Effects of oblique-incidence evaporation on magnetic properties of Fe20Ni80/Fe70Co30 bilayer film

Evaporative deposition at oblique incidence is shown to enhance the magnetic anisotropy of an Fe₂₀Ni₈₀ magnetic film and induce magnetic anisotropy in an overlying, strongly isotropic Fe₇₀Co₃₀ film. This deposition method for the formation of an underlayer of several lattice parameters in thickness and semi-hard overlayer of a few thousands Angstroms in thickness achieves a significant change in the magnetization process and strong suppression of the coercive forces of Fe₇₀Co₃₀ in the hard magnetization direction. Soft magnetization of the Fe₇₀Co₃₀ overlayer is not achieved when one of the layers is deposited at oblique incidence. It is anticipated that shape magnetic anisotropy is responsible in part for the magnetic anisotropy induced in both in Fe₂₀Ni₈₀ under- and Fe₇₀Co₃₀ overlayer by oblique incidence evaporation.     

ZnSe/SiO2复合薄膜光学常数与荧光光谱的研究

采用溶胶-凝胶工艺与原位生长技术，制备了ZnSe/SiO₂复合薄膜.X射线衍射分 析表明薄膜中ZnSe晶体呈立方闪锌矿结构.X射线荧光分析结果显示薄膜中Zn与Se摩尔比为1 ∶1.01—1∶1.19.利用场发射扫描电子显微镜观察了复合薄膜的表面形貌，结果表明复合薄 膜表面既存在尺寸约为400nm的ZnSe晶粒，也存在尺寸小于100nm的ZnSe晶粒.利用椭偏仪测 量了薄膜椭偏角Ψ，Δ与波长λ的关系，采用Maxwell-Garnett有效介质理论对薄膜的光学 常数、厚度、气孔率、ZnS 关键词： 2复合薄膜')" href="#">ZnSe/SiO₂复合薄膜 光学性质 椭偏光度法 荧光光谱     

模拟退火法在吸收薄膜的椭偏反演算法中的应用

将一种广泛用于求解复杂系统优化问题的技术－－模拟退火法－－用来求解椭偏反演方程。首先假设一个薄膜模型，计算出其相应的椭偏参数（Ψ，Δ）的值，在这个计算值的基础上加入不同标准偏差的高斯噪声；然后将加入噪声后的值（Ψm,Δm)作为模拟的测量数据，采用模拟退火算法进行求解，验证得知这种方法求得的薄膜参数很接近于假设的薄膜模型参数的真值，与其他文献的报道结果一致，而且在扩大搜寻范围时，仍然可以得到准确解，从而证明了该方法的可行性以及有效性。     

退火温度对低温生长MgxZn1－xO薄膜光学性质的影响

用射频磁控溅射法在80℃衬底温度下制备出Mg_xZn_1-xO(x=0.16)薄膜，用X射线衍射(XRD)、光致发光(PL)和透射谱研究了退火温度对Mg_xZn_1-xO薄膜结构和光学性质的影响.测量结果显示，Mg_xZn_1-xO薄膜为单相六角纤锌矿结构，并且具有沿c轴的择优取向；随着退火温度的升高，(002)XRD峰强度、平均晶粒尺寸和紫外PL峰强度增大，(002)XRD峰半高宽(F 关键词： xZn_1-xO薄膜')" href="#">Mg_xZn_1-xO薄膜 射频磁控溅射 退火     

Fabrication and characterization of sputtered titanium dioxide films

TiO₂ thin films were prepared under various conditions by using a reactive RF sputtering technique. The structural, optical and electrical characteristics of the films have been investigated. All as-deposited films were amorphous. After annealing at T > 673 K, the crystallinity of the observed tetragonal anatase phase appeared improved. The optical band gap, determined by using Tauc plot, has been found to amount to 3.38 ± 0.03 and 3.21 ± 0.03 eV for the direct and indirect transition, respectively. Also the complex optical constants for the wavelength range 300-2500 nm are reported. Using the two-point probe technique, the dark resistivity has been measured as a function of the film thickness, d. The resistivity, ρ, of the samples has been found to decrease markedly with increasing thickness, but only for d < 100 nm. The behaviour of ρd versus d was found to fit properly with the Fuchs and Sondheimer relation with parameters ρ_o = 4.95 × 10⁶ Ω cm and mean free path, l = 310 ± 2 nm. The log ρ versus 1/T curves show three distinct regions with values for the activation energy of 0.03 ± 0.01, 0.17 ± 0.01 and 0.50 ± 0.02 eV, respectively.     

Probing antiferromagnetic order with heat capacity in exchange-biased structures

We explore the magnetic heat capacity in exchange-biased ferromagnet/antiferromagnet bilayers theoretically. We show that changes in the antiferromagnetic structure due to the reversal of the ferromagnet layer can be detected by distinct features in the heat capacity. This offers a method for probing antiferromagnetic domains in exchange-biased systems.     

Synthesis and Properties of a Heteronuclear Ag（Ⅰ）/Ni（Ⅱ） Complex

Introduction Itiswell knownthatcyanogroupsincyanometa latessuchas[Ag(CN)2]-unitscanbeusedasbridg ingligandsandapolymericstructurecanbeformed throughsilver silver(argentophilic)interactions.This propertyhasbeenexploredintheconstructionofmany oligomericandp…     

溶胶-凝胶VO2薄膜转换特性研究

利用溶胶凝胶法在SiO2Si衬底上沉积高取向的V2O5薄膜,在压强低于2Pa,温度高于400℃的条件下,对V2O5薄膜进行真空烘烤,获得了电阻率变化3个数量级以上、弛豫宽度为62℃的VO2多晶薄膜.以X射线衍射(XRD)、扫描电子显微镜(SEM)图和电阻率转换特性等实验结果为依据,详细分析了溶胶凝胶薄膜在真空烘烤时从V2O5向VO2的转化,它经历了从VnO2n+1(n=2,3,4,6)到VO2的过程.实验证明,根据选择合适的成膜热处理条件和真空烘烤条件是实现溶胶凝胶V2O5结构向VO2结构成功转换的关键 关键词： 溶胶-凝胶法 氧化钒薄膜 VO2膜转换特性     

Very high coercivities of top-layer diffusion Au/FePt thin films

The Au/FePt samples were prepared by depositing a gold cap layer at room temperature onto a fully ordered FePt layer, followed by an annealing at 800 °C for the purpose of interlayer diffusion. After the deposition of the gold layer and the high-temperature annealing, the gold atoms do not dissolve into the FePt Ll₀ lattice. Compared with the continuous FePt film, the TEM photos of the bilayer Au(60 nm)/FePt(60 nm) show a granular structure with FePt particles embedded in Au matrix. The coercivity of Au(60 nm)/FePt(60 nm) sample is 23.5 kOe, which is 85% larger than that of the FePt film without Au top layer. The enhancement in coercivity can be attributed to the formation of isolated structure of FePt ordered phase.