SYNTHESIS AND CHARACTERIZATION OF ORGANO-SOLUBLE FLUORINATED POLYIMIDES FROM 4,4′-BIS(3-AMINO-5-TRIFLUOROMETHYLPHENOXY)-BIPHENYL AND VARIOUS AROMATIC DIANHYDRIDES

An aromatic diamine monomer, 4,4′-bis(3-amino-5-trifluoromethyl phenoxy)-biphenyl (TFBPDA), was synthesized via the nucleophilic displacement reaction of 3,5-dinitrobenzotrifluoride and 4,4′-biphenol. The monomer was reacted with various aromatic dianhydrides via the high temperature polycondensation procedure to provide a series of polyimides. The polyimides, PI-1 to PI-4, show good solubility not only in aprotic solvents, such as N-methyl-2-pyrrolidinone and N,N-dimethylacetamide, but also in many common solvents, such as m-cresol, chloroform and cyclopentanone. PI-4, derived from 4,4′-(hexafluoroisopropylidene)diphthalic anhydride and TFBPDA, was even soluble in toluene. Moreover, PI films exhibit good thermal stability, outstanding transparency in the visible light region and acceptable mechanical and electrical properties. The excellent combined properties of the polyimides make them as a good candidate for fabricating microelectronics.     

含二氮杂萘酮结构磺化聚酰亚胺共聚物的合成及其膜性能研究

将磺化二胺单体4,4′-二(4-氨基苯氧基)联苯-3,3′-二磺酸(BAPBDS),含二氮杂萘酮结构的二胺1,2-二氢-2-(4-氨基苯基)-4-[4-(4-氨基苯氧基)-苯基]-二氮杂萘-1-酮(DHPZDA)和1,4,5,8-萘四甲酸二酐(NTDA)进行缩合聚合反应,通过改变磺化二胺单体BAPBDS的含量,合成了一系列不同磺化度的聚酰亚胺(SPIs).采用FT-IR,1H-NMR表征了聚合物的结构,热重分析仪(TGA)研究了聚合物的耐热稳定性.以间甲酚为溶剂,通过溶液浇铸法成膜研究了该系列聚合物膜的性能.结果表明,与其它磺化聚酰亚胺相比,该系列磺化聚酰亚胺的溶解性以及在高温下(80℃)水解稳定性有较大提高.     

耐超高温双酮酐型聚酰亚胺的合成及性能

以4,4'-对苯二甲酰二邻苯二甲酸酐(TDPA)为芳二酐单体,对苯二胺(PPD)为芳二胺单体,经低温溶液缩聚制得成膜性能优良的高相对分子质量聚酰胺酸(PAA),再经过热亚胺化制备双酮酐型聚酰亚胺(PI)薄膜。 采用傅里叶变换红外光谱仪(FT-IR)、广角X射线衍射(WAXD)、差示扫描量热仪(DSC)、动态热机械分析仪(DMA)、热重分析仪(TGA)、紫外-可见分光光度计(UV-Vis)及力学性能等技术手段表征了聚酰亚胺膜的结构和性能,考察了不同亚胺化温度对合成的双酮酐型聚酰亚胺膜性能的影响。 结果表明,经程序升温至320 ℃能使PAA热亚胺化基本趋于完成。 PI薄膜为部分有序聚集态结构,玻璃化转变温度(T_g)为298 ℃,具有优异的热性能,热失重温度(T_5%)为523 ℃。 拉伸强度达到130 MPa,弹性模量为5.77 GPa。 PI薄膜紫外光透过截止波长为375 nm,在可见光区具有良好的透光性能及耐溶剂性能。     

SYNTHESIS AND CHARACTERIZATION OF HETEROAROMATIC POLYMERS CONTAINING PYRIDINE MOIETIES

The progress on the molecular design, synthesis and characterizations of some kinds of pyridine-containing heteroaromatic polymers in main chain were reviewed in this paper, they would include polyimides (PIs), polypyrrolones (PPYs), poly(pyrrolone-imide)s (PPIs), and poly(pyrrolone-benzimidazone)s (PPBs) containing pyrldine moieties. The pyridine-containing polymers reported all exhibit good processability, excellent thermal properties and mechanical properties. However, the contribution of pyridine ring to polymers properties is still need to research further, the heteroarornatic polymers containing pyridine moieties have focused by more and more researchers.     

Novel hyperbranched polyimides from 2,6,12-triaminotriptycene

The monomer 2,6,12-triaminotriptycene was synthesized and the structure was confirmed by IR and 1H NMR spectra. Hyperbranched polyimides modified with different terminal groups were obtained from precursors, anhydride- and aminoterminated hyperbranched poly（amic acid）s from polymerization of A2 ＋ B3 system. From gel permeation chromatograrn （GPC） characterization, representative products had high molecular weight. All polymers had good solubility in CHCl3, DMF and tetrahydrofuran （THF）, and performed no detective Tgs in the range of 50-300 ℃ and high Tds above 455 ℃ when 5% weight loss.     

含氟聚酰亚胺接枝低聚倍半硅氧烷制备超低介电材料

含氟聚酰亚胺接枝低聚倍半硅氧烷制备超低介电材料;介电常数;纳米复合材料;低聚倍半硅氧烷;接枝共聚;含氟聚酰亚胺     

一步法合成高T_g可溶含偶氮三嗪发色团的新型侧链含氟聚酰亚胺

采用一步法合成了一系列侧链含偶氮三嗪发色团的新型含氟聚酰亚胺FPI(x),并研究其溶解性能、热性能以及光学性能.该系列聚酰亚胺具有优良的溶解性能,不仅溶于NMP,DMAc,DMF,DMSO等强极性非质子性溶剂,而且还溶于THF和乙二醇单甲醚等低沸点溶剂.FPI(x)系列共聚聚酰亚胺具有较高的玻璃化转变温度(T_g,在544～562K之间),且与主链中染料发色团的含量无关.所有聚酰亚胺都表现出优良的高温稳定性,其5%热失重温度(T₅)比T_g高出100K以上,基本能满足电场极化对聚合物材料热稳定性的要求.另外,FPI(x)系列聚酰亚胺的紫外截止吸收波长小于500nm,即在大于500nm波长范围内基本透明.其面内折光指数n_TE随着染料发色团含量的增加而逐渐增加.     

高度可溶聚苝酰亚胺材料的合成及性能研究

聚酰亚胺是一类具有优异综合性能的聚合物材料 [1,2 ] .近年来 ,合成含荧光染料的可溶性聚酰亚胺材料在聚合物化学领域引起了广泛兴趣 [3～ 11] ,人们期望这类聚合物材料会比其小分子材料具有更加优越的性能 .小分子酰亚胺荧光染料具有极高的荧光量子效率、光化学和热稳定性 ,可广泛应用于光学开关[12 ] 、电致发光器件 [13,14 ] 和太阳能转换器 [15] 等领域 ,但是由于的大π键平面共轭结构 ,使得材料的溶解性能极差 ,难以加工 .最近 ,本实验室通过合成含叔丁基的芳香二胺 [4,4′-亚甲基双 ( 2 -叔丁基苯胺 ) ]与各种芳香四酸二酐反应…     

聚酰亚胺材料溶解性能的研究进展

归纳了在利用分子设计理论制备可溶性聚酰亚胺的研究过程中,聚酰亚胺的溶解性能与单体分子结构的关系、在制备可溶性聚酰亚胺的过程中用于改善聚酰亚胺溶解性能的几种常用的分子设计手段。     

气体分离用PI/TiO2纳米复合膜的制备

聚酰亚胺/TiO2;量子尺寸效应;气体分离器;气体分离用PI/TiO2纳米复合膜的制备