitigate the UV damage growth in fused silica by using a 10.6-μm CO2 laser.To verify the mitigation effect of the two methods,the laser induced damage thresholds（LIDTs） of the mitigated sites are tested with a 355-nm,6.4-ns Nd：YAG laser,and the light modulation of the mitigation sites are tested with a 351-nm continuous Nd：YLF laser.The mitigated damaged sites treated with the two methods have almost the same LIDTs,which can recover to the level of pristine material.Compared with Method A,Method B produces mitigated sites with low crater depth and weak light modulation.In addition,there is no raised rim or re-deposited debris formed around the crater edge for Method B.Theoretical calculation is utilized to evaluate the central temperature of the CO2 laser beam irradiated zone and the radius of the crater.It is indicated that the calculated results are consistent with the experimental results.     

高功率脉冲电子束辐照SiO$lt;sub$gt;2$lt;/sub$gt;的光学和激光损伤性能

研究了不同剂量的60 kW高功率脉冲电子束辐照对高纯熔石英玻璃的微观结构、光学性能和激光损伤特性的影响规律. 光学显微图像表明, 辐照后熔石英样品由于热效应导致表面破裂, 裂纹密度和尺寸随辐照剂量增加而增大, 采用原子力显微镜分析表面裂纹的微观形貌, 裂纹宽度约1 um, 同时样品表面分布着大量尺寸约0.1–1μm的碎片颗粒. 吸收光谱测试表明, 所有样品均在394 nm处出现微弱的吸收峰, 吸收强度随着电子束辐照剂量增大呈现先增加后减小的趋势. 荧光光谱测试发现辐照前后样品均有3个荧光带, 分别位于460, 494和520 nm, 荧光强度随辐照剂量的变化趋势与吸收光谱一致. 利用355 nm激光研究了不同剂量电子束辐照对熔石英激光损伤阈值的影响, 结果表明熔石英的损伤阈值随着辐照剂量的增加而降低. 在剂量较低时, 导致熔石英激光损伤阈值下降的原因主要是色心缺陷; 剂量较高时, 导致损伤阈值降低的原因主要是样品表面产生的大量微裂纹和碎片颗粒对激光的调制和吸收. 关键词： 熔石英 电子束辐照 色心 激光损伤阈值     

Two localized CO₂ laser treatment methods for mitigation of UV damage growth in fused silica

Two methods:high-power,short-time,single-shot irradiation(Method A) and low-power,long-time,multi-shot irradiation(Method B) are investigated to mitigate the UV damage growth in fused silica by using a 10.6-μm CO2 laser.To verify the mitigation effect of the two methods,the laser induced damage thresholds(LIDTs) of the mitigated sites are tested with a 355-nm,6.4-ns Nd:YAG laser,and the light modulation of the mitigation sites are tested with a 351-nm continuous Nd:YLF laser.The mitigated damaged sites treated with the two methods have almost the same LIDTs,which can recover to the level of pristine material.Compared with Method A,Method B produces mitigated sites with low crater depth and weak light modulation.In addition,there is no raised rim or re-deposited debris formed around the crater edge for Method B.Theoretical calculation is utilized to evaluate the central temperature of the CO2 laser beam irradiated zone and the radius of the crater.It is indicated that the calculated results are consistent with the experimental results.     

Mitigation of laser damage growth in fused silica by using a non-evaporative technique

A non-evaporative technique is used to mitigate damage sites with lateral sizes in a range from 50 μm to 400 μm and depths smaller than 100 μm.The influence of the pulse frequency of a CO 2 laser on the mitigation effect is studied.It is found that a more symmetrical and smooth mitigation crater can be obtained by increasing the laser pulse frequency form 0.1 to 20 kHz.Furthermore,the sizes of laser-affected and distorted zones decrease with the increase of the laser pulse frequency,leading to less degradation of the wave-front quality of the conditioned sample.The energy density of the CO 2 laser beam is introduced for selecting the mitigation parameters.The damage sites can be successfully mitigated by increasing the energy density in a ramped way.Finally,the laser-induced damage threshold(LIDT) of the mitigated site is tested using 355 nm laser beam with a small spot(0.23 mm 2) and a large spot(3.14 mm 2),separately.It is shown that the non-evaporative mitigation technique is a successful method to stop damage re-initiation since the average LIDTs of mitigated sites tested with small or large laser spots are higher than that of pristine material.     

高功率脉冲电子束辐照SiO_2的光学和激光损伤性能

研究了不同剂量的60 kW高功率脉冲电子束辐照对高纯熔石英玻璃的微观结构、光学性能和激光损伤特性的影响规律.光学显微图像表明,辐照后熔石英样品由于热效应导致表面破裂,裂纹密度和尺寸随辐照剂量增加而增大,采用原子力显微镜分析表面裂纹的微观形貌,裂纹宽度约1μm,同时样品表面分布着大量尺寸约0.1—1μm的碎片颗粒.吸收光谱测试表明,所有样品均在394 nm处出现微弱的吸收峰,吸收强度随着电子束辐照剂量增大呈现先增加后减小的趋势.荧光光谱测试发现辐照前后样品均有3个荧光带,分别位于460,494和520 nm,荧光强度随辐照剂量的变化趋势与吸收光谱一致.利用355 nm激光研究了不同剂量电子束辐照对熔石英激光损伤阈值的影响,结果表明熔石英的损伤阈值随着辐照剂量的增加而降低.在剂量较低时,导致熔石英激光损伤阈值下降的原因主要是色心缺陷;剂量较高时,导致损伤阈值降低的原因主要是样品表面产生的大量微裂纹和碎片颗粒对激光的调制和吸收.     

Effective model for rare-earth Kitaev materials and its classical Monte Carlo simulation

Recently, the family of rare-earth chalcohalides were proposed as candidate compounds to realize the Kitaev spin liquid (KSL) [Chin. Phys. Lett. 38 047502 (2021)]. In the present work, we firstly propose an effective spin Hamiltonian consistent with the symmetry group of the crystal structure. Then we apply classical Monte Carlo simulations to preliminarily study the model and establish a phase diagram. When approaching to the low temperature limit, several magnetic long range orders are observed, including the stripe, the zigzag, the antiferromagnetic (AFM), the ferromagnetic (FM), the incommensurate spiral (IS), the multi-Q, and the 120° ones. We further calculate the thermodynamic properties of the system, such as the temperature dependence of the magnetic susceptibility and the heat capacity. The ordering transition temperatures reflected in the two quantities agree with each other. For most interaction regions, the system is magnetically more susceptible in the ab-plane than in the c-direction. The stripe phase is special, where the susceptibility is fairly isotropic in the whole temperature region. These features provide useful information to understand the magnetic properties of related materials.