YIHn: A New Family of Metal‐rich Hydride Halides

The graphite‐like yttrium hydride halides, YIH_n (0.8 ? n ? 1.0), have been prepared in quantitative yields by heating either YI₃, YH₂ (1:2) or stoichiometric YI₃, YH₂, Y mixtures in sealed Ta ampoules at 900°C. A lower limit of the homogeneity range, n ≈ 2/3, has been determined from dehydrogenation experiments. All YIH_n phases adopt the ZrBr‐type heavy‐atom structure. The hydrogen variation is accompanied by a change in the c lattice constant from 31.162(3) to 31.033(1) Å for n = 0.61(3) to 1.02(3). The YIH_n phases reversibly react with hydrogen at 400‐600°C to form the light green transparent compound YIH₂. However, increasing the reaction temperature above 700°C causes decomposition to an unidentified phase being in equilibrium with YH₂ and YI₃. The arrangement of the heavy atoms in YIH₂ (P m1; a = 3.8579(3) Å, c = 10.997(1) Å) corresponds to a four‐layer I‐Y‐Y‐I slab with the stacking sequence (AbaB) as was found by x‐ray powder diffraction data refinement with the Rietveld method. A miscibility gap exists between YIH and YIH₂. Samples YIH_n (n ? 1.0) show metallic conductivity at room temperature, which changes into semiconducting behavior with decreasing temperature as n approaches its lower value ≈ 2/3.     

The mixed valent tellurate SrTe3O8: Electronic lone pair effect of Te

A novel mixed valent tellurium oxide, SrTe₃O₈, has been synthesized and its crystal structure was determined ab initio from powder X-ray diffraction data. This oxide, which crystallizes in a tetragonal unit-cell, P4₂/m space group, with very close a and c cell parameters (6.8257(1) and 6.7603(1) Å, respectively), exhibits a very original structure built up of corner-sharing TeO₆ (Te⁶⁺) octahedra and Te₂O₈ (Te⁴⁺) twin-pyramidal units. The latter ones form [Te₃O₈]_∞ chains running along the [001] and the [110] directions. Besides the four sided tunnels where the Sr²⁺ cations are located, there are very large four sided tunnels running along the c-axis which are obstructed by the electronic lone pairs of the Te⁴⁺ cations.     

Multi-element characterization of silicon nitride powders by atomic and mass spectrometric solution methods

A sample pretreatment technique for silicon nitride involving digestion and matrix/traces separation was developed by means of radiotracers and applied to analysis of this material by inductively coupled plasma atomic emission spectrometry, inductively coupled plasma mass spectrometry and graphite furnace atomic absorption spectrometry. The results obtained for a high purity silicon nitride material by these methods are compared each with the other and with those obtained by neutron activation analysis. The limits of detection and the capabilities of the methods are compared and discussed.     

Bifonazole-β-cyclodextrin Inclusion Complexes. Thermal analysis and X-ray powder diffraction study

The complexation of bifonazole, an antimycotic hydrophobic imidazole derivative, with β-cyclodextrin (β-CD) was investigated in solid phase, using the following complementary techniques: differential scanning calorimetry (DSC), thermogravimetric analysis (TG) and X-ray powder diffractometry. The β-CD-bifonazole samples were prepared in both aqueous medium by coprecipitation and in solid state by kneading method and the β-CD-bifonazole binary diagrams were drawn. The experimental results demonstrate the formation of two binary compounds, β-CD-bifonazole and (β-CD)_x bifonazole (x =2 or 4). The first compound may be an inclusion compound and the second a crystallized compound, in which the bifonazole is not necessarily included in the cyclodextrin internal cavity. This revised version was published online in July 2006 with corrections to the Cover Date.     

H2S-sensing properties of SnO2 produced by ball milling and different chemical reactions

In this work, the mechanochemical synthesis of a moderately agglomerated tin oxide (SnO₂) powders and the subsequent preparation of semiconductor gas sensors as prototypes, were studied. Tin (II) chloride (SnCl₂) powder was milled with calcium hydroxide (Ca(OH)₂) and potassium carbonate, (K₂CO₃) powder, respectively, in a ball mill at room temperature and in an air atmosphere. Heat treatment of milled mixtures at 400 °C resulted in the formation of a tetragonal phase, confirmed by X-ray diffraction (XRD). During milling in the presence of water, a high number of hydroxide (OH) groups are formed at the surface. When SnCl₂ was milled with K₂CO₃, no water was produced and the Fourier-transform infrared spectrum (FT-IR) of the powder has no surface hydroxyl deformations. On exposure to hydrogen sulfide (H₂S) gas, the particles, prepared from anhydrous powder, have higher sensitivity than these, prepared from hydrated powder. The SnO₂ thick film, prepared from anhydrous powder may be successfully applied to a H₂S gas sensor.     

改进的微波辅助无溶剂法提取薄荷和陈皮中的挥发油组分

An improved solvent free microwave extraction, in which a kind of microwave absorption medium （carbonyl iron powder） was used, was applied to the extraction of essential oil from dried menthol mint and orange peel without addition of any solvent and pretreatment. It took much less time of extraction （30 min） than microwave-assisted hydrodistillation （90 min） and conventional hydrodistillation （180 min）. The kinds of chemical compositions in essential oil extracted by different methods were almost the same and such improved solvent free microwave extraction can be a feasible way in extraction of essential oil from dried plant materials.     

Structural disorder in Ba0.6Sr0.4Al2O4

The structural disorder in Ba_0.6Sr_0.4Al₂O₄ (space group P6₃22) was investigated by X-ray powder diffraction and selected-area electron diffraction (SAED). The initial structural model was determined using direct methods, and it was further modified by the combined use of Rietveld method and maximum-entropy method (MEM). MEM-based pattern fitting method was subsequently applied, resulting in the final reliability indices of R_wp=9.61%, R_p=6.96%, R_B=1.40% and S=1.25. The electron density distribution was satisfactorily expressed by the split-atom model in which the strontium/barium and oxygen atoms were split to occupy the lower symmetry sites. The diffuse scattering in SAED was mainly attributable to the positional disorder of oxygen atoms.     

溶液还原法制备球形超细镍粉

超细镍粉由于表面活性高、导电性和导热性好而被广泛应用于化学催化剂、烧结活化剂、导电浆料门等方面．目前，制备超细镍粉的方法主要有问：真空蒸馏冷凝法、机械粉碎法、电解法、羰基镍热分解法、浆化氢还原法和溶液还原法等．在这些方法中，溶液还原法的工艺简单，所得粉末纯度高，颗粒尺寸小且分布均匀[3]．法国的Figlarz等[4]用弱有机还原剂乙二醇还原粒径小干0．1μm的Ni（OH）2。超细粉末，引入AgNO3。作为成核剂后，制得了粒径＜1μm的超细镍粉，但这种方法需长时间高温回流反应，对原料要求苛刻，且采用有机分散介质成本较高，…     

锂离子电池正极材料LiMn2O4的低热固相合成与性能表征

锂离子电池具有比能量高、环境污染小等优点,广泛应用于手提电话、便携式电脑、摄像机等设备中。其正极材料的研究是锂离子电池的研究重点。层状结构的LiCoO2、LiNiO2和尖晶石结构的LiMn2O4是仅有的三种能在3.5V以上电位可嵌入Li的正极材料[1~3]。目前市售的锂离子电池主要采用LiCoO2作正极材料,但由于Co资源缺乏和价格相对昂贵,而锰资源丰富,价格低廉且无毒,对环境友好,因此世界各国都在大力进行以LiMn2O4为正极材料的锂离子电池的实用化研究。LiMn2O4传统的制备方法是高温固相反应合成法[4~7],但由于Mn的变价多,与Li形成贫Li或…     

Synthesis, characterization and thermal properties of small R2R2NX-type quaternary ammonium halides

Twenty-one R₂R^′₂N⁺X⁻ -type (R=methyl or ethyl, R^′=alkyl, X=Br or I) quaternary ammonium (QA) halides have been prepared by using a novel one-pot synthetic route in which a formamide (dimethyl-, diethylformamide, etc.) is treated with alkyl halide in the presence of sodium or potassium carbonate. The formation of QA halides was verified with ¹H-NMR, ¹³C-NMR, MS and elemental analysis. The crystal structures of four QA halides (two bromide and two iodide) were determined using X-ray single crystal diffraction, and the powder diffraction method was used to study the structural similarities between the single crystal and microcrystalline bulk material. The thermal properties of all compounds were studied using TG/DTA and DSC methods. The smallest compounds decomposed during or before melting. The decreasing trend of melting points was observed when the alkyl chain length was increased. The liquid ranges of 120-180 °C were observed for compounds with 5-6 carbon atoms in the alkyl chain. The low melting points and wide liquid ranges suggest potential applicability of these compounds for example as ionic liquids precursors.