Fabrication of highly ordered TiO2 nanotube arrays using an organic electrolyte

Anodization of titanium in a fluorinated dimethyl sulfoxide (DMSO) and ethanol mixture electrolyte is investigated. The prepared anodic film has a highly ordered nanotube-array surface architecture. Using a 20 V anodization potential (vs Pt) nanotube arrays having an inner diameter of 60 nm and 40 nm wall thickness are formed. The overall length of the nanotube arrays is controlled by the duration of the anodization, with nanotubes appearing only after approximately 48 h; a 72 h anodization results in a nanotube array approximately 2.3 mum in length. The photoelectrochemical response of the nanotube-array photoelectrodes is studied using a 1 M KOH solution under both UV and visible (AM 1.5) illumination. Enhanced photocurrent density is observed for samples obtained in the organic electrolyte, with an UV photoconversion efficiency of 10.7%.     

NH4F/H3PO4体系中阳极氧化法制备TiO2纳米管阵列

以价廉的Ni板代替常用的Pt片为阴极,纯钛为阳极,采用电化学阳极氧化法在NH4F-H3PO4体系中制备出TiO2纳米管阵列.详细研究了制备参数(溶液酸度、氟离子浓度、外加电压和氧化时间)对所获纳米管阵列形貌的影响.采用场发射扫描电镜(FE-SEM)和X射线衍射(XRD)对样品的形貌和晶相结构进行了表征.在最优化的条件下,可以获得形貌规整、表面干净、有序的TiO2纳米管阵列.纳米管阵列的平均管径为60 nm.管长约530 nm.采用阳极氧化法制备的纳米管阵列是非晶态的.经400℃热处理2 h后,可以转变为锐钛矿相.实验结果还发现,经过热处理后,纳米管阵列变得更为有序,管径扩大至约95 nm.     

Anodic growth of uniform nanotube arrays on biphase Ti35Nb5Zr alloy

We report uniform anodization of biphase Ti35Nb5Zr alloy to form doped nanotube arrays in nonaqueous glycerol-based electrolytes rather than in traditional aqueous electrolytes. The electrolyte type played an important role in determining the formation of uniform nanotube arrays. Through using the glycerol-based electrolytes, phase-dependent anodization effect was greatly minimized at both the α-phase regions and the β-phase regions, which makes it possible to grow uniform nanotube arrays on the biphase alloy. The reported anodization method is expected to be useful in fabricating uniformly doped nanotubes on a variety of biphase Ti alloys.     

The Synthesis and Photocatalytic Properties of TiO2 Nanotube Array by Starch‐Modified Anodic Oxidation

In this study, the characterization and photocatalytic activity of TiO₂ nanotube arrays prepared by anodization process with starch addition were investigated in detail. The results suggested that the optimum mass fraction of starch added in anodization process was 0.1%, with which TiO₂ nanotube arrays owning good tubular structure were synthesized. The tube length and average inner diameter of nanotubes were approximately 4 μm and 30 nm, respectively. Through the characterization of TiO₂ nanotube arrays by energy dispersive spectrometer, scanning electron microscopy, transmission electron microscopy, X‐ray diffraction, Fourier Transform Infrared (FTIR) spectroscopy, it was found that the as‐prepared nanotubes possessed well uniformed and higher photodegradation responsive than the pure TiO₂. Moreover, it was expected that the as‐prepared nanotubes exhibited good photocatalytic activity for the degradation of RhB under UV‐light irradiation, which could be ascribed to their good morphology, enhanced UV‐light absorption property and electron transmission ability during the photocatalytic reaction. In addition, the nanotubes were not significantly regenerated during the cycling runs experiment. Overall, this study could provide a principle method to synthesize TiO₂ nanotube arrays with enhanced photocatalytic activity by anodization process with starch addition for environmental purification.     

宽电压范围下阳极氧化制备TiO_2纳米管阵列及其热稳定性

采用电化学阳极氧化技术,以含有NH4F和H2O的甘油溶液为电解液,在宽氧化电压范围(20~100V)下于纯钛表面制备了结构高度有序的TiO2纳米管阵列。利用扫描电子显微镜(SEM)考察了阳极氧化工艺(氧化电压、NH4F浓度、环境温度、水分含量等因素)及退火处理对纳米管形貌的影响;采用X射线衍射分析(XRD)表征了不同氧化电压和退火前后TiO2纳米管阵列的物相;并从电流-时间曲线出发简要地分析了纳米管阵列的形成机理。结果表明,纳米管的内外径和管长随氧化电压的增大而增大;NH4F浓度和环境温度对纳米管形貌有一定的影响;水分含量的多寡决定了能否在高电压下自组装形成纳米管阵列;TiO2纳米管阵列具有良好的热稳定性,管状形貌可以保持到700℃;直接制备的TiO2纳米管阵列均为无定型结构,经450℃退火处理后,无定型的TiO2纳米管转变为锐钛矿相,而600℃退火处理后,部分锐钛矿相转变为金红石相。     

Fe、N共掺杂TiO2纳米管阵列的制备及可见光光催化活性

应用电化学阳极氧化法结合浸渍和退火后处理制备了Fe和N共掺杂的TiO2纳米管阵列光催化剂,并用场发射扫描电镜(FESEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)和俄歇电子能谱(AES)仪对其进行了表征.结果表明,Fe、N共掺杂对TiO2纳米管阵列的形貌和结构没有明显影响,Fe和N均掺入了TiO2晶格.紫外-可见(UV-Vis)漫反射光谱显示Fe和N共掺杂TiO2纳米管阵列的吸收带边较纯TiO2纳米管阵列和单一掺杂TiO2纳米管阵列红移,可见光吸收增强.以可见光催化降解罗丹明B(RhB)考察了材料的光催化活性,Fe和N共掺杂TiO2纳米管阵列对RhB的降解速率较纯TiO2纳米管阵列和单一掺杂TiO2纳米管阵列明显提高,证明了Fe、N共掺杂产生的协同效应提高了TiO2纳米管阵列在可见光照射下的光催化活性.     

High carrier density and capacitance in TiO2 nanotube arrays induced by electrochemical doping

The paper describes the electronic charging and conducting properties of vertically oriented TiO 2 nanotube arrays formed by anodization of Ti foil samples. The resulting films, composed of vertically oriented nanotubes approximately 10 mum long, wall thickness 22 nm, and pore diameter 56 nm, are analyzed using impedance spectroscopy and cyclic voltammetry. Depending on the electrochemical conditions two rather different electronic behaviors are observed. Nanotube array samples in basic medium show behavior analogous to that of nanoparticulate TiO 2 films used in dye-sensitized solar cells: a chemical capacitance and electronic conductivity that increase exponentially with bias potential indicating a displacement of the Fermi level. Nanotube array samples in acidic medium, or samples in a basic medium submitted to a strong negative bias, exhibit a large increase in capacitance and conductivity indicating Fermi level pinning. The contrasting behaviors are ascribed to proton intercalation of the TiO 2. Our results suggest a route for controlling the electronic properties of the ordered metal-oxide nanostructures for their use in applications including supercapacitors, dye-sensitized solar cells, and gas sensing.     

阳极氧化法制备TiO_2纳米管阵列膜及其应用

由阳极氧化法制备的TiO2纳米管阵列,因其独特的有序结构而显示出优异的性能,在许多领域有着广泛的应用,成为一种很有发展前景的新型纳米结构材料。本文简要综述了制备TiO2纳米管阵列结构的方法及其应用研究进展。在比较了当前几种制备TiO2纳米管阵列方法的优缺点后,重点讨论了阳极氧化法制备TiO2纳米管阵列结构过程中,如何通过调整工艺参数来实现此类纳米管阵列结构的可控生长。最后评述了TiO2纳米管阵列材料研究的发展趋势和应用前景。     

TiO2 nanotube/ZnO nanorod/CdS on Ti mesh with three-dimensional array structure for photocatalytic degradation under visible light irradiation

Research on Chemical Intermediates - The three-dimensional (3D) TiO2 nanotube arrays (TNTA) were prepared by electrochemical anodization of Ti mesh in a mixed electrolyte solution of (NH4)2SO4 and...     

不同形态铈改性的TiO2纳米管阵列的制备及其可见光光电响应性质

采用电化学阴极还原和阳极氧化法,制备了还原态铈和氧化态铈改性的TiO2纳米管阵列,通过扫描电子显微镜(SEM)和X射线衍射(XRD)表征样品形貌和晶相,得出还原态铈以单质铈纳米纤维形式存在于TiO2纳米管内及表面,单质铈改性的TiO2纳米管经阳极氧化后,以CeO2和单质Ce形式共存.测定样品的光电流响应并计算样品的能带宽度.结果表明:单质铈改性的TiO2纳米管阵列在可见光区光电流响应较TiO2纳米管增强,单质铈添加存在最佳值,在10 mmol·L-1溶液中制备的单质铈改性的TiO2纳米管阵列光电流响应最强,能带宽度E9减少到2.88 eV,并且随着单质铈含量的增加,载流子浓度增大,且平带电位向负向移动.单质铈改性的样品经阳极氧化后,样品在紫外光区和可见光区光电流响应都增强,但其在可见光区的响应强度要小于单质铈改性的TiO2纳米管在可见光区的响应强度.     

TiO_2纳米管阵列的制备及其对316不锈钢光生阴极保护作用的研究

应用直接电化学阳极氧化法,于含氟电解液中,在纯钛表面制备一层整齐有序的TiO2纳米管阵列.扫描电子显微镜(SEM),X射线衍射(XRD)表征该纳米管阵列的形貌及晶体结构,光电化学联用系统研究其光电响应特性及对316L的光生阴极保护作用.结果表明:以TiO2纳米管阵列膜作为光生阳极时,在紫外光区(λ<387nm)有显著增强的光生电流响应,并对316不锈钢有较好的光生阴极保护作用.暗态下,光生电极电位仍可维持较长的一段时间,继续起到阴极保护作用.     

A facile one-step preparation of hierarchically-structured TiO2 nanotube array photoanodes with enhanced photocatalytic activity

Hierarchically structured TiO₂ (HST) films composed of top porous nanoparticle layer and underneath nanotube array layer are obtained by an anodization method on fluorine doped tin oxide surfaces. Compared with the TiO₂ nanotube arrays photoanode on Ti substrate, the HST photoanode exhibits a higher photoelectrocatalytic activity towards the oxidation of water and organics (e.g., glucose).     

Self-organized TiO2 Nanotube Arrays with Controllable Geometric Parameters for Highly Efficient PEC Water Splitting

In this report,a series of self-organized TiO₂ nanotube arrays were prepared by anodization of titanium foil in mixed electrolytes composed of water,ethylene glycol,and NH₄F.Their photoelectrochemical（PEC） performance as a photoanode was characterized by the PEC water-splitting hydrogen （H₂） generation reaction.The internal relationship between the TiO₂ nanotube arrays （TNTAs） morphology and their PECperformance was thoroughly investigated.Our results ...     

TiO2纳米管阵列光电催化氧化处理氨氮废水

用电化学阳极氧化法制备了高度有序的钛基二氧化钛纳米管阵列薄膜。用场发射扫描电镜(FE-SEM)、X射线衍射(XRD)表征样品的形貌与晶型特征。以二氧化钛纳米管阵列为光阳极,石墨为对电极,测试了不同pH值和外加偏压条件下的光电流响应和光电催化氧化降解NH4Cl水溶液(以N计,100 mg·L-1)的效率。结果表明:所制备的TiO2纳米管阵列具有锐钛矿和金红石的混晶结构,且主要晶型为锐钛矿。光电流响应的强弱与光电催化氧化效率的高低相对应,降解氨氮废水的最佳条件为pH=11,偏压为1.0 V。     

Fabrication of multi-sectional TiO_2 nanotube arrays by anodization

We report a facile method to grow multi-sectional TiO2 nanotube arrays consisting of alternating bamboo-shaped and smooth-walled nanotube sections by anodization.Two key factors are necessary for obtaining these morphologies.First,in order to avoid possible disruptions between the conjoint sections of the nanotube,the distribution of hydrogen ions is suggested not to be fiercely disturbed when switching from the first to the second stage.Second,to avoid the disruption of the nanotube at the joint which resu...     

Characterization of TiO2 nanotube arrays prepared via anodization of titanium films deposited by DC magnetron sputtering

Highly ordered TiO₂ nanotube arrays were fabricated on a conducting glass substrate in NH₄HF₂/glycol electrolyte via anodization of titanium film which was deposited by direct current magnetron sputtering (DCMS) at different temperatures. The results showed that Ti films with good homogeneity and high denseness could be formed under the conditions Ar pressure 0.35 Pa, direct current 3.5 A, and 2 h at 300 °C. Characterization of the TiO₂ nanotube arrays was investigated comparatively, by altering anodization time. The surface morphology of the samples changed as the anodization time was prolonged from 10 to 150 min at 30 V. The TiO₂ thin film was amorphous and could be transformed into anatase by annealing at 450 °C. On the basis of UV?Cvisible transmission spectra the bandgap of the thin film was calculated to be 3.12 eV, and its tail extended to 2.6 eV.     

RGO-TiO2纳米管阵列的制备及其光电性能

采用阳极氧化的方法,通过调节阴、阳两电极间距制备不同壁厚的TiO₂纳米管阵列. 采用脉冲电还原沉积的方法将RGO负载于TiO₂纳米管阵列表面合成了RGO-TiO₂纳米管阵列. 相较于负载在薄壁TiO₂纳米管阵列上的RGO,负载于厚壁TiO₂纳米管阵列上的RGO得以充分还原,覆盖率大幅度提高,并显示出良好的光吸收性质和较低的电荷传输电阻,光电流大幅度增加.     

TiO2 nanorods branched on fast-synthesized large clearance TiO2 nanotube arrays for dye-sensitized solar cells

A large clearance TiO₂ nanotube arrays (LTAs) has been synthesized by a not more than 12 h anodization duration and based on this a branched TiO₂ nanotube arrays (BLTs) has been achieved through TiO₂ nanorods branch-like grown on the LTAs. Some key factors and probable mechanisms of the fabrication processes on two novel nanoarchitectures are discussed. Exhilaratingly, it is found that the obtained LTAs has demonstrated large pore diameter and void spaces (pore diameter ∼350 nm; void spaces ∼160 nm; and tube length ∼3.5 μm), and the synthesized hierarchical BLTs, compared with conventional TiO₂ nanotube arrays, has shown a much stronger dye absorption performance and an approximately double of the solar cell efficiency (in our case from 1.62% to 3.18% under simulated AM 1.5 conditions).     

A humidity-sensitive nanocomposite solid ion conductor: sulfonated poly-ether-ether-ketone in nanotubular TiO2 or ZrO2 matrix

Journal of Solid State Electrochemistry - A nanocomposite solid ion conductor was prepared by infiltrating zirconia or titania nanotube arrays, made by electrochemical anodization of Zr or Ti...     

高度有序的二氧化钛纳米管阵列的制备及其光催化活性的研究

采用电化学阳极氧化法在钛表面构筑了一种结构有序、微米级的TiO₂纳米管阵列膜层. 考察了制备电压、氧化时间、溶液搅拌等实验参数对TiO₂纳米管阵列形貌和尺寸的影响. 应用SEM和XRD对膜层的形貌和晶型进行了分析和表征, 并通过TiO₂纳米管阵列膜对甲基橙的光催化降解, 研究了TiO₂纳米管阵列膜层结构与光催化活性的关系. 结果表明: 阳极电压和溶液搅拌对制备TiO₂纳米管阵列的结构起到关键的作用. 控制20 V电压制备的TiO₂纳米管阵列膜, 管长达2.6～3.3 μm, 经500 ℃热处理后具有最高的光催化活性, 其光催化性能明显优于一般的TiO₂纳米颗粒膜.