Synthesis and characterization of macroporous Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>/C composites as cathode materials for Li-ion batteries

The macroporous Li₃V₂(PO₄)₃/C composite was synthesized by oxalic acid-assisted carbon thermal reaction, and the common Li₃V₂(PO₄)₃/C composite was also prepared for comparison. These samples were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical performance tests. Based on XRD and SEM results, the sample has monoclinic structure and macroporous morphology when oxalic acid is introduced. Electrochemical tests show that the macroporous Li₃V₂(PO₄)₃/C sample has a high initial discharge capacity (130 mAh g⁻¹ at 0.1 C) and a reversible discharge capacity of 124.9 mAh g⁻¹ over 20 cycles. Moreover, the discharge capacity of the sample is still 91.5 mAh g⁻¹, even at a high rate of 2 C, which is better than that of the sample with common morphology. The improvement in electrochemical performance should be attributed to its improved lithium ion diffusion coefficient for the macroporous morphology, which was verfied by cyclic voltammetry and electrochemical impedance spectroscopy.     

Platelike CoO/carbon nanofiber composite electrode with improved electrochemical performance for lithium ion batteries

Platelike CoO/carbon nanofiber (CNF) composite materials with porous structures are synthesized from the thermal decomposition and recrystallization of β-Co(OH)₂/CNF precursor without the need for a template or structure-directing agent. As negative electrode materials for lithium-ion batteries, the platelike CoO/CNF composite delivers a high reversible capacity of 700 mAh g⁻¹ for a life extending over hundreds of cycles at a constant current density of 200 mA g⁻¹. More importantly, the composite electrode shows significantly improved rate capability and electrochemical reversibility. Even at a current of 2 C, the platelike CoO/CNF composite maintain a capacity of 580 mAh g⁻¹ after 50 discharge/charge cycles. The improved cycling stability and rate capability of the CoO/CNF composite electrodes may be attributed to synergistic effect of the porous structural stability and improved conductivity through CNF connection.     

Effects of complexants on [Ni1/3Co1/3Mn1/3]CO3 morphology and electrochemical performance of LiNi1/3Co1/3Mn1/3O2

LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials for the application of lithium ion batteries were synthesized by carbonate co-precipitation routine using different ammonium salt as a complexant. The structures and morphologies of the precursor [Ni_1/3Co_1/3Mn_1/3]CO₃ and LiNi_1/3Co_1/3Mn_1/3O₂ were investigated through X-ray diffraction, scanning electron microscope, and transmission electron microscopy. The electrochemical properties of LiNi_1/3Co_1/3Mn_1/3O₂ were examined using charge/discharge cycling and cyclic voltammogram tests. The results revealed that the microscopic structures, particle size distribution, and the morphology properties of the precursor and electrochemical performance of LiNi_1/3Co_1/3Mn_1/3O₂ were primarily dependent on the complexant. Among all as-prepared LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials, the sample prepared from Na₂CO₃–NH₄HCO₃ routine using NH₄HCO₃ as the complexant showed the smallest irreversible capacity of 19.5 mAh g⁻¹ and highest discharge capacity of 178.4 mAh g⁻¹ at the first cycle as well as stable cycling performance (98.7% of the initial capacity was retained after 50 cycles) at 0.1 C (20 mA g⁻¹) in the voltage range of 2.5–4.4 V vs. Li⁺/Li. Moreover, it delivered high discharge capacity of over 135 mAh g⁻¹ at 5 C (1,000 mA g⁻¹).     

Electrochemical properties of LiFePO4/C synthesized using polypyrrole as carbon source

LiFePO₄/C composites were synthesized by pyrolysis of LiFePO₄/polypyrrole (PPy), which was obtained by an in situ chemical polymerization involving pyrrole monomer and hydrothermal synthesis LiFePO₄. All samples were characterized by X-ray diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy, cyclic voltammetry, and galvanostatic charge–discharge techniques. The results showed the LiFePO₄/C sintered at 800 °C containing 2.8 wt.% carbon exhibited a higher discharge capacity of 49.6 mAh·g⁻¹ at 0.1 C, and bare LiFePO₄ only delivered 11.6 mAh·g⁻¹ in 2 M LiNO₃ aqueous electrolyte. The possible reason for the improvement of electrochemical performance was discussed and could be attributed to the formation of aromatic compounds during the carbonization of PPy.     

共聚物模板辅助合成高倍率性能多孔Li2FeSiO4@C/CNTs纳米复合正极材料

通过溶胶-凝胶法制备了Li₂FeSiO₄@C/CNTs(LFS@C/CNTs)纳米复合材料,其中三嵌段共聚物P123用作结构导向剂和碳源,碳纳米管作为导电线提高材料的导电性。LFS@C/CNTs不仅具有海绵状纳米孔,能够与电解液充分接触改善锂离子的传输路径,同时由非晶碳和碳纳米管构成的三维桥联导电网络利于电子的快速传递,提高了材料大电流充放电能力和循环稳定性。复合后的LFS@C/CNTs的高倍率性能相比LFS@C明显提高, 当CNTs的掺量为4%,电压窗口为1.5~4.5 V,0.1C电流密度下放电比容量为182 mAh·g^-1。在10C经70次循环后该材料的放电比容量能保持在117 mAh·g^-1,是LFS@C放电比容量(55 mAh·g^-1)的两倍。     

共聚物模板辅助合成高倍率性能多孔Li2FeSiO4@C/CNTs纳米复合正极材料

通过溶胶-凝胶法制备了Li₂FeSiO₄@C/CNTs(LFS@C/CNTs)纳米复合材料,其中三嵌段共聚物P123用作结构导向剂和碳源,碳纳米管作为导电线提高材料的导电性。LFS@C/CNTs不仅具有海绵状纳米孔,能够与电解液充分接触改善锂离子的传输路径,同时由非晶碳和碳纳米管构成的三维桥联导电网络利于电子的快速传递,提高了材料大电流充放电能力和循环稳定性。复合后的LFS@C/CNTs的高倍率性能相比LFS@C明显提高, 当CNTs的掺量为4%,电压窗口为1.5~4.5 V,0.1C电流密度下放电比容量为182 mAh·g^-1。在10C经70次循环后该材料的放电比容量能保持在117 mAh·g^-1,是LFS@C放电比容量(55 mAh·g^-1)的两倍。     

The improvement of the high-rate charge/discharge performances of LiFePO4 cathode material by Sn doping

Nanocrystalline LiFePO₄ and LiFe_0.97Sn_0.03PO₄ cathode materials were synthesized by an inorganic-based sol–gel route. The physicochemical properties of samples were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, transmission electron microscopy, and elemental mapping. The doping effect of Sn on the electrochemical performance of LiFePO₄ cathode material was extensively investigated. The results showed that the doping of tin was beneficial to refine the particle size, increase the electrical conductivity, and facilitate the lithium-ion diffusion, which contributed to the improvement of the electrochemical properties of LiFePO₄, especially the high-rate charge/discharge performance. At the low discharge rate of 0.5 C, the LiFe_0.97Sn_0.03PO₄ sample delivered a specific capacity of 158 mAh g⁻¹, as compared with 147 mAh g⁻¹ of the pristine LiFePO₄. At higher C-rate, the doping sample exhibited more excellent discharge performance. LiFe_0.97Sn_0.03PO₄ delivered specific capacity of 146 and 128 mAh g⁻¹ at 5 C and 10 C, respectively, in comparison with 119 and 107 mAh g⁻¹ for LiFePO₄. Moreover, the doping of Sn did not influence the cycle capability, even at 10 C.     

Synthesis and electrochemical performances of Li4Ti4.95Zr0.05O12/C as anode material for lithium-ion batteries

Spinel Li₄Ti_5 − x Zr _x O₁₂/C (x = 0, 0.05) were prepared by a solution method. The structure and morphology of the as-prepared samples were characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The electrochemical performances including charge–discharge (0–2.5 V and 1–2.5 V), cyclic voltammetry, and ac impedance were also investigated. The results revealed that the Li₄Ti_4.95Zr_0.05O₁₂/C had a relatively smaller particle size and more regular morphology than that of Li₄Ti₅O₁₂/C. Zr⁴⁺ doping enhanced the ability of lithium-ion diffusion in the electrode. It delivered a discharge capacity 289.03 mAh g⁻¹ after 50 cycles for the Zr⁴⁺-doped Li₄Ti₅O₁₂/C while it decreased to 264.03 mAh g⁻¹ for the Li₄Ti₅O₁₂/C at the 0.2C discharge to 0 V. Zr⁴⁺ doping did not change the electrochemical process, instead enhanced the electronic conductivity and ionic conductivity. The reversible capacity and cycling performance were effectively improved especially when it was discharged to 0 V.     

The preparation and performance of flocculent polyaniline/carbon nanotubes composite electrode material for supercapacitors

Polyaniline (PANI)/carbon nanotubes (CNTs) composite electrode material was prepared by in situ chemical polymerization. The structure and morphology of PANI/CNTs composite are characterized by Fourier infrared spectroscopy, scanning electron microscope, and transmission electron microscopy. It has been found that a flocculent PANI was uniformly deposited on the surface of CNTs. The supercapacitive behaviors of the PANI/CNTs composite materials are investigated with cyclic voltammetry, galvanostatic charge/discharge, impedance, and cycle life measurements. The results show that the PANI/CNTs composite electrodes have higher specific capacitances than CNT electrodes and better stability than the conducting polymers. The capacitance of PANI/CNTs composite electrode is as high as 837.6 F g⁻¹ measured by cyclic voltammetry at 1 mV s⁻¹. Besides, the capacitance retention of coin supercapacitors remained 68.0% after 3,000 cycles.     

Low-temperature behavior of Li3V2(PO4)3/C as cathode material for lithium ion batteries

The electrochemical performance of Li₃V₂(PO₄)₃/C was investigated at various low temperatures in the electrolyte 1.0 mol dm⁻³ LiPF₆/ethyl carbonate (EC)+diethyl carbonate (DEC)+dimethyl carbonate (DMC) (volume ratio 1:1:1). The stable specific discharge capacity is 125.4, 122.6, 119.3, 116.6, 111.4, and 105.7 mAh g⁻¹ at 26, 10, 0, −10, −20, and −30 °C, respectively, in the voltage range of 2.3–4.5 V at 0.2 C rate. When the temperature decreases from −30 to −40 °C, there is a rapid decline in the capacity from 105.7 to 69.5 mAh g⁻¹, implying that there is a nonlinear relationship between the performance and temperature. With temperature decreasing, R _ct (corresponding to charge transfer resistance) increases rapidly, D (the lithium ion diffusion coefficients) decreases sharply, and the performance of electrolyte degenerates obviously, illustrating that the low-temperature electrochemical performance of Li₃V₂(PO₄)₃/C is mainly limited by R _ct, D _Li, and electrolyte.     

球磨辅助高温固相法制备Li1.0Na0.2Ni0.13Co0.13Mn0.54O2正极材料及其性能

以乙酸盐(乙酸锂、乙酸钠、乙酸钴、乙酸镍、乙酸锰等)为原材料,采用球磨辅助高温固相法制备Li_(1.0)Na_(0.2)Ni_(0.13)Co_(0.13)Mn_(0.54)O_2正极材料。借助XRD、SEM等表征材料的结构和形貌,利用循环伏安、恒流充放电、交流阻抗等方法研究材料的电化学性能。结果表明,钠的掺杂导致颗粒表面光滑度降低,形成Na_(0.77)Mn O_(2.05)新相。0.05C活化过程中,掺钠样品和未掺钠样品首次放电比容量分别为258.4 m Ah·g~(-1)和215.8 m Ah·g~(-1),库伦效率分别为75.2%和72.8%;2C放电比容量分别为116.3 m Ah·g~(-1)和106.2 m Ah·g~(-1)。研究发现,掺钠可减小首次充放电过程的不可逆容量,提高容量保持率;改善倍率性能与容量恢复特性;降低SEI膜阻抗和电荷转移阻抗;掺钠后样品首次循环就可以基本完成Li_2Mn O_3组分向稳定结构的转化,而未掺杂的样品需要两次循环才能逐步完成该过程;XPS结果表明,掺钠样品中Ni~(2+)、Co~(3+)、Mn~(4+)所占比例明显提高,改善了样品的稳定性和电化学性能;循环200次后的XRD结果表明掺钠与未掺钠材料在脱嵌锂反应中的相变化过程基本一致,良好有序的层状结构遭到破坏是循环过程中容量衰减的主要原因。     

Electrochemical properties of tetravalent Ti-doped spinel LiMn2O4

Ti-doped spinel LiMn₂O₄ is synthesized by solid-state reaction. The X-ray photoelectron spectroscopy and X-ray diffraction analysis indicate that the structure of the doped sample is Li( Mn^{3 +} Mn_{1 - x} ^{4 +} Ti_x^{4 +} )O₄ {\hbox{Li}}\left( {{\hbox{M}}{{\hbox{n}}^{3 + }}{\hbox{Mn}}_{1 - x\,}^{4 + }{\hbox{Ti}}_x^{4 + }} \right){\hbox{O}}{}_4 . The first principle-based calculation shows that the lattice energy increases as Ti doping content increases, which indicates that Ti doping reinforces the stability of the spinel structure. The galvanostatic charge–discharge results show that the doped sample LiMn_1.97Ti_0.03O₄ exhibits maximum discharge capacity of 135.7 mAh g⁻¹ (C/2 rate). Moreover, after 70 cycles, the capacity retention of LiMn_1.97Ti_0.03O₄ is 95.0% while the undoped sample LiMn₂O₄ shows only 84.6% retention under the same condition. Additionally, as charge–discharge rate increases to 12C, the doped sample delivers the capacity of 107 mAh g⁻¹, which is much higher than that of the undoped sample of only 82 mAh g⁻¹. The significantly enhanced capacity retention and rate capability are attributed to the more stable spinel structure, higher ion diffusion coefficient, and lower charge transfer resistance of the Ti-doped spinel.     

一种碳纳米管改性富锂锰基正极材料的策略

采用一种新策略对Li1.184[Ni0.15Mn0.516Co0.15]O2进行改性,即通过气流破碎、高压均质混合分散和喷雾干燥的方法得到与碳纳米管复合的富锂锰基正极材料(CNT@LMR)。使用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射仪(XRD)和拉曼光谱(Raman)的方法对改性的材料进行了表征,发现碳纳米管导电网络均匀地分布在富锂锰基正极材料的表面,而且在材料内部的一次颗粒之间也有大量的碳纳米管存在。电化学性能测试表明,碳纳米管改性后的富锂锰基正极拥有更好的倍率性能和循环寿命。在5C倍率下经过改性的富锂锰基正极的放电比容量为141.4 mAh·g-1,远高于未改性的富锂锰基正极的放电比容量(76.6 mAh·g-1)和碳纳米管仅作为富锂锰基正极导电剂时的放电比容量(110.7 mAh·g-1)。在1C倍率下循环100次后,碳纳米管改性的富锂锰基正极的容量保持率在87.2%,高于富锂锰基正极(77.8%)。不同循环次数下的电化学阻抗谱表明,均匀分布在富锂锰基正极材料表面的碳纳米管网状结构有效地改善了电极/电极液的界面反应,抑制了电极固体电解质界面(SEI)膜的增厚和减缓了电极的极化。同时,材料内部的碳纳米管导电网络降低了一次颗粒间的内阻并加快了电极的电荷转移过程。     

N掺杂MnO2/碳布复合材料的制备及储锂性能

采用碳布（CC）为柔性基底,通过水热法制备了MnO₂/CC及N掺杂MnO₂/CC无黏结剂负极材料,借助X射线衍射（XRD）、扫描电镜（SEM）、X射线光电子能谱（XPS）、比表面积测试和恒电流充放电对材料进行了结构表征及电化学性能测试。结果表明N掺杂MnO₂/CC具有良好的倍率性能和循环稳定性。在0.1 A·g^-1的电流密度下,其首次充电比容量为948.8 mAh·g^-1,经过不同倍率测试后电流密度恢复至0.1 A·g^-1时仍然保持有907.9 mAh·g^-1的可逆比容量,容量保持率为95.7%。在1 A·g^-1的大电流密度下,其首次充电比容量为640.3 mAh·g^-1,循环100次后仍然保持有529.9 mAh·g^-1的可逆比容量,容量保持率为82.8%,可逆比容量远高于商用MnO₂。     

Pb-sandwiched nanoparticles as anode material for lithium-ion batteries

A sandwiched SiC@Pb@C nanocomposite was prepared through a simple ball-milling route and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The SiC@Pb@C nanocomposite exhibits a much improved reversible capacity and cycling life as compared with a bare Pb anode. A reversible volumetric capacity of >1,586 mAh cm⁻³ (207 mAh g⁻¹) can be maintained after 600 cycles of charge and discharge in the potential interval between 0.005 and 1.0 V, which far exceeds those reported previously in the literature. The enhanced electrochemical performance is ascribed to the sandwiched structure in which nanosized Pb particles were anchored in between the rigid SiC core and the outer carbon shell, mitigating the damage done by the large volume change of the Pb interlayer during the alloying/dealloying process.     

ZrO2包覆的层状富锂正极材料0.6Li[Li1/3Mn2/3]O2·0.4LiNi5/12Mn5/12Co1/6O2的电化学性能

采用喷雾干燥法合成了富锂层状氧化物正极材料0.6Li[Li_1/3Mn_2/3]O₂·0.4LiNi_5/12Mn_5/12Co_1/6O₂(简称LNMCO),并使用Zr (CH₃COO)₄进行ZrO₂的包覆改性。TEM测试结果显示纳米级的ZrO₂颗粒附着在LNMCO的表面。包覆质量分数为1.5%的ZrO₂包覆样品的首圈库伦效率和放电比容量有着显著提升,在室温下其首圈库伦效率和放电比容量(电流密度：20 mA·g^-1,电压：2.0~4.8 V)分别为87.2%,279.3 mAh·g^-1,而原样则为75.1%,224.1 mAh·g^-1,循环100圈之后,1.5% ZrO₂包覆样品的放电比容量为248.3 mAh·g^-1,容量保持率为88.9%,高于原样的195.9 mAh·g^-1和87.4%。     

Electrochemical behavior of spherical LiNi1/3Co1/3Mn1/3O2 as cathode material for aqueous rechargeable lithium batteries

Spherical LiNi_1/3Co_1/3Mn_1/3O₂ powders have been synthesized from co-precipitated spherical metal hydroxide. The electrochemical performances of the LiNi_1/3Co_1/3Mn_1/3O₂ electrodes in 1 M LiNO₃, 5 M LiNO₃, and saturated LiNO₃ aqueous electrolytes have been studied using cyclic voltammetry and ac impedance tests in this work. The results show that LiNi_1/3Co_1/3Mn_1/3O₂ electrode in saturated LiNO₃ electrolyte exhibits the best electrochemical performance. An aqueous rechargeable lithium battery containing LiNi_1/3Co_1/3Mn_1/3O₂ cathode, LiV_2.9Ni_0.050Mn_0.050O₈ anode, and saturated LiNO₃ electrolyte is fabricated. The battery delivers an initial capacity of 98.2 mAh g⁻¹ and keeps a capacity of 63.9 mAh g⁻¹ after 50 cycles at a rate of 0.5 C (278 mA g⁻¹ was assumed to be 1 C rate).     

Electrochemical performance of LiVPO<Subscript>4</Subscript>F/C composite cathode prepared through amorphous vanadium phosphorus oxide intermediate

LiVPO₄F/C composites with better electrochemical performance were prepared by calcination of LiF and amorphous vanadium phosphorus oxide (VPO) intermediate synthesized by a sol–gel method using H₃PO₄, V₂O₅ and citric acid as raw materials. The properties of LiVPO₄F/C composites were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical tests. The analysis of XRD patterns and Fourier transform infrared spectra (FTIR) reveal that VPO intermediate prepared by sol–gel method is amorphous and VPO₄ may exist in VPO intermediate. The compositions of LiVPO₄F/C composites are related to the calcination temperature for preparation of amorphous VPO/C intermediate and LiVPO₄F/C composite prepared by VPO/C synthesized at 700°C consists of a single crystal phase of LiVPO₄F. The electrochemical tests show that LiVPO₄F/C composite prepared by VPO/C synthesized at 700°C exhibits higher discharge capacity and excellent cycle performance. This LiVPO₄F/C composite displays discharge capacity of 133 mAh g⁻¹ at 0.5 C (78 mA g⁻¹) and remains capacity retention of 96.8% after 30 cycles, even at a high rate of 5 C, the composite exhibits high discharge capacity of 115 mAh g⁻¹ and capacity retention of 97% after 100 cycles.     

Oxalic acid-assisted preparation of LiFePO4/C cathode material for lithium-ion batteries

LiFePO₄/C composite is synthesized by oxalic acid-assisted rheological phase method. Fe₂O₃ and LiH₂PO₄ are chosen as the starting materials, sucrose as carbon sources, and oxalic acid as the additive. The crystalline structure and morphology of the products are characterized by X-ray diffraction and field emission scanning electron microscopy. The charge–discharge kinetics of LiFePO₄ electrode is investigated using cyclic voltammetry and electrochemical impedance spectroscopy. It is found that the introduction of appropriate amount of oxalic acid leads to smaller particle sizes, more homogeneous size distribution, and some Fe₂P produced in the final products, resulting in reduced polarization, impedance, and improved Li⁺ ion diffusion coefficient. The best cell performance is delivered by the sample with R = 1.5 (R of the molar ratio of oxalic acid to LiH₂PO₄). Its discharge capacity is 154 mAh g⁻¹ at 0.2 C rate and 120 mAh g⁻¹ at 5.0 C rate. At the same time, it exhibits an excellent cycling stability; no obvious decrease even after 1,000 cycles at 1.0 C rate.     

ZrO_2包覆的层状富锂正极材料0.6Li[Li_(1/3)Mn_(2/3)]O_2·0.4LiNi_(5/12)Mn_(5/12)Co_(1/6)O_2的电化学性能

采用喷雾干燥法合成了富锂层状氧化物正极材料0.6Li[Li_(1/3)Mn_(2/3)]O2·0.4LiNi_(5/12)Mn_(5/12)Co_(1/6)O_2(简称LNMCO),并使用Zr(CH3COO)4进行ZrO_2的包覆改性。TEM测试结果显示纳米级的ZrO_2颗粒附着在LNMCO的表面。包覆质量分数为1.5%的ZrO_2包覆样品的首圈库伦效率和放电比容量有着显著提升,在室温下其首圈库伦效率和放电比容量(电流密度:20 m A·g-1,电压:2.0~4.8 V)分别为87.2%,279.3 m Ah·g-1,而原样则为75.1%,224.1 m Ah·g-1,循环100圈之后,1.5%ZrO_2包覆样品的放电比容量为248.3 m Ah·g-1,容量保持率为88.9%,高于原样的195.9 m Ah·g-1和87.4%。