硼掺杂VO2（M）纳米棒的合成、相转变及光学特性

采用V2O5和硼酸为原材料,草酸为还原剂,在水热条件下,成功制备出硼(B)掺杂VO2(B)纳米棒,经Ar气环境退火后,得到了V1-xBxO2(M)系列样品。样品的结构、形貌和相转变温度分别用X-射线粉末衍射(XRD)仪、扫描电子显微镜(SEM)和差示扫描量热仪(DSC)等进行表征。用X-射线光电子谱(XPS)来表征样品的组份和元素的价态,样品的红外光吸收谱也被测量。结果显示,当B掺杂达到2.0at%时,V1-xBxO2(M)相的转变温度升高到75.03℃。这个升高的相转变温度可归因于B3+替代V4+引起VO6八面体的晶格畸变,以及局域晶格电子密度的降低。     

多孔复合钙铝氧化物的制备、表征及在重整生成油中的脱氯应用

采用低廉的铝盐和钙盐,通过共沉淀法制备了一系列不同CaO含量的CaO-Al₂O₃复合氧化物,并用XRD、TG-DTG、N₂吸附-脱附、SEM等手段对其进行表征。结果表明,制备的复合氧化物两相分布均匀、孔隙率较高、存在较多的介孔和大孔,比表面积也较大。采用动态吸附法将制备出的复合氧化物应用于重整生成油中氯化氢的脱除反应中,结果表明,高比表面积和大孔容的CAO-1具有最佳的HCl脱除效果,当反应温度为55 ℃、液空速为3 h^-1,重整生成油中氯含量小于等于15 ng/μL时,其氯容可达到18%。     

Mass and isotopic concentrations of water-insoluble refractory carbon in total suspended particulates at Mt.Waliguan Observatory(China)

Mass concentration and isotopic values δ¹³C and ¹⁴C are presented for the water-insoluble refractory carbon（WIRC） component of total suspended particulates（TSP）,collected weekly during 2003,as well as from October 2005 to May 2006 at the WMO-GAW Mt.Waliguan（WLG） site.The overall average WIRC mass concentration was（1183±120）ng/m³（n = 79）,while seasonal averages were 2081 ±1707（spring）,454±205（summer）,650±411（autumn）,and 1019±703（winter） ng/m3.Seasonal variations in WIRC mass concentrations were consistent with black carbon measurements from an aethalometer,although WIRC concentrations were typically higher,especially in winter and spring.The δ¹³C PDB value（-25.3 ± 0.8）%.determined for WIRC suggests that its sources are C₃ biomass or fossil fuel combustion.No seasonal change in δ¹³C PDB was evident.The average percent Modern Carbon（pMC） for ¹⁴C in WIRC for winter and spring was（67.2 ± 7.7）%（n = 29）.Lower pMC values were associated with air masses transported from the area east of WLG,while higher pMC values were associated with air masses from the Tibetan Plateau,southwest of WLG.Elevated pMC values with abnormally high mass concentrations of TSP and WIRC were measured during a dust storm event.     

Microporous Hypercross-linked Conjugated Quinonoid Chromophores of Anthracene: Novel Polymers for CO2 Adsorption

Microporous hypercross-linked conjugated quinonoid chromophores represent a novel class of amorphous polymers, synthesized by the reaction of anthracene with dimethoxy methane in the presence of FeCl3 catalyst. Their N2 adsorption isotherms confirm their microporous nature. Diffuse reflectance UV-Visible(DRS UV-Vis) spectroscopy confirms their matrix built with the conjugated quinonoids by their broad light absorption characteristics extending from 1000 nm to 200 nm with the absorbance maximum close to 400 nm. The catalyst cross-linked anthracene with ―CH2― bridges and subsequently dehydrogenating them to form quinonoids. Their Fourier transform infrared(FTIR) spectra showed their characteristic quinonoid vibrations between 1600 and 1700 cm-1. The synthesis of polymers was carried out at 30, 40, 50, 60, 70 and 80 ℃, but the quinonoid content of the polymer obtained at 80 ℃ was higher than that of the others. Their scanning electron microscopy(SEM) images showed microspheres of 1 to 5 μm size built with tiny particles. Their surfaces were not smooth. The polymer synthesized at 80 ℃ showed 5.1 wt% CO2 sorption at 25 ℃ and 0.1 MPa, but when it was recross-linked, the CO2 sorption increased to 8 wt%. Hence, hypercross-linked conjugated quinonoid chromophores of anthracene are good for sorption of CO2.     

二维CAS小波求解变厚度功能梯度简支梁的弹性静力学问题

利用正交的二维CAS小波方法数值求解了变厚度功能梯度简支梁的二维弹性力学问题,此求解过程相对简单,易于编程,具有可推广性.     

L-fuzzy层双保序算子空间中的(ω_α,υ_α)-仿紧性

首先在层双保序算子空间中引进了两种(ω_α,υ_α)-仿紧性,证明了它们都是好的推广.其次,给出了它们的若干刻画与性质,并指出了它们保持若干拓扑不变性质.最后,讨论了(ω_α,υ_α)-仿紧性、(ω_α,υ_α)-分离性以及(ω_α,υ_α)-紧性之间的关系.     

减反膜对单晶硅太阳能电池性能的影响分析

在太阳能电池效率的评价中，电池材料、掺杂浓度、扩散长度等都是比较重要的参数，合理地改变相关参数可以优化太阳能电池的性能，提高电池效率。此外，在太阳能电池表面镀一层具有减反作用的光学薄膜（简称减反膜）也是提高电池效率的重要手段。以提高电池效率为目标，对单晶硅太阳能电池的掺杂浓度和扩散长度等微观参数进行计算优化，分析了掺杂浓度和扩散长度变化对电池效率的影响。并在此基础上分析了不同类型的减反膜对于电池效率的影响，给出了最佳减反膜材料及其膜系厚度，并且结合镀膜后电池量子效率的变化验证了其准确性。结果表明，在优化电池掺杂浓度和扩散长度的基础上，选择合适的减反膜，电池效率最高可达20.35%，相比于优化前提高了8.25%。     

近紫外激发Gd2ZnTiO6∶Eu3+,Li+红色荧光粉的制备及荧光性能

采用溶胶-凝胶法成功制备出系列Eu³⁺掺杂和Li⁺、Eu³⁺共掺杂Gd₂ZnTiO₆红色荧光粉,并研究Li⁺、Eu³⁺掺杂对样品的晶体结构、微观形貌及发光性能的影响。结果显示,所制备的Gd₂ZnTiO₆∶Eu³⁺,Li⁺(GZT∶Eu³⁺,Li⁺) 荧光粉为双钙钛矿结构,属于单斜晶系(空间群:P2₁/n),大小为10 μm的无规则形状的颗粒。在395 nm近紫外光的激发下,GZT∶Eu³⁺的发射光谱展示出典型的Eu³⁺线状特征光谱,发射峰中心位于615 nm处,归属于Eu³⁺的⁵D₀→⁷F₂跃迁。Eu³⁺的最佳掺杂浓度为0.07(摩尔分数),样品显示明显的浓度猝灭效应,其机制为电偶极子-电偶极子(d-d)相互作用。此外,研究还发现,Li⁺掺杂对样品的晶体结构、微观形貌没有影响,但是一定量的Li⁺掺杂可以显著增强样品的荧光强度。当Li⁺浓度为0.05时,荧光粉发射主峰强度增强程度最大,提高至原来的4.3倍,说明通过Li⁺、Eu³⁺共掺杂可以获得高亮度的GZT红色荧光粉。GZT∶0.14Eu³⁺,0.05Li⁺荧光粉的CIE色坐标为(0.631 1,0.375 3)与标准红光色坐标(0.670,0.330)较为接近,是一种潜在的LED用红色荧光粉。