Structure and properties of the mesophase of syndiotactic polystyrene. VIII. Solvent sorption behavior of syndiotactic polystyrene/p‐chlorotoluene mesophase membranes

A crystalline δ form of a syndiotactic polystyrene (sPS) membrane was prepared from a solution of sPS (1 wt %) and p‐chlorotoluene (p‐CT) by a solution‐casting method. The mesophase (δ empty form) of sPS was obtained by the extraction of the guest solvent from the δ form of sPS by a stepwise solvent‐extraction method. The sPS/p‐CT mesophase membrane [p‐CT (A‐M)] was used for the sorption of 1 mol % p‐CT for different times and for the sorption of different concentrations of p‐CT, chlorobenzene (CB), p‐xylene (p‐X), toluene, and chloroform for 48 h. The presence of solvents in the sPS membrane was confirmed by IR analysis. A thermal study revealed that the sorption amount of 1 mol % p‐CT increased with increasing immersion time, and the sorption amounts of different solvents increased with increasing solvent concentration. Differential scanning calorimetry results showed that the desorption peak temperature increased as the amount of the solvent increased in the clathrated sPS membrane. Wide‐angle X‐ray diffraction results showed that 2θ at 8.25° was slightly shifted toward 8°, and there was no change in the peak position at 10° for p‐CT (A‐M), which was immersed in different solvents (1 mol %); however, the intensity of 2θ at 10° was not similar for all the samples. Among the solvents used for the sorption studies at 1 mol %, p‐CT (A‐M) could sorb more p‐CT and CB than p‐X, toluene, and chloroform. The solvent sorption isotherm was the Langmuir sorption mechanism. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3439–3446, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

Photodegradation of a herbicide derivative, 2,4-dichlorophenoxy acetic acid in aqueous suspensions of titanium dioxide

The photocatalytic degradation of a herbicide derivative, 2,4-dichlorophenoxy acetic acid (2,4-D, 1), has been investigated in aqueous suspensions of titanium dioxide. The degradation was studied by monitoring the change in substrate concentration employing UV spectroscopic analysis and decrease in Total Organic Carbon (TOC) content as a function of irradiation time in the presence of UV light source. The degradation kinetics was investigated under a variety of conditions, such as different types of TiO₂, pH, catalyst and substrate concentrations. Higher photonic efficiencies were observed with Degussa P25 as compared with other photocatalysts. The degradation products were analysed by GC-MS and probable pathways for the formation of different products were proposed.     

高功率LDA紧密侧面抽运Nd:YLF两级双程离轴放大系统实验研究

 介绍了一台10mm口径两级双程离轴放大系统，实现了对5mm×5mm口径光束的激光放大，耦合系统采用高功率LDA紧密侧面直接抽运棒状Nd:YLF方式。分析并实验研究了在不同抽运电流、放大脉冲与放大器LDA抽运时刻的不同延时及不同注入能量条件下，放大系统及光束每次放大时放大特性的规律。实验得到：在放大系统5mm×5mm软光阑处注入1.58mJ能量时，放大系统可输出129.2mJ能量，能量提取效率达到19.5%，满足该系统的设计指标。     

类钙钛矿化合物Ca(Mn2 Cu1)Mn4 O12的磁性与磁电阻效应

利用固相反应法制备了名义成分为Ca(Mn2 Cu1 )Mn4 O1 2 的类钙钛矿锰氧化物 .x射线衍射表明 ,为了获得较为致密的样品和减小杂相含量 ,可以采用高温烧结再在 10 73K长时间空气中退火的制备方法 .样品在低温下同时存在铁磁相和反铁磁相 ,由于反铁磁相的存在导致样品在 4 5K时的磁化强度显著降低 ,并在 8T的高磁场下仍未达到饱和 .样品呈半导体导电性质 ,在 85K和 6T磁场下磁电阻比的最大值可达 - 4 6 % .     

Cr3+：MgAl2O4晶体EPR参量及其电子精细光谱的研究

考虑了SS(Spin-Spin)作用和SOO(Spin-Other-Orbit)作用，采用完全对角化方法，结合自旋Hamiltonian理论，研究了Cr³⁺∶MgAl₂O₄晶体EPR参量及其吸收光谱，理论与实验符合甚好. 在此基础上，进一步研究了⁴A₂(3d³)离子EPR参量的微观起源. 研究表明，EPR参量起源于四种微观机制：(1) SO(Spin-Orbit) 耦合机制；(2) SS耦合机制；(3)SOO耦合机制；(4) SO～SS～SOO总联合作用机制. 在这些机制中，SO机制是最主要的.     

高压增氧T′相R_2CuO_(4+δ)(R=Nd～Tm)低温磁性研究

T′相R2CuO4稀土铜氧化合物由于尺度效应而产生弱铁磁性行为已经被人们关注,报导了通过高温高氧压(6GPa,1000℃)合成稀土T′相R2CuO4(R=Nd,Sm,Eu,Gd,Tb,Dy,Ho,Er和Tm)化合物的结构和磁学性能。磁化率曲线显示,在低温下所有的高压增氧R2CuO4样品都出现新的低温弱铁磁性反常行为,转变温度在28K附近。新的低温弱铁磁性行为是由于CuO2面上微量氧空穴的掺入,使处于反铁磁有序CuO2面形成局域化的铁磁性团簇造成。实验证明新发现的低温弱铁磁性行为与尺度效应产生弱铁磁性行为属于完全不同的物理机制。结果还预示T′相R2CuO4稀土铜氧化合物很难通过空穴掺杂而实现超导。     

Pr(0.5):ZBLAN的双频激发上转换发光的研究

报道了Pr(0.5):ZBLAN玻璃在双频双光束光源激发下的激发态上转换现象.发现上转换发射谱的荧光与常规荧光发射谱的荧光一致，还发现双频激发下的上转换激发谱有3个明显的谱峰，它们依此对应于788.5nm 1G4→3P2,850.5nm 1G4→1I6和805.0nm 3H6→1D2的激发态吸收跃迁，而大的850.5nm上转换激发谱峰是由大的1G4(Pr3+ )→1I6(Pr3+)跃迁的振子强度f=23.04×10-6所致.这说明起源于1G4能级的激发态吸收上转换尤其1G4(Pr3+)→1I6(Pr3+)     

Yb:FAP和Yb:C_3S_2-FAP晶体光谱的温度特性和选择激发

报导了Yb :FAP和Yb :C3S2 _FAP晶体在不同温度下的吸收光谱和荧光光谱实验结果 ,研究发现由于电子_声子近共振耦合作用 ,Yb :FAP和Yb :C3S2 _FAP晶体均存在有明显的振动谱 ,Yb :FAP晶体的零声子线在低温下还劈裂为相差 10cm- 1 的两条线 .采用激光选择激发技术研究了Yb3 离子在FAP和C3S2 _FAP晶体中的格位特征 ,结果表明Yb3 离子在这两种基质中都只占据Ca(Ⅱ )格位 ,但由于CaF2 的挥发 ,导致了Ca(Ⅱ )格位的局部畸变 .     

闪烁光纤在γ射线辐照下部分特性的蒙特卡罗模拟

 闪烁光纤在射线成像方面的应用越来越广泛。为了进一步了解闪烁光纤在射线辐照下的基本特性，基于蒙特卡罗方法，利用计算机模拟分析了γ射线在闪烁光纤中的好事例率与光纤长度及射线能量的关系，能量沉积效率与光纤长度及射线能量的关系。此项工作对于闪烁光纤阵列在射线成像，剂量场测量等方面的研究很有价值。