Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

Thermoelectric properties of polycrystalline La1−xSrxCoO3

Thermoelectric properties of polycrystalline La_1−xSr_xCoO₃, where Sr²⁺ is substituted in La³⁺ site in perovskite-type LaCoO₃, have been investigated. Sr-doping increases the electrical conductivity (σ) of La_1−xSr_xCoO₃, and also decreases the Seebeck coefficient (S) for 0.01?x?0.40. A Hall coefficient measurement reveals that the increase in electrical conductivity arises from increases in both carrier concentration and the Hall mobility. The decrease in the Seebeck coefficient is caused by a decrease in carrier effective mass as well as increase in carrier concentration. The highest power factor (σS²) is 3.7×10⁻⁴ W m⁻¹ K⁻² at 250 K for x=0.10. The thermal conductivity (κ) is about 2 W m⁻¹ K⁻¹ at 300 K for 0?x?0.04, and increases for x?0.05 because of an increase in heat transport by conductive carrier. The thermoelectric properties of La_1−xSr_xCoO₃ are improved by Sr-doping, and the figure of merit (Z=σS² κ⁻¹) reaches 1.6×10⁻⁴ K⁻¹ for x=0.06 at 300 K (ZT=0.048). For heavily Sr-doped samples, the thermoelectric properties diminish mainly because of the decrease in the Seebeck coefficient and the increase in thermal conductivity.     

Thermoelectric properties of Ag-doped n-type (Bi2Te3)0.9-(Bi2−xAgxSe3)0.1 (x=0-0.4) alloys prepared by spark plasma sintering

Ag-doped n-type (Bi₂Te₃)_0.9-(Bi_2−xAg_xSe₃)_0.1 (x=0-0.4) alloys were prepared by spark plasma sintering and their physical properties evaluated. When at low Ag content (x=0.05), the temperature dependence of the lattice thermal conductivity follows the trend of (Bi₂Te₃)_0.9-(Bi₂Se₃)_0.1; while at higher Ag content, a relatively rapid reduction above 400 K can be observed due possibly to the enhancement of scattering of phonons by the increased defects. The Seebeck coefficient increases with Ag content, with some loss of electrical conductivity, but the maximum dimensionless figure of merit ZT can be obtained to be 0.86 for the alloy with x=0.4 at 505 K, about 0.2 higher than that of the alloy (Bi₂Te₃)_0.9-(Bi₂Se₃)_0.1 without Ag-doping.     

Interactions of Ba2YCu3O6+y with the Gd3NbO7 buffer layer in coated conductors

A systematic study of the chemical interaction of Ba₂YCu₃O_6+y and Gd₃NbO₇ was conducted under two processing conditions: purified air (21% p_o2), and 100 Pa p_o2 (0.1% p_o2). Phases present along the pseudo-binary join Ba₂YCu₃O_6z and Gd₃NbO₇ were found to be in two five-phase volumes within the system. Three common phases that are present in all samples are (Y,Gd)₂Cu₂O₅, Ba(Y,Gd)₂CuO₅ and Cu₂O or CuO (depending on the processing conditions). The assemblies of phases can be categorized in three regions, with Ba₂YCu₃O_6+y: Gd₃NbO₇ ratios of (I)<5.5:4.5; (II)=5.5:4.5; and (III)>5.5:4.5. The lowest melting temperature of the system was determined to be ≈938 °C in air, and 850 °C at 100 Pa p_o2. Structure determinations of two selected phases, Ba₂(Gd_xY_1−x)NbO₆ (Fm3¯m, No. 225), and (Gd_xY_3−x)NbO₇ (C222₁, No. 20 and Ccmm, No. 63), were completed using the X-ray Rietveld refinement technique. Reference X-ray powder diffraction patterns for selected phases of Ba₂(Gd_xY_1−x)NbO₆ (x=0.2, 0.4, 0.6, and 0.8) and (Gd_xY_3−x)NbO₇ (x=0.6, 1.2, 1.8, 2.4 and 3) have been prepared for inclusion in the Powder Diffraction File (PDF).     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Enzyme mimics of spinel-type CoxNi1−xFe2O4 magnetic nanomaterial for eletroctrocatalytic oxidation of hydrogen peroxide

A series of spinel-type Co_xNi_1−xFe₂O₄ (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) magnetic nanomaterials were solvothermally synthesized as enzyme mimics for the eletroctrocatalytic oxidation of H₂O₂. X-ray diffraction and scanning electron microscope were employed to characterize the composition, structure and morphology of the material. The electrochemical properties of spinel-type Co_xNi_1−xFe₂O₄ with different (Co/Ni) molar ratio toward H₂O₂ oxidation were investigated, and the results demonstrated that Co_0.5Ni_0.5Fe₂O₄ modified carbon paste electrode (Co_0.5Ni_0.5Fe₂O₄/CPE) possessed the best electrocatalytic activity for H₂O₂ oxidation. Under optimum conditions, the calibration curve for H₂O₂ determination on Co_0.5Ni_0.5Fe₂O₄/CPE was linear in a wide range of 1.0 × 10⁻⁸–1.0 × 10⁻³ M with low detection limit of 3.0 × 10⁻⁹ M (S/N = 3). The proposed Co_0.5Ni_0.5Fe₂O₄/CPE was also applied to the determination of H₂O₂ in commercial toothpastes with satisfactory results, indicating that Co_xNi_1−xFe₂O₄ is a promising hydrogen peroxidase mimics for the detection of H₂O₂.     

Effects of Mg doping on the properties of highly transparent conductive and near infrared reflective Zn1−xMgxO:Ga films

Highly transparent conductive and near infrared (IR) reflective Gallium-doped ZnMgO (Zn_1−xMg_xO:Ga) films with Mg content from 0 to 10 at% were deposited on glass substrate by DC reactive magnetron sputtering. X-ray diffraction shows all the ZnMgO:Ga films are polycrystalline and have wurtzite structure with a preferential c-axis orientation. Hall measurements indicate that the resistivity of these films obviously increases with the Mg concentration increasing. The average transmittance of Zn_1−xMg_xO:Ga films is over 90% in the visible range. All the Zn_1−xMg_xO:Ga films have low transmittance and high reflectance in the IR region.     

Sol-gel synthesized semiconducting LaCo0.8Fe0.2O3-based powder for thick film NH3 gas sensor

Perovskite type LaCo_xFe_1−xO₃ nanoparticles was synthesized by a sol-gel citrate method. The structural, electrical and sensing characteristics of the LaCo_xFe_1−xO₃ system were investigated. The structural characteristics were performed by using X-ray diffraction (XRD) and transmission electron microscopy (TEM) to examine the phase and morphology of the resultant powder. The XRD pattern shows nanocrystalline solid solution of LaCo_xFe_1−xO₃ with perovskite phase. Electrical properties of synthesized nanoparticles are studied by DC conductivity measurement. The sensor shows high response towards ammonia gas in spite of other reducing gases when x = 0.8. The effect of 0.3 wt.% Pd-doped LaCo_0.8Fe_0.2O₃ on the response and a recovery time was also addressed.     

Thermoelectric properties of p-type pseudo-binary (Ag0.365Sb0.558Te)x-(Bi0.5Sb1.5Te3)1−x (x=0-1.0) alloys prepared by spark plasma sintering

In this paper, pseudo-binary (Ag_0.365Sb_0.558Te)_x-(Bi_0.5Sb_1.5Te₃)_1−x (x=0-1.0) alloys were prepared using spark plasma sintering technique, and the composition-dependent thermoelectric properties were evaluated. Electrical conductivities range from 7.9×10⁴ to 15.6×10⁴ Ω⁻¹ m⁻¹ at temperatures of 507 and 318 K, respectively, being about 3.0 and 8.5 times those of Bi_0.5Sb_1.5Te₃ alloy at the corresponding temperatures. The optimal dimensionless figure of merit (ZT) of the sample with molar fraction x=0.025 reaches 1.1 at 478 K, whereas that of the ternary Bi_0.5Sb_1.5Te₃ alloy is 0.58 near room temperature. The results also reveal that a direct introduction of Ag_0.365Sb_0.558Te in the Bi-Sb-Te system is much more effective to the property improvement than naturally precipitated Ag_0.365Sb_0.558Te in the Ag-doped Ag-Bi-Sb-Te system.     

Thermochemistry of Li1+xMn2−xO4 (0?x?1/3) spinel

Lithium substituted Li_1+xMn_2−xO₄ spinel samples in the entire solid solution range (0?x?1/3) were synthesized by solid-state reaction. The samples with x<0.25 are stoichiometric and those with x?0.25 are oxygen deficient. High-temperature oxide melt solution calorimetry in molten 3Na₂O·4MoO₃ at 974 K was performed to determine their enthalpies of formation from constituent binary oxides at 298 K. The cubic lattice parameter was determined from least-squares fitting of powder XRD data. The variations of the enthalpy of formation from oxides and the lattice parameter with x follow similar trends. The enthalpy of formation from oxides becomes more exothermic with x for stoichiometric compounds (x<0.25) and deviates endothermically from this trend for oxygen-deficient samples (x?0.25). This energetic trend is related to two competing substitution mechanisms of lithium for manganese (oxidation of Mn³⁺ to Mn⁴⁺ versus formation of oxygen vacancies). For stoichiometric spinels, the oxidation of Mn³⁺ to Mn⁴⁺ is dominant, whereas for oxygen-deficient compounds both mechanisms are operative. The endothermic deviation is ascribed to the large endothermic enthalpy of reduction.     

Formation of crystalline TiO2−xNx and its photocatalytic activity

Amorphous precursors to nitrogen-doped TiO₂ (NTP) and pure TiO₂ (ATP) powders were synthesized by hydrolytic synthesis and sol-gel method (SGM), respectively. Corresponding crystalline phases were obtained by thermally induced transformation of these amorphous powders. From FT-IR and XPS data, it was concluded that a complex containing titanium and ammonia was formed in the precipitate stage while calcination drove weakly adsorbed ammonium species off the surface, decomposed ammonia bound on surface of precipitated powder and led to substitution of nitrogen atom into the lattice of TiO₂ during the crystallization. The activation energies required for grain growth in amorphous TiO_2−xN_x and TiO₂ samples were determined to be 1.6 and 1.7 kJ/mol, respectively. Those required for the phase transformation from amorphous to crystalline TiO_2−xN_x and TiO₂ were determined to be 129 and 142 kJ/mol, respectively. A relatively low temperature was required for the phase transformation in NTP sample than in ATP sample. The fabricated N-doped TiO₂ photocatalyst absorbed the visible light showing two absorption edges; one in UV range due to titanium oxide as the main edge and the other due to nitrogen doping as a small shoulder. TiO_2−xN_x photocatalyst demonstrated its photoactivity for photocurrent generation and decomposition of 2-propanol (IPA) under visible light irradiation ().     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Evolution of structure and magnetic properties in electron-doped double perovskites, Sr2−xLaxMnWO6 (0?x?1)

Powder neutron and X-ray diffraction studies show that the double perovskites in the region 0?x?1 exhibit two crystallographic modifications at room temperature: monoclinic P2₁/n and tetragonal I4/m, with a boundary at 0.75<x<0.9. Magnetic susceptibility measurements indicate that for x=0 and 0.5 Sr_2−xLa_xMnWO₆ orders antiferromagnetically (AFM) at 15 and 25 K, respectively, for 0.75?x<1.0, a contribution of weak ferromagnetism (FM), probably due to canted-AFM order, increases with increasing x. The end point compound SrLaMnWO₆ shows the strongest FM cluster effect; however, no clear evidence of magnetic order is discernable down to 4.2 K. X-ray absorption spectroscopy (XAS) confirms Mn²⁺ and mixed-valent W^6+/5+ formal oxidation states in Sr_2−xLa_xMnWO₆.     

A novel route to synthesize cubic ZrW2−xMoxO8 (x=0-1.3) solid solutions and their negative thermal expansion properties

Cubic ZrW_2−xMo_xO₈ (c-ZrW_2−xMo_xO₈) (x=0-1.3) solid solutions were prepared by a novel polymorphous precursor transition route. X-ray diffraction (XRD) analysis reveals that the solid solutions are single phase with α- and β-ZrW₂O₈ structure for 0?x?0.8 and 0.9?x?1.3, respectively. The optimum synthesis conditions of ZrWMoO₈ are obtained from differential scanning calorimetry-thermal gravimetric analysis (DSC-TGA), XRD and mass loss-temperature/time curves. Following the above experience, the stoichiometric solid solutions of c-ZrW_2−xMo_xO₈ (x=0-1) are obtained within 1 wt% of mass loss. The relationships of lattice parameters (a), phase transition temperatures (T_c) and instantaneous coefficients of thermal expansion (α_i) against the content x of Mo are discussed based on the variation of order degree parameters of ZrW_2−xMo_xO₈.     

Synthesis of layered cathode material Li[CoxMn1−x]O2 from layered double hydroxides precursors

Cathode materials Li[Co_xMn_1−x]O₂ for lithium secondary batteries have been prepared by a new route—precursor method of layered double hydroxides (LDHs). In situ high-temperature X-ray diffraction (HT-XRD) and thermogravimetric analysis coupled with mass spectrometry (TG-MS) were used to monitor the structural transformation during the reaction of CoMn LDHs and LiOH·H₂O: firstly the layered structure of LDHs transformed to an intermediate phase with spinel structure; then the distortion of the structure occurred with the intercalation of Li⁺ into the lattice, resulting in the formation of layered Li[Co_xMn_1−x]O₂ with α-NaFeO₂ structure. Extended X-ray absorption fine structure (EXAFS) data showed that the Co-O bonding length and the coordination number of Co were close to those of Mn in Li[Co_xMn_1−x]O₂, which indicates that the local environments of the transitional metals are rather similar. X-ray photoelectron spectroscopy (XPS) was used to measure the oxidation state of Co and Mn. The influences of Co/Mn ratio on both the structure and electrochemical property of Li[Co_xMn_1−x]O₂ have been investigated by XRD and electrochemical tests. It has been found that the products synthesized by the precursor method demonstrated a rather stable cycling behavior, with a reversible capacity of 122.5 mAh g⁻¹ for the layered material Li[Co_0.80Mn_0.20]O₂.     

Crystal structure, thermal expansion and conductivity of anisotropic La1−xSrxGa1−2xMg2xO3−y (x=0.05, 0.1) single crystals

Crystal structure and anisotropy of the thermal expansion of single crystals of La_1−xSr_xGa_1−2xMg_2xO_3−y (x=0.05 and 0.1) were measured in the temperature range 300-1270 K. High-resolution X-ray powder diffraction data obtained by synchrotron experiments have been used to determine the crystal structure and thermal expansion. The room temperature structure of the crystal with x=0.05 was found to be orthorhombic (Imma, Z=4, a=7.79423(3) Å, b=5.49896(2) Å, c=5.53806(2) Å), whereas the symmetry of the x=0.1 crystal is monoclinic (I2/a, Z=4, a=7.82129(5) Å, b=5.54361(3) Å, c=5.51654(4) Å, β=90.040(1)°). The conductivity in two orthogonal directions of the crystals has been studied. Both, the conductivity and the structural data indicate three phase transitions in La_0.95Sr_0.05Ga_0.9Mg_0.1O_2.92 at 520-570 K (Imma-I2/a), 770 K (I2/a-R3c) and at 870 K (R3c-R-3c), respectively. Two transitions at 770 K (I2/a-R3c) and in the range 870-970 K (R3c-R-3c) occur in La_0.9Sr_0.1Ga_0.8Mg_0.2O_2.85.     

Transport properties and stability of Ni-containing mixed conductors with perovskite- and K2NiF4-type structure

The total conductivity and Seebeck coefficient of a series of Ni-containing phases, including La₂Ni_1−xM_xO_4+δ (M=Co, Cu; x=0.1-0.2) with K₂NiF₄-type structure and perovskite-like La_0.90Sr_0.10Ga_0.65Mg_0.15Ni_0.20O_3−δ and La_0.50Pr_0.50Ga_0.65Mg_0.15Ni_0.20O_3−δ, were studied in the oxygen partial pressure range from 10⁻¹⁸ Pa to 50 kPa at 973-1223 K. Within the phase stability domain, the conductivity of layered nickelates is predominantly p-type electronic and occurs via small-polaron mechanism, indicated by temperature-activated hole mobility and p(O₂) dependencies of electrical properties. In oxidizing conditions similar behavior is characteristic of Ni-containing perovskites, which exhibit, however, significant ionic contribution to the transport processes. The role of ionic conduction increases with decreasing p(O₂) and becomes dominant in reducing atmospheres. All nickelate-based phases decompose at oxygen pressures considerably lower with respect to Ni/NiO boundary. The partial substitution of nickel in La₂Ni(M)O_4+δ has minor effect on the stability limits, which are similar to that of La_0.90Sr_0.10Ga_0.65Mg_0.15Ni_0.20O_3−δ. On the contrary, praseodymium doping enhances the stability of La_0.50Pr_0.50Ga_0.65Mg_0.15Ni_0.20O_3−δ down to p(O₂) values as low as 10⁻¹⁷-10⁻¹⁰ Pa at 1023-1223 K.     

Crystal structure and magnetic properties of high-oxygen pressure annealed Sr1−xLaxCo0.5Fe0.5O3−δ (0?x?0.5)

Structural and magnetic studies are presented for the perovskite type Sr_1−xLa_xCo_0.5Fe_0.5O_3−δ (0?x?0.5) materials annealed under moderately high-oxygen pressures of ∼200 atm. A detailed analysis of the room temperature neutron time-of-flight diffraction data reveals that the crystal structure of the sample SrCo_0.5Fe_0.5O_2.89(1), previously described as vacancy-disordered cubic, is similar to the formerly reported, oxygen-vacancy ordered Sr₈Fe₈O₂₃ compound, i.e. Sr₈Co₄Fe₄O₂₃ is tetragonal with the I4/mmm symmetry. With an increase of the La content the studied materials become nearly oxygen stoichiometric and a lowering of the crystal symmetry is observed from cubic (x=0.1 and 0.2) to tetragonal I4/mcm (x=0.3 and 0.4), and finally to monoclinic I12/c1 (x=0.5). Low-temperature structural and magnetic measurements show a ferromagnetic ordering with the maximum Curie temperature near 290 K at x=0.2.     

Structure and phase composition of nanocrystalline Ce1−xLuxO2−y

The microstructure and phase stability of nanocrystalline mixed oxide Lu_xCe_1−xO_2−y (x=0-1) are described. Nano-sized (3-4 nm) oxide particles were prepared by the reverse microemulsion method. Morphological and structural changes upon heat treatment in an oxidizing atmosphere were studied by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman and Yb³⁺ emission spectroscopy, the latter ion being present as an impurity in the Lu₂O₃ starting material. Up to 950 °C, the samples were single phase, with structure changing smoothly with Lu content from fluorite type (F) to bixbyite type (C). For the samples heated at 1100 °C phase separation into coexisting F- and C-type structures was observed for 0.35<x<0.7. It was also found that addition of Lu strongly hinders the crystallite growth of ceria during heat treatment at 800 and 950 °C.