白云鄂博天然钕独居石的振动光谱研究(英文)

Raman, infrared and energy dispersive X-ray spectra of monazites have been measured and discussed. The result shows that the mineral is enriched in cerium, lanthanum,neodymium and praseodymium (Ce＞La＞Nd＞Pr)， The monazites have marked spectral characteristics, especially their v1, V3 Raman bands and v1, v4 infrared absorption bands. The characteristics can distinguish between monazite and other phosphate minerals. In addition, based on EDS and infrared absorption spectra, a small amount of fluoro-carbonate is found in the monazites.     

RyMxCO4-xSb12化合物的晶格热导率

系统地研究了离子半径不同的Ba，Ce，Y作为填充原子及Fe，Ni作为置换原子对填充化合物RyMxCO4-xSb12晶格热导率的影响规律．结果表明：在skunemdite结构的sb组成的20面体空洞中，Ba，Ce，Y的填充原子能显著降低其晶格热导率，且晶格热导率降低幅度按Ba，Ce，Y离子半径减小的顺序而增大．Sb组成的20面体空洞部分被Ba，Ce填充时，晶格热导率最小，填充原子的扰动对声子的散射作用最强．在Co位置上Fe和Ni的置换，能显著地降低RyMxCO4-xSb12化合物的晶格热导率，与Fe相比，Ni对晶格热导率的影响更强．     

新铌酸盐Ba_3Ni_(0.33)Nb_(4.67)O_(15)的合成与X射线衍射分析

在BaO -Ni2O3 -Nb2O5 三元系统中 ,用固相反应法合成了新铌酸盐Ba3Ni0.33Nb4.67O15。以BaCl2 和B2O3为主要助熔剂制备了Ba3Ni0.33Nb4.67O15 的单晶体。利用四圆单晶衍射仪测定晶胞参数 ,然后采用X射线粉晶衍射法进行了物相分析,对该化合物的粉晶衍射数据进行了指标化 ,并报道了其X射线衍射数据。分析结果表明 ,该化合物属于填满型四方钨青铜结构 ,空间群P4bm(100),晶胞参数为 :a=1.26092(5)nm ,c=0.40096(4)nm ,α=β=γ=90°,Z=2。     

酞菁钴/铁纳米填充母粒的制备及其稳定性

采用有机／无机原位复合技术，将酞菁钴（ＣｏＰｃ）的ＤＭＦ溶液与Ｆｅ（ＣＯ）５混合、加热回流制备出稳定的、规则球形的、平均粒径为１．４μｍ的酞菁钴／铁纳米填充母料。其内部为１０￣１５ｎｍ的α－Ｆｅ填充，外部为厚５０￣１５０的酞菁钴层包覆。纳米填充母粒的填３实密度为３．６６４ｇ／ｃｍ＾３，比饱和磁化强度为７６．３Ａｍ＾２／ｋｇ，矫顽力为４．１５ｋＡ／ｍ，纳米填充母粒的热稳定性高于１５０℃，与甲基硅油组     

PEG链段对聚乙二醇接枝聚苯胺结构与性能的影响

将苯胺(An)与甲氧基聚乙二醇邻氨基苯基醚氧化共聚,制备了梳状接枝共聚物PAn-g-PEG.研究了梳状接枝共聚物的UV-Vis、微观结构、热稳定性和溶解成膜性等随侧链聚乙二醇(PEG)链段的变化规律.结果表明随PAn-g-PEG中PEG链段长度和含量的提高,共聚物的溶解性和成膜性能显著提高,电子导电率缓慢降低,热稳定性变差.共聚物具有微相分离结构,其形态随PEG链段的改变分别为“海-岛相”和“双连续相”;提高PEG链段长度和含量,PAn-g-PEG能形成稳定的水溶性分散体系,并能浇注成柔韧平整的导电高分子自支撑膜.     

Nafion聚离子修饰钠米Pt的合成及其影响因素

采用化学还原的方法成功地合成了Nafion聚离子修饰的纳米Pt颗粒,平均粒径为～4 nm;由于表面缺电子的特性,纳米Pt粒子与Nafion高分子长链上的-SO-3基团有较强的结合,使粒子随-SO-3的存在状态而分散,在水溶液中呈现与离子团簇相似的分散状态.FTIR显示Pt颗粒存在表面原子暴露在修饰离子之外,因此,这种粒子在具有功能结构的催化领域有着很好的应用前景;合成过程中反应速率随Nafion含量的降低、pH的增加而增大.     

层状类钙钛矿结构新铌酸盐KSr2Nb3O10

A new niobate compound KSr₂Nb₃O₁₀ was synthesized for the first time. The chemical compositions, crystal structure, optical property, density and melting point of the new compound were characterized by EPMA, TEM, XRD, DTA and so on. KSr₂Nb₃O₁₀ crystallizes the orthorhombic system with unit cell parameters a=0.7816(1) nm, b=0.7764(2) nm, c=2.9995(2) nm, V=1.8114(4) nm³, and space group P2₁2₁2₁, Z=8. The structure may be described as treble perovskite sheets ［Sr₂Nb₃O₁₀］^- interleaved with K⁺. Further, it was found that KSr₂Nb₃O₁₀ has intercalation phenomenon. Na⁺, Li⁺, H⁺, NH⁺₄ could exchange the interlayer cations K⁺ of KSr₂Nb₃O₁₀, and n-hexylamine also could intercalate into the place between the layers of ［Sr₂Nb₃O₁₀］^-.     

填充式skutterudite化合物:BayFexCo4-xSb12的多步固相反应合成及结构

以Ba为填充原子 ,在x =0— 3 0 ,y=0— 0 7的组成范围内 ,用多步固相反应法合成了单相BayFexCo4 -xSb12 化合物 .用Rietveld方法对结构的精确化结果表明 :合成的BayFexCo4 -xSb12 化合物具有填充式skutterudite结构 ,Ba的热振动参数 (B)比Sb,Fe/Co的大 ,表明在BayFexCo4 -xSb12 化合物中Ba具有扰动效果 .晶格常量随Ba填充分数及Fe含量的增大而增大 .在BayFexCo4 -xSb12 化合物的Sb的 2 0面体空洞中 ,Ba的最大填充分数随Fe含量的增大而增大 ,并明显地大于Ce的填充分数 .当Fe含量从 0增大到 4 0时 ,Ba的最大填充分数从 0 35增大到 1 0左右     

微波等离子CVD金刚石设备中基片加热材料的三维温度场型研究

在微波等离子CVD设备中,微波电磁场的不均匀分布将导致等离子球和基片的温度不均匀,从而降低CVD金刚石的质量,因而基片加热是需要的.材料的吸收微波能的能力同微波频率、电场强度、材料的介电常数和介电损耗及材料体积相关,材料的介电常数、介电损耗、导热率又同温度相关.基于热力学理论,本文用强吸收微波能的SiC材料作为了基片加热材料,放在微波等离子腔的基片下,研究三维轴对称温度场模型,该模型的基片加热材料的介电常数、介电损耗和体积随温度变化,获得了温度分布的解析式,计算结果显示该模型能得到直径76.2mm的均匀温度分布,温度变化少于10℃,因而可用于基片加热.     

微波等离子化学气相沉积金刚石膜涂层氮化硅刀具

金刚石的成核和生长影响金刚石膜的质量.本文用自制的一种新型的不锈钢谐振腔型微波等离子CVD设备,等离子直径为76mm,均匀的温度分布使得金刚石膜均匀生长,在不同工艺条件下研究Si3N4陶瓷刀具上金刚石涂层的成核质量,用SEM,Raman检测和分析研究了在Si3N4刀具上高速高质量生长金刚石膜涂层的制备工艺,并检测了涂层刀具的切削性能,切削试验表明,在切削18wt;Si-Al合金时,金刚石涂层刀具比未涂层刀具的使用寿命增多10倍以上.