高Fe_3O_4含量单分散P(St/AA)复合微球的合成与表征

在表面由十一烯酸和油酸共同修饰的Fe3O4磁流体存在下,以苯乙烯(St)和丙烯酸(AA)为共聚单体,用细乳液聚合法,制备了单分散,高Fe3O4含量,且表面带有羧基的超顺磁性高分子复合微球.采用透射电镜(TEM),热重分析(TGA),物性测量系统(PPMS),Zeta电位以及红外光谱等手段对磁性复合微球的各项性能进行表征.结果表明,Fe3O4粒子的表面改性是影响复合微球Fe3O4含量及形貌的关键因素.在优化的实验条件下,可以制得Fe3O4含量高达77wt%,平均粒径为137·9nm,表面羧基密度0·0894mmol/g,比饱和磁化强度为44·7emu/g的单分散超顺磁性高分子复合微球.     

控制自由基聚合制备Fe_3O_4/SiO_2/P(AA-MMA-St)磁性复合微球

用原硅酸乙酯对Fe3O4纳米粒子进行表面改性得到Fe3O4/SiO2磁流体.在Fe3O4/SiO2磁流体存在下,以1,1-二苯基乙烯(DPE)为自由基聚合控制剂,利用乳液聚合法制备了Fe3O4/SiO2/P(AA-MMA-St)核-壳磁性复合微球.用红外光谱(FTIR)、振动样品磁强计(VSM)、透射电镜(TEM)、X光电子能谱(XPS)、热重分析(TGA)、示差扫描量热仪(DSC)对所制备的磁流体、磁性高分子复合微球的结构、形态、性能进行了表征.研究发现,原硅酸乙酯水解后能在Fe3O4表面形成硅膜保护层从而避免Fe3O4的酸蚀,使Fe3O4/SiO2/P(AA-MMA-St)复合微球的比饱和磁化强度比同样条件下制备的Fe3O4/P(AA-MMA-St)微球提高了28%;DPE能有效控制自由基在Fe3O4/SiO2磁流体表面均匀地引发单体聚合,得到平均粒径为422 nm,无机粒子含量为40%,比饱和磁化强度为34.850 emu/g,表面羧基含量为0.176 mmol/g的磁性复合微球.     

一种新型氨基磁性微球的制备及表征

采用化学共沉淀法制备油酸包被的Fe3O4纳米粒子,以此Fe3O4纳米粒子为核,采用分散聚合法合成了表面带有氨基功能基团的磁性微球。利用透射电镜(TEM)、X射线衍射仪(XRD)、振动样品磁强计(VSM)和傅里叶变换红外光谱仪(FT-IR)对两种磁性微球进行了表征,并采用电位滴定法测定了微球表面的氨基含量。结果表明,微球粒径均匀,为10 nm左右,具有超顺磁性,饱和磁化强度约为50 emu/g,氨基基团含量达486μmol/g。     

1,1-二苯基乙烯存在下无皂乳液聚合制备磁性复合微球

报道了一种制备磁性复合微球的方法——DPE法.在自由基控制剂1,1-二苯基乙烯(DPE)存在条件下,甲基丙烯酸甲酯(MMA)与丙烯酸(AA)发生无皂乳液聚合,制备能与Fe3O4粒子相螯合的活性短链共聚物,加入Fe3O4粒子把短链共聚物引到其表面,引发其它单体继续在Fe3O4粒子表面聚合,制备磁性复合微球.研究了AA、DPE、引发剂及Fe3O4粒子加入量等对制备磁性复合微球的影响.并在此基础上,对优化后工艺制备的磁性复合微球进行了TEM、TGA及磁响应性表征.结果表明,利用该新的方法制备出了磁含量为20%、比饱和磁化强度为32.2emu/g、平均粒径为265nm且表面不含任何杂质的磁性复合微球.     

P(St-GMA)/Fe3O4磁性聚合物微球的制备及表征

采用沉淀法制备了Fe3O4纳米粒子, 以苯乙烯(St)、甲基丙烯酸缩水甘油酯(GMA)为聚合单体, 使用分散聚合法制备了P(St-GMA)/Fe3O4磁性聚合物微球. 分析了Fe3O4粒子的形貌和结构. 研究了制备条件对磁性聚合物微球磁含量的影响. 采用FTIR, XRD, TG及TEM等手段对磁性聚合物微球的微观结构及形貌、磁含量等进行了分析表征. 研究结果表明, 制备的磁性聚合物微球粒径均一, 磁含量高达74%.     

亲水性含环氧基磁性聚合物微球的制备与性能表征

选择甲酰胺作磁性Fe3O4微晶的分散剂,通过设计反相悬浮聚合体系,合成了粒径分布窄、球状亲水性含环氧基磁性聚合物(MGM).利用扫描电子显微镜(SEM)、红外光谱(FT-IR)、X射线粉末衍射仪(XRD)、振动样品磁强计(VSM)和低温N2吸附以及化学分析方法对聚合物进行了性能表征.结果表明,合成的MGM呈球形,且粒度分布较窄,粒径为0.13~0.28 mm的粒子占91%;甲酰胺分散Fe3O4,微晶表面的亲水性进一步增强,单体甲基丙烯酸缩水甘油酯和N,N′-亚甲基双丙烯酰胺交联共聚生成的胶粒能够包埋Fe3O4微晶形成胶核,胶核聚集形成均匀、稳定的MGM微球.MGM中Fe3O4含量为6.17%时,比饱和磁化强度σs达6.5 emu/g;其比表面积、平均孔径和孔容分别为117.6 m2/g,15.6 nm和0.46 cm3/g,表面环氧基团含量为0.53 mmol/g.MGM借助自身的活性环氧基团在十分温和的条件下共价偶联青霉素酰化酶(penicillin G acylase EC 3.5.1.11,简称PGA),制备的固定化酶在37℃下催化水解青霉素G钾生成6-氨基青霉烷酸(6-APA)的表观活性达502IU/g,并且在使用过程中没有出现磁聚集现象.     

介孔SiO_2/Fe_3O_4中空磁性复合微球的制备与表征

采用多步包覆法在自制的240nm的单分散SiO2微球表面进行β-FeOOH的包覆,在5wt%的NaOH溶液中去除核心SiO2后,得到β-FeOOH纳米结构空心微球。将单分散的β-FeOOH空心球作为内核,十六烷基三甲基溴化铵(CTAB)为模板剂,正硅酸乙酯(TEOS)为硅源,经水解缩聚反应得到空心核壳复合微球。在空气中焙烧(500℃,5h)对样品去除模板剂,并在还原气氛(5%H2/95%Ar,350℃,3h)下焙烧得到介孔SiO2/Fe3O4中空磁性复合微球。结果表明,所制得的介孔SiO2/Fe3O4中空磁性复合微球中的Fe3O4层厚度约60nm,是由Fe3O4纳米棒搭接而成的三维网络结构,复合微球的整体平均直径为390nm,比表面积较高约693m2·g-1,孔体积为0.63cm3·g-1,平均孔径为3.6nm,其饱和磁化强度可达13.6emu·g-1,同时较低的矫顽力(50Oe)有利于颗粒的再分散。     

基于Fe3O4@SiO2/Ni-NTA磁性微球的His-tag融合蛋白纯化体系的建立

合成了表面共价结合Ni-氨基三乙酸(Ni-NTA)基团的Fe3O4@ SiO2微球,这种磁性微球可用于分离含有His-tag标签的融合蛋白.微球中心由尺寸约402 nm的Fe3O4微粒组成,赋予了微球极好的磁性分离和离心分离的特性.应用Fe3O4@ SiO2/Ni-NTA磁性微球对含有6×His-tag(6聚组氨酸)标签的蛋白进行了分离纯化,结果表明,10 mg Fe3O4@ SiO2/Ni-NTA微球能够从10mL重组蛋白裂解液中纯化出约1 mg带有6×His-tag标签的融合蛋白.微球的高效分离效果使其能够用于含量较低的带有6×His-tag标签蛋白的分离纯化.     

内部结构不对称磁性复合微球的制备及其影响因素探究

内部结构不对称复合微球是指无机粒子在复合微球内部呈现规律性、不对称分布的一类微球.采用细乳液聚合的方法一步合成了平均粒径0.8μm、磁含量为46.67%、比饱和磁化强度为23.20 emu/g的内部结构不对称PSt/Fe3O4磁性复合微球.详细考察了Fe3O4纳米粒子表面修饰剂含量、乳化剂、助乳化剂、超分散剂、细乳化时间等因素对于复合微球形貌的影响,探讨了内部结构不对称复合微球的形成机理.同时通过TEM(透射电子显微镜),FTIR(红外光谱),VSM(振动样品磁强计),TG(热失重分析)以及激光粒度仪等表征手段对微球内部形貌、磁化强度及粒径等进行了表征,确定Fe3O4纳米粒子表面性质是微球呈现内部结构不对称的决定性因素.     

高Fe3O4含量微米尺寸磁性复合微球的合成及其在化学发光免疫检测中应用初探

采用种子乳液聚合方法制得了微米尺度的高磁性物质含量的磁性复合微球.聚合体系中,以0.7～0.8 μm的Fe3O4磁性聚集体细乳液作为种子,将苯乙烯,二乙烯基苯作为聚合单体加入到磁性聚集体细乳液中,对Fe3O4磁性聚集体进行溶胀后进行聚合.研究了聚合过程中,溶胀时间对复合微球形貌和磁性物质含量的影响,获得系列形貌微球.通过透射电镜(TEM)、热重分析(TGA)、红外分析(FTIR)、振动样品磁强计(VSM)等表征手段对所制备的磁性聚合物微球进行分析表征.结果显示,所得到的磁性聚合物微球粒度为0.7～1 μm,尺寸分布较均一,具有超顺磁性,磁性物质含量为29 wt%～57 wt%.然后又通过丙烯酸和苯乙烯共聚对微球表面羧基功能化后,得到了表面羧基密度为0.92 mmol/g的微球,再将所制备的微球与生物分子偶联后(以hCG作为模式待检分子),在化学发光免疫检测上进行了初步的应用,取得到了较好的应用结果.     

热敏性高分子包裹的磁性微球的合成

磁性高分子微球由于其在外加磁场作用下简单、快速易行的磁分离特性，其在细胞分离、固定化酶、靶向药物等领域的应用研究日益活跃，并显示出较好的应用前景［１］．有关文献报道了制备磁性微球的不同方法［２］．Ｎ 异丙基丙烯酰胺（Ｎ ｉｓｏｐｒｏｐｙｌａｃｒｙｌａ...     

亲/疏水不对称空心聚合物微球制备及磁性粒子装载研究

首先将(马来酸酐-醋酸乙烯酯共聚物)核/(马来酸酐-二乙烯基苯共聚物)壳微球的壳层外表面酐基烷基溴化,然后将核溶蚀、壳层内表面酐基水解,制得内表面含亲水羧基、外表面含烷基溴、具有微孔(Barrett-Joyner-Halenda平均孔径14.9nm)的空心聚合物微球.以此空心微球为微反应器,使Fe2+和Fe3+通过球壁...     

Facile method for synthesis of hollow porous magnetic microspheres with controllable structure

Hollow porous magnetic microspheres with strong magnetization and controllable structure were prepared via a facile electrostatic self-assembly of the positively charged Fe(3)O(4) nanoparticles onto the surface of the negatively charged poly(N,N'-methylenebisacrylamide-co-methacrylic acid) (P(MBAAm-co-MAA)) microspheres with subsequent removal of the polymer core through calcination at high temperature. The shell thickness was facilely tuned through the ratio between Fe(3)O(4) and polymer, and the void space was conveniently changed through the size of polymer microspheres. The hollow magnetic microspheres possessed high saturation magnetization value (51.38 emu/g) and porous structure with high specific surface area (108.04 m(2)/g). Based on these properties, the drug loading and release behaviors were investigated, which indicated that the hollow magnetic microspheres exhibited a controlled release process.     

Preparation of Fe3O4@SiO2@layered double hydroxide core-shell microspheres for magnetic separation of proteins

Three-component microspheres containing an SiO(2)-coated Fe(3)O(4) magnetite core and a layered double hydroxide (LDH) nanoplatelet shell have been synthesized via an in situ growth method. The resulting Fe(3)O(4)@SiO(2)@NiAl-LDH microspheres display three-dimensional core-shell architecture with flowerlike morphology, large surface area (83 m(2)/g), and uniform mesochannels (4.3 nm). The Ni(2+) cations in the NiAl-LDH shell provide docking sites for histidine and the materials exhibit excellent performance in the separation of a histidine (His)-tagged green fluorescent protein, with a binding capacity as high as 239 μg/mg. The microspheres show highly selective adsorption of the His-tagged protein from Escherichia coli lysate, demonstrating their practical applicability. Moreover, the microspheres possess superparamagnetism and high saturation magnetization (36.8 emu/g), which allows them to be easily separated from solution by means of an external magnetic field and subsequently reused. The high stability and selectivity of the Fe(3)O(4)@SiO(2)@NiAl-LDH microspheres for the His-tagged protein were retained over several separation cycles. Therefore, this work provides a promising approach for the design and synthesis of multifunctional LDH microspheres, which can be used for the practical purification of recombinant proteins, as well as having other potential applications in a variety of biomedical fields including drug delivery and biosensors.     

两亲磁性高分子微球的合成与表征

在Fe3O4磁流体存在下 ,通过苯乙烯与聚氧乙烯大分子单体 (MPEO)分散共聚制备两亲磁性高分子微球 .研究了聚氧乙烯大分子单体对微球粒径的影响 .用扫描电子显微镜 (SEM)、原子力显微镜 (AFM)表征了磁性微球的粒径、表面形貌以及表面粗糙度 ,用傅立叶红外光谱 (FTIR)鉴定了共聚物的结构 .随着聚合物中聚氧乙烯大分子单体含量的增加 ,微球表面的粗糙度增加 ,通过改变共聚物中MPEO的含量 ,可以得到含有 0 4～ 3 5mg g羟值的两亲磁性高分子微球     

具有核壳结构磁性复合微球的制备与表征

采用两步法制备了具有核壳结构的Fe3O4/P(MMA/DVB)(core)-P(St/GMA/DVB)(shell)磁性复合微球.首先,用改进的细乳液聚合制备了Fe3O4/P(MMA/DVB)微球;然后,加入总量不同的苯乙烯(St)、甲基丙烯酸缩水甘油酯(GMA)和二乙烯基苯(DVB),通过种子乳液聚合,制备了不同磁含量的核壳结构的磁性复合微球.分别用X-射线衍射(XRD)、高倍透射电镜(HR-TEM)、热重分析(TGA)、振动样品磁力计(VSM)等手段对磁性微球的性能进行了表征.实验结果表明,Fe3O4/P(MMA/DVB)微球的磁含量为84 wt%;通过改变加入壳层单体的量,核壳复合微球的磁含量可控在20 wt%~76 wt%之间.该微球具有超顺磁性,相应的饱和磁化强度为12~50Am2/kg.     

细乳液聚合法制备磁性复合微球及其表征

在制备超细Fe3O4 磁性粒子的基础上 ,以 3种低分子量聚合物Disperbyk 1 0 6、Disperbyk 1 0 8和Disperbyk 1 1 1为Fe3O4 微粒在单体相中的分散稳定剂 ,采用细乳液聚合法制备了平均粒径为 3 40nm的PS Fe3O4 磁性复合微球 .详细研究了分散剂种类对细乳液聚合制备磁性复合微球的影响 ,并采用XRD、TGA和TEM等手段对磁性复合微球的形态、结构及磁响应性等进行了表征 .实验结果证明分散剂的选择对磁性复合微球的成功制备起着至关重要的作用 ,兼具酸性和碱性功能基的分散剂Disperbyk 1 0 6具有更好的分散和稳定效果 .TEM结果表明 ,所制备的复合微球具有一些缺陷 ,而缺陷处往往是Fe3O4 磁性粒子聚集的地方     

磁性Fe_3O_4-聚吡咯纳米微球的合成与表征

报道了具有核壳结构的Fe3O4 聚吡咯磁性纳米微球的合成方法和表征结果 .微球同时具有导电性和磁性能 .在优化的实验条件下 ,可得到饱和磁化强度为 2 3 4emu g ,矫顽力为 45 2Oe的磁性微球 .微球的导电性随着微球中Fe3O4含量的增加而下降 .微球的磁性能则随着Fe3O4含量的增加而增大 .Fe3O4磁流体的粒径和磁性聚吡咯微球的粒径均在纳米量级 .纳米Fe3O4粒子能够提高复合物的热性能 .实验表明 ,磁流体和聚吡咯之间存在着一定的相互作用 ,正是这种相互作用使磁性聚吡咯纳米微球的热稳定性提高 .     

尺寸可控的聚苯胺复合微球的电纺制备与表征

以十二烷基苯磺酸(DBSA)掺杂的导电聚苯胺与聚乙二醇(PEG)及Fe3O4的混合氯仿溶液,采用静电纺丝(spinning technology)方法制备含Fe3O4纳米颗粒的导电聚苯胺(PANI)/PEG/Fe3O4复合微球.SEM结果表明,电纺所得的PANI/PEG/Fe3O4复合微球结构依赖于PEG聚合物浓度、静...