白光LED用Sr0.955Al2Si2-xTixO8：Eu2+荧光粉的晶体结构和光谱特性

由高温固相反应制得Sr_0.955Al₂Si_2-xTi_xO₈：Eu²⁺（x=0~1.0）系列试样,研究了Ti⁴⁺置换Si⁴⁺对其晶体结构和光谱特性的影响。Ti⁴⁺以类质同相替代Si⁴⁺进入晶体晶格中,形成了连续固溶体,其晶胞参数a,b,c,β和晶胞体积V随Ti⁴⁺置换量呈线性递增。Ti⁴⁺置换Si⁴⁺对晶胞参数c的影响显著,b其次,a最小。荧光激发谱为宽带,位于230~400nm,由267nm、305nm、350nm和375nm 4个峰拟合成,表观峰值位于351nm;随着Ti⁴⁺置换量的增加,半高宽（FWHM）从105nm减小到93nm。发射光谱位于380~600nm,表观峰值位于407nm,可由406nm和441nm两峰拟合而成并且随Ti⁴⁺置换量增加线性红移,Ti⁴⁺进入晶格对长波长发射中心影响较少;Ti⁴⁺置换量为1.0时,表观发射峰位从407nm红移至417nm;利用试样荧光光谱和VanUitert经验公式,得出SrAl₂Si₂O₈：Eu²⁺中Sr²⁺的配位数为9。随着Ti⁴⁺置换量Si⁴⁺进入基质晶格,造成Eu-O距离变小,使得Eu²⁺所处的晶体场强度增强,发光中心Eu²⁺的5d能级分裂增大,造成Eu²⁺最低发射能级重心下移,两拟合谱峰峰位均呈线性红移。     

Cr2O3和CrO3/Cr2O3催化剂的2-氯-1，1，1-三氟乙烷气相氟化反应的活性物种和失活

采用沉淀法和浸渍法制备了2种铬基（Cr₂O₃和CrO₃/Cr₂O₃）催化剂,用于气相氟化2-氯-1,1,1-三氟乙烷合成1,1,1,2-四氟乙烷。研究发现含有低价铬（Cr³⁺）物种的Cr₂O₃催化剂上2-氯-1,1,1-三氟乙烷的稳态转化率为18.5%,而含有高价铬（Cr⁶⁺）物种和低价铬（Cr³⁺）物种的CrO₃/Cr₂O₃催化剂初始转化率达到30.6%,然而存在明显的失活。含有Cr⁶⁺物种的CrO₃/Cr₂O₃催化剂的2-氯-1,1,1-三氟乙烷氟化反应初始TOF值为1.71×10^-4 mol_HCFC-133a·mol_Cr(Ⅵ)^-1·s^-1,高于含有Cr³⁺物种的Cr₂O₃催化剂（4.16×10^-5 mol_HCFC-133a·mol_Cr(Ⅲ)^-1·s^-1）。Cr₂O₃催化剂在氟化反应前后催化剂的物相结构保持不变;而含有高价铬物种的CrO₃/Cr₂O₃催化剂经HF反应后生成了CrO_xF_y活性物种。然而,CrO_xF_y物种在反应中挥发或转化成稳定但无活性的CrF₃,从而导致催化剂失活。     

掺杂和取代对红色荧光材料SrAl12O19:Mn4+发光性能的影响

SrAl₁₂O₁₉：Mn⁴⁺是一种用于高显色性白光发光二极管的候选红色荧光材料。本论文研究了Mg²⁺、Zn²⁺和Ge⁴⁺离子的掺杂效应以及Ga³⁺、Ca²⁺和Ba²⁺离子的取代效应对SrAl₁₂O₁₉：Mn⁴⁺荧光材料性能的影响。样品通过高温固相反应制备,焙烧温度在1 250~1 500 ℃之间。利用X射线衍射技术表征了材料的相纯度,用荧光激发光谱和发射光谱表征了材料的荧光性能。研究结果指出,与未进行Mg²⁺或Zn²⁺掺杂的样品相比,Mg²⁺或Zn²⁺离子对Al³⁺格位的掺杂可以使材料的发光强度提高~60%,其原因被认为是掺杂促进了激活剂Mn⁴⁺离子进入晶格,其过程可以表示为：MO+MnO₂⇔M_Al^''+M_Al^·+3O_O^×（M=Mg,Zn）,电子顺磁共振谱支持这一结果。Ge⁴⁺离子的掺杂使材料的发光性能明显下降。Ga³⁺离子可以取代Al³⁺离子形成全范围的固溶体,其中少量Ga³⁺离子的掺杂可以使材料的荧光发射强度提高~13%,而掺杂量进一步提高使材料的荧光性能下降。Ca²⁺和Ba²⁺对Sr²⁺的取代仅形成有限范围的固溶体。Ca²⁺的取代使材料的发光性能提高;而 Ba²⁺的取代使材料的发光强度下降。     

ZnAl2O4:Mn材料的制备及发光性能

以共沉淀法与煅烧法联用,成功制备了一系列ZnAl₂O₄:xMn样品。通过扫描电镜和X射线粉末衍射测试研究了样品的形貌和物相特征,结果表明尖晶石结构的ZnAl₂O₄中[AlO₆]的八面体位可以有效被Mn⁴⁺替代。通过荧光激发和发射光谱研究了样品的发光性能,发现Mn⁴⁺在ZnAl₂O₄体系中掺杂可以显示出明亮的红色发光(发射峰值位于680 nm处)。比较不同Mn⁴⁺浓度(Mn与Al的物质的量之比)掺杂样品的发光强度时发现,Mn⁴⁺最佳掺杂浓度为0.06%。通过德克斯特公式分析了发光强度与浓度关系,探究浓度猝灭机制,结果表明最邻近离子之间能量传递造成Mn⁴⁺浓度猝灭的发生。为了提高Mn⁴⁺的发光强度,选择了7种金属离子(Li⁺、Na⁺、K⁺、Ca²⁺、Sr²⁺、Sn²⁺和Ga³⁺)与Mn⁴⁺共掺杂进入ZnAl₂O₄基质中,其中效果较突出的为Li⁺和Ga³⁺,其共掺杂使Mn⁴⁺发光强度分别增强0.6倍和1倍。     

电荷补偿对Ba2ZnGe2O7：Bi3+荧光粉发光性质的影响

采用高温固相法制备了2个系列的荧光粉样品：Ba_2-xZnGe₂O₇：xBi³⁺（系列Ⅰ）和Ba_1.994-yK_yZnGe₂O₇：0.006Bi³⁺（系列Ⅱ）。X射线衍射（XRD）测试结果表明,少量Bi³⁺、K⁺的掺杂不会明显改变材料的物相结构。样品的荧光光谱测试结果表明,虽然2个系列样品的发光光谱都随组成成分变化有少量变化,但发光颜色基本上均为黄绿色。在358 nm的激发下,荧光粉的发射光谱呈现一个峰值在500 nm的宽发射带,归属于³P₁→¹S₀能级跃迁。在500 nm监测下,荧光粉的最强激发峰位于358 nm,归属于¹S₀→³P₁能级跃迁,此外还有一个位于320 nm的肩峰归属于O^2--Bi³⁺电荷转移带。系列Ⅰ样品的光谱数据结果指出,Bi³⁺的最佳掺杂量x为0.006。在该基质中,Bi³⁺掺杂取代Ba²⁺属于不等价取代,会在晶格中产生Ba²⁺空位或间隙O^2-,对材料的发光强度产生负面影响。对此,采用K⁺与Bi³⁺协同掺杂起到电荷补偿的作用,填补Ba²⁺空位或捕获间隙O^2-缺陷。空位被填补或间隙被捕获均减少了晶格畸变,从而使发光强度明显提高。系列Ⅱ样品的光谱数据表明,完全电荷补偿的荧光粉样品相比于没有掺K⁺的样品,其发光强度提高了约2.5倍。     

Fe3+掺杂三维分级纳米Bi2WO6的合成及其光催化活性增强机理

利用水热法合成了Fe³⁺掺杂的三维分级纳米Bi₂WO₆,借助X射线衍射（XRD）、场发射扫描电镜（FE-SEM）、透射电镜（HRTEM）、能谱（EDS）、紫外可见漫反射（UV-Vis-DRS）等测试手段对所得样品的相组成、形貌和谱学特征进行了表征。选择罗丹明B为模型污染物研究所得样品在可见光下的催化活性。结果表明,Fe³⁺掺杂Bi₂WO₆为新颖的分级纳米结构,且Fe³⁺掺杂能有效提高Bi₂WO₆的光催化活性,Fe³⁺掺杂量对Bi₂WO₆活性的影响显著;实验结果还表明,所得Fe³⁺掺杂Bi₂WO₆催化剂的稳定性较好,易于回收。此外,还对Fe³⁺掺杂Bi₂WO₆的光催化活性增强机理进行了研究,缺电子的Fe³⁺作为电子捕获中心有利于促进光生电子-空穴对的分离,从而提高Bi₂WO₆的光催化活性。     

双钙钛矿型Ca2Gd1-xTaO6：xTb3+绿色荧光粉的合成与荧光性质

通过高温固相法合成了双钙钛矿型Ca₂Gd_1-xTaO₆：xTb³⁺（CGTO：xTb³⁺）绿色荧光粉。采用X射线衍射、扫描电镜、荧光光谱、荧光衰减曲线、量子效率（η）测试分别表征了CGTO： xTb³⁺荧光粉的物相、形貌和荧光性质。在紫外光激发下,CGTO： xTb³⁺荧光粉实现了较强的绿光发射,绿光为Tb³⁺离子的⁵D₄-⁷F₅跃迁。通过变温发射光谱研究发现CGTO：0.15Tb³⁺荧光粉的热猝灭活化能为0.181 9 eV。在255 nm的激发下,最佳Tb³⁺掺杂浓度的CGTO：0.15Tb³⁺荧光粉的量子效率为32.32%。     

Sr0.955Al2-xBxSi2O8:0.025Eu2+荧光粉的制备、晶体结构及发光性能

通过高温固相反应在弱还原气氛下制备了Sr_0.955Al_2-xB_xSi₂O₈：0.025Eu²⁺（x=0~0.9）一系列荧光粉,研究了B（Ⅲ）取代基质晶格中的Al（Ⅲ）对荧光粉晶体结构和Eu²⁺发光性能的影响。B（Ⅲ）以类质同相取代基质晶格中Al（Ⅲ）,形成了连续固溶体。随着B（Ⅲ）取代量的增加,荧光粉的晶胞参数（a、b、c）和晶胞体积（V）呈线性递减,而晶胞参数（β）呈线性递增。荧光粉的激发光谱为位于225~400 nm的宽峰,表观峰值位于350 nm,激发峰的半高宽（FWHM）随着B（Ⅲ）取代量的增加,从90 nm减小到102 nm。发射光谱位于370~600 nm的宽峰,可拟合为409和447 nm两个峰,表观峰值位于409 nm。随着B（Ⅲ）取代量的增加,2个拟合峰位均出现蓝移且2个峰强度比呈线性递减。根据试样荧光光谱,通过Van Uitert经验公式计算得出SrAl₂Si₂O₈：Eu²⁺中Sr²⁺的配位数为9。随着B（Ⅲ）取代Al（Ⅲ）进入基质晶格,造成发光中心Eu与配体O距离增加,使得Eu²⁺所处的晶体场强度减小,发光中心Eu²⁺的5d能级分裂减小,造成Eu²⁺最低发射能级重心上移,2个拟合谱峰峰位均呈线性蓝移。     

Li4SrCa (SiO4)2:Eu3+红色荧光粉的合成及其发光性能

采用硅酸盐作为基质材料,通过高温固相法合成了Li₄SrCa（SiO₄）₂：Eu³⁺红色荧光粉。通过X射线粉末衍射、X射线光电子能谱、透射电镜和荧光光谱,对所得样品的物相、形貌及其发光性能进行了表征分析。结果表明,掺入Eu³⁺后,Li₄SrCa（SiO₄）₂的晶体结构并没有发生改变。在393 nm光激发下,荧光粉的荧光光谱中693 nm处发射峰强度最强。以693 nm作为监测波长,荧光激发峰分别为361 nm（⁷F₀→⁵D₄）、375 nm（⁷F₀→⁵G₃）、413 nm（⁷F₀→⁵D₃）、393 nm（⁷F₀→⁵L₆）和464 nm（⁷F₀→⁵D₂）,即样品对近紫外和蓝光有较好的吸收。利用发射光谱研究了Eu³⁺掺杂浓度（物质的量分数）对荧光粉发光强度的影响。当Eu³⁺的掺杂浓度x=0.10时,样品发射强度最强,发射红光,其色坐标为（0.637 5,0.353 7）。通过Dexter强度与浓度关系分析了浓度猝灭机制。     

CaSb2O6:Bi3+,Eu3+荧光粉的制备和发光性质

采用共沉淀法及1 200 ℃后续煅烧4 h,成功制备了CaSb₂O₆:Bi³⁺,Eu³⁺荧光粉,并对其结构及发光性能进行了研究。所制备荧光粉颗粒为六边形类圆饼状,平均尺寸在100~600 nm之间。对CaSb₂O₆:Bi³⁺,Eu³⁺发光的机理分析表明,Bi³⁺对Eu³⁺的发光存在高效的敏化与能量传递。当Bi³⁺和Eu³⁺的掺杂浓度分别为0.5%和8%,Eu³⁺位于580 nm(⁵D₀→⁷F₀ )处的荧光发射显著增强,Bi³⁺,Eu³⁺共掺样品的荧光强度是CaSb₂O₆:Eu³⁺的10倍左右。调节Bi³⁺/Eu³⁺离子掺杂比,色坐标呈现了从蓝、白光到红光的变化,表明该荧光粉可分别作为蓝或红色荧光粉使用,甚至可实现从蓝、白光到红光的自由调控,这为白光LED荧光粉的发展提供了参考。     

Theoretical study of the mechanism for C-H bond activation in spin-forbidden reaction between Ti<Superscript>+</Superscript> and C<Subscript>2</Subscript>H<Subscript>4</Subscript>

The mechanism of the spin-forbidden reaction Ti⁺(⁴F, 3d²4s¹) + C₂H₄→TiC₂H₂ ⁺ (²A₂) + H₂ on both doublet and quartet potential energy surfaces has been investigated at the B3LYP level of theory. Crossing points between the potential energy surfaces and the possible spin inversion process are discussed by means of spin-orbit coupling (SOC) calculations. The strength of the SOC between the low-lying quartet state and the doublet state is 59.3 cm⁻¹ in the intermediate complex IM1-⁴B₂. Thus, the changes of its spin multiplicity may occur from the quartet to the doublet surface to form IM1-²A₁, leading to a sig-nificant decrease in the barrier height on the quartet PES. After the insertion intermediate IM2, two distinct reaction paths on the doublet PES have been found, i.e., a stepwise path and a concerted path. The latter is found to be the lowest energy path on the doublet PES to exothermic TiC₂H₂ ⁺(²A₂) + H₂ products, with the active barrier of 4.52 kcal/mol. In other words, this reaction proceeds in the following way: Ti⁺+C₂H₄→⁴IC→IM1-⁴B₂→^4,2ISC→IM1-²A₁→[²TS_ins]→IM2→[²TS_MCTS]→IM5→TiC₂H₂ ⁺(²A₂)+H₂. Supported by ‘Qinglan’ Talent Engineering Funds by Tianshui Normal University.     

La_7O_6(BO_3)(PO_4)_2∶Eu~(3+)/Tb~(3+)荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu~(3+)和Tb~(3+)掺杂的La_7O_6(BO_3)(PO_4)_2系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La_7O_6(BO_3)(PO_4)_2∶Eu~(3+)材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为5D0→7F2特征能级跃迁,Eu~(3+)的最优掺杂浓度为0.08,对应的CIE坐标为(0.610 2,0.382 3);La_7O_6(BO_3)(PO_4)_2∶Tb~(3+)材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb~(3+)的5D4→7F5能级跃迁,Tb~(3+)离子的最优掺杂浓度为0.15,对应的CIE坐标为(0.317 7,0.535 2)。此外,对2种材料的变温光谱分析发现Eu~(3+)和Tb~(3+)掺杂的La_7O_6(BO_3)(PO_4)_2荧光材料均具有良好的热稳定性。     

Ca9Y(PO4)7:Ce3+,Tb3+纳米荧光粉的制备及发光性能

采用水热法制备出Ca_9Y(PO4)7∶Ce~(3+),Tb~(3+)纳米荧光粉,通过XRD、SEM和荧光光谱等对样品进行了分析,研究在Ca_9Y(PO4)7基质中引入Ce~(3+),Tb~(3+)离子对发光性能的影响规律。研究发现因Tb~(3+)离子自身能量交叉驰豫的存在,使得单掺Tb~(3+)时,通过调节Tb~(3+)离子的浓度可以实现对发光颜色的控制。同时研究了Ce~(3+)-Tb~(3+)之间的能量传递为电多极相互作用的偶极-四极机制,Ce~(3+)-Tb~(3+)之间最大的能量传递效率为55.6%。Ca_9Y(PO4)7∶Ce~(3+),Tb~(3+)的发光颜色可以通过激活离子之间的能量传递和共发射得到可控调节。SEM分析表明荧光粉颗粒尺寸在100 nm左右,分散性好。     

Ho3+/Yb3+共掺ZnO-Al2O3-GeO2-SiO2玻璃陶瓷的制备和上转换发光性质

综合ZnO-Al_2O_3-SiO_2系和锗酸盐玻璃陶瓷的优点,采用熔融-晶化法首次制备了Ho~(3+)/Yb~(3+)共掺以ZnAl_2O_4为主晶相的ZnO-Al_2O_3-GeO_2-SiO_2系玻璃陶瓷。因[GeO_4]四面体和[SiO_4]四面体都是玻璃网络形成体,讨论了GeO_2取代SiO_2对玻璃陶瓷样品硬度及发光性能的影响,最终确定GeO_2的取代量为10.55%(w/w)时,玻璃陶瓷综合性能最佳。在980 nm泵浦光的激发下,发现强的绿色(546 nm)和弱的红色(650 nm)上转换发光,并研究了不同Ho~(3+)/Yb~(3+)掺杂比对样品上转换发光的影响,最终结果表明当Ho~(3+)/Yb~(3+)掺杂比为1∶11(n/n)时样品荧光强度最强,在绿色上转换发光材料方面具有潜在的应用。     

Cr3+在不同基质Y3Ga5O12或Ga2O3中的荧光特性

以Ga_2O_3、Y_2O_3、Cr(NO_3)_3·9H_2O为原料,柠檬酸为配位剂,通过溶胶-凝胶高温固相合成法制备出Ga_(2-2x)O_3∶2xCr~(3+)(Ga_2O_3∶xCr)与Y_3Ga_(5-5x)O_(12)∶5xCr~(3+)(YGG∶xCr)2种多晶粉体(x=0.01,0.03,0.05,0.07)。并采用X射线衍射(XRD)、红外光谱(IR)、扫描电镜(SEM)、荧光光谱(PL)对样品的结构、组成、形貌和荧光性能进行测试分析。XRD和IR分析结果显示在900℃煅烧后Ga_2O_3∶xCr和YGG∶xCr两种样品均成相。SEM照片显示Ga_2O_3∶xCr样品形貌为柱形多面体,YGG∶xCr为短棒状。PL结果显示Cr~(3+)在Ga_2O_3和YGG两种基质中的最强荧光发射峰分别位于742和740 nm,均属于Cr~(3+)的~2E-~4A_2跃迁,对比发现Cr~(3+)在YGG基质中的荧光发射强度更强,在远红光区的荧光性能更好,能满足温室照明中植物光合作用的需求。     

五元瓜环与钕离子在四氯酸锌离子诱导下构筑的配合超分子自组装

在四氯酸锌离子诱导下,五元瓜环能与钕离子构筑形成二维配合超分子自组装。在HCl介质中,Zn²⁺容易形成四氯酸锌离子,在其诱导作用下,钕离子和五元瓜环端口羰基氧直接配位形成二维超分子自组装体。结果表明锌离子作为一种结构导向剂在形成瓜环基超分子自组装体中起到重要作用。     

CaWO_4∶xEu~(3+),ySm~(3+),zLi~+红色荧光粉的制备及光学性能

采用微波固相法制备了CaWO_4∶xEu~(3+),ySm~(3+),zLi~+红色荧光粉。测量样品的XRD图、激发谱、发射谱及发光衰减曲线,研究并分析了Eu~(3+)、Sm~(3+)、Li~+的掺杂浓度,对样品微结构、光致发光特性、能量传递及能级寿命的影响。结果表明,Eu~(3+)、Sm~(3+)、Li~+掺杂并未引起合成粉体改变晶相,仍为CaWO_4单一四方晶系结构。Eu~(3+)、Sm~(3+)共掺样品中,Sm~(3+)掺杂为3%时,Sm~(3+)对Eu~(3+)的能量传递最有效。Li~+掺杂起到了助熔剂和敏化剂的作用,使样品发光更强。在394 nm激发下,与CaWO_4∶3%Eu~(3+)样品比较,3%Eu~(3+)、3%Sm~(3+)共掺CaWO_4及3%Eu~(3+)、3%Sm~(3+)、1%Li~+共掺CaWO_4样品的发光分别增强2倍及2.4倍。同一激发波长下,单掺Eu~(3+)样品寿命最短,Sm~(3+)、Eu~(3+)共掺样品随Sm~(3+)浓度增加,寿命先减小后增加,且掺杂了Li~+的样品比不掺Li~+的样品~5D_0能级寿命有所增加。     

CMPO/[Cnmim][NTf2]体系对Eu3+和UO22+的萃取行为

讨论了辛基(苯基)-N,N-二异丁基胺甲酰基甲基氧化膦(CMPO)/1-烷基-3-甲基咪唑双(三氟甲烷磺酰)亚胺盐([C_nmim][NTf_2],n=2,8,12)萃取体系分别对硝酸溶液中的铕离子(Eu~(3+))和铀酰根离子(UO_2~(2+))的萃取行为。主要研究了硝酸浓度、接触时间、温度、CMPO浓度对CMPO/[C_nmim][NTf_2]体系萃取性能的影响,并选取CMPO/[C_2mim][NTf_2]体系对模拟高放废液中的镧锕元素进行了萃取分离。结果表明:随着离子液体侧链长度增长,萃取平衡时间逐渐延长;CMPO/[C3+2mim][NTf_2]体系对Eu的萃取是放热反应,萃取率随酸度增加而逐渐降低,对UO_2~(2+)则是吸热反应,萃取率随酸度增加而逐渐升高;通过机理研究,推测出对Eu~(3+)的萃取反应是离子交换,而对UO_2~(2+)的萃取反应则是中性配位;CMPO/[C_2mim][NTf_2]体系能有效的萃取模拟高放废液中的镧系、锕系元素,且在高酸下有一定的镧锕分离效果。     

空气中合成固溶体荧光粉Ba_2(Zn,Mg)Si_2O_7∶Eu~(2+),Eu~(3+),Ce~(3+)及其发光特性

采用高温固相法在空气中合成了Ba1.97-yZn1-xMgxSi2O7∶0.03Eu,y Ce3+系列荧光粉。分别采用X-射线衍射和荧光光谱对所合成荧光粉的物相和发光性质进行了表征。在紫外光330~360 nm激发下,固溶体荧光粉Ba1.97-yZn1-xMgxSi2O7∶0.03Eu的发射光谱在350~725 nm范围内呈现多谱峰发射,360和500 nm处有强的宽带发射属于Eu2+离子的4f 65d1-4f 7跃迁,590~725 nm红光区窄带谱源于Eu3+的5D0-7FJ(J=1,2,3,4)跃迁,这表明,在空气气氛中,部分Eu3+在Ba1.97-yZn1-xMgxSi2O7基质中被还原成了Eu2+;当x=0.1时,荧光粉Ba1.97Zn0.9Mg0.1Si2O7∶0.03Eu的绿色发光最强,表明Eu3+被还原成Eu2+离子的程度最大。当共掺入Ce3+离子后,形成Ba1.97-yZn0.9Mg0.1Si2O7∶0.03Eu,y Ce3+荧光粉体系,其发光随着Ce3+离子浓度的增大由蓝绿区经白光区到达橙红区;发现名义组成为Ba1.96Zn0.9Mg0.1Si2O7∶0.03Eu,0.01Ce3+的荧光粉的色坐标为(0.323,0.311),接近理想白光,是一种有潜在应用价值的白光荧光粉。讨论了稀土离子在Ba2Zn0.9Mg0.1Si2O7基质中的能量传递与发光机理。