Carbon coated Na3V2(PO4)3 as novel electrode material for sodium ion batteries

A Na₃V₂(PO₄)₃ sample coated uniformly with a layer of 6 nm carbon has been successfully synthesized by a one-step solid state reaction. This material shows two flat voltage plateaus at 3.4 V vs. Na⁺/Na and 1.63 V vs. Na⁺/Na in a nonaqueous sodium cell. When the Na₃V₂(PO₄)₃/C sample is tested as a cathode in a voltage range of 2.7-3.8 V vs. Na⁺/Na, its initial charge and discharge capacities are 98.6 and 93 mAh/g. The capacity retention of 99% can be achieved after 10 cycles. The electrode shows good cycle performance and moderate rate performance. When it is tested as an anode in a voltage range of 1.0-3.0 V vs. Na⁺/Na, the initial reversible capacity is 66.3 mAh/g and the capacity of 59 mAh/g can be maintained after 50 cycles. These preliminary results indicate that Na₃V₂(PO₄)₃/C is a new promising material for sodium ion batteries.     

Electrochemical Li insertion studies on WNb12O33—A shear ReO3 type structure

Electrochemical lithium insertion studies on WNb₁₂O₃₃ synthesized by solid state reaction (SSR) are carried out in the voltage range 1.0-3.2 V. During first discharge 15.6 Li are inserted with a specific capacity of 221 mAh/g. WNb₁₂O₃₃ is also synthesized by sol-gel (SG) technique with a view to enhance the rate capability and cycling properties. The SSR and SG samples are characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and galvanostatic cycling. Electrochemical cycling performance of SG samples is superior to that of the SSR sample at high ‘C’ rates. The sample synthesized by SG method exhibits high specific capacity of 142 mAh/g after 20 cycles at 20C rate.     

A combined diffraction and dielectric properties investigation of Ba3MnNb2O9 complex perovskites

A combined synthesis, diffraction and dielectric properties investigation of the dependence (and effect) of Mn²⁺/Nb⁵⁺ ordering in Ba₃MnNb₂O₉ (BMN) upon annealing atmosphere and processing conditions has been carried out. Annealing in different atmospheres was not found to significantly alter either nominal stoichiometry or structure type. The obtained structure type (disordered metrically cubic or ordered trigonal) as well as the measured electrical properties (in particular, the dielectric loss) were, however, found to be sensitive to the synthesis route. Samples obtained via solid-state reaction were found to be predominantly of 1:2 Mn²⁺/Nb⁵⁺ ordered, trigonal structure type whereas samples obtained via an aqueous solution route were found to be of a Mn²⁺/Nb⁵⁺ ‘disordered’, metrically cubic structure type. All solid-state synthesized samples showed reasonable dielectric properties. The microwave dielectric constant and dielectric quality factor, Q, at 8 GHz of an as-synthesized BMN sample were 38 and 100, respectively. By contrast, the dielectric loss of the metrically cubic, Mn²⁺/Nb⁵⁺ ‘disordered’ samples obtained via an aqueous solution synthesis process were significantly worse.     

流变相法合成LiNi0.85Co0.15O2的结构与电化学性能

以一种新型的软化学方法——流变相法, 成功地合成了锂离子电池正极材料LiNi_0.85Co_0.15O₂. 将在600～850 ℃氧气氛下处理6 h后得到的LiNi_1－yCo_yO₂ (y＝0.10, 0.15, 0.20, 0.25), 进行X射线粉末衍射(XRD)与电化学测试. 测试结果表明, 流变相前体经过800 ℃烧结后合成的LiNi_0.85Co_0.15O₂晶胞参数a＝0.2866 nm, c＝1.4193 nm及晶胞体积V＝0.1010 nm³, 以0.1 C倍率在3.0～4.3 V (vs. Li^＋/Li)放电时, 首次放电容量可以达到198.2 mAh/g, 20次循环后, 其放电容量仍在174 mAh/g以上.     

Effect of sintering on the ionic conductivity of garnet-related structure Li5La3Nb2O12 and In- and K-doped Li5La3Nb2O12

Garnet-structure related metal oxides with the nominal chemical composition of Li₅La₃Nb₂O₁₂, In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ and K-substituted Li_5.5La_2.75K_0.25Nb₂O₁₂ were prepared by solid-state reactions at 900, 950, and 1000 °C using appropriate amounts of corresponding metal oxides, nitrates and carbonates. The powder XRD data reveal that the In- and K-doped compounds are isostructural with the parent compound Li₅La₃Nb₂O₁₂. The variation in the cubic lattice parameter was found to change with the size of the dopant ions, for example, substitution of larger In³⁺(r_CN6: 0.79 Å) for smaller Nb⁵⁺ (r_CN6: 0.64 Å) shows an increase in the lattice parameter from 12.8005(9) to 12.826(1) Å at 1000 °C. Samples prepared at higher temperatures (950, 1000 °C) show mainly bulk lithium ion conductivity in contrast to those synthesized at lower temperatures (900 °C). The activation energies for the ionic conductivities are comparable for all samples. Partial substitution of K⁺ for La³⁺ and In³⁺ for Nb⁵⁺ in Li₅La₃Nb₂O₁₂ exhibits slightly higher ionic conductivity than that of the parent compound over the investigated temperature regime 25-300 °C. Among the compounds investigated, the In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ exhibits the highest bulk lithium ion conductivity of 1.8×10⁻⁴ S/cm at 50 °C with an activation energy of 0.51 eV. The diffusivity (“component diffusion coefficient”) obtained from the AC conductivity and powder XRD data falls in the range 10⁻¹⁰-10⁻⁷ cm²/s over the temperature regime 50-200 °C, which is extraordinarily high and comparable with liquids. Substitution of Al, Co, and Ni for Nb in Li₅La₃Nb₂O₁₂ was found to be unsuccessful under the investigated conditions.     

Synthesis, structure and electrical properties of Cu3.21Ti1.16Nb2.63O12 and the CuOx-TiO2-Nb2O5 pseudoternary phase diagram

Subsolidus phase relations in the CuO_x-TiO₂-Nb₂O₅ system were determined at 935 °C. The phase diagram contains one new phase, Cu_3.21Ti_1.16Nb_2.63O₁₂ (CTNO) and one rutile-structured solid solution series, Ti_1−3xCu_xNb_2xO₂: 0<x<0.2335 (35). The crystal structure of CTNO is similar to that of CaCu₃Ti₄O₁₂ (CCTO) with square planar Cu²⁺ but with A site vacancies and a disordered mixture of Cu⁺, Ti⁴⁺ and Nb⁵⁺ on the octahedral sites. It is a modest semiconductor with relative permittivity ∼63 and displays non-Arrhenius conductivity behavior that is essentially temperature-independent at the lowest temperatures.     

Origin of the irreversible plateau (4.5 V) of Li[Li0.182Ni0.182Co0.091Mn0.545]O2 layered material

Layered LiNi_0.4Co_0.2Mn_0.4O₂, Li[Li_0.182Ni_0.182Co_0.091Mn_0.545]O₂, Li[Li_1/3Mn_2/3]O₂ powder materials were prepared by rheological phase method. XRD characterization shows that these samples all have analogous structure to LiCoO₂. Li[Li_0.182Ni_0.182Co_0.091Mn_0.545]O₂ can be considered to be the solid solution of LiNi_0.4Co_0.2Mn_0.4O₂ and Li[Li_1/3Mn_2/3]O₂. Detailed information from XRD, ex situ XPS measurement and electrochemical analysis of these three materials reveals the origin of the irreversible plateau (4.5 V) of Li[Li_0.182Ni_0.182Co_0.091Mn_0.545]O₂ electrode. The irreversible oxidation reaction occurred in the first charging above 4.5 V is ascribed to the contribution of Li[Li_1/3Mn_2/3]O₂ component, which maybe extract Li⁺ from the transition layer in Li[Li_1/3Mn_2/3]O₂ or Li[Li_0.182Ni_0.182Co_0.091Mn_0.545]O₂ through oxygen release. This step also activates Mn⁴⁺ of Li[Li_1/3Mn_2/3]O₂ or Li[Li_0.182Ni_0.182Co_0.091Mn_0.545]O₂, it can be reversibly reduced/oxidized between Mn⁴⁺ and Mn³⁺ in the subsequent cycles.     

正极材料Li_(0.99)Nb_(0.01)Fe_(1-x)Mg_xPO_4/C的制备及电化学性能的研究

采用两步固相反应合成了锂、铁双位掺杂的锂离子电池正极材料Li0.99Nb0.01Fe1-xMgxPO4/C(x=0,0.01,0.02,0.03,0.04)。通过X射线衍射(XRD)、扫描电镜(SEM)以及恒电流充放电测试,研究了复合材料的晶体结构、形貌以及电化学性能。实验结果表明,制备的Li0.99Nb0.01Fe1-xMgxPO4/C(x=0,0.01,0.02,0.03,0.04)为纯相,掺杂适量的Nb5+、Mg2+离子可减小材料的晶粒尺寸,当Nb离子掺杂量为1mol%、Mg离子掺杂量为3mol%时,Li0.99Nb0.01Fe0.97Mg0.03PO4/C的电化学性能最佳。室温下,0.2C、1C、2C、4C(1C=170mA·g-1)倍率充放电其首次放电比容量分别为153.7、149.7、144.6、126.4mAh·g-1,即使在8C倍率下放电其放电比容量也有92.2mAh·g-1,并表现出良好的循环性能。     

Electronic parameters of Sr2Nb2O7 and chemical bonding

X-ray photoelectron spectroscopy (XPS) measurements were carried out on a strontium pyroniobate (Sr₂Nb₂O₇) powder sample, which was synthesized using standard solid-state method. The binding energy (BE) differences between the O 1s and cation core levels, Δ(O-Nb)=BE(O 1s)-BE(Nb 3d_5/2) and Δ(O-Sr)=BE(O 1s)-BE(Sr 3d_5/2), were used to characterize the valence electron transfer on the formation of the Nb-O and Sr-O bonds. The chemical bonding effects were considered on the basis of our XPS results for Sr₂Nb₂O₇ and earlier published structural and XPS data for other Sr- or Nb-containing oxide compounds. The new data point for Sr₂Nb₂O₇ is consistent with the previously derived relationship for a set of Nb⁵⁺-niobates that Δ(O-Nb) increases with increasing mean Nb-O bond distance, L(Nb-O). A new empirical relationship between Δ(O-Sr) and L(Sr-O) was also obtained. Interestingly, the correlation between Δ(O-Sr) and L(Sr-O) was found to differ from that between Δ(O-Nb) and L(Nb-O). Possible cause for the difference is discussed.     

球磨辅助高温固相法制备Li1.0Na0.2Ni0.13Co0.13Mn0.54O2正极材料及其性能

以乙酸盐(乙酸锂、乙酸钠、乙酸钴、乙酸镍、乙酸锰等)为原材料,采用球磨辅助高温固相法制备Li_(1.0)Na_(0.2)Ni_(0.13)Co_(0.13)Mn_(0.54)O_2正极材料。借助XRD、SEM等表征材料的结构和形貌,利用循环伏安、恒流充放电、交流阻抗等方法研究材料的电化学性能。结果表明,钠的掺杂导致颗粒表面光滑度降低,形成Na_(0.77)Mn O_(2.05)新相。0.05C活化过程中,掺钠样品和未掺钠样品首次放电比容量分别为258.4 m Ah·g~(-1)和215.8 m Ah·g~(-1),库伦效率分别为75.2%和72.8%;2C放电比容量分别为116.3 m Ah·g~(-1)和106.2 m Ah·g~(-1)。研究发现,掺钠可减小首次充放电过程的不可逆容量,提高容量保持率;改善倍率性能与容量恢复特性;降低SEI膜阻抗和电荷转移阻抗;掺钠后样品首次循环就可以基本完成Li_2Mn O_3组分向稳定结构的转化,而未掺杂的样品需要两次循环才能逐步完成该过程;XPS结果表明,掺钠样品中Ni~(2+)、Co~(3+)、Mn~(4+)所占比例明显提高,改善了样品的稳定性和电化学性能;循环200次后的XRD结果表明掺钠与未掺钠材料在脱嵌锂反应中的相变化过程基本一致,良好有序的层状结构遭到破坏是循环过程中容量衰减的主要原因。     

球磨辅助高温固相法制备Li1.0Na0.2Ni0.13Co0.13Mn0.54O2正极材料及其性能

以乙酸盐(乙酸锂、乙酸钠、乙酸钴、乙酸镍、乙酸锰等)为原材料,采用球磨辅助高温固相法制备Li_1.0Na_0.2Ni_0.13Co_0.13Mn_0.54O₂正极材料。借助XRD、SEM等表征材料的结构和形貌,利用循环伏安、恒流充放电、交流阻抗等方法研究材料的电化学性能。结果表明,钠的掺杂导致颗粒表面光滑度降低,形成Na_0.77MnO_2.05新相。0.05C活化过程中,掺钠样品和未掺钠样品首次放电比容量分别为258.4 mAh·g^-1和215.8 mAh·g^-1,库伦效率分别为75.2%和72.8%;2C放电比容量分别为116.3 mAh·g^-1和106.2 mAh·g^-1。研究发现,掺钠可减小首次充放电过程的不可逆容量,提高容量保持率;改善倍率性能与容量恢复特性;降低SEI膜阻抗和电荷转移阻抗;掺钠后样品首次循环就可以基本完成Li₂MnO₃组分向稳定结构的转化,而未掺杂的样品需要两次循环才能逐步完成该过程;XPS结果表明,掺钠样品中Ni²⁺、Co³⁺、Mn⁴⁺所占比例明显提高,改善了样品的稳定性和电化学性能;循环200次后的XRD结果表明掺钠与未掺钠材料在脱嵌锂反应中的相变化过程基本一致,良好有序的层状结构遭到破坏是循环过程中容量衰减的主要原因。     

Phase formation, crystal chemistry, and properties in the system Bi2O3-Fe2O3-Nb2O5

Subsolidus phase relations have been determined for the Bi₂O₃-Fe₂O₃-Nb₂O₅ system in air (900-1075 °C). Three new ternary phases were observed—Bi₃Fe_0.5Nb_1.5O₉ with an Aurivillius-type structure, and two phases with approximate stoichiometries Bi₁₇Fe₂Nb₃₁O₁₀₆ and Bi₁₇Fe₃Nb₃₀O₁₀₅ that appear to be structurally related to Bi₈Nb₁₈O₅₇. The fourth ternary phase found in this system is pyrochlore (A₂B₂O₆O′), which forms an extensive solid solution region at Bi-deficient stoichiometries (relative to Bi₂FeNbO₇) suggesting that ≈4-15% of the A-sites are occupied by Fe³⁺. X-ray powder diffraction data confirmed that all Bi-Fe-Nb-O pyrochlores form with positional displacements, as found for analogous pyrochlores with Zn, Mn, or Co instead of Fe. A structural refinement of the pyrochlore 0.4400:0.2700:0.2900 Bi₂O₃:Fe₂O₃:Nb₂O₅ using neutron powder diffraction data is reported with the A cations displaced (0.43 Å) to 96g sites and O′ displaced (0.29 Å) to 32e sites (Bi_1.721Fe_0.190(Fe_0.866Nb_1.134)O₇, Fd3¯m (#227), ). This displacive model is somewhat different from that reported for Bi_1.5Zn_0.92Nb_1.5O_6.92, which exhibits twice the concentration of small B-type cations on the A-sites as the Fe system. Bi-Fe-Nb-O pyrochlores exhibited overall paramagnetic behavior with large negative Curie-Weiss temperature intercepts, slight superparamagnetic effects, and depressed observed moments compared to high-spin, spin-only values. The single-phase pyrochlore with composition Bi_1.657Fe_1.092Nb_1.150O₇ exhibited low-temperature dielectric relaxation similar to that observed for Bi_1.5Zn_0.92Nb_1.5O_6.92; at 1 MHz and 200 K the relative permittivity was 125, and above 350 K conductive effects were observed.     

V2.38Nb10.7O32.7: A V2O5-Nb2O5 mixed oxide tunnel structure related to the tetragonal tungsten bronzes

A crystal structural model for the orthorhombic compound V_2.38Nb_10.7O_32.7, which is known as “V₂Nb₉O_27.5”, was developed by means of selected area electron diffraction (SAED), Rietveld refinement and high resolution electron microscopy (HREM). The metastable compound is obtained by thermal decomposition of freeze-dried precursors as chain-like agglomerated nanoparticles or by reaction of V₂O₅ with fresh-precipitated Nb₂O₅ as more compact micro-scaled crystals. With the latter, it was possible to identify its structure for the first time (space group Cmmm). The tetragonal tungsten bronze (TTB)-type structure shows high potential for ionic intercalation, since easily reducible [V⁵⁺₂O²⁻] units are implemented in the tunnels of a rigid niobium oxide framework.     

Spectroscopic and photoelectrochemical differences between racemic and enantiomeric [Ru(phen)3] ions intercalated into layered niobate K4Nb6O17

Chirality effects have been observed in the intercalation, spectroscopic and photoelectrochemical behavior when enantiomeric and racemic [Ru(phen)₃]²⁺ complexes were intercalated in the interlayer spaces of K₄Nb₆O₁₇. The results were interpreted in terms of a [Nb₆O₁₇]⁴⁻-chelate and chelate–chelate interactions. The faster luminescence decay and higher photocurrent of the enantiomeric [Ru(phen)₃]²⁺–K₄Nb₆O₁₇ compounds than the racemic ones suggest that the emission of adsorbed [Ru(phen)₃]²⁺ ions was not only quenched by adsorbed complexes (or concentration quenching) but also by the semiconductive host lattices.     

Comparative computational investigation of N and F substituted polyoxoanionic compounds: The case of Li2FeSiO4 electrode material

First principles calculations are used to anticipate the electrochemistry of polyoxoanionic materials consisting of XO_{4 − y}A_y (A = F, N) groups. As an illustrative case, this work focuses on the effect of either N or F for O substitution upon the electrochemical properties of Li₂FeSiO₄. Within the Pmn2₁–Li₂FeSiO₄ structure, virtual models of Li₂Fe₂^2.5+SiO_3.5N_0.5 and Li_1.5Fe²⁺SiO_3.5F_0.5 have been analyzed. We predict that the lithium deinsertion voltage associated to the Fe^3+/Fe⁴⁺ redox couple is decreased by both substituents. The high theoretical specific capacity of Li₂FeSiO₄ (330 mAh/g) could be retained in N-substituted silicates thanks to the oxidation of N³⁻ anions, whilst Li_1.5Fe²⁺SiO_3.5F_0.5 has a lower specific capacity inherent to the F substitution. Substitution of N/F for O will respectively improve/worsen the electrode characteristics of Li₂FeSiO₄.     

Structure Study of Bi2.5Na0.5Ta2O9 and Bi2.5Nam−1.5NbmO3m+3 (m=2-4) by Neutron Powder Diffraction and Electron Microscopy

The crystal structures of Bi_2.5Na_0.5Ta₂O₉ and Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=3,4) have been investigated by the Rietveld analysis of their neutron powder diffraction patterns (λ=1.470 Å). These compounds belong to the Aurivillius phase family and are built up by (Bi₂O₂)²⁺ fluorite layers and (A_m-1B_mO_3m+1)^2- (m=2-4) pseudo-perovskite slabs. Bi_2.5Na_0.5Ta₂O₉ (m=2) and Bi_2.5Na_2.5Nb₄O₁₅ (m=4) crystallize in the orthorhombic space group A2₁am, Z=4, with lattice constants of a=5.4763(4), b=5.4478(4), c=24.9710 (15) and a=5.5095(5), b=5.4783(5), c=40.553(3) Å, respectively. Bi_2.5Na_1.5Nb₃O₁₂ (m=3) has been refined in the orthorhombic space group B2cb, Z=4, with the unit-cell parameters a=5.5024(7), b=5.4622(7), and c=32.735(4) Å. In comparison with its isostructural Nb analogue, the structure of Bi_2.5Na_0.5Ta₂O₉ is less distorted and bond valence sum calculations indicate that the Ta-O bonds are somewhat stronger than the Nb-O bonds. The cell parameters a and b increase with increasing m for the compounds Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=2-4), causing a greater strain in the structure. Electron microscopy studies verify that the intergrowth of mixed perovskite layers, caused by stacking faults, also increases with increasing m.     

CdS插层的K4Nb6-xCuxO17复合物的制备及其光催化制氢活性

以Nb2O5,K2CO3和CuO为原料经高温固相反应合成K4Nb6-xCuxO17催化剂,并通过层间离子交换反应,胺插入反应以及硫化反应制备CdS插层K4Nb6-xCuxO17复合催化剂(K4Nb6-xCuxO17/CdS)。利用X射线衍射(XRD),X射线光电子能谱(XPS),场发射扫描电镜(SEM),X射线能谱仪(EDX),紫外-可见漫反射(UV-Vis),分子荧光光谱(PL)等技术对催化剂进行表征。考察了催化剂的可见光催化制氢活性。结果表明,Cu离子掺杂进入K4Nb6O17晶格中,CdS位于K4Nb6O17层间。CdS插层K4Nb6-xCuxO17催化剂的最大吸收光波长约为550 nm。催化剂制氢活性有明显提高,紫外光和可见光下3 h产氢量分别达到279.83 mmol.gcat-1和7.11 mmol.gcat-1。最后讨论了复合催化剂光生电荷转移机理。     

Ca9Y(PO4)7:Ce3+,Tb3+纳米荧光粉的制备及发光性能

采用水热法制备出Ca₉Y（PO₄）₇：Ce³⁺,Tb³⁺纳米荧光粉,通过XRD、SEM和荧光光谱等对样品进行了分析,研究在Ca₉Y（PO₄）₇基质中引入Ce³⁺,Tb³⁺离子对发光性能的影响规律。研究发现因Tb³⁺离子自身能量交叉驰豫的存在,使得单掺Tb³⁺时,通过调节Tb³⁺离子的浓度可以实现对发光颜色的控制。同时研究了Ce³⁺-Tb³⁺之间的能量传递为电多极相互作用的偶极-四极机制,Ce³⁺-Tb³⁺之间最大的能量传递效率为55.6%。Ca₉Y（PO₄）₇：Ce³⁺,Tb³⁺的发光颜色可以通过激活离子之间的能量传递和共发射得到可控调节。SEM分析表明荧光粉颗粒尺寸在100 nm左右,分散性好。     

Dopant substitution and oxygen migration in the complex perovskite oxide Ba3CaNb2O9: A computational study

Atomistic simulation methods have been used to study the defect chemistry of the complex perovskite oxide Ba₃CaNb₂O₉. Calculations were carried out for the hexagonal (P-3m1) phase and the cubic (Fm-3m) phase. The hexagonal structure is predicted to be energetically more stable at room temperature. In both structures the most favourable dopant for Nb⁵⁺ is found to be Ca²⁺ rather than Mg²⁺, in contrast to the generally accepted rule that size similarities govern such processes. The diffusion of oxygen vacancies in the hexagonal and cubic phases occurs within different networks of corner-sharing NbO₆ and CaO₆ octahedra. Irrespective of the arrangement of octahedra, however, migration of oxygen vacancies around NbO₆ octahedra takes place with lower activation energies than around the CaO₆ octahedra.