N-烷基壳聚糖玻璃化转变温度的研究

采用差示扫描量热(DSC)法和热释电流(TSC)法研究了N-烷基壳聚糖的玻璃化转变行为. DSC法中采用二次扫描以消除溶剂和热历史的影响, 并利用物理老化方法来增强N-烷基壳聚糖在DSC曲线上的玻璃化转变区域的热焓吸热峰, 以克服DSC法的不灵敏性. 两种研究方法的结果一致表明, 三种N-烷基壳聚糖的玻璃化转变均发生在110～150 ℃温区内；取代的柔性烷基越大, 玻璃化转变温度(Tg)越低；但N-甲基壳聚糖例外, 其Tg略高于壳聚糖, 空间阻碍在这里起决定的作用.     

氨基酸水杨醛席夫碱与铜(Ⅱ)配合物的合成及其抗菌活性和稳定性、结构间的关系

n-Salicylideneamino acids and their Cu(Ⅱ) complexes are synthesized. The structures of the compounds are characterized by elementary analysis, molar conductance, magnetic susceptibility, electronic and infrared spectra. The stability constants and the antibacterial activities have been determined. The relativity between antibacterial activities and structures of ligands and stability of complexes has been preliminarily studied.     

选相示波伏安法

选相示波伏安法毕树平，都思丹，高鸿（南京大学化学系，２１０００８）关键词示波计时电位法，选相示波伏安法，切口示波计时电位法是利用ｄＥ／ｄｔ～Ｅ曲线上切口的高度或深度进行定量分析的方法［１］，但由于ｄＥ／ｄｔ曲线主要反映充电电流的变化，从而使该方法的检...     

超临界水中聚乙烯油化的研究

采用125mL间歇式高压釜反应器，在超临界水条件下考察了反应温度、反应时间、水/聚乙烯比和水填充率对聚乙烯降解油化的影响。实验结果表明,聚乙烯在超临界水中迅速降解，油收率可达90%以上；随温度从450℃提高到480℃，油收率从91.4％下降到61.7％，气体收率从1.9％提高到27.7％；在450 ℃反应时间从1 min延长到30 min时，油收率略有下降，油品中C7-11组分所占比例增大一倍。水/聚乙烯比和水填充率的增加在一定程度上对聚乙烯的降解起抑制作用。     

TiO2-双亲共聚物复合纳米粒子的合成与紫外光敏特性

用偶联剂乙烯基三乙氧基硅烷改性纳米粒子TiO₂, 应用超声技术将TiO₂ 纳米粒子分散在甲醇介质中, 然后用苯乙烯(ST)原位聚合包封, 再用丙烯酰胺或乙烯基吡咯烷酮(VP)共聚, 两步原位分散聚合得到了有机聚合物为壳、TiO₂为核的有机/无机复合粒子. 用红外光谱、紫外-可见光谱、透射电子显微镜等检测手段进行表征. 结果显示: 由于双亲共聚物对TiO₂纳米粒子的敏化作用, 紫外-可见光谱图上两种纳米复合粒子的最大吸收峰均有明显红移, 并且吸收光谱的范围扩大了, 其中尤以TiO₂/(PST-co-PVP)为甚. 意味着光敏化活性的提高, 特别是在可见光谱的范围内. 这种情形对宽带隙半导体材料如TiO₂纳米粒子的光催化特性是有利的, 表明这类材料的应用空间得到了拓展.     

炉前煤低温干馏工艺中的挥发分除尘

为了寻求优化的炉前煤低温干馏工艺中的挥发分除尘方案，在使用400目金属滤网对间歇式粉煤固体热载体热解装置挥发分除尘研究的基础上，将颗粒床过滤器用于该过程的除尘研究。热态除尘实验表明，颗粒床的使用有效地降低了滤网的过滤负荷。选用2mm石英砂和φ5mm×2mm瓷环作为滤料，通过对比实验发现，两种滤料除尘效率均在90％以上；随着过滤操作的进行，由于颗粒床内粉尘的沉积使其过滤效率有所提高，而对气、液收率的影响很小。结果表明，颗粒床与滤网结合可作为粉煤炉前低温干馏工艺中可供选择的挥发分除尘方案。     

黑米花色苷酰化修饰红外光谱分析

黑米花色苷易受外部环境影响发生降解致使局部分子结构破坏而使营养价值和保健功能有所下降。利用有机酸提供酰基对黑米花色苷进行修饰来提高花色苷结构的稳定性。利用红外光谱分析经咖啡酸酰化修饰黑米花色苷的结构变化。结果表明：黑米花色苷酰化修饰前后于官能团区3 650~3 200和1 680~1 620 cm-1处均有吸收峰，且其于指纹区1 282.68和1 277.51 cm-1处出现酚羟基吸收峰，于1 056.07和1 054.03 cm-1处出现醇羟基吸收峰，719.90和719.71 cm-1处出现苯环上C-H面外弯曲振动吸收峰。由此可见，黑米花色苷酰化修饰后主要结构框架仍为花色苷的芳环结构。此外，黑米花色苷酰化修饰前后于1 900~1 650 cm-1间1 714.28和1 728.13 cm-1处均出现共轭羰基的特征吸收峰，对应于可直接连接在苯环上的α-羰基结构，由此说明黑米花色苷结构中存在着酰基基团。黑米花色苷经酰化修饰后红外图谱于1 517.20 cm-1处出现新吸收峰，其正好处于1 800~900 cm-1双键(不含氢)伸缩振动区，指纹区876.65 cm-1处亦出现了苯环上的C-H面外弯曲振动吸收峰。与之相呼应在经二阶导数处理后红外光谱图中在2 500～2 000 cm-1间出现了新的波动，此波段为累积双键伸缩振动区，而官能团区3 650~3 200 cm-1间3 370.20 cm-1处的吸收峰正好处于多分子缔合区。由此可见，在咖啡酸作为酰基供体，酰化修饰黑米花色苷时由于分子间的重新缔合于结构中引入了新的酰基基团而呈现出一种双酰化的空间结构。黑米花色苷酰化结构中有机酸与糖链相连，将有机酸置于2-苯基苯并吡喃骨架的表面，这种堆积作用模式可以较好地抵抗水的亲核攻击和其他降解反应进而提高黑米花色苷结构的稳定性。     

Unsupervised cell identification on multidimensional X‐ray fluorescence datasets

A novel approach to locate, identify and refine positions and whole areas of cell structures based on elemental contents measured by X‐ray fluorescence microscopy is introduced. It is shown that, by initializing with only a handful of prototypical cell regions, this approach can obtain consistent identification of whole cells, even when cells are overlapping, without training by explicit annotation. It is robust both to different measurements on the same sample and to different initializations. This effort provides a versatile framework to identify targeted cellular structures from datasets too complex for manual analysis, like most X‐ray fluorescence microscopy data. Possible future extensions are also discussed.     

2,4-二甲基吡咯-3,5-二羧酸二乙酯的合成——推荐一个大学有机化学实验

采用Knorr吡咯合成法，以乙酰乙酸乙酯和亚硝酸钠为原料，在醋酸和锌粉作用下采用“一锅法”得到2,4-二甲基吡咯-3,5-二羧酸二乙酯。本实验涉及到控温、回流、重结晶、熔点测定、红外光谱及核磁共振等实验操作和分析检测方法。该实验原料简单易得、产物收率高，结合波谱解析方法，可以培养和提高学生合成实验的能力，加强学生对杂环合成和波谱解析的理解与分析。     

Adsorption of thorium(IV) on magnetic multi-walled carbon nanotubes

The influences of pH, contact time, solid-liquid ratio, temperature and C60(C(COOH)2)n on Th(IV) adsorption onto the magnetic multi-walled carbon nanotubes(MMWCNTs) were studied by batch technique. The dynamic process showed that the adsorption of Th(IV) onto MMWCNTs could reach equilibrium in 40 h and matched the pseudo-second-order kinetics model. The adsorption of Th(IV) onto MMWCNTs was significantly dependent on pH values, the adsorption ratio increased markedly at pH 3.0–5.0, and then maintained a steady state as pH values increased. At low pH, different C60(C(COOH)2)n content could enhance the adsorption content of Th(IV) onto MMWCNTs, but restrained it at higher pH. Through simulating the adsorption isotherms by Langmuir, Freundlich and Dubini-Radushkevich models, it could be seen respectively that the adsorption pattern of Th(IV) onto MMWCNTs was mainly surface complexation, and that the adsorption process was endothermic and irreversible.