核壳结构MoOx/C微球的制备及储锂性能

采用水热法合成了MoO_3/酚醛树脂前驱体,然后在空气中进行煅烧处理,成功制备了一种新型核壳MoOx/C微球。对材料的晶体结构、形貌和元素价态进行分析表明,该材料的主要成分是单斜相MoO_2、正交晶系MoO_3和碳。树脂在空气中的煅烧碳化将MoO_3/酚醛树脂前驱体中的六方晶系的MoO_3还原为单斜相MoO_2。其中少量的MoO_2会在空气中重新被氧化成正交晶系的MoO_3,形成了MoO_2/MoO_3异质结构。在这一系列反应的综合作用下,形成这种表面有裂纹的核壳MoOx/C微球复合材料。将该材料用作锂离子电池负极材料,表现出了循环稳定性高、倍率性能好等优异的电化学性能。在100 mA·g-1的电流密度下充放电循环100次之后,可逆容量达640.6 mAh·g-1。     

MoO3/HBZSM-5催化剂上甲烷的无氧芳构化反应

以含硼杂原子分子筛HBZSM-5为载体,考察了其担载MoO3后催化甲烷无氧芳构化反应的性能,并结合XRD,IR,TG和SEM等手段对催化剂进行了表征.实验结果表明,MoO3/HBZSM-5催化剂具有较高的甲烷芳构化活性,但稳定性较差.随着引入分子筛骨架中硼量的增大,甲烷的极值转化率增高;随着反应温度的升高,MoO3/HBZSM-5催化剂的甲烷芳构化活性升高.从产物分布的变化来看,硼的引入对于催化剂上乙烯的选择性影响较大;与MoO3/HZSM-5催化剂相比,MoO3/HBZSM-5催化剂上乙烯选择性大大提高.     

MoO3和CuCl在γ-Al2O3表面分散速度和分散机理的研究

It has been shown that many oxides and salts can disperse spontaneously onto supports with large surface area~[1]. A typical example studied widely is the dispersion of MoO_3 on γ-Al_2O_3. However, the research work about the dispersion mechanism and kinetics is quite few.Knozinger etc.~[2] suggested that the dispersion of MoO_3 onto the surface of γ-Al_2O_3 may occur through a "gas phase transport" mechanism mainly by assuming an intermediate MoO_2(OH)_2(g), and the presence of water is necessary. Their conclusion was based on a fact that after heating a mixture of MoO_3 and γ-Al_2O_3 in the presence of H_2O vapour at 450 ℃, the characteristic peak at 950 cm~(-1) of monolayer dispersed MoO_3 in Laser Raman Spectrum (in situ) appears, but after heating the mixture in dry oxygen, it can not be observed...     

Mo/SiO_2及V改性的Mo/SiO_2催化剂的微孔特征及其对甲烷部分氧化合成甲醛反应的影响

在常压下评价了Ｍｏ／ＳｉＯ２催化剂的制备条件对反应性能的影响．利用Ｎ２的吸附等温线计算了ＭｏＶ／ＳｉＯ２催化剂的比表面积和孔径分布，进而讨论了不同的Ｖ加入量对Ｍｏ／ＳｉＯ２催化剂的微孔特征及其催化性能的影响，找到了适宜的Ｖ／Ｍｏ质量比及使甲醛收率最高的最佳孔径．通过ＸＲＤ和ＴＥＭ的测试分析讨论了制备条件对微观状态的影响和Ｖ与Ｍｏ之间的相互作用．     

MoO3在γ—Al2O3表面分散过程的动力学研究

采用原位X-光衍射仪对MoO_3在γ—Al_2O_3表面上的分散过程进行动力学研究。测定了不同温度下的MoO_3分散量随时间的变化。认为分散过程对于表面有效位置是一级反应,并得到了不同温度下的速率常数和分散过程的活化能。     

TiO2-MoO3/SiO2催化碳酸二甲酯与乙酸苯酯酯交换合成碳酸二苯酯

采用分步等体积浸渍法制备了催化剂r%TiO2-q%MoO3/SiO2(1q-r)。以碳酸二甲酯(DMC)与乙酸苯酯(PA)酯交换合成碳酸二苯酯(DPC)为探针反应,考察了1的催化活性。优化反应条件为:PA 290 mmol,n(PA):n(DMC)=2:1,18-4 1.4 g,于180℃反应7 h。在优化反应条件下,DMC转化率77.5%,DPC选择性49.4%,碳酸甲苯酯和DPC的总选择性87.2%。催化剂重复使用时,活性下降很快,也很难通过高温焙烧再生。     

High CO methanation activity on zirconia-supported molybdenum sulfide catalyst

In this study, different methods were used to prepare MoO3/ZrO2 catalysts for sulfur resistant methanation reaction. It was found that MoO3/ZrO2 catalyst prepared by one-step co-precipitation method achieved high methanation performance. CO conversion could reach up to 90% on 25 wt% MoO3/ZrO2 catalyst, much higher than that on the conventional 25 wt% MoO3/Al2O3 catalyst. The Mo-based catalysts were characterized by XRF, XRD, Raman, BET, TEM and H2-TPR etc. It was found that MoO3 particles were highly dispersed on ZrO2 support for 25 wt% MoO3/ZrO2 catalyst prepared at 65-85℃ because of its relatively larger pore size, which contributed to a high CO conversion. Meanwhile, when MoO3 loading exceeded the monolayer coverage, the formed crystalline MoO3 and ZrM020g might block the micropores of the catalyst and make the methanation activity declined. These results are useful for preparing highly efficient catalyst for CO methanation process.     

三氧化钼纳米带/石墨烯纳米复合材料的简单制备及其在超级电容器中的应用

采用简单的超声自组装法制备了石墨烯/三氧化钼纳米带复合材料。最终产物的组成和结构采用多种不同的手段进行了表征,包括扫描电镜、透射电镜、X射线衍射、拉曼光谱以及热分析等。该复合材料可以用作超级电容器电极材料。电化学实验结果表明石墨烯/三氧化钼纳米带复合材料比电容可达到285.5 F·g^-1,且在电流密度为1 A·g^-1时经过1 000次循环后其电容值能保持初始值的99.5%.     

MoO3/介孔Al2O3催化氧化脱除模拟油中的硫

以环己烷为溶剂,二苯并噻吩（DBT）、苯并噻吩（BT）、4,6-二甲基二苯并噻吩（4,6-DMDBT）、噻吩（Th）作为模型含硫化合物配制成模拟油,在MoO3/介孔Al2O3-H2O2体系中对模拟油催化氧化脱硫进行了研究. 考察了MoO3负载量、氧化剂用量、催化剂用量、氧化反应温度及反应时间对DBT脱除效果的影响. 实验结果表明：在MoO3负载量为20%,催化剂用量为1.5%,氧化剂H2O2与模拟油中硫的摩尔比为4,反应温度为60℃,反应时间为40分钟时DBT脱除率最高,达99.4%,几乎可以被完全脱除;在此条件下模型化合物的氧化反应活性顺序为：DBT > 4,6-DMDBT >BT>Th.     

三氧化钼纳米带/石墨烯纳米复合材料的简单制备及其在超级电容器中的应用

采用简单的超声自组装法制备了石墨烯/三氧化钼纳米带复合材料。最终产物的组成和结构采用多种不同的手段进行了表征,包括扫描电镜、透射电镜、X射线衍射、拉曼光谱以及热分析等。该复合材料可以用作超级电容器电极材料。电化学实验结果表明石墨烯/三氧化钼纳米带复合材料比电容可达到285.5 F·g^-1,且在电流密度为1 A·g^-1时经过1 000次循环后其电容值能保持初始值的99.5%.