中空介孔SiO2纳米球的制备、改性及其对Al3+荧光识别研究

中空介孔SiO2由于中空多孔的结构而常用作功能材料的基底.将中空介孔SiO2进行官能团修饰,并应用为荧光传感材料是中空介孔SiO2一个重要的研究领域.本论文采用聚丙烯酸(PAA)为中空模板,聚醚F127为造孔剂,正硅酸乙酯(TEOS)为硅源,氨水为催化剂在乙醇体系中制备了中空介孔SiO2纳米球.系统研究了搅拌速度和聚醚F127引入量对中空介孔SiO2纳米球形貌及比表面积的影响.通过透射电镜、N2-等温吸附脱附曲线等表征说明该合成方法具有很好的普适性,通过调节F127的引入可以实现对比表面积的有效控制.通过氨基化、席夫碱反应进行荧光修饰,进一步研究表明荧光修饰后的中空介孔SiO2纳米球在水溶液中能够实现对Al3+的有效检测,检测限为1.19×10 -7M.     

烧结温度对煤系高岭土制备堇青石陶瓷的影响

我国的煤系高岭土具有明显的资源优势,应对其进行充分地研究和合理地应用,以缓和优质高岭土资源枯竭的燃眉之急.以鄂尔多斯煤系高岭土、鄂尔多斯滑石、工业氧化铝为原料,通过反应烧结一步合成堇青石,探讨了堇青石合成温度范围,以拓宽该煤系高岭土的应用范围.通过高温显微镜观察堇青石试样的合成温度范围为1400～1420℃.经1420℃合成的堇青石试样的吸水率为16.11;,显气孔率为28.44;,体积密度为1.77 g/cm3,径向烧成收缩为1.77;,厚度烧成收缩为4.80;,抗折强度为43.56 MPa.镁铝尖晶石是合成堇青石的重要中间产物,适当提高烧结温度可以促进镁铝尖晶石相向堇青石相转变,有利于堇青石晶粒的生长与发育.烧结温度的变化是堇青石晶粒发生变化的原因,同时导致液相量的变化,最终影响堇青石试样显微结构和烧结性能.     

Characteristics of black carbon aerosol in Jiaxing,China during autumn 2013

We conducted measurements of black carbon（BC） aerosol in Jiaxing,China during autumn from September 26 to November 30,2013.We investigated temporal and diurnal variations of BC,and its correlations with meteorological parameters and other major pollutants.Results showed that hourly mass concentrations of BC ranged from 0.2 to 22.0 μg/m³,with an average of 5.1 μg/m³.The diurnai variation of BC exhibited a bimodal distribution,with peaks at 07:00 and 18:00.The morning peak was larger than the evening peak.The mass percentages of BC in PM_2.5 and PM₁₀ were 7.1%and 4.8%,respectively.The absorption coefficient of BC was calculated to be 44.4 Mm^-1,which accounted for 11.1%of the total aerosol extinction.BC was mainly emitted from local sources in southwestern Jiaxing where BC concentrations were generally greater than 11 μg/m³ during the measurement period.Correlation analysis indicated that the main sources of BC were motor vehicle exhaust,and domestic and industrial combustion.     

Atomic-scale simulations for lithium dendrite growth driven by strain gradient

Dendrite formation is a major obstacle, e.g., capacity loss and short circuit, to the next-generation high-energy-density lithium (Li)-metal batteries. The development of successful Li dendrite mitigation strategies is impeded by an insufficient understanding in Li dendrite growth mechanisms. The Li-plating-induced internal stress in Li-metal and its effects on dendrite growth have been widely studied, but the underlying microcosmic mechanism is elusive. In the present study, the role of the plating-induced stress in dendrite formation is analyzed through first-principles calculations and ab initio molecular dynamic (AIMD) simulations. It is shown that the deposited Li forms a stable atomic nanofilm structure on the copper (Cu) substrate, and the adsorption energy of Li atoms increases from the Li-Cu interface to the deposited Li surface, leading to more aggregated Li atoms at the interface. Compared with the pristine Li-metal, the deposited Li in the early stage becomes compacted and suffers the in-plane compressive stress. Interestingly, there is a giant strain gradient distribution from the Li-Cu interface to the deposited Li surface, making the deposited atoms adjacent to the Cu surface tend to press upwards with perturbation and causing the dendrite growth. This provides an insight into the atomicscale origin of Li dendrite growth, and may be useful for suppressing the Li dendrite in Li-metal-based rechargeable batteries.     

The Effect of the Spacer of Bis(biurea) Ligands on the Structure of A2L3‐type (A=anion) Phosphate Complexes

By tuning the length and rigidity of the spacer of bis(biurea) ligands L, three structural motifs of the A₂L₃ complexes (A represents anion, here orthophosphate PO₄^3?), namely helicate, mesocate, and mono‐bridged motif, have been assembled by coordination of the ligand to phosphate anion. Crystal structure analysis indicated that in the three complexes, each of the phosphate ions is coordinated by twelve hydrogen bonds from six surrounding urea groups. The anion coordination properties in solution have also been studied. The results further demonstrate the coordination behavior of phosphate ion, which shows strong tendency for coordination saturation and geometrical preference, thus allowing for the assembly of novel anion coordination‐based structures as in transition‐metal complexes.     

GZO/Al复合背电极对非晶硅太阳能电池的影响

随着能源紧缺与环境污染问题的日益严重,太阳能的开发利用越来越受到重视,其中非晶硅薄膜太阳能电池由于其制备工艺简单、价格低廉等优点被广泛地研究.为了使非晶硅薄膜太阳能电池得到更好地利用,提高其转换效率和稳定性显得尤为重要.引入复合背电极是提高非晶硅太阳能电池性能的有效手段,其中对GZO/Al复合背电极的研究还未见报道.在该工作中,利用磁控溅射法在非晶硅电池上制备了GZO/Al复合背电极,研究了复合背电极的制备条件及其对非晶硅太阳能电池性能的影响.结果显示,当GZO层的溅射功率为90 W、Al层的溅射功率为90 W时,具有复合背电极的太阳能电池表现出较好的光电转换性能,其短路电流(ISC)、开路电压(VOC)、填充因子(FF)和电池的光电转换效率(η)分别为8.92 mA、1.55 V、54.48;和7.53;.相较于单层Al背电极的太阳能电池,其光电转换效率大幅提高了47.6;(相对效率).     

A multiaxial elastic potential with error-minimizing approximation to rubberlike elasticity

This study is concerned with a new,explicit approach by means of which forms of the large strain elastic potential for multiaxial rubberlike elasticity may be obtained based on data for a single deformation mode.As a departure from usual studies,here for the first time errors may be estimated and rendered minimal for all possible deformation modes and,furthermore,failure behavior may be incorporated.Numerical examples presented are in accurate agreement with Treloar's well-known data.     

Te溶剂Bridgman法CdMnTe晶体核辐射探测器的制备和表征

碲锰镉(CdMnTe)作为性能优异的室温核辐射探测器材料,可用于环境监测和工业无损检测领域。本文中采用Te溶剂Bridgman法生长In掺杂Cd_0.9Mn_0.1Te晶体,制备成10 mm×10 mm×2 mm大小的室温单平面探测器,研究了该探测器对²⁴¹Am@59.5 keV γ射线源的能谱响应。通过表征红外透过率、电阻率以及探测器能谱响应等参数,综合评定了探测器用CdMnTe晶体的质量、电学和探测器性能。结果表明,晶片的红外透过率均在55%以上,最好可达到60%。采用湿法钝化,100 V偏压下的漏电流由钝化前的9.48 nA降为钝化后的7.90 nA,钝化后的电阻率为2.832×10¹⁰ Ω·cm。在-400 V反向偏压下,CdMnTe探测器对²⁴¹Am@59.5 keV γ射线源的能量分辨率在钝化前后分别为13.53%和12.51%,钝化后的电子迁移率寿命积为1.049×10^-3 cm²/V。研究了探测器的能量分辨率随电压的变化特性,当偏压≤400 V时,探测器的能量分辨率主要由载流子的收集效率决定,而当偏压>400 V时,能量分辨率由漏电流决定。本文研究结果表明,Te溶剂Bridgman法生长的CdMnTe晶体质量较好,电阻率和电子迁移率寿命积满足探测器制备需求。