Nd∶Y_3Al_5O_(12)单晶及纳米粉体的Raman光谱分析

测量了YAG（Y3Al5O12）/Nd∶YAG单晶、Nd∶YAG前驱物及其在不同温度下煅烧获得粉体的拉曼光谱,对谱峰的振动模式进行了指认,对结果进行了分析。Nd∶YAG前驱物在煅烧时,有一个由非晶态向晶态的转化过程;700℃下烧结前驱物获得非晶态产物的结构中含有AlO4四面体结构;随着煅烧温度的升高,拉曼光谱的变化主要表现在两个方面：一是谱峰半高宽（FWHM）减小,谱峰强度增大;二是一些拉曼光谱谱峰发生了频移,这是纳米多晶粉体的界面组元的有序度提高所致。另外,800℃下煅烧获得的Nd∶YAG纳米粉体的晶格振动模式与Nd∶YAG晶体的晶格振动模式存在差异,这是纳米多晶粉体的界面组元的贡献所致。     

共格外延的La_(0.7)Sr_(0.3)MnO_3薄膜的应变弛豫

厚度为7～100nm La0.7Sr0.3MnO3(LSMO)薄膜是由脉冲激光法生长在(001)(LaAlO3)0.3(Sr2AlTaO6)0.7(LSAT)衬底上.薄膜的结构演变是由高分辨X-射线ω-摇摆曲线及倒易空间(103)反射来表征.我们的结果表明所有的LSMO薄膜是共格生长在LSAT(001)上.对厚度大于(或等于)22nm的LSMO薄膜既显示可调制的单斜(MA)结构,也包含切应变弛豫诱导的有序畴结构和平面内超格子.薄膜的厚度依赖的结构畴宽,以及切应变对薄膜居里温度Tc的影响被仔细研究.作为对比,晶格失配对LSMO薄膜中周期畴形成的影响也被讨论.     

Mn掺杂对多铁性BiFeO_3薄膜铁电性能以及漏电流的影响

本文利用脉冲激光沉积技术在(LaAlO3)0.3(Sr2AlTaO6)0.7(001)衬底上生长了BiFe1-xMnxO3(x=0～5%)外延薄膜,研究了Mn掺杂对BiFeO3(BFO)薄膜结构、铁电特性和漏电流的影响.XRD和SEM结果表明薄膜具有良好的结晶质量.漏电流测量显示Mn掺杂有效地减小了BFO薄膜的漏电流密度,因而在室温下5%Mn掺杂的BFO薄膜能够获得饱和的电滞回线.XPS分析证明,Mn掺杂改善BFO薄膜性能的可能原因在于其极大地减少了BFO薄膜中的Fe2+离子.     

弹性反冲探测分析技术在材料氦行为研究中的应用

弹性反冲探测分析技术（ERDA）对轻元素的测定具有灵敏度高、包含深度信息的优势,因此在材料氦行为研究中发挥着重要作用。镍基哈氏N合金被认为是未来熔盐堆的结构材料,氦脆是其服役性能下降的主要因素之一。利用掠入射模式的ERDA,解析了哈氏N合金样品中的氦原子浓度及其分布,但仅局限于0~175 nm深度范围内。结果表明:在800℃的退火条件下,距离样品辐照表面~33 nm深度区域内,出现了氦原子逃逸现象。更高温度的退火（1 050℃）可加剧氦原子的逃逸,但样品中仍有氦原子滞留。另外,采用透射式的ERDA,极大地扩大了对氦原子分析的深度范围,得到了纯镍薄膜在0~950 nm深度区域内的氦原子浓度分布。这表明将块体材料制备成薄膜样品,利用透射模式的ERDA,将可以得到氦原子在更大范围内的扩散、逃逸行为。Since the elastic recoil detection analysis (ERDA) technique has the advantages of high sensitivity and deep information in analyzing the light elements, it plays an important role in the study of helium behavior in materials. Helium embrittlement is one of the main reasons for the degradation of the Hastelloy N alloy, which has been considered as the promising candidate structural material for the further molten salt reactor. In this work, the profile of helium concentrationin sample of Hastelloy N alloy was analyzed by ERDA experiments applying grazing-incidence geometry. However, the result was limited within the depth range of 0~175 nm, and it shown that helium atoms escaped in the range from the irradiated surface of the sample to the depth of ~33 nm when annealing the sample at 800℃ The annealing at higher temperature (1 050℃) increased the escape of helium atoms, but a small fraction of helium atoms still trapped in the sample. In addition, the profile of helium concentration was obtained in the helium-irradiated pure nickel film in the depth range of 0~950 nm, using the ERDA experiments in transmission geometry. This indicates that the diffusion behavior of helium atoms in bulk samples can be completely obtained using the ERDA experiments in tranmission geometry if the bulk material can be prepared into a thin film sample.     

合金凝固过程的数学模型

对合金凝固过程的数值研究自80年代以来取得了很大的发展,文中讨论了当前针对宏观过程的主要的数学模型,介绍了它们的基本思想,求解方法,以及优缺点.指出了微观过程对宏观行为的重要影响及在模型构造过程中考虑宏观-微观耦合的必要性,并针对在工程实际中的应用和以后的研究进行了有关的探讨.      

全超导托卡马克极向场超导线圈的失超检测

EAST装置做为全超导托卡马克装置,其纵场和极向场线圈全部由超导磁体组成,所以进行安全,准确,有效的超导线圈的失超保护是装置安全运行的首要环节.由于等离子体电流的建立必须由极向场线圈系统提供极快速的磁通变化,随之产生较高的交流损耗使得极向场线圈很容易发生失超.如何对快速交变脉冲磁场下的超导线圈进行有效的失超检测,这在世界上也无先例可循.EAST装置的失超检测系统经过几十轮单饼超导线圈实验及多轮装置正式放电实验后逐步建立和完善起来,并已通过工程验收满足了装置实验运行要求.本文主要介绍了EAST装置失超检测系统的基本结构和检测原理,重点阐述了极向场超导磁体失超检测的设计方法及实验结果。