PTC特性的复合导电体系中炭粒子分布的逾渗模型与电阻率的计算

综述了炭黑填充型导电高分子复合体系的几种导电理论；讨论了导电载流子分布的各种假说及模型；比较了不同模型的理论预测与实验结果的差异性。     

Structure and properties of the Nafion—polyaniline—palladium composite electrodes

Effect of conditions of deposition of palladium onto a composite polymeric film Nafion—polyaniline on the properties of the system thus obtained is studied. It is shown that the effect of the said conditions on the character of distribution of palladium in a polymer may be used when estimating electrocatalytic potentialities of such composites.Translated from Elektrokhimiya, Vol. 41, No. 2, 2005, pp. 213–218.Original Russian Text Copyright © 2005 by Andreev, Zolotarevskii.This revised version was published online in April 2005 with corrections to the article note and article title and cover date.     

Preparation of spherical spinel LiMn2O4 cathode material for lithium ion batteries

A novel process is proposed for synthesis of spinel LiMn₂O₄ with spherical particles from the inexpensive materials MnSO₄, NH₄HCO₃, and NH₃H₂O. The successful preparation started with carefully controlled crystallization of MnCO₃, leading to particles of spherical shape and high tap density. Thermal decomposition of MnCO₃ was investigated by both DTA and TG analysis and XRD analysis of products. A precursor of product, spherical Mn₂O₃, was then obtained by heating MnCO₃. A mixture of Mn₂O₃ and Li₂CO₃ was then sintered to produce LiMn₂O₄ with retention of spherical particle shape. It was found that if lithium was in stoichiometric excess of 5% in the calcination of spinel LiMn₂O₄, the product had the largest initial specific capacity. In this way spherical particles of spinel LiMn₂O₄ were of excellent fluidity and dispersivity, and had a tap density as high as 1.9 g cm^–3 and an initial discharge capacity reaching 125 mAh g^–1. When surface-doped with cobalt in a 0.01 Co/Mn mole ratio, although the initial discharge capacity decreased to 118 mAh g^–1, the 100th cycle capacity retention reached 92.4% at 25°C. Even at 55°C the initial discharge capacity reached 113 mAh g^–1 and the 50th cycle capacity retention was in excess of 83.8%.     

SnO2TiO2 复合半导体纳米薄膜的研究进展

本文概述了SnO₂TiO₂ 复合半导体纳米薄膜的发展历史和研究现状,对比分析了“混合”、“核壳”和“叠层”3 种复合薄膜的结构和性能特点,着重论述了叠层结构的SnO₂ /TiO₂复合薄膜的光电化学和光催化特性。结合作者的研究工作,探讨了SnO₂ /TiO₂双层复合薄膜上下层厚度对其光催化活性的影响,指出复合薄膜光催化活性的提高可归因于电子从TiO₂ 向SnO₂ 的迁移。最后对SnO₂ /TiO₂复合薄膜的局限性和发展潜势做一简要分析,强调了该复合薄膜本身的应用特点。     

四苯硼钠-甲苯胺蓝缔合物纳米微粒体系减色效应研究

在PH4.0醋酸-醋酸钠介质中，甲苯胺蓝在600nm处有一个吸收峰，随着四苯硼钠浓度的增大甲苯胺蓝在600nm处吸收峰降低，颜色减弱，这是由于甲苯胺蓝-四苯硼钠缔合物分子间存在较强的疏水作用及分子间作用力，聚集形成纳米微粒所致，甲苯胺蓝-四苯硼钠纳米微粒体系亦在600mm处有1个吸收峰，在400mm、470mm和580mm处产生3共振散射峰，其中400mm和580mm为甲苯胺蓝-四苯硼钠复合纳米微粒产生的特征共振散射峰，这也表明有纳米微粒存在，丙酮浓度的影响实验结果等表明，纳米微粒的形成是产生其减色效应的原因。     

Morphology control of soap-free seeded P(St-EA-AA) latex particles

Soap-free poly(styrene-ethyl acrylate-acrylic acid) latex particles with narrow size distribution and with surface carboxyl groups were synthesized by semicontinuous emulsion polymerization, and the particles with homogeneous multihollow structure were obtained after alkali posttreatment. Effects of treatment conditions and crosslinking agents on particle morphology were investigated. Results showed that the multihollow structure can be formed inside the uncrosslinked particles only when the treatment temperature exceeded 50 °C, the pH was higher than 10.0, the amount of 2-butanone was more than 3.0 ml and the treatment time was longer than 30 min. Furthermore, the volume expansion of the particles increased with the temperature increased to 90 °C, the pH to 12.5 or the amount of 2-butanone to 7.0 ml, and this value increased first and then decreased with the treatment time prolonged. Fine pores can be generated in the shell of particles crosslinked by 0.2 g of ethyl glycol dimethylacrylate (EGDMA), while no hollow structure formed inside particles when 0.4 g of EGDMA or 0.2 g of divinyl benzene was used.     

LSGMC5含量对于二甲醚燃料电池复合Ni-Fe阳极性能的影响

用浸渍法制备了掺杂不同质量分数的La0.8Sr0.2Ga0.8Mg0.15Co0.05O3-δ (LSGMC5)粉末的Ni8-Fe2-LSGMC5复合阳极, 并采用交流阻抗和直流极化技术考察了以氢气和二甲醚为燃气时该复合阳极的电化学性能及相应电池的功率输出特性. 结果表明, 在电极中掺入LSGMC5 粉末, 能显著地改善电极的形貌和电极/电解质界面结构, 减小欧姆电阻和极化电阻. 电极中LSGMC5 粉末含量对于氢气及二甲醚电化学氧化性能的影响显著不同. 以二甲醚为燃气时, 电极极化电阻随LSGMC5 粉末含量的增加而减小, 其中LSGMC5 掺杂量为30%的复合阳极具有最高的电化学性能, 相应电池在1073、1023、973 K 时的输出功率分别为1.00、0.61、0.40 W·cm-2; 以氢气为燃气时, LSGMC5 掺杂量为20%的复合阳极具有最好的电化学性能, 随着LSGMC5 掺杂量的进一步增加, 电极极化电阻显著增大.     

中药配方颗粒红外光谱法的快速鉴别

采用红外光谱法对中药配方颗粒及其辅料进行了鉴别研究。结果表明：不同生产厂商的配方颗粒中所添加的辅料类型及用量有较大差别；不同种的配方颗粒在辅料含量较低的情况下有较明显的指纹性，而辅料含量较高时，采用差谱技术可以提高谱图的指纹性，达到中药配方颗粒--鉴别的目的。该法简便、快速、可靠，是中药配方颗粒宏观质控的一个强有力的手段。     

单分散交联聚甲基丙烯酸环氧丙酯树脂的制备及亲合纯化伴刀豆球蛋白-A

采用一步种子溶胀聚合法制备了颗粒呈单分散的交联聚甲基丙烯酸环氧丙南树脂，对其环氧基的组成比进行了表征，并以氨基葡萄糖为配基，首次制备了纯化粗品伴刀豆球蛋白-A(Ⅲ）(Con-A，Ⅲ)的聚合物基质的高效亲合色谱柱。配基在树脂上的键合量为8．2mg／g，对纯化后的Con-A（Ⅲ）的吸附量为13．4mg／g。使用该亲合色谱介质成功地从粗品Con-A中快速纯化了Con-A，电泳分析显示为一个主要的谱带，纯度从15％提高到95％。     

聚酰亚胺／聚N－乙烯吡咯烷酮分子复合物的合成和表征

由原位缩聚制备了刚性高分子聚酰亚胺（ＰＩ）和柔性基体聚Ｎ－乙烯吡咯烷附（ＰＶＰ）的分子复合物，并由实验证明了中间体聚酰胺酸（ＰＡ）和聚乙烯吡咯烷酮大分子之间存在的酸一碱相互作用．这种相互作用促进了混容性，使聚酰亚胺能以分子水平或接近分子水平分散在聚毗咯烷酮的基体之中．聚酰亚胺／聚Ｎ－乙烯吡咯烷团分子复合物的薄膜呈透明性，在整个组成范围内只有一个Ｔｇ，显示单相行为。当ＰＩ含量＜２０％时，ＳＥＭ相片呈现均相形貌，看不到ＰＩ微晶．广角Ｘ－ｒａｙ衍射图表明ＰＩ特征结晶峰消失，和无定形的ＰＶＰ完全混容．当ＰＩ含量＞４０％，ＳＥＭ显示有均匀分布的、棒状ＰＩ微晶存在．通过分子复合，即使ＰＩ含量为１０％，聚Ｎ－乙烯吡咯烷酮不再溶于乙醇，耐热性也有提高．