纳米TiO2-MnO2复合材料的合成、结构与光催化性能

以TiCl₄, MnSO₄·H₂O, NH₃·H₂O为原料, 把TiCl₄和MnSO₄·H₂O按照化学计量比共同水解, 得到的水合氧化物中间体放入高压釜中在150℃, 0.5 MPa下进行反应, 经过滤、洗涤、烘干, 得到纳米TiO₂-MnO₂复合材料. XRD结合DTA-TG分析证明产品为非晶态, 780℃以上转变为金红石型的Ti_1-xMn_xO₂. TEM形貌观察, 粒子基本为球形, 平均粒径20 nm; 将样品均匀分散在甘油-水混合液中, 利用UV-1200紫外-可见分光光度计测试了样品的光吸收性能, 发现该纳米复合材料秉承了纳米TiO₂和MnO₂两者的优点, 对紫外光和可见光均有很强的吸收. 利用该纳米复合材料作为光催化剂对有机染料溶液进行了降解实验, 发现在日光照射60 min后, 对酸性红B、酸性黑234以及两者混合染料的降解率可达100%.     

NH3在Ni(111)面吸附的理论研究

The bonding and configuration of the chemisorption of NH_3 at the on-top and hollow sites of Ni(111) surfaces are calculated and discussd by use of MO theory and energy band theory. The results show that the density of state and crystal orbital overlap population of the adsorption state at the on-top site have superiority over those of hollow site.     

B环取代的新型磺烷酮衍生物的合成及杀菌活性

植物抗毒素;构效关系;B环取代的新型磺烷酮衍生物的合成及杀菌活性     

电极/碱性聚电解质界面的微分电容曲线和零电荷电位测定（英文）

碱性聚合物电解质作为现代碱性氢氧燃料电池的核心组成部分,其单离子导体的特性使得“电极/碱性聚电解质”界面的性质与“电极/溶液”界面有所不同。本文使用微电极,运用循环伏安、电化学交流阻抗以及浸入法等方法,测定了电极/碱性聚电解质界面的微分电容曲线和零电荷电位。该界面的微分电容曲线呈“U”状,且存在局域极小值,该极小值所对应的电位与浸入法测得的零电荷电位数值一致。单离子导体的特性使得“电极/碱性聚电解质”界面在零电荷电位两侧表现出不同的电化学极化行为。     

双温区热扩散掺杂Fe2+∶ZnSe激光晶体的制备及激光输出性能

本文以CVD ZnSe晶片为基质材料,以FeSe粉末为掺杂物,采用双温区热扩散掺杂技术获得了尺寸为Ø22 mm×4 mm的Fe²⁺∶ZnSe激光晶体。通过二次离子质谱(SIMS)测试该晶体样品表面铁离子浓度为3.43×10¹⁸ cm^-3,并通过X射线光电子能谱(XPS)分析了晶体样品中铁元素的离子价态。采用UV/Vis/NIR分光光度计和傅里叶红外光谱仪测试了Fe²⁺∶ZnSe激光晶体的透过谱图。测试结果显示,在3.0 μm处出现了明显的Fe²⁺吸收峰,峰值透过率为5.5%。以波长为2.93 μm的Cr, Er∶YAG激光器为泵浦源,温度77 K时抽运尺寸10 mm×10 mm×4 mm的 Fe²⁺∶ZnSe晶体,获得了能量为191 mJ、中心波长4.04 μm的中红外激光输出,光光转换效率13.84%。     

指示离子Cd2+测定维生素B1的方波极谱法研究

根据Cd2+对维生素B1(VB1)的指示作用,建立了用方波极谱法测定VB1的新方法.在氨-氯化铵缓冲溶液中,VB1不出峰,加入Cd2+后在-0.856 V(vs.SCE)处出现1个固定还原峰,并在-0.360 V(vs.SCE)处可见1个峰高与VB1浓度呈正比的还原峰.依据该还原峰峰高的变化规律可测定VB1的含量.VB1在1.35μg/mL~1.35 mg/mL的范围内有良好的线性关系,检出限可达0.13μg/mL,r为0.999 7.平均加样回收率为99.6%(n=9),RSD为0.9%.利用方法测定营养胶囊中VB1的含量,效果理想,可作为VB1含量的测定方法.     

Hydrothermal synthesis, structure and photocatalytic property of nano-TiO_2-MnO_2

TiCI4 and MnSO4.H2O as raw materials are hydrolyzed stiochiometrically, following the intermediate of oxide hydrating reacts at 150℃, 0.5 MPa in high-pressure reactor, after filtering, washing and drying, nanometric TiO2-MnO2 (Ti1-xMnxO2) is prepared. The effects of the reaction temperature and time on nanometric TiO2-MnO2 are also discussed. XRD shows that the product is TiO2-MnO2 with amorphous phase. After being sintered at above 780℃, it transfers into Ti1-xMnxO2 with a rutile structure. TEM shows that TiO2-MnO2 is the spherical particle. And the average diameter of the particles is 20 nm. The optical absorbance was determined by UV-265 spec-trophotometer after dispersing the sample in the mixture of water and glycerol with the ratio of 1 : 1 equably. It is found that the nano-material possesses the advantages of both nano-TiO2 and nano-MnO2, and it has strong absorption in the UV and visible region. Photodegradation of dyes in an aqueous solution is investigated using nanometricTiO2-MnO2 as a pho     

纳米TiO2-ZnO复合材料的合成、结构与光催化性能

二氧化钛是一种重要的半导体光催化材料，它具有光催化降解有机物活性高、化学性质稳定、耐化学和光化学腐蚀以及无毒等特性，因而在污水处理及空气净化等方面有着重大的潜在应用价值。然而二氧化钛是宽禁带材料，仅能吸收太阳光谱的紫外光部分，太阳能利用效率低，通常需要用紫外光     

纳米TiO2-MnO2复合材料的合成、结构与光催化性能

以TiCl_4,MnSO_4·H_2O,NH_3·H_2O为原料,把TiCl_4和MnSO_4·H_2O按照化学计量比共同水解,得到的水合氧化物中间体放入高压釜中在150℃,0.5MPa下进行反应,经过滤、洗涤、烘干,得到纳米TiO_2-MnO_2复合材料。XRD结合DTA-TG分析证明产品为非晶态,780℃以上转变为金红石型的Ti(1-x)Mn_xO_2。TEM形貌观察,粒子基本为球形,平均粒径20um;将样品均匀分散在甘油-水混合液中,利用UV-1200紫外-可见分光光度计测试了样品的光吸收性能,发现该纳米复合材料秉承了纳米TiO_2和MnO_2两者的优点,对紫外光和可见光均有很强的吸收。利用该纳米复合材料作为光催化剂对有机染料溶液进行了降解实验,发现在日光照射60min后,对酸性红B、酸性黑234以及两者混合染料的降解率可达100％。     

新型黄烷酮类衍生物的合成、杀菌活性及定量构效关系研究

设计合成了14个含不同性质取代基的黄烷酮类化合物,并采用核磁共振氢波谱、质谱和元素分析对所有化合物的结构进行了表征.在系统测定化合物对水稻稻瘟病抑制活性的IC₅₀值的基础上,采用Hansch-Fujita方法和CoMFA方法对其定量结构活性关系进行了系统研究,结果发现,化合物的疏水性质、极化效应以及最高空轨道能级对杀菌活性有重要影响,化合物的疏水参数越小,分子越容易极化,则化合物的杀菌活性越高.此外,最高空轨道能级越低,化合物越容易接受电子,其杀菌活性也相应提高.通过考察∑π、clgP以及lgK与化合物杀菌活性的相关性,发现lgK能较好地反映该类化合物的疏水效应.三维定量构效关系研究表明,B环2,3,4位上含有较大体积的取代基,而6位含较小体积的取代基,有利于提高其杀菌活性.