Bi4Ge3O12:Er3+晶体中的高阶混合效应对EPR g因子的影响

通过对角化364×364完全能量矩阵的理论方法,对掺杂在Bi₄Ge₃O₁₂晶体中的Er³⁺的Stark能级和EPR参数进行了研究,同时,定量分析了高阶晶体场混合效应和J-J混合效应对EPR g因子的影响。研究结果表明:对Er³⁺来说,最主要的J-J混合效应来源于多重态谱项²K_15/2,其对EPR g因子的贡献约占2.5%,而最主要的高阶晶体场混合效应来源于第一激发多重态⁴I_13/2和基态多重态⁴I_15/2之间的晶体场混合,其对各向异性g因子中g_⊥的贡献大致是g_//的两倍(即g_⊥约占 0.21%,g_//约占0.092%),其他更高阶的晶体场混合和J-J混合效应可以忽略不计。因此,对于Er³⁺掺杂的络合物系统来说,只考虑基态多重态⁴I_15/2对EPR g因子的贡献应该是一个很好的近似。     

g-C3N4-W18O49复合光催化剂的制备及其光催化机理研究

通过简单的溶剂热法成功制备出了g-C3N4-W18O49复合光催化剂,采用XRD、SEM、TEM以及PL对所得催化剂的物相结构及形貌和光学性能进行了表征,通过降解甲基橙和光解水产氢实验研究所得催化剂的催化性能及其催化机理.由实验可知,W18O49的含量为50;时所得g-C3N4-W18O49复合光催化剂的降解性能最好,其降解率比纯g-C3N4纳米片提高48;;为进一步研究复合光催化剂的电子-空穴传输机理,我们又进行了光解水制氢实验.结果表明:单一的W18O49无产氢活性,它的复合明显降低了g-C3N4的产氢速率,说明复合结构中光生电子是从g-C3N4传递到了W18O49,表现出明显的Ⅱ型异质结复合特征,而不是部分文献所提出的Z型方式.     

掺杂稀土铁磁性纳米复合粉体的制备

采用水热法以FeCl2和KOH为原料制备Fe3 O4粉体,以氧化钇、氧化铕和氧化铽为原料制备Y2 O3:1;Eu3+,5;Tb3+粉体,然后以Fe3 O4粉体,Y2 O3:1;Eu3+,5;Tb3+粉体和三聚氰胺为原料,采用微波烧结法在Ar气气氛下制备FeYO3/Y2 O3:1;Eu3+,5;Tb3+复合粉体,利用XRD衍射仪对各种粉体的结构进行分析,利用扫描电镜对复合粉体的形貌进行观察,并利用振动样品磁强计对复合粉体的磁学性能进行研究.结果表明:复合粉体均呈针状,长度和细度均为纳米级.当Fe3 O4,Y2 O3:1;Eu3+,5;Tb3+和三聚氰胺比例为1:3:4时,所制备的FeYO3/Y2 O3:1;Eu3+,5;Tb3+粉体磁力最强,磁力饱和强度为11.3 emu·g-1.     

基于NiCo2O4纳米片电极的非对称混合电容器

The looming global energy crisis and ever-increasing energy demands have catalyzed the development of renewable energy storage systems. In this regard, supercapacitors (SCs) have attracted widespread attention because of their advantageous attributes such as high power density, excellent cycle stability, and environmental friendliness. However, SCs exhibit low energy density and it is important to optimize electrode materials to improve the overall performance of these devices. Among the various electrode materials available, spinel nickel cobaltate (NiCo₂O₄) is particularly interesting because of its excellent theoretical capacitance. Based on the understanding that the performances of the electrode materials strongly depend on their morphologies and structures, in this study, we successfully synthesized NiCo₂O₄ nanosheets on Ni foam via a simple hydrothermal route followed by calcination. The structures and morphologies of the as-synthesized products were characterized by X-ray diffraction, scanning electron microscopy, and Brunauer-Emmett-Teller (BET) surface area analysis, and the results showed that they were uniformly distributed on the Ni foam support. The surface chemical states of the elements in the samples were identified by X-ray photoelectron spectroscopy. The as-synthesized NiCo₂O₄ products were then tested as cathode materials for supercapacitors in a traditional three-electrode system. The electrochemical performances of the NiCo₂O₄ electrode materials were studied and the area capacitance was found to be 1.26 C·cm^-2 at a current density of 1 mA·cm^-2. Furthermore, outstanding cycling stability with 97.6% retention of the initial discharge capacitance after 10000 cycles and excellent rate performance (67.5% capacitance retention with the current density from 1 to 14 mA·cm^-2) were achieved. It was found that the Ni foam supporting the NiCo₂O₄ nanosheets increased the conductivity of the electrode materials. However, it is worth noting that the contribution of nickel foam to the areal capacitance of the electrode materials was almost zero during the charge and discharge processes. To further investigate the practical application of the as-synthesized NiCo₂O₄ nanosheets-based electrode, a device was assembled with the as-prepared samples as the positive electrode and active carbon (AC) as the negative electrode. The assembled supercapacitor showed energy densities of 0.14 and 0.09 Wh·cm^-3 at 1.56 and 4.5 W·cm^-3, respectively. Furthermore, it was able to maintain 95% of its initial specific capacitance after 10000 cycles. The excellent electrochemical performance of the NiCo₂O₄ nanosheets could be ascribed to their unique spatial structure composed of interconnected ultrathin nanosheets, which facilitated electron transportation and ion penetration, suggesting their potential applications as electrode materials for high performance supercapacitors. The present synthetic route can be extended to other ternary transition metal oxides/sulfides for future energy storage devices and systems.     

基于Matlab GUI的微观化学反应过程可视化设计

Based on the quasi-classical trajectory (QCT) method and Matlab GUI technology, we developed a program code for visualizing the collision process of the elementary chemical reactions of the a + bc type. The general methodology of QCT, abstraction of dynamical properties of molecular collisions and the making of Graphical User Interface are introduced. The running results of an application to the reaction F + HCl→HF + Cl is also presented. The results showed that this program could vividly demonstrate the behavior and final state of the atom-diatom collision process in animated form. Students can interact with internal MATLAB code through graphical user interface, observe the reactive behavior and final results in real-time from multiple angles, which helps students to understand the complex reaction mechanism and deepen their perceptual impression of the chemical process at a microscopic atomic/molecular level.     

半导体纳米复合材料的制备及其光电催化CO2还原

本实验通过模拟植物光合作用,设计制备了新颖的光电联合催化池3D-ZnO/Ni BiVO4/FTO,用电化学沉积法制备了泡沫镍负载的ZnO纳米棒光电阴极和BiVO4光电阳极,以0.1 mol·L^−1 KHCO3水溶液作为电解质,1 mmol·L^−1曙红Y为光敏剂,在−0.6 V硅太阳电池的电压下光电催化还原CO2得到了乙醇、乙酸和甲醇,总产率22.5μmol·L^−1·h^−1·cm^−2。实现了将太阳能贮存为化学能并减少了空气中的CO2,加深了学生对绿色化学和植物Calvin循环机理的理解。     

电化学促进铱催化乙烯基C-H键官能团化高效合成α-吡喃酮

电化学有机合成技术在过去十年来蓬勃发展,越来越受到学术和企业界合成化学工作者的青睐[1-5].跟传统化学反应相比,它的优势是利用电流代替常规的化学氧化剂或还原剂来促进化学反应,同时通过电势的调节,实现独特的反应性和化学选择性.电化学和过渡金属协同催化的碳氢键官能团化修饰(C-Hfunctionalization),不仅有效避免底物的预官能团化,而且为逆合成分析提供了可能的新颖断键方法,日益成为一种更为绿色经济的反应类型[6].     

碱金属盐催化1,2,4-三唑与α,β-不饱和酮及二酰亚胺的氮杂Michael反应

发展了一种高效的碱金属盐催化1,2,4-三唑与α,β-不饱和酮及α,β-不饱和二酰亚胺的氮杂Michael加成反应的新方法,以中等到优异的产率得到目标产物.该方法原料易得,底物普适性好,反应条件温和,易实现克级规模的制备.产物容易转化为相应的γ-氨基醇.