分子筛表面酸性对微波固相法制备ZnCl2/Y催化剂的影响

 采用XRD和原子吸收光谱法研究了微波作用下分子筛表面酸性对ZnCl2与Y分子筛固态相互作用的影响．结果表明，微波辐射可显著促进ZnCl2在分子筛表面分散，其分散阈值与分子筛表面酸性有关．随着分子筛表面酸量和酸强度增加，ZnCl2在分子筛表面的最大分散量减少，分散的ZnCl2与Y分子筛的固态离子交换量也减少；NaY型分子筛比HY分子筛更容易发生固态离子交换反应．考察了微波固相法制备的ZnCl2／HY催化剂在苯甲醚与乙酰氯酰化反应中的催化性能．结果表明，在分子筛表面分散的ZnCl2具有更高的催化活性及对甲氧基苯乙酮选择性．     

微波固相法制备ZnCl2/MCM-41催化剂及其催化性能

采用微波固相法、普通加热法和溶剂分散法等不同方法制备了ZnCl2/MCM-41催化剂,以XRD、FT-IR和TG-DSC等表征手段,比较了不同方法制备的催化剂中ZnCl2在分子筛表面的存在状态.XRD测定结果表明,微波固相法和溶剂分散法制备的样品可使ZnCl2完全分散于MCM-41分子筛表面,而加热法制备的样品中仍存在ZnCl2的晶相衍射峰.FT-IR、DSC和原子吸收光谱的测定结果表明,微波辐射可使ZnCl2与分子筛表面羟基发生固态相互作用形成O－Zn－Cl活性位,具有更加温和的Lewis酸性.考察了不同方法制备和不同ZnCl2负载量的催化剂在月桂烯与丙烯醛Diels-Alder反应中的催化性能,与普通加热法制备的催化剂相比,微波固相法与溶剂分散法制备的催化剂具有更好的催化活性和选择性,但微波固相法制备催化剂更为简单.     

微波辐射促进ZnCl_2与Y分子筛固相反应的研究

采用XRD、IR和原子吸收光谱等手段对微波固相法制备的ZnCl2／Y催化剂进行了表征·微波辐射促进了ZnCl2在分子筛表面分散和固态离子交换，分散的ZnCl2可与分子筛表面氧原子发生较强的配住键合作用．当ZnCl2的负载量达到37．5％时，ZnCl2仍可完全分散于NaY分子筛表面，此时的固态离子交换度为84％．随着分子筛表面酸菌和区强度的增加，ZnCl2与分子筛的固态离子交换量减少．     

微波固相法制备ZnCl2／NaY催化剂

比较了微波固相法，普通加热法和简单混合法制备的ＺｎＣｌ２／ＮａＹ及溶液离子交换法制备的ＺｎＮａＹ在月桂烯与丙烯醛Ｄｉｅｌｓ－Ａｌｄｅｒ反应中的催化性能，发现微波固相法制备的催化剂表现出最高的环加成选择性和区域选择性。     

微波固相法制备ZnCl2/Y在α-蒎烯环氧化物重排反应中的催化性能

 考察了微波固相法制备的ZnCl2／Y分子筛催化剂在α－蒎烯环氧化物重排反应中的催化性能．催化剂活性及产物选择性与分子筛表面的酸性有关．在微波作用下,ZnCl2可分散于分子筛表面且可与分子筛中的阳离子发生固态离子交换反应．分散的ZnCl2（中强L酸）有利于生成龙脑烯醛,固态离子交换生成的ZnY（弱L酸）有利于α－蒎烯环氧化物重排生成松蒎酮;不同Na＋交换度的HY分子筛表面具有不同的B酸中心,B酸的存在可使重排反应产物松香芹醇和香芹醇发生分子内脱水二次反应生成单萜烯．用微波固相法制备催化剂时,随着ZnCl2负载量的增加,产物香芹醇的选择性升高,分散于分子筛孔道内的ZnCl2有利于生成香芹醇．比较了不同溶剂对α－蒎烯环氧化物重排反应产物分布的影响,以环己烷作溶剂时,松蒎酮选择性可达24％．通过对分子筛表面酸性的调变可实现选择合成．     

微波固相法制备的ZnCl_2/Y在α-蒎烯环氧化物重排反应中的催化性能

考察了微波固相法制备的ZnCl2 /Y分子筛催化剂在α 蒎烯环氧化物重排反应中的催化性能 .催化剂活性及产物选择性与分子筛表面的酸性有关 .在微波作用下 ,ZnCl2 可分散于分子筛表面且可与分子筛中的阳离子发生固态离子交换反应 .分散的ZnCl2 (中强L酸 )有利于生成龙脑烯醛 ,固态离子交换生成的ZnY(弱L酸 )有利于α 蒎烯环氧化物重排生成松蒎酮 ;不同Na+ 交换度的HY分子筛表面具有不同的B酸中心 ,B酸的存在可使重排反应产物松香芹醇和香芹醇发生分子内脱水二次反应生成单萜烯 .用微波固相法制备催化剂时 ,随着ZnCl2 负载量的增加 ,产物香芹醇的选择性升高 ,分散于分子筛孔道内的ZnCl2 有利于生成香芹醇 .比较了不同溶剂对α 蒎烯环氧化物重排反应产物分布的影响 ,以环己烷作溶剂时 ,松蒎酮选择性可达 2 4% .通过对分子筛表面酸性的调变可实现选择合成 .     

ZnCl2改性离子交换树脂的制备及其催化乙醇和乙酸酯化反应性能

 采用离子交换法制备了 ZnCl2 改性的阳离子交换树脂催化剂, 考察了 ZnCl2 浓度、离子交换时间和溶剂等对催化剂催化乙酸和乙醇微波酯化反应性能的影响. 结果表明, 以去离子水为溶剂, 以 0.15%ZnCl2 溶液进行离子交换 30 h, 所得催化剂的性能较好. 采用酸碱滴定法、紫外-可见光谱、傅里叶变换红外光谱、扫描电镜和 N2 吸附脱附等手段对催化剂进行了表征. 结果表明, 改性后的催化剂 H+交换量约为原来的 1.5 倍, 表面酸强度增加; 树脂骨架结构变化不大; 紫外吸收峰发生蓝移, 吸收强度减小; 比表面积略有减小; 催化剂在含水体系中表现出较高的催化活性, 且重复使用性能大大提高.     

CuCl_2和HY分子筛的表面反应及Cu/Y分子筛的制备及其催化甲醇氧化羰基化（英文）

以CuCl2为前驱物与HY分子筛进行固相离子交换制备了Cu/Y催化剂,采用热重方法研究了CuCl2与HY分子筛的表面固相离子交换反应,结合活性测试表明催化剂中高度分散的CuCl和离子交换形式的Cu+物种是甲醇氧化羰基化合成碳酸二甲酯的催化活性中心.X射线光电子能谱表征和元素分析结果表明,活性金属Cu主要以CuCl形式存在于分子筛外表面,而在分子筛笼内则以交换的Cu+和少量吸附的CuCl形式存在.与以CuCl为交换铜源所制催化剂相比,以CuCl2为铜源制备的催化剂Cu含量低,催化活性更高.     

ZnCl2/NaY催化邻苯二酚与甲醇醚化反应

ZnCl2/NaY催化邻苯二酚与甲醇醚化反应;固体酸催化剂;愈创木酚     

不同方法制备的Cu/HZSM-5催化剂上NO的催化分解反应

采用离子交换法、固相分散法和微波固相法等不同方法制备了Cu/HZSM-5催化剂,以BET、XRD和XPS等手段对催化剂样品进行了表征。结果表明,不同方法制备的Cu/HZSM-5催化剂上Cu物种的落位分布状态不同,离子交换法制备的催化剂Cu物种更多地落位于分子筛孔道内,微波固相法和固相分散法制备的催化剂Cu物种较多地落位分布在分子筛外表面。固相分散法制备的样品未能使铜物种完全分散于分子筛表面,在13.1°、16.8°、35.5°和38.0°等处仍存在CuO的晶相衍射峰。催化分解NO反应的活性考察结果表明,用微波固相法制备的催化剂催化分解NO的活性及稳定性明显超过另两种方法所制备的催化剂,在无氧条件下NO最初转化率高达89.2%,经反应25h后,转化率仍维持在70%以上;在富氧气氛下催化分解NO活性降低速率低于由离子交换法制备的催化剂。结合表征结果可以得出,落位于分子筛外表面以离子交换态形式存在的Cu物种对催化分解NO反应更为有利,而且催化稳定性更好。     

微波辐射促进ZnCl2与Y分子筛固相反应的研究

ZnCl2/Y catalysts prepared by solid-state reaction of anhydrous ZnCl2 and Y zeolites under microwave irradiation were characterized by XRD, IR and AAS. ZnCl2 was intercalated in Y zeolites and dispersed on the surface of Y zeolite, part of ZnCl2 dispersed could result in solid-state ion exchange with Y. The amount of dispersion and solid-state ion exchange were related to ZnCl2 loading and the surface acid property of the zeolite. When ZnCl2 loading was 37.5% (mass fraction) in NaY zeolite, ZnCl2 was still completely dispersed on the surf are of zeolite and the degree of solid- state ion exchang was 84%. The appearance of new band at 890 cm-l in the framework IR spectra of ZnCl2/NaY sample was due to the dispersed ZnCl2 coordinating strongly with oxygen of NaY surface. With the increasing of the number of arid centers and the acid strength of the surface of Y zeolite the amount of solid-state ion exchange decreased.     

Dehydrogenation activities of highly dispersed transition metal oxides on NaY zeolite

Highly dispersed α-Fe_2O_3/NaY,NiO/NaY,and CuO/NaY catalyst systems were pre-pared by impregnation method.Dispersion thresholds of the transition metal oxides on NaY" zeolitewere determined by XRD phase analysis.The dispersion capacities of the transition metal oxides on NaYzeolite are much lower than that estimated on the basis of a closed packed monolayer in the micropores.The catalytic activity and selectivity of the highly dispersed oxide catalyst systems for ethylben-zene and cyclohexane dehydrogenation reactions were reported.     

MgO在NaY沸石上的分散及其催化性能

采用微波辐射方法将ＭｇＯ直接分解在ＮａＹ沸石上,从而获得强碱性活性位。ＭｇＯ／ＮａＹ具有耐水冲刷性,克服了通常负载型固体碱在水中易流失的弱点,并在２７３Ｋ的顺式－２－丁烯异构化反应中具有催化活性。     

十二烷基硫酸钠对原位晶化制备小晶粒NaY的影响

研究了十二烷基硫酸钠对原位晶化制备小晶粒NaY的影响,并以包含小晶粒NaY的原位晶化产物为母体,通过铵交换和稀土离子交换制备出了REUSY催化剂.采用X射线衍射(XRD)、扫描电镜(SEM)、X射线荧光(XRF)及N₂物理吸附-脱附等手段对样品进行了表征,采用微反活性评价装置和小型固定流化床(ACE)评价了所制备催化剂在重油催化裂化反应中的催化性能.结果表明:在原位晶化合成NaY的体系中,添加高岭土微球质量5%的十二烷基硫酸钠,可以将分子筛的平均晶粒尺寸由540 nm减小到250 nm.相比于常规的原位晶化型流化催化裂化(FCC)催化剂,以包含小晶粒NaY的原位晶化产物为母体所制备出的催化剂,在反应原料的转化率、裂化产物的选择性以及抗积碳性能等方面均有明显的提高或改善.     

Glucose Isomerization into Fructose Catalyzed by MgO/NaY Catalyst

The MgO/NaY catalysts prepared by impregnation method were used for the conversion of glucose to fructose in water medium.The effects of MgO loading, reaction temperature, glucose concentration and reaction time on the catalytic performance for the reaction were studied.The activity testing results indicated that fructose could be generated effectively by controlling the components of the catalyst and reaction conditions.The maximal fructose yield of 33.8% with the selectivity of 67.3% was achieved over the 10% MgO/NaY catalyst at 100 ℃ for 2 h.Moreover, the catalysts were characterized by XRD, BET, and CO₂-TPD techniques.The structural property of NaY with higher surface area facilitated glucose conversion, and the modulated basicity of the catalyst with MgO addition contributed to the formation of fructose in the tautomerization of aldose to ketose.     

CuCl2/NaY体系表面分散态研究

铜负载分子筛作为催化剂或吸附剂，在石油化工、环境保护等方面有许多用途[1，2]．已有研究发现，铜交换的Y型分子筛对NO分解等反应具有较高活性及稳定性［3-5］．因此研究铜负载Y型分子筛对有关吸附剂和催化剂的制备有重要意义．我们实验室在研究活性组分在载体表面分散现象时