微乳液法合成LiFePO4 / C正极材料及其电化学性能

本文采用微乳液方法合成了纳米LiFePO₄ / C正极材料。制备样品分别用XRD和SEM进行表征，充放电测试其电化学性能。600 ℃制备样品为单一物相，平均粒径90 nm，在室温2.0～4.0 V (vs Li) 放电电压范围和15 mA·g^-1放电速率下，首次放电容量达到159 mAh·g^-1。制备样品同样展现良好的循环性能。在15 mA·g^-1速率下40次循环后，制备样品放电容量仍保持首次放电容量的98.9%。优异的电化学性能得益于样品颗粒的纳米尺寸、均匀分布以及表面碳层包覆提高了活性材料的电子电导率。     

Nucleophilic reactivity of the peroxide anion in aqueous-alcoholic solutions in the presence of detergents

The reactivity of hydroxide and peroxide anions with 4-nitrophenyl N,N-dimethylcarbamate in aqueous-alcoholic detergent media and in “oil in water” microemulsions has been studied. Aqueous-alcoholic solutions of cationic (CTAB) and neutral (Triton X-100) surface active substances have promise for decomposition of substrates by a nucleophilic mechanism. __________ Translated from Teoreticheskaya i éksperimental’naya Khimiya, Vol. 43, No. 6, pp. 358–363, November–December, 2007.     

水热法合成多金属氧酸盐棒状超细晶体

以SrCl₂·6H₂O、(NH₄)₆P₂Mo₁₈O₆₂·nH₂O为原料，在PEG-600/H₂O微乳体系中于80～130 ℃温度下水热反应8～12 h，从而制得一种多金属氧酸盐棒状超细晶体，组成是Sr₃P₂Mo₁₈O₆₂·nH₂O。该超细晶体具有长棒状形貌、高结晶度且分散性能较好，长度范围在10.0～20.0 μm，径度在1.0～2.0 μm。对反应体系中的PEG-600/H₂O体积比(V_PEC-600∶V_H2O)、水热温度以及(NH₄)₆P₂Mo₁₈O₆₂·nH₂O/SrCl₂·6H₂O质量比(W_POMs∶W_SrCl2·6H2O)3个影响因素进行了探讨，结果表明：V_PEC-600∶V_H2O主要对棒状超细晶体的形貌、长径比以及晶体结晶度有着重要影响，体积比在范围V_PEC-600∶V_H2O=(1.50～2.00)∶1.00有利于大长径比的棒状超细晶体的形成；水热温度则优选80～130 ℃范围，过低则不发生反应，过高则发生了多金属氧酸盐与PEG-600的氧化-还原反应；W_POMs∶W_SrCl2·6H2O基本上不影响超细晶体的形成。还初步探讨了该棒状超细晶体的形成机理。     

Selenium Nanoparticles Prepared from Reverse Microemulsion Process

Selenium nanoparticles were prepared by a reverse microemulsion system. Sodium selenosulfate was used as selenium source. The results showed that hydrochloric acid concentration and reaction temperature had great influence on the morphology of products. The crystalline selenium nanowires and amorphous selenium nanorods were obtained in given condition.     

四磺化酞菁钴在微乳液、醇-水体系中的二聚现象研究

采用分光光度法研究了四磺化酞菁钴（ＣｏＴＳＰｃ），在微乳液（ＴｒｉｔｏｎＸ－１００－壬烷－正戊醇－水）、醇－水（甲醇、乙醇、丙醇）体系中的二聚现象，计算了ＣｏＴＳＰｃ的二聚常数ＫＤ。结果表明，ＣｏＴＳＰｃ的二聚常数ＫＤ值随着微乳液中表面活性的浓度及醇－水溶液的介电常数的增加而减小。     

Volume and heat capacity of model non-aqueous self-assembly systems

Blends of immiscible polymers are often stabilized by block copolymers which can form non-aqueous micelles and microemulsions in the liquid polymers. The phase diagrans, apparent volumes and apparent heat capacities of model non-aqueous binary and ternary systems were studied in order to investigate the conditions under which such self-assembly systems could form. 1,2-Hexanediol, which can cosolubilize hexane and ethyleneglycol, forms inverse micelles in hexane and weak microaggregates in ethyleneglycol. Genapol X-060, a commercial alcoholic surfactant containing on the average an aliphatic chain of 13 carbons and 6 oxyethylenes (C₁₃E₆), forms microaggregates in poly(ethyleneglycol) 400. These self-assembly systems are strengthen in the presence of a third component which has an affinity for the inner phase.Presented at the Symposium, 76^th CSC Congress, Sherbrooke, Quebec, May 30–June 3, 1993, honoring Professor Donald Patterson on the occasion of his 65^th birthday.     

Optimized Separation of Nine Xanthones by Microemulsion Electrokinetic Chromatography

A microemulsion electrokinetic chromatography method has been firstly used for the separation of the therapeutically important xanthones from Securidaca inappendiculata. The separation of the nine xanthones was systematically optimized with respect to pH, composition of microemulsion,addition of cyclodextrins, applied voltage and column temperature. Baseline separation was successfully achieved for the nine xanthones, which was also compared with that by micellar electrokinetic chromtography.     

过硫酸钾引发丙烯酰胺微乳液聚合

以山梨醇酐单月桂酸醋（Ｓｐａｎ２０）和聚氧乙烯山梨醇酐单硬醋酸酯（Ｔｗｅｅｎ６０）的混合物为乳化剂制备丙烯酰胺微乳液，研究了体系中Ｔｗｅｅｎ６０浓度、水相丙烯酰胺浓度对微乳液电导行为的影响．用过硫酸钾引发微乳液聚合，发现聚合开始后，体系电导率迅速下降，在聚合进入恒速期后电导不再降低．聚合的动力学表达式为：Ｒｐ∝［ＡＭ］１．１７［Ｅ］－１．２６［Ｉ］０．５；Ｍｖ∝［ＡＭ］１．０５［Ｅ］－０．９４［Ｉ］－０．６２．它与常规乳液聚合的动力学相差较大，却类似于悬浮聚合．     

表面活性剂的协同作用在甲维盐微乳剂中的应用

通过测定不同类型的单一及复配型表面活性剂水溶液的临界胶束浓度和表面张力,研究了它对W(甲维盐)=1%微乳剂的性能影响。膦酸酯类阴离子表面活性剂A的临界胶束浓度为1.79×10-4mol/L,表面张力为28.90mN/m;苯乙烯基酚聚氧乙烯聚氧丙烯醚嵌段型非离子表面活性剂B(EPE型)的临界胶束浓度为1.91×10-4mol/L,表面张力为20.70mN/m;按m(A)∶m(B)=2∶3形成的复配型表面活性剂2#的水溶液的临界胶束浓度为9.30×10-5mol/L,表面张力为25.66mN/m。当W(2#)=10%时,配制W(甲维盐)=1%的微乳剂物理稳定性最佳,各项指标均合格。对甘蓝小菜蛾幼虫的田间药效的试验,结果表明该药剂具有较强的杀虫作用和较长的持效期,具有较好的推广应用前景。     

Fe、Mn掺杂六铝酸镧的微乳液制法及性能研究

以TX-100/正己醇/环己烷组成的反相微乳液为媒介，采用反相微乳 共沉淀法制备系列金属掺杂的六铝酸镧催化剂。用BET、XRD进行物性表征, 以甲烷燃烧为探针反应考察了催化剂的催化活性。结果表明，反相微乳液合成催化剂的最佳成晶温度可降至1100℃。 LaMx Al12－x O19－α 中M的最佳掺杂数为1(x1)。单金属Mn的存在可以降低甲烷的起燃温度，使催化剂具有良好的低温活性；单金属Fe掺杂的六铝酸镧催化剂具有较低的完全转化温度；而Fe、Mn共同掺杂的LaMnFeAl-10O19－α催化剂具有低、高温活性和高温稳定性。100h稳定性运转的转化率始终保持在99.7％，无失活现象。