PLA/EMAG共混物的制备与表征

通过熔融共混挤出法制备了不同乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯(EMAG)含量下的聚乳酸(PLA)/EMAG共混物,考察共混体系中EMAG与PLA基体之间的相互作用,研究了PLA/EMAG共混物的结晶性能、力学性能、熔体指数、加工性能以及热稳定性.表征结果显示:EMAG中的环氧基团与PLA的端羟基或端羧基发生化学反应,形成反应性共混体系,PLA/EMAG共混物的韧性较纯PLA有大幅提高,在EMAG含量为15;时达到最大.     

SYNTHESIS OF MACROPOROUS COPOLYMER OF VCA AND DVB

The reactivity ratios of vinyl acetate(VAc) and divinyl benzene (DVB) were calculated from the Q and e values.The possibility of the copolymerization of these two monomers was predicted and the copolymerization was carried out by suspension polymerization technique in the presence of pore producing agent (toluene and gasoine).The relative ratio of acetoxy group and benzene ring in the copolymer were monitored by IR measurement during the polymerization.The variation of pore properties,such as spectific surface area,porosity and average pore diameter,with polymerization time were determined.The copolymers at various polymerization time were alcoholyzed and thus the variation of the hydroxyl group content with polymerization time was studied.     

热等离子体裂解天然气制备C2烃

采用氮气热等离子体来裂解天然气制备乙炔乙烯,着重研究了天然气转化率和乙炔、乙烯收率随氮气流量和天然气流量的变化.结果表明,天然气流量与氮气流量之比为11时,可得到较好的结果.当等离子体功率为15kW、天然气流量为3Nm3*h-1、氮气流量为3Nm3*h-1时得到最好的结果.这时天然气转化率为57%,乙炔、乙烯的收率分别为34%和9%;乙炔在反应气中的体积浓度为7.5%,与部分氧化法相似;扣除不参加反应的氮气,乙炔在气相产品中的体积浓度为13.2%,与热力学平衡计算结果基本符合.     

高抗冲聚丙烯序列结构的综合表征

用高分辨＾１３Ｃ ＮＭＲ、ＦＴＩＲ等手段获得了高抗冲聚丙烯的组成和序列分布等链结构方面的信息。用ＤＳＣ、ＷＡＸＤ等方法研究了它们的结晶行为、熔融转变及晶体结构，多种方法相结合有效地表征了高抗冲聚丙烯的序列结构。     

Three Stilbene Tetramers from the Roots of Caragana sinica

Three stilbene tetramers, carasinols A-C (1-3), along with three known substances, leachianol C, cararosinol A and stenophyllol B, were isolated from the roots of Caragana sinica. Their structures were elucidated by spectroscopy. It was found that compounds isolated except for stenophyllol B stimulated the proliferation of cultured osteoblasts.     

取代基效应(SCS)与乙烯-α-烯烃共聚物的序列结构Ⅲ.定量分析

本文在分析乙烯-α-烯烃共聚物序列结构时,把代表共单体反接单元的亚甲基(CH₂)βγ和γδ分别归属给了二元组VV和三元组EEV。与此同时,CH₂-δδ和δδ⁺归属给了二元组EE。表征乙烯长序列的CH₂-δ⁺δ⁺分属二元组EE和三元组EEE,对应峰强度在EE和EEE之间的分配是处理序列分布的关键。在本文中运用序列结构的Bovey关系和Randall统计进行演算,求得了修正值△的数学表达式,严格解和近似解。在规则链条件下得到的近似解与G.J.Ray的结果完全相同。当共单体含量较少时,谱峰强度Iδ⁺δ⁺的分配接近相等。在二元组和三元组的水平上,乙烯-α-稀烃共聚物的¹³C NMR谱中共有十三个峰,属于CH₂的有十个,属于CH的有三个。利用这些谱峰的强度数据可以建立一套计算公式,由此提供共聚物序列结构的全部信息。因此这是一个研究乙烯-α-烯烃共聚物序列结构的普适方法。     

聚偏氟乙烯辐射效应的研究——II.晶区辐射损伤点的研究

研究了聚偏氟乙烯 (PVDF)晶体结构与辐射效应的关系 .利用不同的热处理条件 ,获得了 7种不同规整性、不同结晶度的样品 ;通过对其辐射效应的研究 ,探讨了材料结晶区和晶区内不同部位的辐射效应以及这些不同的结构对材料辐射效应的影响 .使用示差扫描量热分析 (DSC)测量样品零熵产生相变温度、结晶度等随吸收剂量的改变 ,以及不同退火条件样品的辐射效应 .讨论了PVDF样品晶体辐射损伤与样品结构的关系 .利用电子自旋共振谱仪 (ESR)测量不同辐照后样品残余自由基的浓度及这些残余自由基加热条件下的不同命运 .结合DSC分析及X射线衍射分析得到晶体辐射损伤是从晶体表面折叠圈区和晶体茎杆内部缺陷区同时开始的结论     

可溶于水的钉原子簇新体系催化丙烯和乙烯的醛化

1.前言 近年来,随着金属簇合物合成化学的迅速发展,已出现了一类可溶于水的金属簇合物。分子中含有55个金属原子的可溶于水的簇合物Au_(55)[Ph_2PC_6H_4SO_3Na)_12Cl_6已被合成和表征。金属簇合物被期待发挥特异的催化性能。用水作反应溶剂,好处很多。水不仅便宜易得,反应原料气无须经除水净化,反应体系简单,而且某些反应,例如水煤气变换和