Effect of the extent of reduction of V2O5 on the adsorption of propylene and the oxidative dehydrogenation of propane to give propylene on V2O5 and V2O5/TiO2-SiO2

An increase in the propylene output in the oxidative dehydration of propane on V₂O₅/TiO₂-SiO₂ was observed after prior reduction of V₂O₅ in the reaction mixture to V₂O₄, which reduces the destructive chemisorption of propylene. A low titanium dioxide content in TiO₂-SiO₂ hinders the deep reduction of V₂O₅ to V₂O₃, which reduces the conversion of propane. __________ Translated from Teoreticheskaya i éksperimental’naya Khimiya, Vol. 43, No. 6, pp. 373–378, November–December, 2007.     

液膜法分离钒(Ⅳ)的研究

本文用P204-兰113A-煤油组成的滤膜体系处理钒(Ⅳ)的溶液,并考察了表面活性剂、载体、外相pH值、内相酸度、起始钒(Ⅳ)浓度以及乳水比等因素对分离的影响。     

戊二酸钛（Ⅲ）与氮化钛的制备

戊二酸钛（Ⅲ）与氮化钛的制备陈吉书，吕真国，徐其亨（曲靖师专化学系曲靖）（曲靖地区环境监测站曲靖）（云南大学化学系昆明６５００９１）关键词戊二酸钛，氮化钛，热分解氮化钛具有硬度大、熔点高、耐磨、耐腐蚀、导电性好、美观（金黄色）等优点，具有重要的工业用...     

Vanadium Doped Sol-Gel TiO2 Coatings

A study of the experimental conditions required to obtain vanadium doped sol-gel TiO2 coatings is presented. Tetraethyl orthotitanate was employed as the TiO2 source and VCl3, VOSO4 · H2O and VOSO4 dissolved H2SO4 where employed as vanadium sources.Dip coating has been used to produce coatings on silicon wafers, spectral carbon electrodes and titanium electrodes. Both supported and unsupported films have been studied by UV-Vis spectra, IR spectroscopy and X-ray diffraction (XRD). The measurements have been made on samples as prepared and treated thermally at temperatures between 100°C and 300°C. The thermal treatment temperatures have been established from DTA/TGA measurements.The vanadium doped sol-gel TiO2 coatings have been tested as sensors for redox potential measurements in electrochemical processes. The influence of both the thickness of films and the nature of substrate has been investigated.     

正丁烷氧化制顺酐流化床催化剂的性能

 考察了前驱体制备过程中水合肼／五氧化二钒摩尔比（以下简记\r\n为n（N2H4）／n（V2O5））对催化剂性能的影响．由较高的n（N2H4）\r\n／n（V2O5）比制得的催化剂，其（VO）2P2O7相含量较多，正丁烷转化\r\n率较高．随着n（N2H4）／n（V2O5）比的减小，δ－VOPO4相的含量逐\r\n渐增多，正丁烷转化率随之升高；而顺酐选择性开始时升高，达到最大\r\n值后逐渐降低．在n（N2H4）／n（V2O5）＝0．34时制备的催化剂最佳\r\n，在丁烷浓度为4．0％、空速为500h－1及反应温度为420℃的反应条件\r\n下，顺酐收率可达49．74％．本文中细粒床催化剂有较大的操作弹性．     

Dispersion state and catalytic properties of vanadia species on the surface of V_2O_5/TiO_2 catalysts

The dispersion state and catalytic properties of anatase-supported vanadia species are studied by means of X-ray diffraction (XRD), laser Raman spectroscopy (LRS), H2 temperature-programmed reduction (TPR) and the selective oxidation of o-xylene to phthalic anhydride. The almost identical values of the experimental dispersion capacity of V2O5 on anatase and the surface vacant sites available on the preferentially exposed (001) plane of anatase suggest that the highly dispersed vanadium cations are bonded to the vacant sites on the surface of anatase as derived by the incorporation model. When the loading amount of V2O5 is far below its dispersion capacity, the dispersed vanadia species might mainly consist of isolated VOx species bridging to the surface through V-O-Ti bonds. With the increase of V2O5 loading the isolated vanadia species interact with their nearest neighbors (either isolated or polymerized vanadia) through bridging V-O-V at the expenses of V-O-Ti bonds, resulting in the increase of the ra     

CO2氧化异丁烷制异丁烯用Pd/V2O5-SiO2催化剂

 利用表面化学反应改性法制备了不同V2O5负载量的V2O5-SiO2表面复合物载体,进而采用等体积浸渍法制备了负载型Pd催化剂. 用N2吸附、 X射线衍射、透射电镜、 X射线光电子能谱、程序升温脱附、化学吸附-红外光谱和微反技术对系列Pd/V2O5-SiO2催化剂的比表面积、晶相结构、价态、异丁烷的化学吸附性能和CO2部分氧化异丁烷制异丁烯的催化性能进行了研究. 结果表明, Pd/V2O5-SiO2催化剂中的钒以V5+形式存在, V5+在催化剂表面形成活性位V=O, 其中 V=O 晶格氧与 i-C4H10分子的-CH3 和-CH 中的H产生化学吸附作用; 催化剂中金属Pd与V4+协同作用使CO2在催化剂上产生了卧式吸附态; 晶格氧参加了催化氧化反应,催化剂中 V5+←→V4+ 的变化构成了催化反应的氧化还原过程. 在525 ℃, CO2/i-C4H10体积比为1和空速为 1200 h-1的条件下,以Pd/25%V2O5-SiO2为催化剂时异丁烷转化率为22.8%, 异丁烯选择性为89.1%.     

Dehydrogenation of isobutane in the presence of carbon dioxide over supported vanadium oxide catalysts

Summary The dehydrogenation of isobutane to isobutene in the presence of carbon dioxide was carried out over supported vanadium oxide catalysts. The influence of the support on the catalytic performance was investigated. The isobutane conversion and isobutene selectivity in the presence of carbon dioxide were compared with the results obtained during the dehydrogenation reaction in the presence of helium (inert gas). The catalysts were characterized by temperature-programmed techniques (TPR, TPD-NH₃, TPD-CO₂).     

High temperature enthalpy and heat capacity of GaN

The heat capacity and the heat content of gallium nitride were measured by calvet calorimetry (320-570 K) and by drop calorimetry (670-1270 K), respectively. The temperature dependence of the heat capacity in the form C_pm=49.552+5.440×10⁻³T−2.190×10⁶T⁻²+2.460×10⁸T⁻³ was derived by the least squares method. Furthermore, thermodynamic functions calculated on the basis of our experimental results and literature data on the molar entropy and the heat of formation of GaN are given.     

Li/富锂钒青铜(Li_6V_6O_(15))二次电池正极材料研究

近年来,人们对二次锂电池的正极进行了不少研究。许多过渡金属氧化物或硫化物,如V_6O(13),Li_(1+x)V_3O_8,TiS_2,MoS_2等被认为是较好的正极材料。Pistoia等研究了Li_(1+x)V_3O_8钒青铜的电化学性能得出,当Li浓度高时,由于电子定域作用使电荷屏蔽效应