高密度聚乙烯/全同立构聚丙烯共混物超拉伸纤维的热行为与力学行为

用热拉法制备了高密度聚乙烯(HDPE)/全同立构聚丙烯(iPP)共混物超拉伸纤维,研究了拉伸比对其热行为及力学行为的影响,随拉伸比增加,纤维中HDPE与iPP的结晶度增大,熔融温度升高、熔程变宽;纤维中HDPE与iPP的结晶度低于其纯组分,熔融湿度与熔程基本不受组分比的影响,随拉伸比增加,纤维的模量增高,以HDPE为主的纤维的拉伸强度增大,以iPP为主的纤维拉伸强度增至一定值后,不再随拉伸比增加而增大,并有下降趋势。     

Electrospun nanofibers of poly（vinyl pyrrolidone）/Eu^3＋ and its photoluminescence properties

Nanofibers of poly（vinyl pyrrolidone） （PVP）/Eu^3＋ with diameters of 300-900 nm were prepared by using sol-gel processing and electrospinning technique. The products were characterized by scanning electron microscope （SEM）, Fourier transform infrared spectroscopy （FT-IR）, and photoluminescence （PL）. The results indicated that, Eu^3＋ was successfully embedded in the onedimensional hybrid nanofibers, and the PVP/Eu^3＋ hybrid nanofibers had favorable photoluminescence properties.     

CRYSTALLIZATION AND MELTING OF POLY（ETHYLENE OXIDE） CONFINED IN NANOSTRUCTURED PARTICLES WITH CROSS-LINKED SHELLS OF POLYBUTADIENE

Small fixed aggregates of a poly(ethylene oxide)-block-polybutadiene diblock copolymer(PEO-b-PB)in THFsolution were obtained by adding a selective solvent for PB blocks,followed by cross-linking the PB shells.Themorphologies of the nanostructured particles with a cross-linked shell were investigated by atomic force microscopy andtransmission electron microscopy.The average behaviors of the PEO crystallization and melting confined within thenanostructured particles were studied by using differential scanning calorimetry experiments.For the deeply cross-linkedsample(SCL-1),the crystallization of the PEO blocks was fully confined.The individual nanoparticles only crystallized atvery low crystallization temperatures(T_cs),wherein the homogenous primary nucleation determined the overallcrystallization rate.For the lightly cross-linked sample(SCL-2),the confinement effect was T_c dependent.At T_c(?)42℃,thecrystallization and melting behaviors of SCL-2 were similar to those of the pure PEO-b-PB diblock copolymer.At T_c>42℃,SCL-2 could form PEO lamellae thicker than those of the pure PEO-b-PB crystallized at the same T_c.     

用熔融指数仪测定聚乙烯熔体表观流动活化能实验中的有关问题

用熔融指数仪测定聚乙烯熔体表观流动活化能实验中的有关问题陈九顺（黑龙江大学化学系１５００８０）高聚物熔体的熔融指数（ＭＩ）是评价高聚物熔体流动行为的常用指标，它是在标准的熔融指数仪上测定的。所谓ＭＩ值是指高聚物熔体在规定温度、压力下，在１０ｍｉｎ内通...     

氯化聚乙烯弹性体的固相法合成

讨论了以固相法合成氯化聚乙烯（ＣＰＥ）弹性体的过程．实验结果表明，以固相氯化反应所得的ＣＰＥ，其大分子链上Ｃｌ取代基的分布比水相悬浮法更均匀．氯化过程的温度直接影响氯化速度及分子结构，如残留结晶、氯分布等．而聚乙烯颗粒表面与内部的氯化程度取决于氯化速度．大分子链上Ｃｌ取代基对邻近基团的氯化起阻碍作用     

LOW DENSITY POLYETHYLENE/CLAY NANOCOMPOSITES MODIFIED BY ETHYLENE COPOLYMERS： EFFECTS OF FUNCTIONALIZED SEGMENTS ON MORPHOLOGY

Melt extrusion was used to prepare binary nanocomposites of ethylene copolymers and organoclay and trinary nanocomposites of low-density polyethylene （LDPE）, ethylene copolymer and organoclay. X-ray diffraction （XRD） and transmission electron microscopy （TEM） were used to analyze the structure of the clay phase and the morphology of the nanocomposites. Influences of the comonomer in the copolymer and the content of the copolymer on the morphology of the resulting nanocomposites were discussed. The binary and the trinary composites may form intercalated or exfoliated structures depending on the interaction between the copolymer and the clay layers and the content of the copolymer.     

氧气氛中紫外光辐照官能化HDPE的结构与性能研究

采用FT－IR，XPS，WAXD，DXC，凝胶和表面自由能力分析，研究了氧化氛中紫外辐照官能化高密度聚乙烯（HDPE）的化学结构、晶体结构和表面自由能的变化。与空气相比，在氧气氛中紫外辐照HDPE能提高C－O，C（＝O）O和C＝O等含氧基团的引入速度，同时又能降低HDPE中的凝胶含量，在空气和氧气氛中紫外辐照后，HDPE的晶型没有发生变化，仍为正交晶系；HDPE的晶胞参数a,b,c以及（110），（200），（020），（011），（111）等晶面间距基本保持不变；HDPE的熔融温度下降，但熔融热焓升高，结晶度增大，表面自由能增大，且在氧气氛中辐照HDPE的变化幅度较大。     

基于小波变换模极大法的聚乙烯催化剂表面分形分析

运用分形和小波相结合的方法研究负载型聚乙烯催化剂(简称催化剂)表面形态. 采用小波变换模极大(WTMM)法提取了催化剂表面多尺度边缘(细节)图像, 用分形和多重分形方法研究了各尺度边缘图像中边缘点的分布情况, 并用基于小波变换模极大的多重分形谱法讨论了催化剂边缘点奇异强度的分布状况. 研究结果表明, 催化剂的较小尺度边缘图像的分维和多重分形谱可以与催化剂的表面形态和活性进行较好的关联; 高活性催化剂的基于WTMM的多重分形谱的奇异强度跨度更宽, 拥有较多具有较高奇异强度的奇异点. 基于小波和分形对催化剂表面形态的研究, 发挥了小波和分形各自的优点, 为研究物体表面形态提供了思路.     

Cr/MCM-41催化剂上的乙烯聚合行为

以纯硅ＭＣＭ４１为载体，负载Ｐｈｉｌｉｐｓ烯烃聚合催化剂活性组分Ｃｒ．ＸＲＤ及ＴＥＭ表征结果表明，所得到的Ｃｒ／ＭＣＭ４１催化剂具有良好的晶体结构和较理想的长程有序一维孔道．ＦＴＩＲ和Ｒａｍａｎ光谱表征结果表明，Ｃｒ／ＭＣＭ４１上不仅可发生乙烯聚合过程，而且形成的聚乙烯以结晶和无定形两种形态存在．乙烯聚合活性不仅与反应参数有关，而且与Ｃｒ的负载量密切相关．用于乙烯聚合后，Ｃｒ／ＭＣＭ４１催化剂仍保持其特征的晶体结构和一维孔道结构．     

超拉伸聚乙烯的弹性模量和导热性能

为了揭示聚合物分子链伸展、取向的本征特性，发展了两个新的测量方法和实验装置，用于研究拉伸比高达２００的超拉伸聚乙烯凝胶的弹性性能、传热性能和聚合物结构的关系．应用激光脉冲热致超声法给出材料拉伸方向和横向杨氏模量，应用激光脉冲光热辐射法给出拉伸方向，横向和厚度方向的导热系数．随拉伸比λ的增加，轴向杨氏模量急剧的增加，而横向的仅有少许减小．导热系数具有相似的特性．本文发现当λ＝２００时，这种拉伸取向聚乙烯的轴向模量可达钢的８０％，而导热系数甚至可达２倍，直至成为热的良导体，这是由于在高拉伸比时形成了相当数量的伸展分子链构成的针状晶体———晶桥．本文提出晶桥作为短纤维分散相的取向聚合物的结构模型，对于超拉伸聚乙烯的上述特性可以进行统一描述和定量化分析，和实验结果很好符合．