魔芋葡甘聚糖/聚乙烯醇纳米纤维膜及其释药行为研究

为了研制药物缓释效果优良的薄膜材料,利用静电纺丝设备研制不同比重的魔芋葡甘露聚糖/聚乙烯醇纳米纤维膜,并通过扫描电镜、傅里叶变换红外光谱和示差扫描量热法表征纳米纤维膜的结构和性能,结合体外实验和数学模型研究其缓释行为.结果显示当魔芋葡甘露聚糖含量占纳米纤维膜总质量约76%时,纳米纤维膜中微纤丝粗细最均匀且结点较少,纳米纤维膜中魔芋葡甘聚糖和聚乙烯醇之间存在明显的相互作用,含有5-氨基水杨酸的纳米纤维膜在pH=7.4 PBS磷酸盐缓冲液中25 h的累积释放量大约为45%,显示出良好的药物缓释效果,其缓释行为与Higuchi模型具有较高的拟合度.研究表明利用静电纺丝设备研制的魔芋葡甘聚糖/聚乙烯醇纳米纤维膜可以为药物缓释载体的开发提供理论依据.     

明胶/葡甘聚糖/聚乙烯醇缓释肥料包膜的表征

以甲醛作交联剂,甘油为增塑剂,用溶液共混法制备了明胶/葡甘聚糖/聚乙烯醇缓释尿素包膜。采用红外光谱(FT-IR)、X-射线衍射、扫描电镜、热重分析和差示量热扫描等表征了包膜的结构,结果表明该条件下包膜中原料之间产生了较强的相互作用,形成了一个较稳定的复合体。     

响应面法优化棉籽壳木聚糖的超声提取工艺

以木聚糖提取率为评价指标,提取温度、NaOH浓度、提取时间为自变量,进行3因素3水平Box-Behnken实验设计,利用响应面法优化新疆棉籽壳中木聚糖的超声辅助碱法提取工艺.结合实际可操作性得出最佳提取工艺为固定超声功率150W,按照料液比1∶14(g/mL)加入7％ NaOH溶液,70℃下提取80min,木聚糖提取率为36.77％,达到预测值的99.6％.Box-Behnken实验设计用于优化木聚糖的提取工艺稳定、可行.     

GPC-LS联用法研究魔芋葡甘聚糖分子链形态

采用凝胶渗透色谱-激光光散射联用(GPC-LS)研究了经酶解后的魔芋葡甘聚糖(KGM)重均分子量(Mw)、均方根旋转半径(Rg)、构象指数(β)与温度的相关性,并结合KGM的特性粘度拟合酶解KGM的Mark-Houwink方程。结果显示:Rg与Mw表现出近似的正相关性,且Mw、Rg及β随温度升高而逐渐增大,酶解KGM的Mark-Houwink方程为[η]=5.9×10-1Mw0.562。     

魔芋全降解荧光薄膜的制备和性能研究

魔芋精粉糊化后加入改性剂NaOH、增塑剂甘油、交联剂甲醛及CaS:Eu红色荧光粉,混合溶胶在自然条件下干燥成膜,测试了薄膜的光学、力学性能.结果表明,薄膜荧光光谱与其添加的荧光粉光谱一致,具有吸收紫外光和绿光发射645nm红光的作用,薄膜转光行为有利于植物光合作用,可用于农作物栽培;薄膜力学性能较好,可见光区透光率在68%-70%.     

Studies on the Hydrogen Bonding Network Structures of Amino-konjacglucomannan-zinc Chelate

Amino-Konjacglucomannan(NH2-KGM) was prepared through the reaction of ammonium hydroxide with KGM by ultrasonic. The influence of amount of ammonium hydroxide, concentration of KGM and ultrasonic time on the extent of amination was studied. Then, NH2-KGM and zinc sulfate were used as materials for the preparation of NH2-KGM-Zn complex. The results indicated that the extent of amination increases with increasing the ammonium hydroxide. The optimum concentration of KGM and ultrasonic time are 0.3% and 75 min respectively. IR showed KGM is successfully aminated and NH2-KGM forms stable complex with zinc(Ⅱ). The hydrogen bonding network structures of NH2-KGM-Zn are more stable and the key linking points of hydrogen bonding network are at the OH(6) and O(3) positions of mannose and OH(2) of glucose and O(3) of mannose on the KGM ring. It is more favorable for NH2-KGM-Zn to form intermolecular hydrogen bonds between KGM.     

蔗渣木聚糖磷酸酯-壳聚糖水凝胶的制备及其药物缓释作用

以蔗渣木聚糖磷酸酯和壳聚糖为主要原料,三聚磷酸钠为离子交联剂,制备了蔗渣木聚糖磷酸酯-壳聚糖水凝胶,并用SEM、IR表征了其结构。考察了影响制备及水凝胶粒子应用的因素,探讨了诸因素对水凝胶性能的影响。通过正交试验,分别得出两种方法制备水凝胶的优化条件:在pH=1.7的缓冲溶液中,蔗渣木聚糖磷酸酯浓度为0.10g/mL,壳聚糖浓度为0.04g/mL,三聚磷酸钠的浓度为0.20g/mL,成膜时间120min,用直接造粒法;在pH=6.8的缓冲溶液中,蔗渣木聚糖磷酸酯浓度为0.10g/mL,壳聚糖浓度为0.04g/mL,三聚磷酸钠浓度为0.20g/mL,成膜时间为90min,用间接造粒法。在优化制备条件下,通过模拟十二指肠缓冲溶液,得出在pH 4.8、三聚磷酸钠浓度为0.20mol/L时,水凝胶的载药量和药物释放行为较佳。