ZnO/Ag微米球的合成与光催化性能

用微波辅助多元醇法对预先制备的ZnO微米球进行修饰,合成了载银氧化锌微米球（ZnO/Ag）. 利用X射线衍射仪、场发射扫描电子显微镜、透射电子显微镜、X射线光电子能谱仪、紫外-可见双光束分光光度计和光致发光光谱仪等对样品的结构、形貌和光学性能进行了表征. 在紫外光照射下,通过亚甲基蓝的降解反应研究了样品的光催化活性. 结果表明,所制备的ZnO/Ag微米球是由面心立方的Ag纳米颗粒附着在纤锌矿结构的ZnO球表面形成;与ZnO相比,ZnO/Ag的紫外-可见光吸收光谱发生明显红移,在紫外和可见光范围均有较强的吸收;随着Ag含量的增加,ZnO/Ag荧光光谱强度先减弱后增强;与ZnO相比,ZnO/Ag的光催化活性明显提高,AgNO₃ 浓度为0.05 mol/L时制得的ZnO/Ag光催化活性最高.     

Sb2S3纳米粒子修饰ZnO纳米片微纳分级结构的光电化学性能

采用恒电位方法,选择氯化钾和乙二胺(EDA)为添加剂,在氧化铟锡(ITO)导电玻璃上制备了高度有序的ZnO纳米片阵列,通过二次电沉积得到了ZnO纳米片上生长纳米棒的微纳分级结构.利用化学浴沉积法在ZnO基底上沉积Sb₂S₃纳米粒子制备出了Sb₂S₃/ZnO纳米片壳核结构和Sb₂S₃/ZnO微纳分级壳核结构.利用扫描电子显微镜(SEM)、X射线衍射(XRD)、紫外-可见(UV-Vis)吸收光谱、瞬态光电流等对其形貌、结构组成和光电化学性能进行了表征和分析.结果表明, Sb₂S₃/ZnO纳米片上生长纳米棒分级壳核结构的光电流明显高于Sb₂S₃/ZnO纳米片壳核结构.在Sb₂S₃/ZnO纳米片壳核结构和Sb₂S₃/ZnO微纳分级壳核结构的基础上旋涂一层P3HT薄膜形成P3HT/Sb₂S₃/ZnO复合结构,以上述复合结构薄膜为光活性层组装成杂化太阳电池,其中, P3HT/Sb₂S₃/ZnO分级壳核结构杂化太阳电池的能量转换效率最高,达到了0.81%.     

Pd/ZnO和Ag/ZnO复合纳米粒子的SPS和XPS研究

用焙烧前驱物碱式碳酸锌的方法制备了ZnO纳米粒子，采用光还原沉积贵金属的方法分别得到了质量分数为0.5％的Pd/ZnO和Ag/ZnO复合纳米粒子，并利用XRD、TEM、XPS和SPS等测试技术对样品进行表征.初步探讨了贵金属在ZnO纳米粒子表面形成原子簇的原因及沉积贵金属对ZnO纳米粒子表面光电压信号的影响.以光催化氧化气相正庚烷为模型反应，考察了沉积贵金属对ZnO纳米粒子光催化活性的影响，并探讨了光催化活性有所提高的内在原因.结果表明， ZnO纳米粒子沉积贵金属后，其表面光电压信号明显下降，而光催化活性却大大地提高，这说明可以通过表面光电压谱的测试来初步的评估纳米粒子的光催化活性，即粒子的表面光电压信号越弱，其光催化活性越高.     

共沉淀法制备Ag/AgCl-TiO2空心复合纳米微球及其光催化性能

通过甲基丙烯酸与苯乙烯聚合制备了表面负电性的聚苯乙烯(PSt)纳米乳胶粒. 在乙醇与水的混合溶剂中, 用硅烷偶联剂乙烯基三甲氧基硅烷对其进行表面改性后加入钛酸四丁酯、 氯化钠和硝酸银, 以PSt乳胶粒为模板采用共沉淀法制备了PSt-AgCl-TiO₂复合微球. 在180 ℃对其进行液相预处理及煅烧去除PSt模板后制备了Ag/AgCl-TiO₂空心复合粒子. 对各阶段产物的形貌、 晶体结构和比表面积等进行了表征. 结果表明, 所得产物为Ag/AgCl与锐钛矿型TiO₂复合的空心粒子, 其比表面远大于商品TiO₂(P25). 考察了Ag/AgCl-TiO₂复合粒子在紫外光与可见光下对罗丹明B(RhB)降解的催化活性. 结果表明, 在紫外光下n(Ag)/n(Ti)=0.1%的Ag/AgCl-TiO₂复合粒子活性最高, 30 min时对RhB的降解率比不含Ag/AgCl的TiO₂空心微球提高了13%; 虽然Ag/AgCl-TiO₂在可见光下的催化活性远比紫外光下低, 但与纯TiO₂空心纳米微球相比其催化活性仍明显增强. n(Ag)/n(Ti)=2.0%的Ag/AgCl-TiO₂复合粒子催化活性最高, 120 min时对RhB的降解率比不含Ag/AgCl的TiO₂空心微球提高了38%.     

ZnO纳米柱状阵列表面AgX等离子基元修饰及其可见光光催化活性

采用浸渍法制备了表面AgX（X=I,Br）等离子基元修饰的ZnO纳米柱状阵列,研究了浸渍浓度和时间以及紫外光光照预处理对ZnO纳米柱状阵列可见光光催化活性的影响.采用场发射扫描电子显微镜、X射线衍射仪、紫外可见漫反射吸收光谱以及X射线光电子能谱仪等手段对ZnO纳米柱状阵列的形貌、相组成、禁带宽度及其表面特性进行了表征.结果显示,AgBr颗粒分布于ZnO纳米柱状阵列的顶端及顶端侧面,同时AgBr颗粒之间相互接触而形成网状结构.通过紫外光光照预处理,AgBr表面出现细小颗粒,形成Ag/AgBr/ZnO纳米复合结构.可见光光催化降解甲基橙结果表明,在相同工艺条件下所制AgBr/ZnO的可见光光催化活性明显优于AgI/ZnO,且与浸渍浓度及时间有关.由于ZnO纳米柱状阵列的比表面积大,AgBr的可见光响应特性以及Ag/AgBr纳米结构的表面等离子效应,经过紫外光光照预处理形成的Ag/AgBr/ZnO纳米复合结构表现出最好的可见光光催化活性.     

聚苯乙烯/银纳米粒子复合微球的合成及催化性能

首先通过乳液聚合和浓硫酸酸化制备表面富含磺酸根的磺化聚苯乙烯(PS)微球(直径532 nm),再用其静电吸附[Ag(NH_3)_2]~+离子,最后采用聚乙烯吡咯烷酮还原表面吸附的[Ag(NH_3)_2]~+离子,得到了负载银纳米粒子的PS/AgNPs复合微球.采用扫描电子显微镜、透射电子显微镜、紫外-可见光谱、红外光谱和X射线衍射表征了PS/AgNPs复合微球,并考察了其对甲基蓝(MB)的催化性能.结果表明,Ag纳米粒子高度分散在磺化PS微球表面;该PS/AgNPs复合微球对催化转化MB有较高的催化活性,并可多次重复利用.本研究在催化降解有机污染物方面有一定的实用价值.     

Ag+/Ag/ZnO多孔纳米结构纤维材料的制备及可见光催化性能

借助棉花纤维模板, 采用两步法制备了Ag⁺/Ag/ZnO多孔纳米结构纤维材料, 并利用X射线衍射(XRD)、 X射线光电子能谱(XPS)、 扫描电子显微镜(SEM)和紫外-可见光谱(UV-Vis)等对其进行了表征. 以亚甲基蓝(MB)的脱色降解为模型反应, 考察了银修饰量(摩尔分数, 0~1.50%)对ZnO纳米结构纤维材料光催化性能的影响. 结果表明, 利用模板辅助的两步法制备了Ag⁺-Ag共修饰的ZnO多孔纳米结构纤维材料Ag⁺/Ag/ZnO, Ag⁺和Ag通过改变ZnO的晶胞结构、 光吸收特性及形貌等影响其光催化性能; 在可见光条件下, Ag⁺/Ag/ZnO的催化性能优于纯ZnO, 且与修饰量有关.     

ZnO纳米粒子的表面光电压谱和光催化性能

采用焙烧前驱物碱式碳酸锌的方法制备了不同粒径的ZnO纳米粒子，而用粒径 最小的作为光催化剂，通过光还原过程分别得了贵金属质量分数为0.5%和0.75%的 Pd/ZnO或Ag/ZnO复合纳米粒子。利用XRD，TEM，XPS，SPS和EFISPS等测试技术对样 品进行了表征，并通过光催化氧化气相正庚烷评估了样品的光催化活性，考察了微 晶尺寸和贵金属Pd或Ag的沉积对ZnO纳米粒子表面光电压信号以及光催化活性的影 响，探讨了样品表面光电压谱与其光催化活性的关系，说明了可以通过表面光电压 谱的测试来初步地评估纳米粒子的光催化活性。结果表明：随着ZnO纳米微晶尺寸 的减小，其SPS信号强度逐渐变弱，而光催化活性逐渐升高；沉积适量的贵金属Pd 或Ag后，ZnO纳米粒子的SPS信号强度明显下降，而其光催化活性却有所升高。此外 ，对ZnO纳米粒子光催化剂的失活机理进行了分析。     

ZnO纳米粒子的表面光电压谱和光催化性能

采用焙烧前驱物碱式碳酸锌的方法制备了不同粒径的ZnO纳米粒子，而用粒径 最小的作为光催化剂，通过光还原过程分别得了贵金属质量分数为0.5%和0.75%的 Pd/ZnO或Ag/ZnO复合纳米粒子。利用XRD，TEM，XPS，SPS和EFISPS等测试技术对样 品进行了表征，并通过光催化氧化气相正庚烷评估了样品的光催化活性，考察了微 晶尺寸和贵金属Pd或Ag的沉积对ZnO纳米粒子表面光电压信号以及光催化活性的影 响，探讨了样品表面光电压谱与其光催化活性的关系，说明了可以通过表面光电压 谱的测试来初步地评估纳米粒子的光催化活性。结果表明：随着ZnO纳米微晶尺寸 的减小，其SPS信号强度逐渐变弱，而光催化活性逐渐升高；沉积适量的贵金属Pd 或Ag后，ZnO纳米粒子的SPS信号强度明显下降，而其光催化活性却有所升高。此外 ，对ZnO纳米粒子光催化剂的失活机理进行了分析。     

Pd/ZnO和Ag/ZnO复合纳米粒子的制备、表征及光催化活性

 用焙烧前驱物碱式碳酸锌的方法制备了ZnO纳米粒子，采用光还原沉积贵金属的方法制备了Pd／ZnO和Ag／ZnO复合纳米粒子，并利用ICP，XRD，TEM和XPS等测试技术对样品进行了表征，初步探讨了贵金属在ZnO纳米粒子表面形成原子簇的原因．以光催化氧化气相正庚烷为模型反应，考察了样品的光催化活性以及贵金属沉积量对催化剂活性的影响．结果表明：沉积适量的贵金属，ZnO纳米粒子光催化剂的活性大幅度提高．同时，深入探讨了表面沉积贵金属的ZnO纳米粒子光催化剂活性有所提高的内在原因．     

One pot synthesis of Ag nanoparticle modified ZnO microspheres in ethylene glycol medium and their enhanced photocatalytic performance

Ag nanoparticles (NPs) modified ZnO microspheres (Ag/ZnO microspheres) were prepared by a facile one pot strategy in ethylene glycol (EG) medium. The EG played two important roles in the synthesis: it could act as a reaction media for the formation of ZnO and reduce Ag⁺ to Ag⁰. A series of the characterizations indicated the successful combination of Ag NPs with ZnO microspheres. It was shown that Ag modification could greatly enhance the photocatalytic efficiency of ZnO microspheres by taking the photodegradation of Rhodamine B as a model reaction. With appropriate ratio of Ag and ZnO, Ag/ZnO microspheres showed the better photocatalytic performance than commercial Degussa P-25 TiO₂. Photoluminescence and surface photovoltage spectra demonstrated that Ag modification could effectively inhibit the recombination of the photoinduced electron and holes of ZnO. This is responsible for the higher photocatalytic activity of Ag/ZnO composites.     

Microwave-assisted solution synthesis and photocatalytic activity of Ag nanoparticles supported on ZnO nanostructure flowers

Ag nanoparticles supported on the surface of three-dimensional (3D) flower-like ZnO nanostructure were synthesized by a microwave-assisted solution method. The obtained products were characterized by X-ray diffraction analysis, field-emission scanning electron microscopy, Fourier-transform infrared spectroscopy, Raman spectrophotometry, X-ray photoelectron spectroscopy, and photoluminescence spectroscopy. The analytical results confirmed homogeneously distributed Ag nanoparticles supported on the surface of flower-like ZnO nanostructure. The photocatalytic effect of the heterostructure Ag/ZnO nanocomposites was investigated using photodegradation under ultraviolet (UV) light of methylene blue as model dye. The heterostructure Ag/ZnO nanocomposites exhibited much higher photocatalytic activity than pure ZnO flowers. The improved photocatalytic properties are attributed to formation of a Schottky barrier at the metal–semiconductor interface of the Ag/ZnO nanocomposites.     

A Facile One‐Pot Synthesis of Layered Protonated Titanate Nanosheets Loaded with Silver Nanoparticles with Enhanced Visible‐Light Photocatalytic Performance

Layered protonated titanate nanosheets (LPTNs) loaded with silver nanoparticles are prepared by a simple one‐pot hydrothermal route in silver‐ammonia solution. The as‐synthesized Ag‐loaded LPTNs possess large specific surface area. The Ag nanoparticles are highly dispersed on the surface of the LPTNs. They have negligible effects on the crystal structure, crystallinity, and surface area of the LPTNs but result in considerable enhancement of visible‐light absorption and in a red‐shift of the band gap for the LPTNs. The Ag‐loaded LPTNs show enhanced photocatalytic activity for both liquid‐ and gas‐phase reactions under visible‐light irradiation. Moreover, the photocatalytic activity first increases gradually with increasing Ag loading content, and then decreases after maximizing at an optimal Ag content. At the Ag loading content of 2.87 mol % and 1.57 mol %, the Ag‐loaded LPTNs exhibit the highest visible‐light photocatalytic activity for degradation of rhodamine B in water and mineralization of benzene in air, respectively. An alternative possible mechanism for the enhancement of the visible‐light photocatalytic activity is also proposed.     

花形ZnO纳米片微球的合成、表征及光催化性能

以ZnCl2和尿素为原料,采用水热法合成了由纳米片组成的花形微球碱式碳酸锌前驱体,然后在300℃下煅烧0.5 h得到了形貌一致的ZnO产物。采用XRD、FTIR、TG、SEM、TEM、XPS对其进行表征,结果表明产物为六方纤维矿结构ZnO;组成3D花型微球的纳米片构筑单元厚度为10 nm,表面呈孔装结构,比表面积为72 m2.g-1。分别以花形ZnO纳米片、单分散ZnO纳米片和商用ZnO纳米颗粒为光催化剂,通过降解罗丹明B(Rh B)进行了光催化活性研究。结果表明,与商用ZnO纳米颗粒相比,水热法制备的花形ZnO纳米片显示了更好的光催化活性,可能是由于花形ZnO纳米片微球有较高的比表面积和3D花形形貌所致。     

Synthesis and photocatalytic performance of Ag/AgCl/ZnO tetrapod composites

Ag/AgCl is a visible-light plasmonic photocatalyst that has attracted considerable attention because of its high visible-light absorption and activity owing to the surface plasmon resonance of noble-metal nanoparticles. In this study, Ag/AgCl/ZnO tetrapod composite was prepared by introducing ZnO tetrapods into Ag/AgCl prepared by a polydopamine reduction route. Ag/AgCl was densely deposited on the three-dimensional support framework provided by the ZnO tetrapods. The framework possessed a certain degree of porosity, thereby improving the specific surface area of the Ag/AgCl/ZnO composite. The interaction of ZnO with Ag/AgCl further increased the separation and transfer of electron–hole pairs. The Ag/AgCl/ZnO composite showed excellent photocatalytic activity and good stability. Under xenon lamp irradiation for 20 min, degradation of rhodamine B reached 90%. After four recycling tests, degradation remained stable without any sign of reduction. Ag/AgCl/ZnO tetrapod composite is shown to be a kind of green photocatalyst offering high activity, good stability, and recyclability.

     

ZnO-based hollow microspheres with mesoporous shells: Polyoxometalate-assisted fabrication, growth mechanism and photocatalytic properties

With the assistance of Keggin-type polyoxometalate, ZnO hollow microspheres with mesoporous shells were synthesized via a simple solvothermal approach without any templates and surfactants. The observations of morphology and structure performed by field emission scanning electronic microscopy and transmission electron microscopy indicated that the shells of the ZnO hollow spheres were built from nanosheets which were composed of nanoparticles. The transformation of structure and composition of samples were investigated by X-ray diffraction, X-ray photoelectron spectrometry and fourier transform infrared absorption spectroscopy. The formation mechanism of the hollow spheres is proposed based on time-dependent experimental results. The ZnO hollow microspheres exhibited a high photocatalytic activity for decolorization of Rhodamine B under ultraviolet irradiation.