实验研究了烧结金属纤维板在大空间下的自然对流换热,分析了倾角、孔隙率、纤维丝经、Ra数和金属纤维导热系数对换热性能的影响.实验结果表明:存在最优的角度(60°左右)使烧结金属纤维板的自然对流换热性能最好,但倾斜角度对烧结金属纤维板的换热影响没有光板显著;加热面的平均Nu数随着纤维直径和孔隙率的增加均先增加后减小;在实验...     

三维尖晶石Li4Ti5O12纳米丝网状电极的构置与电化学性能

首次采用电纺丝技术结合高温退火成功地构置了含尖晶石Li₄Ti₅O₁₂的纳米纤维丝三维(3D)网状结构，并测量了三维电池的充放电性能。X射线衍射谱(XRD)、扫描电子显微镜(SEM)和电池循环性能测试等方法表征纤维丝3D结构和电化学性能。研究结果表明了Li₄Ti₅O₁₂纳米丝的零应变特性、构建的3D阵列的结构稳定性和在大电流密度下较好的充放电性能。显示了Li₄Ti₅O₁₂可作为3D电池的电极材料。     

LD-pumped 6 W cw Tm^3＋-Doped Silica Double-Cladding Fibre Laser

We report a thulium-doped silica fibre laser that generates a maximum cw output power of 6 W in a 2 μm wavelength range when cladding-pumped by a laser diode （LD） operating at approximately 791 nm at room temperature. The slope efficiency with respect to the launched pump power is 50% and 38.4%, with and without an output coupler mirror, respectively. The corresponding thresholds are 2.8 W and 4.8 W, respectively. The beam qualities Mx^2 and My^2 are 1.26 and 1.32, respectively. The experimental results are also analysed.     

植物固体纤维丝在NiMo柴油加氢脱硫催化剂中的应用

通过在氧化铝载体加入微米级植物固体纤维丝扩孔，制备出NiMo柴油加氢脱硫催化剂。采用BET、XRD、SEM、Raman与TEM对制备的载体及催化剂进行表征研究。结果表明，植物固体纤维丝能够在催化剂中构建出部分直筒大孔，NiMo活性组分在催化剂载体上实现了高度分散，活性相MoS₂堆叠层数集中在3-5层，平均MoS₂条长度为4.49 nm。研究了催化剂载体中植物固体纤维丝含量对催化剂活性的影响，并与常规氧化铝载体催化剂进行了对比，高压微反评价结果表明，开发的含有3%（质量分数）植物固体纤维丝NiMo柴油加氢脱硫催化剂比常规NiMo催化剂活性更高，其加氢脱硫活性提高了5%-15%。     

α-K8P2W17CuO61纳米纤维的制备与表征

运用高压静电纺丝和程序焙烧方法，制备α-K8P2W17CuO61纳米纤维丝．通过红外光谱（FT-IR），X-射线粉末衍射（XRD）进行了表征，结果表明制备的纳米丝是纯α-K8P2W17CuO61，扫描电子显微镜照片（SEM）显示焙烧后产物为纳米纤维丝，其平均直径大约为150nm．