Mg_(0.9-x)Ti_(0.1)Pd_xNi(x=0.04～0.1)贮氢合金电极腐蚀行为研究

研究了Pd部分替代Mg对Mg0.9-xTi0.1PdxNi(x=0.04～0.1)贮氢合金腐蚀性能的影响.利用机械合金化方法制备了Mg0.9-xTi0.1PdxNi(x=0.04～0.1)贮氢合金.XRD和TEM分析表明经120h球磨后该合金完全非晶化.循环充放电测试结果表明,Pd的替代有效地延长了Mg0.9-xTi0.1PdxNi(x=0.04～0.1)合金的循环寿命.采用开路电位测量,阳极极化,电化学阻抗和X射线光电子能谱研究了该合金的腐蚀行为.结果表明,随着Pd含量增加,合金腐蚀电位正移,初始腐蚀电流下降,腐蚀电流增加的速度变缓.采用本文提出的等效电路模型较好地拟合了合金的电化学阻抗谱.分析表明,随着Pd含量的增加,合金表面钝化膜厚度和电阻逐渐增大.X射线光电子能谱分析表明,Pd的加入减弱了合金在充放电过程中的氧化程度.当Pd含量达到0.1时,Mg0.9-xTi0.1PdxNi(x=0.04～0.1)合金的耐腐蚀性能最好,其放电容量保持率最高.     

Microencapsulation of n-Eicosane as Energy Storage Material

For heat energy storage application, polynrea microcapsules containing phase change material, n-eicosane, were synthesized by using interfacial polymerization method with toluene-2,4-diisocyanate (TDI) and diethylenetriamine(DETA) as monomers in an emulsion system. Poly(ethylene glycol)octyl-phenyl ether (OP), a nonionic surfactant,was the emulsifier for the system. The experimental result indicates that TDI was reacted with DETA in a mass ratio of 3 to 1. FF-IR spectra confirm the formation of wall material, polyurea, from the two monomers, TDI and DETA.Encapsulation efficiency of n-eicosane is about 75%. Microcapsule of n-eicosane melts at a temperature close to that of n-eicosane, while its stored heat energy varies with core material n-eicosane when wall material fixed.Thermo-gravimetric analysis shows that core material n-eicosane, micro-n-eicosane and wall material polyurea can withstand temperatures up to 130, 170 and 250℃, respectively.     

纳米三氧化二钴低温热容和热力学性质的研究

The isobaric molar heat capacities of nano Co₂O₃ were determined by an adiabatic calorimeter in the temper-ature range from 78 to 350K. No phase transition takes place in this temperature range. The relationship of C_p，m with respect to thermodynamic temperature T was established as C_p，m=-11.998X³-9.6431X²+63.478X+81.291(J·K^-1·mol^-1) ， where X=(T-201.903)/121.535， the correlation coefficient R₂=0.9996. Ac-cording to this relationship and the relationships between thermodynamic functions， the thermodynamic functions of nano Co₂O₃ relative to the standard temperature of 298.15K were derived based on the measured heat capacity data. The average grain size of the studied nano Co₂O₃ sample was determined to be 12nm by TEM.     

Studies on optimization of a platinum catalyst and porphine modified, pyrolytic graphite, amperometric, glucose sensor by sequential level elimination experimental design

A new amperometric glucose sensor based on the glucose oxidase immobilized on pyrolytic graphite (PG) modified with tetraammineplatinum(II) chloride (TAPtCl) and 5,10,15,20-tetrakis (4-methoxy-phenyl)-21H,23H-porphine cobalt(II) (TMPPCo) as well as Nafion was studied. The performances amongst the glucose sensors with or without TAPtCl or/and TMPPCo measured with oxygen present in the solution were compared. The compositions of the membranes of the glucose sensors were optimized by a new orthogonal experimental design technique–sequential level elimination method according to chemometric approaches. Our studies show that the prepared sensor with optimal membrane composition in this study gives satisfactory performance in terms of long-term stability, fast amperometric response, good detection limits and satisfactory recovery. The study provides a useful basis for developing other sensors with corresponding optimal membranes.     

磺苄青霉素药物电极的研究

报道了一种磺苄青霉素药物电极，以十六烷基三辛基碘化铵为载体，用邻苯二甲酸二壬酯为增塑剂，运用序贯淘汰水平法对膜组成进行了优化；确定了电极最佳膜组成，讨论了一些因素对电极性能的影响。电极响应快速，选择性、稳定性、重现性均较好。电极检测下限可达１．６６×１０＾－６ｍｏｌ／Ｌ，线性范围为６．０３×１０＾－６～１．０×１０＾－１ｍｏｌ／Ｌ，斜率为２８．０ｍＶ／ｐＣ，回收率为９６．１％～１００．４％。可用…     

Low-temperature heat capacity and standard molar enthalpy of formation of the complex Zn(Thr)SO4·H2O (s)

Low-temperature heat capacities of the complex Zn(Thr)SO₄·H₂O (s) have been precisely measured with a small sample adiabatic calorimeter over the temperature range from 78 to 373 K. The initial dehydration temperature of the complex (T_d=325.50 K) has been obtained by analysis of the heat-capacity curve. The experimental values of molar heat capacities have been fitted to a polynomial equation by least square method. The standard molar enthalpy of formation of the complex has been determined from the enthalpies of dissolution (Δ_dH_m^Θ) of [ZnSO₄·7H₂O (s) +Thr (s)] and Zn(Thr)SO₄·H₂O (s) in 100 ml of 2 mol dm⁻³ HCl solvent as: Δ_fH_{m,Zn(Thr)SO4·H2O}^Θ=−2111.7±3.4 kJ mol⁻¹. These experiments were made by using an isoperibol solution calorimeter at 298.15 K.     

Mg0.9－xTi0.1PdxNi(x=0.04～0.1)贮氢合金电极腐蚀行为研究

研究了Pd部分替代Mg对Mg0.9－xTi0.1PdxNi(x=0.04～0.1)贮氢合金腐蚀性能的影响. 利用机械合金化方法制备了Mg0.9－xTi0.1PdxNi(x=0.04～0.1)贮氢合金. XRD和TEM分析表明经120 h球磨后该合金完全非晶化. 循环充放电测试结果表明, Pd的替代有效地延长了Mg0.9－xTi0.1PdxNi(x=0.04～0.1)合金的循环寿命. 采用开路电位测量, 阳极极化, 电化学阻抗和X射线光电子能谱研究了该合金的腐蚀行为. 结果表明, 随着Pd含量增加, 合金腐蚀电位正移, 初始腐蚀电流下降, 腐蚀电流增加的速度变缓. 采用本文提出的等效电路模型较好地拟合了合金的电化学阻抗谱. 分析表明, 随着Pd含量的增加, 合金表面钝化膜厚度和电阻逐渐增大. X射线光电子能谱分析表明, Pd的加入减弱了合金在充放电过程中的氧化程度. 当Pd含量达到0.1时, Mg0.9－xTi0.1PdxNi(x=0.04～0.1)合金的耐腐蚀性能最好, 其放电容量保持率最高.     

室温离子液体电化学稳定性的研究

随着绿色化学的发展,人们对室温离子液体(RTIL)的研究已日益备受重视,较早发现的如由二烷基咪唑正离子(EMI^ )和氯化铝负配离子(A1Cl4^-)组成的离子液体(氯化铝类离子液体),具有许多优良的物理化学性质,如电导率高,在高温下仍有很低的蒸汽压,电化学稳定性好(即有宽阔的电化学窗口),     

四元Mg0.9Ti0.1Ni0.9X0.1(X=Mn,Zn,Co,Fe)系列合金的制备及性能研究

用机械合金化法合成了Mg0·9Ti0·1Ni0·9X0·1(X=Mn,Zn,Co,Fe)系列合金.X射线衍射(XRD)结构分析表明,用X部分替代Ni后,促进了Mg0·9Ti0·1Ni合金的非晶化过程.用Co和Fe部分替代Ni提高了合金的放电容量,但却降低了合金的循环稳定性.用Zn和Mn部分替代Ni提高了合金电极的循环寿命,尤其是Mg0·9Ti0·1Ni0·9Zn0·1合金电极经10个充放电循环后,其放电容量仍可达到313·8mA·h/g.对添加Co后的合金进行p-c-T测试发现,Mg0·9Ti0·1Ni0·9Co0·1合金的吸放氢容量明显比Mg0·9Ti0·1Ni合金高,这与电化学所测到的结果一致.     

三元脂肪酸/膨胀石墨复合相变材料的制备、包覆定形及热性能

采用癸酸、 月桂酸和棕榈酸的三元共晶混合物作为相变材料, 以膨胀石墨为基体, 通过膨胀石墨多孔结构的毛细吸附和复合涂饰剂的包覆定形, 将多元相变材料固定在膨胀石墨的孔道结构中, 制备出结构稳定、 密封性能优异、 热稳定性好和高导热的新型三元脂肪酸/膨胀石墨复合定形相变材料. 膨胀石墨具有膨胀疏松的多孔结构和良好的吸附性能; 其熔融潜热为95.6 J/g, 结晶焓为82.8 J/g, 说明其具有很好的相变蓄热特性和热循环稳定性; 材料的导热性能可增加至0.738 W/(m·K), 与脂肪酸相比得到大幅度提高.