负载型钙钛矿催化氧化NO及抗SO_2性能研究

采用柠檬酸络合浸渍法制备了负载型钙钛矿氧化物La1-xCexCoO3/CeO2(x=0~0.3)催化剂,考察了不同Ce掺杂量对其催化氧化NO和抗硫性能的影响,并运用X射线衍射(XRD)、傅里叶红外光谱(FT-IR)、氮气物理吸附、程序升温还原(H2-TPR)、氧气程序升温脱附(O2-TPD)等手段对催化剂进行了表征。结果表明,催化剂的活性与其比表面积大小和氧化还原性质密切相关;其中,负载型钙钛矿La0.8Ce0.2CoO3/CeO2催化剂在300℃时催化氧化NO的转化率达78%。在添加CeO2作载体后,不仅改善了非负载性钙钛矿的低温活性,而且抗硫性能也显著提高。     

Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33,用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体.采用这些固溶体作载体,以Fe2O3为活性组分,用浸渍法制备了一系列催化剂.BET结果显示,将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积.TPR结果显示,载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能.XRD结果表明,Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况,老化前后催化剂的晶相结构基本无明显变化.特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时,Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33, 用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体. 采用这些固溶体作载体, 以Fe2O3为活性组分, 用浸渍法制备了一系列催化剂. BET结果显示, 将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积. TPR结果显示, 载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能. XRD结果表明, Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况, 老化前后催化剂的晶相结构基本无明显变化. 特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时, Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

Cu/La/CeO2-Al2O3的制备及其对丙烯选择性还原NO的催化活性

将Al(NO3)3-Ce(NO3)3混合溶液滴入到NH4HCO3-NH3.H2O混合溶液中,采用共沉淀法制备了CeO2-Al2O3复合载体.采用等体积浸渍法分别浸渍助剂La和活性组分Cu,制备了Cu/La/CeO2-Al2O3催化剂.考察了催化剂在富氧条件下对丙烯选择性还原NO反应的催化活性,并借助扫描电镜、原子力显微镜、X射线衍射、比表面积测定、红外光谱、热重分析、X射线光电子能谱和程序升温还原等方法研究了催化剂活性与结构之间的关系.结果表明,CeO2-Al2O3复合载体能显著增大催化剂的比表面积和孔径,增加表面Lewis酸酸量,改善催化剂的还原性能;助剂La能进一步增大催化剂的比表面积和孔径,增加表面Br nsted酸酸量,显著提高催化剂的热稳定性;催化剂的粒径较小,对丙烯选择性还原NO反应具有较高的催化活性,最高催化活性时的温度较低.     

Cu/Al2O3催化剂的改性及其对NO选择性还原的催化性能

 以 γ-Al2O3 为载体,采用SO2-4进行改性并添加助剂La,再负载上Cu2+, 制备了改性的Cu/Al2O3催化剂(Cu/La/SO2-4/Al2O3),考察了SO2-4改性和助剂La对催化剂在富氧条件下催化丙烯选择性还原NO 反应的影响,并借助红外光谱、X射线衍射、扫描电镜、热重分析、程序升温还原和X射线光电子能谱等方法研究了改性催化剂的性能与结构的关系. 结果表明,改性催化剂的催化活性较高, NO转化率可高达83.7%. 采用SO2-4改性可促进催化剂表面的酸量增加,并促使产生B酸中心; 助剂La可提高Cu物种的分散程度,并提高催化剂的热稳定性和还原性,从而可有效提高催化剂在富氧条件下对丙烯选择性还原NO反应的催化活性和水热稳定性.     

Au／Fe2O3／Al2O3催化剂上丙烯选择催化还原NO

以浸渍法制备的Fe2O3/γ-Al2O3为载体,采用均相沉积沉淀方法制备了Au/Fe2O3/Al2O3催化剂.该催化剂在丙烯选择催化还原NO反应中显示出很好的低温催化活性,300℃时NO被选择还原为N2的转化率可达43%,而在Au/Al2O3催化剂上,NO的转化率仅为21%.水蒸气的加入对催化剂活性的影响较小.X射线衍射结果表明,Au和Fe2O3高度分散在Al2O3载体上.吸附氢气的程序升温还原结果表明,Au与Fe2O3之间存在着强相互作用,Au的存在促进了Fe2O3的还原,Au和Fe2O3之间的协同作用可能是Au/Fe2O3/Al2O3催化剂在丙烯选择还原NO反应中具有较高低温催化活性的原因之一.     

CO_2加氢活性与担载铁催化剂表面Fe-O键强度的关系

采用浸渍 -还原法 ,制备了 Al2 O3、 Ti O2 、 Zr O2 担载铁催化剂 ,并在温度 6 2 3K、压力 1.5 MPa、空速80 0～ 10 0 0 h- 1、原料气组成 CO2 /H2 为 1∶ 2等实验条件下 ,考察了不同还原温度的催化剂在 CO2 加氢制低碳(C2 ～ C5 )烃中的反应活性 .结果表明 ,以 CO2 转化率计 ,各催化剂均存在最佳还原温度 (Fe/Al2 O3:873K;Fe/Ti O2 :773K;Fe/Zr O2 :72 3K) .将此温度与催化剂表面 Fe- O键强度相关联 ,发现在相同条件下 ,与载体 M-O键长有关的 Fe- O键越强 ,催化剂越容易被还原 ,最佳还原温度越低 ,反应活性越好 .     

堇青石负载La-Mn-O复合氧化物催化剂的甲苯催化燃烧性能

以堇青石蜂窝陶瓷为载体,以La2O3,Mn(NO3)2为基本原料,掺杂一些稀土等非贵重金属元素,采用浸渍法制备了系列负载La-Mn-O复合氧化物催化剂.考察了焙烧温度等对甲苯催化燃烧性能的影响,并对催化剂进行了XRD,TPR表征.结果表明,800 ℃焙烧的LaMn/Cord催化剂具有较高的甲苯催化燃烧性能;Ce取代催化剂中部分La后能改善催化剂的氧化活性,当Ce∶La=1∶1(摩尔比)时催化性能最佳,在260 ℃的反应温度下甲苯转化率达到90%以上.     

LaAl1-xFexO3/Al2O3/FeCrAl催化剂的制备及其对甲烷燃烧的催化性能

 以FeCrAl合金薄片为载体,以LaAl1-xFexO3为活性组分,以Al2O3为过渡层,制备了LaAl1-xFexO3/Al2O3/FeCrAl金属基整体式催化剂,并用XRD和SEM等方法对催化剂的物相和形貌进行了表征,对催化剂上甲烷催化燃烧活性进行了评价. 结果表明,催化剂物相中有LaAl1-xFexO3型钙钛矿及 α-Al2O3 和 γ-Al2O3; 催化剂的颗粒小于2 μm, 并且颗粒的尺寸及形貌与LaAl1-xFexO3中的Fe/Al摩尔比有关; 催化剂样品对甲烷催化燃烧活性的大小顺序为LaAl0.3Fe0.7O3/Al2O3/FeCrAl＞LaFeO3/Al2O3/FeCrAl＞LaAl0.5Fe0.5O3/Al2O3/FeCrAl＞LaAl0.7Fe0.3O3/Al2O3/FeCrAl＞LaAlO3/Al2O3/FeCrAl.     

低温熔盐法制备球状多孔 La1-xSrxMn0.8Fe0.2O3（0≤x≤0.6）及其催化 CO氧化性能

汽车尾气中 CO, HC, NOx,硫化物及其颗粒粉尘严重危害人们身体健康和大气环境,是大气环境的主要污染源之一.目前,尾气净化是其减排的最主要方式.汽车尾气催化剂的发展经历了几代的研究,一直以来广泛采用 Pt, Pd和 Rh等贵金属,但因其资源匮乏,价格昂贵,容易被 S和 P中毒,因此人们逐渐将目光投向非贵金属催化剂的研发.钙钛矿复合氧化物因具有独特的物理化学性质以及灵活的“化学剪裁”特性而在材料研究等领域颇受青睐,有望成为贵金属催化剂的替代品.一般而言,催化剂的比表面积越大,表面活性位点越多,其催化活性越高,且会明显降低起燃温度.目前,一些制备工艺,如水热法、共沉淀法、微乳液法和硬模板法,虽可在一定程度上提高催化剂的比表面积,但却存在费时、耗能及制备工艺复杂等缺点.因此,如何简单有效地制备出大比表面积的钙钛矿型催化剂依然是一个难题.本文以合成的分级多孔δ-MnO2微球为模板,采用熔盐法制备出球状多孔 La1-xSrxMn0.8Fe0.2O3(0≤x≤0.6)钙钛矿氧化物,研究了球状多孔钙钛矿氧化物的形成过程和合适的制备温度,以及 B位 Fe3+掺杂量为20%时 A位 Sr2+掺杂量对钙钛矿催化剂结构和催化活性的影响.采用 X射线粉末衍射、扫描电子显微镜、透射电子显微镜、N2吸附-脱附、傅里叶红外光谱(FT-IR)和 X射线能谱(XPS)等方法对催化剂进行了表征.在固定床石英管反应器上评价了催化剂催化 CO氧化活性及稳定性,采用气相色谱联接氢火焰离子化检测器检测了产物和反应物的组成.结果表明,以分级多孔δ-MnO2微球为模板,采用熔盐法在450oC反应4 h制备出的球状多孔 La1-xSrxMn0.8Fe0.2O3(0≤x≤0.6)钙钛矿氧化物具有良好的结晶性、较大的比表面积(55.73 m2/g)和孔体积(0.37 cm3/g).其球状多孔结构的形成可分为两个阶段：原位形成钙钛矿相和纳片表面析出钙钛矿晶粒及钙钛矿晶粒的再生长.另外, FT-IR光谱表明, Fe3+和 Sr2+成功进入 A, B位.同时, CO转化曲线表明, B位 Fe3+的掺杂量为20%时, A位 Sr2+的掺杂量高于30%时可以明显改善催化剂催化 CO氧化活性： La1-xSrxMn0.8Fe0.2O3(0≤x≤0.3)的T50和T90分别在180和198oC左右;而 La0.55Sr0.45Mn0.8Fe0.2O3和 La0.4Sr0.6Mn0.8Fe0.2O3的T50均低于125oC; La0.55Sr0.45Mn0.8Fe0.2O3的T90为181oC,而 La0.4Sr0.6Mn0.8Fe0.2O3却仍低于125oC. XPS结果则证明,较高的催化活性得益于 La0.4Sr0.6Mn0.8Fe0.2O3表面存在较多的 Mn4+、氧空位及吸附氧.最后, La0.55Sr0.45Mn0.8Fe0.2O3和 La0.4Sr0.6Mn0.8Fe0.2O3的稳定性测试结果表明,采用熔盐法以δ-MnO2为模板在450oC焙烧4 h制备的多孔球状钙钛矿具有较好的催化稳定性.虽然催化剂制备工艺简单,周期短,但比表面积最大只有55.73 m2/g,为硬模板法的1/2,因此提高比表面积将是今后研究的方向.     

Investigation of Propene Oligomerization Catalyst Series Derived from Complex of Ferric Sulfate and Nickel Sulfate

Some paper have reported that catalyt of NiSO₄/γAlO₃ has a very high oligomerization activity for propene, but the over tri oligomerization selectivity is very low^[1].The catalyt of Fe₂(SO₄)₃/γ-Al₂O₃ has a very high over trioligomerization selectivity, but oligomerization activity was lower then catalysis of NiSO₄/γ-Al₂O₃ for propene and stability of catalysis was not as good as catalysis of NiSO₄/γ-Al₂O₃^[2].In this paper the catalysis of Fe_(2/3)xNi_1-xSO₄-P₂O₅/γ-Al₂O₃ for propene oligomerization has been systematically studied, the effect of the activation method, the stability and reaction conditions on activity and selectivity were investigated. Fe_(2/3)xNi_1-xSO₄-P₂O₅/γ-Al₂O₃ catalysis was preparared by impregnation.The factors affecting catalyst performance for propene oligomerization are as follows.     

Ni的引入对Cu/γ-Al_2O_3催化剂上含硫低浓度甲烷燃烧特性的影响

采用共浸渍法制备了不同Ni含量的Cu/γ-Al2O3催化剂,在固定床反应器上考察了该催化剂在含硫(SO2,0.01%,体积分数)气氛中对低浓度甲烷(3%)的催化燃烧活性及抗硫中毒稳定性。结果表明,SO2会使Cu/γ-Al2O3催化剂发生硫中毒,Ni的加入可增强其抗硫性能,而且随着Ni含量的增加,其抗硫性改善效果越明显。在Ni含量为10%的Cu/γ-Al2O3催化剂上反应10 h后,甲烷转化率仍可保持在96%以上。SEM、XRD和TPD表征结果显示,Ni的加入促使Cu/γ-Al2O3催化剂表面生成NiAl2O4尖晶石相,提高了催化剂的稳定性。随着Ni含量的增加,催化剂表面Lewis酸性降低,吸附SO2的能力减弱,可延缓催化剂硫中毒,同时也缩短了CO2分子在催化剂表面的停留时间,从而提高了甲烷催化燃烧效率。     

Mg改性对Co/γ-Al2O3-TiO2催化燃烧丙烷性能影响

采用分步浸渍法制备了系列Mg改性的Co/γ-Al_2O_3-TiO_2催化剂,通过X射线衍射(XRD)、紫外可见漫反射光谱(DR-UV-vis)、N_2吸附-脱附(BET)、X射线光电子能谱(XPS)和H_2程序升温还原(H_2-TPR)等技术对催化剂进行表征,并考察了其对丙烷燃烧的催化性能。结果表明,Co在原始γ-Al_2O_3-TiO_2载体和Mg改性MgO/γ-Al_2O_3-TiO_2载体上均以Co_3O_4的形式存在;Mg掺入后与Al_2O_3作用形成MgAl_2O_4尖晶石,改善了载体的织构性质,提升了Co_3O_4在催化剂载体表面的暴露数量和分散程度。此外,MgAl_2O_4与Co_3O_4相互作用提升了Co_3O_4颗粒表面Co~(3+)/Co~(2+)和O_(ads)/O_(latt)的比例,并削弱了Co-O键键能,从而提升了其对丙烷的催化燃烧活性。当Mg负载量为15%(质量分数)时,在Co/MgO(15%)/γ-Al_2O_3-TiO_2催化剂上进行丙烷燃烧,丙烷90%转化率的温度比无Mg掺杂的Co/γ-Al_2O_3-TiO_2催化剂的降低了45℃,并且连续反应40 h其活性保持稳定。     

原位共沉淀法制备NiMg(Al)O/γ-Al2O3催化剂及其酯交换性能

以γ-Al₂O₃为载体通过原位共沉淀法制备NiMgAl-LDHs/γ-Al₂O₃,经焙烧后得到NiMg（Al）O/γ-Al₂O₃催化剂,通过TG-DTG、XRD、SEM、BET、FT-IR、CO₂-TPD等手段对催化剂进行了表征,并对其在酯交换制备生物柴油反应中的催化性能进行了研究。结果表明,NiMgAl-LDHs和NiMg（Al）O成功在γ-Al₂O₃内孔表面生长,并有良好的结合度。催化剂对酯交换具有很高的催化活性;在醇油物质的量比为12：1的条件下反应3 h,生物柴油产率为95%,重复使用七次后,生物柴油产率仍然在82%以上。     

基于改性Ni/γ-Al_2O_3催化剂的电催化甲烷水蒸气重整的研究

提出了电催化作用下甲烷水蒸气催化重整的新工艺。基于工业常规Ni基催化剂,采用等体积浸渍法,以Ni为活性组分,γ-Al_2O_3为载体,MgO、CaO为助剂,制备了Ni/γ-Al_2O_3、Ni-MgO/γ-Al_2O_3和Ni-CaO/γ-Al_2O_3催化剂,考察了电流强度、重整温度、水蒸气与甲烷的物质的量比(水碳比,S/C)对不同催化剂的CH_4转化率、H_2产率、CO选择性和催化剂稳定性的影响。结果表明,电催化工艺有着良好的普适性,电流的引入能够提升CH_4转化率、增加H_2产率,尤其在低温下电流的促进作用显著。在三种催化剂中,Ni-CaO/γ-Al_2O_3催化效果最佳,在电流为4.5 A、S/C为3、重整温度为700℃时,CH_4转化率就高达95%以上。稳定性测试表明,电流的通入还能显著提高催化剂的稳定性,延缓催化剂的积炭失活。通过对催化剂的分析表征,发现电流的通入提升了催化剂中NiO的还原程度,同时抑制了反应过程中NiC_x向石墨炭的转化,从而可延缓催化剂因积炭覆盖反应活性位点而造成的失活。     

不同形貌Ni/γ-Al2O3催化剂催化CO甲烷化反应的研究

采用沉淀法分别以乙二醇、水、乙二醇-聚乙二醇600为修饰剂,制备了形貌分别为棒状（a-NiO）、粒状（b-NiO）和片状（c-NiO）结构的NiO催化剂,然后和γ-Al₂O₃通过研混法制得NiO/γ-Al₂O₃催化剂。采用XRD、TEM及H₂-TPR等技术手段对催化剂进行了表征。TEM观察NiO的形貌分别为棒状、粒状和片状。H₂-TPR结果表明,NiO/γ-Al₂O₃催化剂的氧化中心数量顺序为b-NiO/γ-Al₂O₃＜a-NiO/γ-Al₂O₃＜c-NiO/γ-Al₂O₃。XRD结果表明,NiO/γ-Al₂O₃催化剂还原后的Ni晶粒尺寸大小为b-Ni＞a-Ni＞c-Ni。在连续流动固定床反应装置上考察了Ni/γ-Al₂O₃对CO甲烷化反应的催化活性,研究了混合方法和形貌对CO甲烷化反应的影响。结果表明,研混法制得催化剂的活性及稳定性较好。催化剂形貌对CO甲烷化反应的催化活性顺序为c-Ni/γ-Al₂O₃＞a-Ni/γ-Al₂O₃＞b-Ni/γ-Al₂O₃,常压、593K和2500h^-1反应条件下,w_Ni为15% c-Ni/γ-Al₂O₃催化CO合成CH₄选择性及CO转化率分别达90.80%和99.63%。     

Zr改性Ni/γ-Al2O3催化剂用于浆态相合成气的低温甲烷化

采用浆态床反应器,在低温(300~330 ℃)下进行合成气的甲烷化反应.实验中通过共浸渍法(包括含浸-旋蒸法)制备了锆(Zr)修饰的Ni/γ-Al₂O₃催化剂,并考察其与单一NiO、未掺杂Zr 的Ni/γ-Al₂O₃催化剂的催化性能差异.研究表明,载体γ-Al₂O₃的引入能够明显地提高CO的转化率和甲烷的选择性,而Zr的掺杂会进一步提升催化剂的催化活性.在325 ℃,空速为4 200 mL·g^-1·h^-1时,CO的转化率可以达到86.41%,甲烷选择性为90.53%.催化剂的表征结果表明,Zr的添加促进了Ni在催化剂表面的分散、减弱了活性Ni与载体的相互作用,抑制了低甲烷化活性的NiAl₂O₄的生成,使得催化剂的反应性能得到较大提高.     

Pd/γ-Al2O3-TiO2催化剂上乙醇乙醛的催化氧化性能研究

采用混胶法和机械混合等方法制备了Pd质量分数为1%的Pd/γ-Al₂O₃-TiO₂催化剂,并对其催化活性、影响条件进行了考察。结果说明,由混胶法制备的Pd/γ-Al₂O₃-TiO₂催化剂对乙醇和乙醛的完全氧化表现出优异的催化性能,其活性明显高于单一载体催化剂Pd/TiO₂和Pd/Al₂O₃,150℃时乙醇和乙醛的转化率分别达到98.9%和98.5%。在较宽温度范围内和高空速条件下表现出良好的稳定性。同时运用XRD、TEM和FT-IR等技术对催化剂进行了表征。结果表明,在Pd/γ-Al₂O₃-TiO₂催化剂中Al₂O₃与TiO₂之间存在着较强的相互作用,使γ-Al₂O₃-TiO₂的比表面积和孔容积均调变到一个适中的数值,同时在催化剂表面Al₂O₃参与形成了有利于其催化活性的表面结构。     

Ni-Fe/γ-Al2O3双金属催化剂的制备及其CO甲烷化性能研究

采用等体积浸渍法制备了Ni-Fe/γ-Al₂O₃双金属催化剂和Ni/γ-Al₂O₃、Fe/γ-Al₂O₃单金属催化剂,在连续流动微反装置上考察了催化剂的CO甲烷化催化活性,采用XRD、N₂物理吸附、H₂-TPR、H₂-TPD和TPSR等手段对催化剂进行表征。结果表明,Ni-Fe/γ-Al₂O₃双金属催化剂中Ni、Fe之间产生了明显的相互作用,还原后催化剂中形成Ni-Fe合金,对氢气吸附量显著增加。在CO体积分数为0.5%、空速5000h^-1、常压的反应条件下,Ni-Fe/γ-Al₂O₃双金属催化剂表现出高的甲烷化活性,220℃时将CO完全转化为甲烷。     

Cu-Ce/γ-Al2O3对硬脂酸催化水热脱氧产生烷烃的效果

利用等体积浸渍法制备Cu-Ce/γ-Al₂O₃催化剂，并在无H₂存在的条件下对硬脂酸进行催化水热液化。对催化剂进行BET比表面积分析和X射线衍射（XRD）分析可知，Cu-Ce/γ-Al₂O₃催化剂中存在CuO和CeO₂两种晶型，在300℃条件下水热反应12 h后具有更好的热稳定性。通过对硬脂酸进行水热液化实验和对生物油进行气相色谱-质谱（GC-MS）分析发现，加入Cu-Ce/γ-Al₂O₃催化剂能够获得最高的硬脂酸转化率（94.71%）和总烃产率（81.41%），水热液化脱氧效果最好。分析正烷烃的产率，结果发现硬脂酸在高温水热条件下主要发生脱羧反应。Cu-Ce/γ-Al₂O₃催化剂的加入能够同时促进反应过程中脱羧反应、加氢脱氧反应和裂化反应。此外，Cu-Ce/γ-Al₂O₃还能够促进羰基基团的脱除，有效减少产物中的醛和酮类物质。