Structural studies on W and Nd substituted La2Mo2O9 materials

The structure of a series of new ionic conductors based in lanthanum molybdate (La₂Mo₂O₉) has been investigated using transmission electron microscopy (TEM), high-resolution X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The superstructure 2a_c×3a_c×4a_c of the low temperature α-polymorph relative to the β-polymorph was confirmed by HRTEM imaging and electron diffraction. Furthermore, the effects of partial cation substitution in the La_2−xNd_xMo₂O₉ and La₂Mo_2−yW_yO₉ series have been also evaluated in the search of new clues to understand the structure and stabilisation of the high temperature and better conductor β-polymorph. The thermal analysis studies show that Nd-substitution does not stabilise completely the β-polymorph at room temperature, although no superstructure ordering was observed by both XRD and HRTEM. On the other hand, W-substitution stabilises the cubic β-polymorph for y>0.25, although, electron diffraction indicates a slight distortion from the cubic symmetry for low W-content. This distortion disappears as the W content increases and the Rietveld refinements gradually render better results.     

Sol-gel synthesized semiconducting LaCo0.8Fe0.2O3-based powder for thick film NH3 gas sensor

Perovskite type LaCo_xFe_1−xO₃ nanoparticles was synthesized by a sol-gel citrate method. The structural, electrical and sensing characteristics of the LaCo_xFe_1−xO₃ system were investigated. The structural characteristics were performed by using X-ray diffraction (XRD) and transmission electron microscopy (TEM) to examine the phase and morphology of the resultant powder. The XRD pattern shows nanocrystalline solid solution of LaCo_xFe_1−xO₃ with perovskite phase. Electrical properties of synthesized nanoparticles are studied by DC conductivity measurement. The sensor shows high response towards ammonia gas in spite of other reducing gases when x = 0.8. The effect of 0.3 wt.% Pd-doped LaCo_0.8Fe_0.2O₃ on the response and a recovery time was also addressed.     

The Crystal Structures, Microstructure and Ionic Conductivity of Ba2In2O5 and Ba(InxZr1−x)O3−x/2

This paper describes the results of electron microscopy, high-temperature powder neutron diffraction, and impedance spectroscopy studies of brownmillerite-structured Ba₂In₂O₅ and perovskite structured Ba(In_xZr_1−x)O_3−x/2. The ambient temperature structure of Ba₂In₂O₅ is found to adopt Icmm symmetry, with disorder of the tetrahedrally coordinated (In³⁺) ions of the type observed previously in Sr₂Fe₂O₅. Ba₂In₂O₅ undergoes a ∼6-fold increase in its ionic conductivity over the narrow temperature range from ∼1140 K to ∼1230 K, in broad agreement with previous studies. This transition corresponds to a change from the brownmillerite structure to a cubic perovskite arrangement with disordered anions. Electron microscopy investigations showed the presence of extended defects in all the crystals analyzed. Ba(In_xZr_1−x)O_3−x/2 samples with x=0.1 to 0.9 adopt the cubic perovskite structure, with the lattice parameter increasing with x.     

XRD and Si MAS-NMR spectroscopy across the β-Lu2Si2O7-β-Y2Si2O7 solid solution

Samples in the system Lu_2−xY_xSi₂O₇ (0?x?2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu₂Si₂O₇ and Y₂Si₂O₇. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y₂Si₂O₇ in β-Lu₂Si₂O₇ at 1300 °C. ²⁹Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the ²⁹Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict ²⁹Si chemical shifts in silicates is applied here to obtain the theoretical variation in ²⁹Si chemical shift values in the system Lu₂Si₂O₇-Y₂Si₂O₇ and the results compare favorably with the values obtained experimentally.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Structure and phase composition of nanocrystalline Ce1−xLuxO2−y

The microstructure and phase stability of nanocrystalline mixed oxide Lu_xCe_1−xO_2−y (x=0-1) are described. Nano-sized (3-4 nm) oxide particles were prepared by the reverse microemulsion method. Morphological and structural changes upon heat treatment in an oxidizing atmosphere were studied by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman and Yb³⁺ emission spectroscopy, the latter ion being present as an impurity in the Lu₂O₃ starting material. Up to 950 °C, the samples were single phase, with structure changing smoothly with Lu content from fluorite type (F) to bixbyite type (C). For the samples heated at 1100 °C phase separation into coexisting F- and C-type structures was observed for 0.35<x<0.7. It was also found that addition of Lu strongly hinders the crystallite growth of ceria during heat treatment at 800 and 950 °C.     

A novel route to synthesize cubic ZrW2−xMoxO8 (x=0-1.3) solid solutions and their negative thermal expansion properties

Cubic ZrW_2−xMo_xO₈ (c-ZrW_2−xMo_xO₈) (x=0-1.3) solid solutions were prepared by a novel polymorphous precursor transition route. X-ray diffraction (XRD) analysis reveals that the solid solutions are single phase with α- and β-ZrW₂O₈ structure for 0?x?0.8 and 0.9?x?1.3, respectively. The optimum synthesis conditions of ZrWMoO₈ are obtained from differential scanning calorimetry-thermal gravimetric analysis (DSC-TGA), XRD and mass loss-temperature/time curves. Following the above experience, the stoichiometric solid solutions of c-ZrW_2−xMo_xO₈ (x=0-1) are obtained within 1 wt% of mass loss. The relationships of lattice parameters (a), phase transition temperatures (T_c) and instantaneous coefficients of thermal expansion (α_i) against the content x of Mo are discussed based on the variation of order degree parameters of ZrW_2−xMo_xO₈.     

Solvothermal Synthesis of Superfine Li1−xMn2O4−σ Powders

Superfine Li_1−xMn₂O_4−σ powders were successfully synthesized by the alcohol-thermal method using 0.01 mol of MnO₂, 0.01mol of LiOH·H₂O, and 0.06mol of NaOH as starting materials at 160-200°C. The products are characterized by XRD, TEM, ED, BET, and ICP. Results show that the Li_0.74Mn₂O_3.74 powder prepared at 200°C has an average size of 180 nm with BET surface areas of 16.44 m²/g. A possible formation mechanism is proposed. It was concluded that the alcohol acts not only as the solvent but also as the reducing agent in the synthesis of Li_1−xMn₂O_4−σ powders. The effects of reaction temperature and the contents of NaOH and LiOH on the formation of single phase Li_1−xMn₂O_4−σ were investigated.     

Synthesis, structure and electrical properties of Cu3.21Ti1.16Nb2.63O12 and the CuOx-TiO2-Nb2O5 pseudoternary phase diagram

Subsolidus phase relations in the CuO_x-TiO₂-Nb₂O₅ system were determined at 935 °C. The phase diagram contains one new phase, Cu_3.21Ti_1.16Nb_2.63O₁₂ (CTNO) and one rutile-structured solid solution series, Ti_1−3xCu_xNb_2xO₂: 0<x<0.2335 (35). The crystal structure of CTNO is similar to that of CaCu₃Ti₄O₁₂ (CCTO) with square planar Cu²⁺ but with A site vacancies and a disordered mixture of Cu⁺, Ti⁴⁺ and Nb⁵⁺ on the octahedral sites. It is a modest semiconductor with relative permittivity ∼63 and displays non-Arrhenius conductivity behavior that is essentially temperature-independent at the lowest temperatures.     

Cr3+在不同基质Y3Ga5O12或Ga2O3中的荧光特性

以Ga_2O_3、Y_2O_3、Cr(NO_3)_3·9H_2O为原料,柠檬酸为配位剂,通过溶胶-凝胶高温固相合成法制备出Ga_(2-2x)O_3∶2xCr~(3+)(Ga_2O_3∶xCr)与Y_3Ga_(5-5x)O_(12)∶5xCr~(3+)(YGG∶xCr)2种多晶粉体(x=0.01,0.03,0.05,0.07)。并采用X射线衍射(XRD)、红外光谱(IR)、扫描电镜(SEM)、荧光光谱(PL)对样品的结构、组成、形貌和荧光性能进行测试分析。XRD和IR分析结果显示在900℃煅烧后Ga_2O_3∶xCr和YGG∶xCr两种样品均成相。SEM照片显示Ga_2O_3∶xCr样品形貌为柱形多面体,YGG∶xCr为短棒状。PL结果显示Cr~(3+)在Ga_2O_3和YGG两种基质中的最强荧光发射峰分别位于742和740 nm,均属于Cr~(3+)的~2E-~4A_2跃迁,对比发现Cr~(3+)在YGG基质中的荧光发射强度更强,在远红光区的荧光性能更好,能满足温室照明中植物光合作用的需求。     

Correlation of crystal structures with electric field gradients in the fluorite- and pyrochlore-type compounds in the Gd2O3-ZrO2 system

Correlation of crystal structure with electric field gradient (EFG) in the fluorite- and pyrochlore-type compounds in the Gd₂O₃-ZrO₂ system Gd_xZr_1−xO_2−x/2 with 0.18?x?0.62 were investigated by ¹⁵⁵Gd Mössbauer spectroscopy, powder X-ray diffraction and point-charge model (PCM) calculation. An intermediate ordered pyrochlore phase forms for 0.45?x?0.55, sandwiched with a disordered fluorite phase for 0.18?x<0.45 and 0.55<x?0.62. Some ¹⁵⁵Gd Mössbauer parameters, especially the quadrupole coupling constant (e²qQ), were found to exhibit a characteristic maximum around the ideal-pyrochlore Gd₂Zr₂O₇ (x=0.50) composition. The validity of the proposed pyrochlore-based structural model was examined by comparing the experimental values of EFG at the Gd sites with those calculated by the PCM calculations.     

Fluorinated transition alumina with Al2−x/3O3−xFx compositions: Thermal, chemical, structural and morphological investigations

Fluorinated transition aluminas (Al_2−x/3O_3−xF_x) with hexagonal platelet shape were synthesized via decomposition of α-AlF₃ under air; they are thermally stable up to 1000 °C and exhibit at 1150 °C a weight loss with volume reduction caused by fluorine departure corresponding to a phase transition toward corundum alumina. The different characterizations performed in this study are structural (XRD), chemical (TGA-MS and microprobe analysis) and morphological (SEM, TEM and dilatometry). The evidence provided from this study is consistent with the formation of an Al-O-F phase as an intermediate compound in the pyrohydrolysis of an aluminium trifluoride phase to α-Al₂O₃.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Comprehensive survey of Nd substitution In La2Mo2O9 oxide-ion conductor

Differential thermal analysis coupled to temperature-controlled diffraction have given evidence of a topological metastability phenomenon in an extended compositional range of the La_2−xNd_xMo₂O₉ solid solution. A metastable-stable phase diagram is proposed for this series of LAMOX-type fast oxide-ion conductors. In the Nd range 0<x?0.35, a freezing of the oxygen/vacancy disorder of the β-phase at ambient temperature can be achieved through a splat-quenching to water-ice mixture or/and shaping/sintering into pellet. In the intermediate 0.4?x?1.2 range, the amount of β-metastable phase grows upon substitution for powders. The negative impact of β-metastable to α phase transition on conductivity tends to disappear through the partial stabilization of the β phase by shaping/sintering.     

Enzyme mimics of spinel-type CoxNi1−xFe2O4 magnetic nanomaterial for eletroctrocatalytic oxidation of hydrogen peroxide

A series of spinel-type Co_xNi_1−xFe₂O₄ (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) magnetic nanomaterials were solvothermally synthesized as enzyme mimics for the eletroctrocatalytic oxidation of H₂O₂. X-ray diffraction and scanning electron microscope were employed to characterize the composition, structure and morphology of the material. The electrochemical properties of spinel-type Co_xNi_1−xFe₂O₄ with different (Co/Ni) molar ratio toward H₂O₂ oxidation were investigated, and the results demonstrated that Co_0.5Ni_0.5Fe₂O₄ modified carbon paste electrode (Co_0.5Ni_0.5Fe₂O₄/CPE) possessed the best electrocatalytic activity for H₂O₂ oxidation. Under optimum conditions, the calibration curve for H₂O₂ determination on Co_0.5Ni_0.5Fe₂O₄/CPE was linear in a wide range of 1.0 × 10⁻⁸–1.0 × 10⁻³ M with low detection limit of 3.0 × 10⁻⁹ M (S/N = 3). The proposed Co_0.5Ni_0.5Fe₂O₄/CPE was also applied to the determination of H₂O₂ in commercial toothpastes with satisfactory results, indicating that Co_xNi_1−xFe₂O₄ is a promising hydrogen peroxidase mimics for the detection of H₂O₂.     

Phase equilibria in the pseudo-binary system SrO-Fe2O3

The phase relations in the pseudo-binary system SrO-Fe₂O₃ have been investigated in air up to 1150°C by means of powder X-ray diffraction and thermal analysis. Sr₃Fe₂O_7−δ, SrFeO_3−δ and SrFe₁₂O₁₉ are stable phases in the entire investigated temperature region, whereas Sr₂FeO_4−δ and Sr₄Fe₃O_10−δ decompose above 930±10°C and 850±25°C, respectively. Sr₄Fe₆O_13±δ is entropy-stabilized relative to SrFeO_3−δ and SrFe₁₂O₁₉ above 775±25°C. Extended solid-solution Sr_1±xFeO_3−δ was demonstrated. On the Fe-deficient side, the extent of solid solubility appeared to decrease gradually with temperature, whereas an abrupt decrease due to formation of Sr₄Fe₆O_13±δ was observed above 775°C on the Sr-deficient side.     

High-pressure transitions in MgAl2O4 and a new high-pressure phase of Mg2Al2O5

Phase transitions in MgAl₂O₄ were examined at 21-27 GPa and 1400-2500 °C using a multianvil apparatus. A mixture of MgO and Al₂O₃ corundum that are high-pressure dissociation products of MgAl₂O₄ spinel combines into calcium-ferrite type MgAl₂O₄ at 26-27 GPa and 1400-2000 °C. At temperature above 2000 °C at pressure below 25.5 GPa, a mixture of Al₂O₃ corundum and a new phase with Mg₂Al₂O₅ composition is stable. The transition boundary between the two fields has a strongly negative pressure-temperature slope. Structure analysis and Rietveld refinement on the basis of the powder X-ray diffraction profile of the Mg₂Al₂O₅ phase indicated that the phase represented a new structure type with orthorhombic symmetry (Pbam), and the lattice parameters were determined as a=9.3710(6) Å, b=12.1952(6) Å, c=2.7916(2) Å, V=319.03(3) Å³, Z=4. The structure consists of edge-sharing and corner-sharing (Mg, Al)O₆ octahedra, and contains chains of edge-sharing octahedra running along the c-axis. A part of Mg atoms are accommodated in six-coordinated trigonal prism sites in tunnels surrounded by the chains of edge-sharing (Mg, Al)O₆ octahedra. The structure is related with that of ludwigite (Mg, Fe²⁺)₂(Fe³⁺, Al)(BO₃)O₂. The molar volume of the Mg₂Al₂O₅ phase is smaller by 0.18% than sum of molar volumes of 2MgO and Al₂O₃ corundum. High-pressure dissociation to the mixture of corundum-type phase and the phase with ludwigite-related structure has been found only in MgAl₂O₄ among various A²⁺B³⁺₂O₄ compounds.     

Structural and magnetic characterization of BiFexMn2-xO5 oxides (x=0.5, 1.0)

The title compounds have been synthesized by a citrate technique followed by thermal treatments in air (BiFe_0.5Mn_1.5O₅) or under high oxygen pressure conditions (BiFeMnO₅), and characterized by X-ray diffraction (XRD), neutron powder diffraction (NPD) and magnetization measurements. The crystal structures have been refined from NPD data in the space group Pbam at 295 K. These phases are isostructural with RMn₂O₅ oxides (R=rare earths) and contain infinite chains of Mn⁴⁺O₆ octahedra sharing edges, linked together by (Fe,Mn)³⁺O₅ pyramids and BiO₈ units. These units are strongly distorted with respect to those observed in other RFeMnO₅ compounds, due to the presence of the electronic lone pair on Bi³⁺. It is noteworthy the certain level of antisite disorder exhibited in both samples, where the octahedral positions are partially occupied by Fe cations, and vice versa. BiFe_xMn_2−xO₅ (x=0.5, 1.0) are short-range magnetically ordered below 20 K for x=0.5 and at 40 K for x=1.0. The main magnetic interactions seem to be antiferromagnetic (AFM); however, the presence of a small hysteresis in the magnetization cycles indicates the presence of some weak ferromagnetic (FM) interactions.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

Interactions of Ba2YCu3O6+y with the Gd3NbO7 buffer layer in coated conductors

A systematic study of the chemical interaction of Ba₂YCu₃O_6+y and Gd₃NbO₇ was conducted under two processing conditions: purified air (21% p_o2), and 100 Pa p_o2 (0.1% p_o2). Phases present along the pseudo-binary join Ba₂YCu₃O_6z and Gd₃NbO₇ were found to be in two five-phase volumes within the system. Three common phases that are present in all samples are (Y,Gd)₂Cu₂O₅, Ba(Y,Gd)₂CuO₅ and Cu₂O or CuO (depending on the processing conditions). The assemblies of phases can be categorized in three regions, with Ba₂YCu₃O_6+y: Gd₃NbO₇ ratios of (I)<5.5:4.5; (II)=5.5:4.5; and (III)>5.5:4.5. The lowest melting temperature of the system was determined to be ≈938 °C in air, and 850 °C at 100 Pa p_o2. Structure determinations of two selected phases, Ba₂(Gd_xY_1−x)NbO₆ (Fm3¯m, No. 225), and (Gd_xY_3−x)NbO₇ (C222₁, No. 20 and Ccmm, No. 63), were completed using the X-ray Rietveld refinement technique. Reference X-ray powder diffraction patterns for selected phases of Ba₂(Gd_xY_1−x)NbO₆ (x=0.2, 0.4, 0.6, and 0.8) and (Gd_xY_3−x)NbO₇ (x=0.6, 1.2, 1.8, 2.4 and 3) have been prepared for inclusion in the Powder Diffraction File (PDF).