A BGK-type Boltzmann equation for a neutral gas is considered as a model for electron swarms, because the gas and the electron Boltzmann equation have a common diffusion approximation. Both full- and half-range theory are developed using orthogonality methods of solution. Preliminary comparisons with diffusion theory are presented.     

多钼酸盐–柠檬酸复合膜的多色光致变色

制备了多钼酸盐–柠檬酸光致变色复合膜，紫外光照后发现不同摩尔比的复合膜呈现不同的颜色。当摩尔比为1.0，0.3和0.2时，变色后的薄膜分别显深蓝色，深黄褐色和淡海绿色。通过对薄膜的拉曼光谱分析证实呈现不同的颜色是由于在变色后的膜中生成了不同的物种。柠檬酸在光致变色过程中起着重要的作用, 在紫外光的照射下它作为空穴的捕获剂, 抑制了光生电子和空穴的复合, 使多钼酸盐呈现紫外光致变色现象。     

LaB6-ZrB2共晶复合材料的组织特征及控制

用电弧炉和电子束悬浮区熔炉法制备了ＬａＢ６ＺｒＢ２共晶复合材料，并用ＳＥＭ和ＴＥＭ方法对其显微组织进行了研究。结果表明，ＬａＢ６ＺｒＢ２形成纤维状共晶组织，控制凝固条件可得到定向排列的组织，ＬａＢ６基体上均匀分布着直径为０２～１２μｍ的ＺｒＢ２纤维，纤维长度可达１００μｍ以上。对于固液界面为平面生长的试样，其结晶学取向关系为［００１］ＬａＢ６∥［００１］ＺｒＢ２，（１１０）ＬａＢ６∥（０１０）ＺｒＢ２。     

表面包覆改性对纳米CeO2分散性的影响

了改善纳米CeO2在Zn-Al类共晶合金中的分散性,采用超声液相包覆法对纳米CeO2进行表面活性剂表面包覆改性,并用AES测定了包覆层的厚度,用TEM研究了CeO2的团聚状况,用TGA分析了有机物包覆层的炭化温度范围,最后用FE-SEM观察了CeO2在复合材料中的分散情况。结果表明,包覆在纳米CeO2表面的厚度约为20 nm的表面活性剂层提高了微粒的分散性,而且该包覆层在495℃时已经炭化。热力学计算的结果也表明,炭化层能与氧化膜反应,该反应提高了CeO2与基体间的润湿性,并使其均匀分布在基体合金中。     

镧掺杂粘土源含铜氧化物催化剂的制备、表征及催化性能

采用共沉淀和水热法合成了不同阴离子粘土前驱型复合氧化物催化材料,样品经XRD,FTIR,TPR,TG-DSC,SEM进行表征.同时考察了铜含量在掺杂和不掺杂稀土时对甲烷催化燃烧的影响,结果发现随含铜量增加催化活性增加;未掺杂La的催化剂在高温下出现失活现象,而掺杂型催化剂稳定性良好.同时,制备方法对催化剂的性能有显著影响,在不同制备前驱物pH的条件下,使用共沉淀和水热法合成的阴离子粘土材料,合成时的pH均对催化剂的活性影响较大;同时焙烧温度对催化活性有不同程度的影响.     

酯交换法合成碳酸二苯酯用氧化铅－氧化锌催化剂的研究

 制备了一种用于苯酚与碳酸二甲酯酯交换合成碳酸二苯酯的新型氧化铅－氧化锌多相催化剂．研究了制备方法、焙烧温度、不同母体和母体配比对催化剂催化性能的影响．应用XRD，TPR和原子吸收光谱对催化剂结构进行了表征，发现Pb3O4是主活性物相，ZnO为助催化剂，并以非晶态或微晶态存在于催化剂体系中．当焙烧温度为500℃，n（Pb）／n（Zn）≈2时，催化剂的活性最高，碳酸二苯酯产率可达45．6％．考察了催化剂的重复使用效果，并对失活原因进行了探讨．     

四元配合物[Nd(C_4H_3OCOO)_2·NO_3·C_(10)H_8N_2]_2的合成与晶体结构

稀土羧酸配合物在萃取分离、杀菌、催化和发光材料等方面有广泛的应用[1]。将氮杂环双齿配位体引入到这类配合物中可增强配合物的共轭作用,提高稳定性并增强其杀菌能力和发光性质[2]。虽然氮杂环双齿配位体邻菲咯啉的稀土羧酸配合物报道较多,但含2,2′联吡啶配位的稀土羧酸配合物的研究相对较少,尤其是含2,2′联吡啶的四元稀土羧酸混配配合物的研究更为少见[3]。2呋喃甲酸是糠醛在人体中的代谢产物,可做为防腐剂、熏蒸剂等,本文报道[Nd(C4H3OCOO)2·NO3·C10H8N2]2配合物的合成和单晶X射线衍射分析结果。2呋喃甲酸(分析纯)、2,2′联吡…     

Low Dimension Semiconducting Composite Nanomaterials

Recently, low dimension nanostructures have gained considerable attention due to their technological potential as unique types of nanoscale building blocks for future optoelectronic devices and systems. Semiconducting composite nanomaterials, which can combine the advantages of two or more components, have been the focus in the area of nanomaterials synthesis and device application.In this paper, we report our work on the preparation of composite nanomaterials based on CNTs.CNTs were coated by organic or inorganic species via novel and facile methods (Fig. 1 and Fig.2).These functional CNTs based composites show eminent prospects and opportunities for new applications in a wide variation of areas.     

Tribological properties of ormosil coatings

Transparent plastics are not scratch resistant. The damage leads to a loss of optical properties. Coatings prepared using either tetraethoxysilane or colloidal silica particles embedded in glymo is a way to avoid these disadvantages. Tribological experiments are carried out to better understand the surface modification due to a sliding friction. It is shown that the wear track is not directly related to usual mechanical properties such as Young's modulus and the hardness of the coating. The different stages leading to material loss are discussed in term of particle removal and debris circulation (accumulation or elimination) through the friction track. The mechanical properties of the film combined with the film to substrate adhesion are expected to play an important role as it can be deduced from results obtained as a function of the coating composition.