固相反应法制备磷钼酸(H3PMo12O40)掺杂聚苯胺对其电化学活性的影响

利用固相反应法制备了磷钼酸(H3PMo12O40,简称PMA)掺杂聚苯胺,并以红外光谱(FT-IR)、X-射线衍射(XRD)、循环伏安(cyclic voltamm ogram)等测试方法对聚苯胺进行了表征。结果表明,无论是液相法还是固相法,磷钼酸掺杂于聚苯胺中,仍保持自身结构特征,与传统液相合成的磷钼酸掺杂聚苯胺相比,固相反应法合成的磷钼酸掺杂聚苯胺的晶化率和电活性略差。固相反应法制备的磷钼酸掺杂聚苯胺在对抗坏血酸(AH2)电催化氧化中,表现出比液相合成更好的电催化活性。     

改性LiMn_2O_4的高温电化学性能

采用高温固相反应法制备改性的LiMn2O4锂离子电池正极材料.利用SEM、XRD等方法表征产物的结构特性.结果表明:所得产物均具尖晶石型LiMn2O4结构,该样品经Li2CO3改性后用作锂离子电池正极,于常温和高温下的循环性能均得到明显改善.     

溶剂对固相反应法制备H7PW12O42掺杂聚苯胺的影响

利用固相反应法,分别以微量的水和乙腈作为溶剂,制备了磷钨酸(H7PW12O42)掺杂聚苯胺,并以红外光谱(FTIR),电子扫描显微镜(SEM),X射线衍射(XRD),循环伏安(cyclic voltamogram)等测试方法对聚苯胺进行了表征。结果表明,固相反应法合成的聚苯胺分子链排列有序,晶化率较好,并且表现出有较好的电化学稳定性。而以微量的乙腈作为溶剂通过固相反应法得到的磷钨酸掺杂聚苯胺在颗粒形貌、结晶性、导电率等方面均优于相同条件微量的水作为溶剂时的掺杂聚苯胺。     

β-萘磺酸掺杂聚苯胺纳米粒子的固相反应法制备及其表征

利用固相反应法制备了 β 萘磺酸掺杂的聚苯胺纳米粒子 ,并以红外光谱 (FTIR) ,扫描电子显微镜(SEM) ,透射电镜 (TEM) ,X 射线衍射 (XRD)以及粉末微电极等测试方法对其进行了表征 .结果表明 ,固相反应法合成的 β 萘磺酸掺杂聚苯胺粒子直径为 30～ 5 0nm ,聚苯胺分子链排列有序 ,晶化率较好 .粉末微电极的循环伏安测试表明 ,β 萘磺酸掺杂聚苯胺有较好的电化学活性 .     

掺杂Y^3+的锂锰尖晶石的合成及其电化学性能研究

采用流变相反应法合成了掺杂稀土钇离子的锂锰尖晶石LiYxMn2-xO4，并对其 结构和电化学性能进行了初步研究。结果表明，当掺入的Y^3+的含量较低（x≤0. 02)时，得到的产物能保持完整的尖晶石结构，并表现出极佳的电化学性能。Y^3+ 的掺入使材料的循环稳定性能大幅度提高，而这种提高是源于Y^3+对尖晶石结构的 稳定作用。电极材料LiY0.02Mn1.98O4显示了最优的电化学性能，在0.2℃放电速率 下，其初始放电容量为118mA·h·g^-1，100次循环后仍能保持初始容量的98％。     

淀粉与丙烯酰胺流变相的微波辐射接枝共聚

微波辐射淀粉接枝乙烯基类单体的共聚反应，一般都采用溶液聚合，得到的产物含水量大，产物分离困难。本文将流变相反应法用于接枝共聚反应，探讨微波辐射下玉米淀粉与丙烯酰胺流变相态接枝共聚反应。     

尖晶石LiMn2O4前驱体的低热固相反应法合成机理及其结构与热分解过程研究

以氢氧化锂、醋酸锰和柠檬酸为原料,采用低热固相反应法制备了Li+与Mn2+摩尔比为1∶2的前驱体化合物LiMn2L(Ac)2.通过元素分析、红外光谱、质谱和热重/差热等测试方法对前驱体的组成、结构、合成反应机理及热分解过程进行了研究.结果表明,可在全固相条件下通过低热固相反应得到锂离子与锰离子达到分子级混合水平的前驱体,该前驱体在350℃下焙烧4h即可出现明显的尖晶石相LiMn2O4产物.     

气敏材料Cd2V2O7的制备和性能

采用固相反应法制备了Ｃｄ２Ｖ２Ｏ７半导体气敏材料．研究了制备条件对产物物相的影响及高温固相反应机理．电导测量表明：材料具有典型的表面电阻控制型电导行为．探讨了制备条件对气敏性能的影响．气敏测试表明,Ｃｄ２Ｖ２Ｏ７对乙醇有较好的灵敏度、选择性和稳定性以及较快的响应———恢复速度．     

掺杂Y~(3+)的锂锰尖晶石的合成及其电化学性能研究

采用流变相反应法合成了掺杂稀土钇离子的锂锰尖晶石LiYxMn2 -xO4 ,并对其结构和电化学性能进行了初步研究.结果表明,当掺入的Y3+的含量较低(x≤ 0 0 2 )时,得到的产物能保持完整的尖晶石结构,并表现出极佳的电化学性能.Y3+的掺入使材料的循环稳定性能大幅度提高,而这种提高是源于Y3+对尖晶石结构的稳定作用.电极材料LiY0.0 2 Mn1.98O4 显示了最优的电化学性能,在 0 2C放电速率下,其初始放电容量为 118mA·h·g-1,10 0次循环后仍能保持初始容量的 98%     

锂离子电池正极材料线团状α-MnO_2的合成及电化学性能（英文）

以MnSO_4,(NH_4)_2S_2O_8为反应物,Ag~+作为催化剂的溶液相方法合成了线团状的α-MnO_2。采用XRD、SEM和TEM等手段对合成产物进行了表征。发现反应温度和反应时间对产物的结晶度和形貌有很大的影响。通过恒电流充电/放电测试和循环伏安法(CV)对最终产物的电化学性能进行了表征。结果表明,由于其独特的形态,25℃下反应2d的产物作为锂离子电池正极材料,表现出良好的循环稳定性(100次循环后放电比容量为124 m Ah·g~(-1))。线团状α-MnO_2在锂离子电池应用中可能是一个潜在的正极材料。     

Mn2O3纳米结构的简易合成与电化学性质

用简易的室温或水热方法制备出不同形貌的MnCO₃微结构。经600 ℃热处理后,室温制备MnCO₃转变成Mn₂O₃胶体片,而水热制备MnCO₃样品则形成多孔Mn₂O₃纳米结构。然而,室温制备MnCO₃经120 ℃热处理后形成Mn₂O₃晶相。制备样品经过XRD和SEM表征表明,热处理MnCO₃前驱物形成Mn₂O₃过程导致产物形貌与结构变化。其形成机理又通过TEM和FTIR进一步研究。Mn₂O₃纳米结构的电容性质通过循环伏安法表征,结果表明Mn₂O₃形貌与结构对其电容有重要影响。     

流变相法制备倍率性能优异的LiFePO4/C复合材料

以月桂酸为碳源和表面活性剂,氢氧化锂、碳酸锂和醋酸锂为锂源,采用流变相法制备LiFePO4/C复合材料。运用X射线衍射(XRD)、扫描电子显微镜(SEM)、粒度分析、恒流充放电测试、循环伏安以及交流阻抗测试等方法对复合材料进行表征。结果表明,不同的锂源对LiFePO4/C复合材料的结构和电化学性能均有很大影响,以氢氧化锂为锂源合成的LiFePO4/C材料展示出最佳的循环性能和倍率性能。该材料在0.1C下放电比容量为153.4 mAh.g-1,在大倍率10 C下,容量保持率仍可达76%,甚至10C下循环800次后,容量衰减率仅有4%,SEM结果显示该材料具有较小的粒径(～200 nm),且分布集中,有效提高了电子迁移速率,从而改进了LiFePO4/C的倍率性能。     

Synthesis and electrochemical properties of spinel LiMn2O4 prepared by the rheological phase method

Pure-phase and well-crystallized spinel LiMn₂O₄ powders were successfully synthesized by a simple rheological phase method. The thermal behavior and structure properties of the powders prepared by the rheological phase method compared with the solid-state reaction were investigated by thermogravimetry, powder X-ray diffraction , scanning electron microscopy and transmission electron microscopy. According to the results of the electrochemical tests, it is obvious that the sample resulting from the rheological phase method shows higher discharge capacity and better cycling stability than one formed in the solid-state reaction. The cyclic voltammogram and columbic efficiency curves also confirm that the product by the rheological phase method has a good cycling performance due to its fine cubic spinel structure and morphology.     

Superparamagnetic Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> Nanoparticles Decorated Multiwalled Carbon Nanotubes: Preparation via Cyclic Microwave Approach and Their Drug Release Behavior

Superparamagnetic Fe₃O₄ nanoparticles decorated multiwalled carbon nanotubes were synthesized by cyclic microwave method and the effect of different reaction parameters on the products were also investigated. The as synthesized products were characterized by XRD, TEM, SEM, EDS, FT-IR, VSM, and Uv–Vis spectroscopy. It was observed that precursors’ concentration ratio had great effect on the particle size and decorating quality. Also the effect of the other parameters including irradiation power and time on product size and uniformity of the product were also investigated. The best products with desired particle size distribution obtained when irradiation power and reaction time were 900 W and 6 min, respectively. Aspirin and acetaminophen were applied as a model drug and the drug release behavior of the composite was investigated. It was observed that the drug discharge was highly dependent to the pH and can be tuned by applying magnetic field.     

焦粉活性炭/Al-Ni(OH)2复合电极材料的制备及其超级容器性能

以焦粉为原料,用HNO3预处理除灰,采用KOH浸渍-煅烧活化法制备焦粉活性炭(CPAC),通过场发射扫描电子显微镜、X射线衍射等表征其形貌,采用BET测试其比表面积、孔结构及孔径分布。初步考察了活化温度、活化时间等对焦粉活性炭电极材料电化学性能的影响。采用共沉淀法制备CPAC/Al-Ni(OH)2复合电极材料,通过恒电流充放电测试及循环伏安测试表征CPAC/Al-Ni(OH)2复合电极材料的电化学性能。结果表明,当活化温度为800℃、活化时间为3 h制得的焦粉活性炭电极材料的电化学性能最佳,比电容达到211 F/g。CPAC-800℃-3 h/Al-Ni(OH)2复合电极材料随Al掺杂量的增大呈现先增大后减小的趋势。在固定Al质量掺杂量为4%,炭镍质量比为1∶1时所得复合材料的比电容量最大:1173.6 F/g。恒电流充放电及循环伏安测试表明Al掺杂量为4%、炭镍比为1∶1的复合材料具有较好的电化学性能。     

Co3O4空心球的简易合成及其电化学性能

通过简易的水热法"一锅"制备了Co3O4空心球。借助X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和傅里叶变换红外光谱法(FTIR)等对Co3O4的结构和形貌进行了表征。结果表明,产物由Co3O4纳米粒子构成,并形成明显的空心多孔结构。循环伏安法(CV)测试表明,所制得的Co3O4空心球呈现良好的电化学性能。本文同时对Co3O4空心球结构的形成过程和可能的机理进行了分析和讨论。     

氯化铵对TiO2纳米晶的形成、 结构及性能的影响

以四氯化钛为原料, 通过氯化铵诱导晶化和热挥发分解法制备了二氧化钛纳米晶, 经粉末XRD, TEM, IR和比表面积及热重分析等手段进行了表征. 通过对粒子生长动力学分析, 在700 ℃以下存在两种生长势, 400 ℃时出现转折, 400 ℃以下粒子生长所需活化能为8.23 kJ/mol; 400 ℃以上粒子生长需活化能为45.71 kJ/mol. 于200 ℃时灼烧样品的表面积最大, 对甲基橙光催化降解活性最高.     

超细4A分子筛的超声波低温快速合成

在低温条件下用超声波快速合成了4A分子筛.产物分别用XRD,IR,SEM和DSC等进行了表征.结果表明,用超声波法合成4A分子筛的速度是常规法的24倍.合成产物的白度为95%,钙离子交换容量为335mgCaCO₃/g4A分子筛,平均粒径为280nm.与采用常规方法合成的产物相比,超声波法合成的产物热稳定性有所下降.     

微波-固相复合加热技术合成LiNi0.5Co0.5O2及其性能研究

用高分子分散及微波-固相复合加热技术合成了层状锂离子电池正极材料LiNi0.5Co0.5O2. 采用循环伏安、充放电循环、扫描电子显微镜(SEM)以及X射线粉末衍射(XRD)等测试技术, 研究了煅烧条件对材料微观形貌、相结构以及电化学性能的影响规律. 研究结果表明: 在750 ℃煅烧4 h即可得到形状为类球形的纯相层状LiNi0.5Co0.5O2正极材料, 该材料的最大放电容量达到154 mA·h/g, 循环10周后放电容量仍保持在148 mA·h/g以上.     

Synthesis of Strontium Carbonate by the Induction of Microbiology

Spherical strontium carbonate was synthesized by the induction of microbial bacillus pasteurii at ambient temperature with strontium chloride and urea as the raw materials. The phase composition, particle size and morphology of the product were studied by XRD and SEM. The results indicated that the strontium carbonate synthesized by the induction of microbial bacillus pasteurii was of good dispersion and uniform particle size. The spherical strontium carbonate particles obtained by adding different control agents were constructed by numerous flakes or olive-shaped nano-particles. The products were orthorhombic according to their XRD patterns.