惰性盐辅助合成介孔石墨化碳片及其电容性能

以惰性盐KCl为模板、硝酸镍为金属催化剂镍源、葡萄糖为碳源,通过碳化处理制备了介孔石墨化碳片。利用扫描电子显微镜、透射电子显微镜、X-射线衍射仪和比表面测试仪对介孔石墨化碳片进行了表征。探讨了碳片形成的机理,采用三电极测试体系研究了介孔石墨化碳片电极材料的电化学性能。结果表明,10 g KCl制备的碳片比表面积最大(989 m2·g-1),在6 mol·L-1KOH电解液中,当电流密度为0.5 A·g-1时,比电容达到180 F·g-1;当电流密度达到10 A·g-1时,比电容维持在148 F·g-1,显示了电极具有较好的倍率性能;在10 A·g-1条件下,2 000次循环充放电测试后电容没有发生衰减,展示了在超级电容器方面的应用潜力。     

A hierarchical porous carbon membrane from polyacrylonitrile/polyvinylpyrrolidone blending membranes:Preparation,characterization and electrochemical capacitive performance

Novel hierarchical porous carbon membranes were fabricated through a simple carbonization procedure of well-defined blending polymer membrane precursors containing the source of carbon polyacrylonitrile （PAN） and an additive of polyvinylpyrrolidone （PVP）, which was prepared using phase inversion method. The as-fabricated materials were further used as the active electrode materials for supercapacitors. The effects of PVP concentration in the casting solution on structure feature and electrochemical capacitive performance of the as-prepared carbon membranes were also studied in detail. As the electrode material for supercapacitor, a high specific capacitance of 278.0 F/g could be attained at a current of 5 mA/cm2 and about 92.90% capacity retention could be maintained after 2000 charge/discharge cycles in 2 mol/L KOH solution with a PVP concentration of 0.3 wt% in the casting solution. The facile hierarchical pore structure preparation method and the good electrochemical capacitive performance make the prepared carbon membrane particularly promising for use in supercapacitor.     

3D amorphous carbon and graphene co-modified LiFePO4 composite derived from polyol process as electrode for high power lithium-ion batteries

Amorphous carbon and graphene co-modified LiFePO_4 nanocomposite has been synthesized via a facile polyol process in connection with a following thermal treatment.Various characterization techniques,including XRD.Mossbauer spectra,Raman spectra,SEM,TEM,BET,O_2-TPO,galvano charge-discharge,CV and EIS were applied to investigate the phase composition,carbon content,morphological structure and electrochemical performance of the synthesized samples.The effect of introducing way of carbon sources on the properties and performance of LiFePO_4/C/graphene composite was paid special attention.Under optimized synthetic conditions,highly crystalized olivine-type LiFePO_4was successfully obtained with electron conductive Fe_2P and FeP as the main impurity phases.SEM and TEM analyses demonstrated the graphene sheets were randomly distributed inside the sample to create an open structured LiFePO_4 with respect to graphene,while the glucosederived carbon mainly coated over LiFeP04 particles which effectively connected the graphene sheets and LiFePO_4 particles to result in a more efficient charge transfer process.As a result,favorable electrochemical performance was achieved.The performance of the amorphous carbon-graphene co-modified LiFePO_4 was further progressively improved upon cycling in the first 200 cycles to reach a reversible specificcapacity as high as 97 mAh·g~(-1) at 10 C rate.     

Sulfur/carbon composites prepared with ordered porous carbon for Li-S battery cathode

Ordered porous cabon with a 2-D hexagonal structure,high specific surface area and large pore volume was synthesized through a twostep heating method using tri-block copolymer as template and phenolic resin as carbon precursor.The results indicated the electrochemical performance of the sulfur/carbon composites prepared with the ordered porous carbon was significantly affected by the pore structure of the carbon.Both the specific capacity and cycling stability of the sulfur/carbon composites were improved using the bimodal micro/meso-porous carbon frameworks with high surface area.Its initial discharge capacity can be as high as 1200 mAh·g~(-1) at a current density of 167.5 mA·g~(-1)The improved capacity retention was obtained during the cell cycling as well.     

Effect of the graphitic degree of carbon supports on the catalytic performance of ammonia synthesis over Ba-Ru-K/HSGC catalyst

A series of high surface area graphitic carbon materials （HSGCs） were prepared by ball-milling method. Effect of the graphitic degree of HSGCs on the catalytic performance of Ba-Ru-K/HSGC-x （x is the ball-milling time in hour） catalysts was studied using ammonia synthesis as a probe reaction. The graphitic degree and pore structure of HSGC-x supports could be successfully tuned via the variation of ball-milling time. Ru nanoparticles of different Ba-Ru-K/HSGC-x catalysts are homogeneously distributed on the supports with the particle sizes ranging from 1.6 to 2.0 nm. The graphitic degree of the support is closely related to its facile electron transfer capability and so plays an important role in improving the intrinsic catalytic performance of Ba-Ru-K/HSGC-x catalyst.     

Alkali metal cation doping of metal-organic framework for enhancing carbon dioxide adsorption capacity

Metal-organic frameworks （MOFs） have attracted much attention as adsorbents for the separation of CO2 from flue gas or natural gas. Here, a typical metal-organic framework HKUST-I（also named Cu-BTC or MOF-199） was chemically reduced by doping it with alkali metals （Li, Na and K） and they were further used to investigate their CO2 adsorption capacities. The structural information, surface chemistry and thermal behavior of the prepared adsorbent samples were characterized by X-ray powder diffraction （XRD）, thermo-gravimetric analysis （TGA） and nitrogen adsorption-desorption isotherm analysis. The results showed that the CO2 storage capacity of HKUST-1 doped with moderate quantities of Li＋, Na＋ and K＋, individually, was greater than that of unmodified HKUST-1. The highest CO2 adsorption uptake of 8.64 mmol/g was obtained with 1K-HKUST-1, and it was ca. 11% increase in adsorption capacity at 298 K and 18 bar as compared with HKUST- 1. Moreover, adsorption tests showed that HKUST-1 and 1K-HKUST-1 displayed much higher adsorption capacities of CO2 than those of N2. Finally, the adsorption/desorption cycle experiment revealed that the adsorption performance of 1K-HKUST-1 was fairly stable, without obvious deterioration in the adsorption capacity of CO2 after 10 cycles.     

Interconnected sandwich structure carbon/Si-SiO2/carbon nanospheres composite as high performance anode material for lithium-ion batteries

In the present work,an interconnected sandwich carbon/Si-SiO2/carbon nanospheres composite was prepared by template method and carbon thermal vapor deposition（TVD）.The carbon conductive layer can not only efficiently improve the electronic conductivity of Si-based anode,but also play a key role in alleviating the negative effect from huge volume expansion over discharge/charge of Si-based anode.The resulting material delivered a reversible capacity of 1094 mAh/g,and exhibited excellent cycling stability.It kept a reversible capacity of 1050 mAh/g over 200 cycles with a capacity retention of 96%.     

Performance of Co/MgO catalyst for C02 reforming of toluene as a model compound of tar derived from biomass gasification

Catalytic performances of the CO2 reforming of toluene on Co/MgO catalysts with different cobalt loadings were evaluated in a fluidized-bed reactor. The results showed that the conversion of toluene and the stability of Co/MgO increased, but the apparent reaction rate decreased at the initial stage with increasing the amount of metallic Co formed from the reduction of Co/MgO catalysts at 700 ~C. The deactivation of Co/MgO catalysts was mainly resulted from that a part of the metallic Co was oxidized by CO2 and could not be re-reduced by H2 at reaction temperature. Therefore, the excess metallic Co on the higher Co loading catalysts was beneficial to the catalyst stability.     

多壁碳纳米管修饰玻碳电极测定铜离子

以多壁碳纳米管(MWCNTs)修饰玻碳电极为工作电极,采用阳极溶出线性扫描法研究了铜离子的电化学测定方法。探讨了MWCNTs修饰层数、富集电位、富集时间、溶液pH、支持电解质对峰电流的影响。实验表明,铜离子浓度在1.0×10-8~1.0×10-5mol·L-1范围内与峰电流呈良好的线性关系,检测限为2.0×10-9mol·L-1,且该电极具有良好的稳定性和抗干扰能力。     

谷胱甘肽在高岭土修饰碳糊电极上的电化学研究

制备了高岭土修饰碳糊电极(KCPE),并以氢醌(HQ)为电催化介质测定还原型谷胱甘肽(GSH)。实验结果表明,在该电极上谷胱甘肽(GSH)的加入对氢醌的电化学响应有明显提高,且电催化氧化峰电流与GSH浓度呈良好的线性关系,由此可采用差分脉冲伏安法(DPV)对GSH进行定量测定。对修饰电极的电化学性能进行了表征,测得电极有效表面积为0.118 6 cm2、电荷传递系数为0.68、表观速率常数为1.08×104cm3·mol-1·s-1。在优化条件下,测得GSH在KCPE上的线性范围为0.1~1,2.5~25μmol/L,检出限为0.073μmol/L。用该方法对含GSH的市售药进行测定,结果满意。