RGD改性聚醚氨酯及其内皮细胞相容性的研究

利用氢键稳定的溶液互穿技术对聚醚氨酯(PEU)进行改性.用ATR-FTIR对十八烷基-聚氧乙烯-4,4'-二苯甲烷二异氰酸酯-聚氧乙烯-十八烷基(MSPEO)与PEU共混膜表面进行研究,结果表明,MS-PEO中的氨基甲酸酯链段与PEU基材之间发生了氢键缔合的作用.通过水化处理PEO及十八烷基自发地富集在基材表面.根据氢键缔合和表面自迁移原理,设计了两种RGD改性聚醚氨酯的方法:(1)将含RGD端基的聚氧乙烯-4,4'-二苯甲烷二异氰酸酯-聚氧乙烯偶联物(MPEO-RGD)与PEU进行共混改性,利用RGD端基及PEO的自迁移特性获得RGD富集的表面;(2)将含甲磺酸酯端基的聚氧乙烯-4,4'-二苯甲烷二异氰酸酯-聚氧乙烯偶联物(MPEO-mesyl)与PEU共混成膜,并对膜片进行水化处理,使甲磺酸酯端基富集在PEU表面,浸泡于RGD的PBS溶液中,在膜片表面成功地原位接枝了RGD.对两种RGD改性方法获得的表面进行了内皮细胞的培养,结果表明,两种改性方法均大大提高了PEU的细胞相容性,其中方法(1)共混改性的表面细胞相容性略优于方法(2)的接枝改性表面.     

聚苯胺-聚乙烯醇电致变色复合膜

以微型高分子化学实验的方法设计了合成聚苯胺／聚乙烯醇电致复合膜实验。讨论了聚合时间、电压、酸浓度、聚乙烯醇含量等因素对复合膜电致变色性的影响。将较为复杂的生产工艺以简单直观的学生实验表现出来,对学生实践能力的培养具有一定的意义。     

HDI作为扩链剂合成含PLLA和PBS链段的聚酯氨酯

以数均分子量为6350g/mol端羟基聚L-乳酸(PLLA-OH)与10500g/mol端羟基聚丁二酸丁二酯(PBS-OH)为预聚物,六亚甲基二异氰酸酯(HDI)为扩链剂,通过熔融反应制备了分子量高达30×104g/mol的可完全生物降解聚酯氨酯(PEU).研究了异氰酸根(NCO)与羟基比例对扩链反应的影响.结果表明,当[NCO]/[OH]=1∶1时,扩链效果最好,PEU分子量最大;PEU分子量随着预聚物中PBS含量增大而提高.通过核磁共振谱(1H-NMR)确定了PEU的结构与组成,并对聚酯氨酯进行了凝胶渗透色谱(GPC)、差示扫描量热(DSC)、热重分析(TGA)以及拉伸性能测试.DSC结果显示,扩链后PEU的结晶主要由PBS链段产生,而PLLA链段几乎不结晶;TGA结果表明,PEU的热降解分两步进行,第一步为PEU中PLLA链段的热降解,第二段为其中PBS链段的降解;拉伸测试结果表明,PBS与PLLA的共聚能够制备拉伸强度与断裂伸长率优异的聚合物材料.     

PEU/PES共混膜的制备工艺条件研究

利用L-S相转化法将聚醚型聚氨酯（PEU）和聚醚砜（PES）共混,以聚乙二醇（PEG）为添加剂,制备PEU/PES共混膜,并通过测定比较共混膜的结构与性能.结果表明：聚合物浓度、共混组成比、添加剂种类与浓度是影响PEU/PES共混膜性能的主要因素.     

引入离子基团改善聚苯乙烯与热致液晶聚合物的相容性Ⅱ.用FTIR研究分子间特殊相互作用

向聚苯乙烯(PS)中引入磺酸基团可以有效地改善PS与一种热致液晶聚合物(LCP)之间的相容性.用溶液共混的方法制备了PS和磺化聚苯乙烯(HSPS)与LCP的共混物.用FTIR以及红外光谱的合成技术对LCP共混体系进行了表征.共混物中组分聚合物特征吸收的位置和谱图的形状表明在LCP与PS分子间没有相互作用发生,而在LCP与HSPS分子间则存在较强的相互作用.谱图差减技术确认了LCP分子中C==O与C--O基团和HSPS中的磺酸基团参与了相互作用,使得这些基团的特征吸收发生了偏移.     

多壁碳纳米管/液晶高分子复合材料的制备及其对PP结晶行为的影响

首先通过原位聚合法合成了一种新型多壁碳纳米管/液晶高分子复合材料(MCNT/LCP),然后将其与聚丙烯共混,制备了一系列的共混样品。采用FT-IR、DSC与POM等表征了MCNT/LCP复合材料的结构与液晶性能,利用XRD与DSC研究了聚丙烯共混物的结晶结构与结晶动力学,探讨了MCNT/LCP含量与结晶温度对聚丙烯共混物结晶行为的影响。结果表明:所合成的MCNT/LCP呈现近晶相的扇形织构,当MCNT/LCP被引入到聚丙烯中后,不仅起到异相成核的作用,而且能诱导β晶的形成,同时,DSC降温曲线峰型也变得比较尖锐,结晶峰温度提高,结晶速度加快。     

PLA/MWNTs/HA复合材料的制备和性能研究

采用超声辅助原位湿法合成多壁碳纳米管／羟基磷灰石纳米复合材料(MWNTs／HA),并通过溶液浇铸法制备了PLA／MWNTs／HA复合材料薄膜。考察了MWNTs／HA纳米粒子含量对复合膜性能的影响,并通过力学性能、SEM、FTIR、以及DMTA对复合膜性能进行了表征,结果表明：随着纳米粒子质量分数的增加,复合膜的拉伸强度呈下降趋势;拉伸模量和储能模量呈现先下降后上升的趋势;玻璃化转变温度则呈现不断上升趋势。     

功能性CdSe纳米晶的合成及自组装膜光致发光

以巯基丙酸(RSH)为稳定剂,采用湿化学法合成了功能性CdSe纳米晶,用XRD、TEM表征其粒度和形貌,用UV-Vis监测成核及成膜过程。结果表明：制得的CdSe近似呈球形,平均粒径为48 nm。利用静电自组装法层层组装成CdSe-PDDA复合膜,荧光测试表明：所得CdSe纳米晶自组装复合膜(CdSe-PDDA)的荧光强度随着组装层数的增加而呈线性增强,该复合膜在582 nm附近有黄绿色荧光发射。     

复合纤维素金属螯合膜色谱介质的制备及其分离生物大分子的研究

以棉纤维为基质 ,通过聚合、接枝、开环反应合成了亚氨二乙酸型金属螯合复合膜色谱介质 ,考察了反应温度 ,反应时间对合成介质性能的影响 ,并对复合纤维素膜的表面物理性能及蛋白质的结合性能进行了表征 .实验结果表明 ,膜色谱介质对蛋白质具有较大的吸附容量 ,分离效果与凝胶介质相当 ,但分离速度快 3～ 5倍 .复合膜色谱介质还具有负压低 ,成本低 ,使用寿命长等特点 ,适于生物大分子的快速大规模分离纯化 ,并用于高效液相色谱对生物大分子的快速定量分析 .     

超疏水聚苯胺/聚四氟乙烯复合膜的制备及油-水乳液分离性能

以苯胺为原料, 采用原位聚合法在聚四氟乙烯(PTFE)基体上合成聚苯胺/聚四氟乙烯(PANI/PTFE)复合膜. 利用光学显微镜、 扫描电子显微镜(SEM)、 傅里叶变换红外光谱(FTIR)、 紫外-可见吸收光谱(UV-Vis)和静态水接触角测试对PANI/PTFE复合膜的形貌、 结构和浸润性进行分析, 并对其油包水乳液分离性能、 通量和循环使用性能进行了测试. 研究结果表明, PANI/PTFE复合膜仅在重力条件就能有效分离油包水乳液; 而且重复数十次过滤后, PANI/PTFE复合膜仍具有良好的抗污能力和分离性能.     

Synthesis and Characterization of Novel Poly-thiophene-nanoporous Silica and its Application for Mercury Removal from Waste Waters

In this work, MCM-41 (Mobil Composition of Matter number 41) nanoporous silica has been synthesized and characterized by X-ray powder diffraction and IR spectroscopy. In the next step, poly-thiophene was coated on the nanoporous silica in order to increase its surface area. This composite was characterized by X-Ray powder diffraction, High resolution transmission electronic microscopy micrograph (HRTEM), elemental analysis (CHNS) and Thermal analysis (TG/DTA). The application of this composite was investigated in mercury ions removal from waste water prior to determination by inductively coupled plasma atomic emission spectroscopy (ICP-OES). In order to investigate the effect of nanoporous structure on the efficiency of this composite, the same composite without porous structure has been synthesized and the results were compared.     

聚二甲基硅氧烷-纳米金复合材料的制备与生物传感应用

作为一种新型复合材料,聚二甲基硅氧烷-纳米金复合材料兼具聚二甲基硅氧烷和纳米金的良好导电性、生物亲和性及超疏水性等优点,广泛用于生物传感、生物功能材料、环境保护、微流控等领域.该文评述了常规实验室制备聚二甲基硅氧烷-纳米金复合材料的两种主要方法及其在生物传感领域中的应用,并对聚二甲基硅氧烷-纳米金复合材料的发展趋势和应...     

Preparation of a Conducting Flexible Material from Silane Coupling Agent and Hydroxyl Terminated Polybutadiene Rubber by Hydrolysis and Condensation

Abstract

Synthesis and characterization of a flexible polymer produced from silane coupling agent (SCA) and hydroxyl terminated polybutadiene (HTPB) were performed. Mechanical properties of chemically and electrochemically prepared conducting composites synthesized from this polymer were investigated. Conductivities of the composites were also measured. Polypyrrole enhanced the mechanical properties of the chemically prepared conducting composite. Doping with iodine greatly changed the conductivity of the composite. However, the change in mechanical properties and the conductivities of the electrochemically prepared composite were not as significant when compared with the electrochemically prepared polypyrrole. Among the composites, a chemically prepared composite was highly flexible like rubber. However, the electrochemically produced composite possesses two orders of magnitude higher conductivity. Also, this composite revealed higher tensile strength and elasticity with respect to pristine polypyrrole.     

Temperature-induced crystallization and compactibility of spray dried composite particles composed of amorphous lactose and various types of water-soluble polymer

The purpose of this study was to investigate the temperature-induced crystallization and the compactibility of the composite particles containing amorphous lactose and various types of polymers. The composite particles were prepared by spray-drying an aqueous solution of lactose and various types of gel forming water-soluble polymers at various formulating ratios. The stabilizing effect of hydroxypropylcellulose (HPC) and polyvinyl pyrrolidone (PVP) on amorphous lactose in the composite particles was smaller than that of sodium alginate in comparing at the same formulating ratios. The difference in the stability of amorphous lactose in the composite particles was attributed to the difference in the glass transition temperature (Tg) of the composite particles caused by the polymers formulated. The tensile strength of compacted spray-dried composite particles containing the polymers was higher than commercial lactose for direct tabletting (DCL21). The tensile strength of the composite particles was increased with an increase in water content in the particles. The difference in compactibility of the composite particles containing the different amount of polymer and water could be explained by the difference in Tg of the particles.     

Microstructure and mechanical properties of isotactic polypropylene composite with two‐scale reinforcement

Isotactic polypropylene (iPP) composite with two‐scale reinforcement structure, i.e. nanoscale shish–kebab structure and micron‐scale glass fiber (GF) with orientation, was fabricated by an oscillatory shear injection molding (OSIM) technology. The oscillatory shear flow provided by the OSIM gave rise to a high fraction of shish–kebab structures in the iPP composite, characterized by X‐ray scattering technique. On the other hand, the oscillatory shear flow oriented GFs in the iPP composite, which was revealed by scanning electron microscopy measurement. The iPP composite with this two‐scale reinforcement structure exhibited simultaneously remarkably enhanced tensile strength and impact strength. Fracture mechanism of this iPP composite was also proposed. Copyright © 2012 John Wiley & Sons, Ltd.     

纳米TiO2-SiO2复合氧化物的制备与性质

采用溶胶-凝胶结合CO2超临界干燥方法制备了比表面积大、热稳定性好的纳米TiO2-SiO2复合氧化物.考察了原料组成和焙烧温度对复合氧化物比表面积、热稳定性和酸性的影响,通过加氢脱硫反应考察了该复合氧化物作为加氢精制催化剂载体的可行性.结果表明,采用该方法制备的复合氧化物为纳米颗粒,在n(Ti)/n(Si)=1时,其比表面积和孔容最大;与纯TiO2相比,引入SiO2明显提高了复合氧化物的热稳定性和晶型稳定性;以此复合氧化物为载体的加氢精制催化剂具有很好的低温脱硫活性,TiO2-SiO2复合氧化物载体的酸性特征影响了催化剂的加氢脱硫活性.     

镁铝复合氧化物载体的制备与性质研究

以硝酸镁和硝酸铝为原料，用氨水溶液作为pH调节剂，采用共沉淀法制备了镁铝复合氧化物载体，研究了制备过程中镁铝比、pH调节剂种类、水解过程pH值的大小、反应温度、焙烧温度及回流晶化温度对复合氧化物载体理化性质的影响。并以RFCC汽油加氢脱硫为探针反应，考察了以镁铝复合氧化物为载体的催化剂选择性加氢脱硫性能。实验结果表明，在镁铝分子比为10、反应温度为80℃、pH值为9.5条件下制备的镁铝复合氧化物载体具有适宜的比表面积和均匀的孔分布，且晶型较完整，结晶度高。以该复合氧化物为载体制备的催化剂具有良好的RFCC汽油选择性加氢脱硫反应性能。     

脉冲电化学驱动壳聚糖原位调控制备羟基磷灰石/银复合涂层

采用脉冲电化学驱动壳聚糖原位调控制备了具有抗菌性的羟基磷灰石/银纳米复合涂层.考察了电解液中银离子浓度、钙磷盐浓度等对复合涂层的形貌及成分的影响.探讨了壳聚糖调控羟基磷灰石和银纳米粒子的形成机理,发现在本研究的较佳实验条件为电位-1.3 V,Ag~+浓度为0.06 g·L~(-1),Ca~(2+)浓度为5 mmol·L~(-1).在此基础上对复合涂层的生物活性、生理稳定性能、抗菌性能进行分析.结果表明:复合涂层呈纳米球状,由羟基磷灰石、银、壳聚糖三相组成,并且表面有一层壳聚糖覆盖.银纳米粒子和羟基磷灰石纳米粒子在复合涂层中均匀分布.将复合涂层浸泡在SCPS溶液中37°C浸泡矿化10天后,在复合涂层表面生产细针状排列整齐的羟基磷灰石,且在(002)晶面25.8°处发生显著择优生长,表明复合涂层在快速矿化液中能诱导磷灰石生成,生物活性好.将复合涂层浸泡在37°C PBS溶液中考察其生理稳定性,壳聚糖对复合涂层中Ca~(2+)和Ag~+实现双重离子释放,且降低了离子释放速度,涂层具有良好的生理稳定性.抗菌实验表明复合涂层对大肠杆菌和金黄色葡萄球菌抗菌率达到99%以上,抗菌能力强.     

壳聚糖-g-N-羧甲基-2-硫代-4,5-2H咪唑啉酮-多壁碳纳米管复合物固定漆酶基化学传感器的性能

通过壳聚糖-g-N-羧甲基-2-硫代-4,5-2H咪唑啉酮(CTS-g-N-CSIDZ)非共价功能化多壁碳纳米管(MWCNTs)的方式制备固定漆酶载体,该复合物载体主要通过物理吸附和漆酶活性中心与载体上配体之间的配位作用来固定漆酶,较大程度地保持了游离漆酶活性位原始构象.将固定了漆酶的复合物附着在裸玻碳电极上便构筑了复合物固定漆酶修饰玻碳电极.在以分光光度法测定了这种复合物载体对漆酶的担载量、固定漆酶比活力、稳定性、重复使用性及其催化2,6-二甲氧基苯酚(DMP)氧化动力学参数的基础上,还对基于此种复合物固定漆酶修饰玻碳电极作为化学传感器(以DMP作为底物)的性能进行了研究.结果表明,该复合物具有较高的固酶担载量(81.7 mg/g)和固定漆酶比活力(1.33 U/mg);而作为电化学传感器的复合物固定漆酶修饰玻碳电极对底物DMP具有较高的亲和力(对DMP的米氏常数KM是0.0918 mmol/L),较高的灵敏度( 3680 mA· L/mol),较低的检测限(3.3×10-4 mmol/L),较高的响应选择性,良好的重现性、重复使用性和长期稳定性.这种漆酶基电极有望用作电流型特定结构的酚类传感器.     

纳米羟基磷灰石/丝素蛋白复合支架材料的降解特性及生物相容性研究

应用共混法制备了纳米羟基磷灰石/丝素蛋白复合支架材料, 通过体外降解和细胞培养实验研究了复合支架材料的降解特性和生物相容性. 体外降解实验结果显示, 复合支架材料具有稳定的降解能力; 在降解过程中, 羟基磷灰石由于与降解液发生钙、磷等离子的交换, 使其结晶得到了进一步生长和完善. 利用细胞计数法、四甲基偶氮唑盐(MTT)比色法和碱性磷酸酶(ALP)活性测定等分析了复合支架材料的生物相容性, 结果表明, MG63细胞在复合支架材料上具有良好的粘附、增殖能力, 并可引起早期的骨分化. 因此, 纳米羟基磷灰石/丝素蛋白复合支架作为骨组织工程的支架材料具有良好的应用前景.