A novel anode supported BaCe0.4Zr0.3Sn0.1Y0.2O3−δ electrolyte membrane for proton conducting solid oxide fuel cells

A novel BaCe_0.4Zr_0.3 Sn_0.1Y_0.2O_3−δ (BSY) electrolyte membrane with thickness of 20 μm was fabricated on NiO-based anode substrate via a one-step all-solid-state method followed by a co-sintering at 1450 °C for 5 h. Chemical stability test demonstrated that BSY electrolyte showed adequate chemical stability against CO₂ and H₂O at intermediate temperature. Besides, the doping of Sn also enhanced the conductivity in humidified hydrogen. With Nd_0.7Sr_0.3MnO_3−σ cathode and hydrogen fuel, the fuel cell generated maximum output of 320, 185 and 105 mW cm⁻² at 700, 650 and 600 °C, respectively. The interfacial resistance of the fuel cell was studied under open circuit conditions and the short-term cell performance also confirmed the stability of BSY electrolyte membrane.     

Conductivity studies of dense yttrium-doped BaZrO3 sintered at 1325 °C

High-temperature proton conductors have wide applications in the areas of fuel cells, electrolysis and hydrogen separation. Barium zirconate-based materials are of interest due to their good stability and high protonic conductivity. The reported conductivity of these ceramic materials is generally less than 10⁻² S/cm, even at high temperatures. This is not high enough for an electrolyte-supported device to achieve an ASR of less than 0.2 Ω cm² therefore thin film electrolytes are required for successful application. As BaZrO₃-based materials have to be sintered at temperatures as high as 1700 °C, this makes it difficult to find a suitable supporting electrode which will not undergo significant chemical reaction with the BaZrO₃-based electrolyte during fabrication of the required electrode supported electrolyte. In this paper, proton-conducting BaZr_0.8Y_0.2O_2.9 was successfully sintered at 1325 °C with a relative density of 96% via addition of 1 wt% ZnO. Fabrication of electrochemical cells using proton-conducting BaZr_0.8Y_0.2O_2.9 as the electrolyte thus becomes possible. The formula of the 1 wt% ZnO added sample is Ba_0.97Zr_0.77Y_0.19Zn_0.04O_3−δ which exhibits a tetragonal structure with space group P4/mbm (127); a=5.9787(1) Å, c=4.2345(1) Å, V=151.36(1) Å³. It was found that a solid solution was formed for a limited range of Zn doping. Conductivity has been studied as a function of atmosphere (air, dry and wet 5% H₂/Ar) with the changes in bulk and grain boundary on changing atmosphere being monitored as a function of time. The total conductivity of Ba_0.97Zr_0.77Y_0.19Zn_0.04O_3–δ is 1.0×10⁻³ S/cm above 600 °C therefore it may be used as a proton-conducting thin film electrolyte for efficient electrochemical devices at such temperatures. The grain boundary resistance is insignificant at high temperature for the well-sintered sample.     

Preparation and hydrogen permeation of SrCe0.95Y0.05O3−δ asymmetrical membranes

Asymmetrical thin membranes of SrCe_0.95Y_0.05O_3−δ (SCY) were prepared by a conventional and cost-effective dry pressing method. The substrate consisted of SCY, NiO and soluble starch (SS), and the top layer was the SCY. NiO was used as a pore former and soluble starch was used to control the shrinkage of the substrate to match that of the top layer. Crack-free asymmetrical thin membranes with thicknesses of about 50 μm and grain sizes of 5–10 μm were successfully pressed on to the substrates. Hydrogen permeation fluxes (J_H2) of these thin membranes were measured under different operating conditions. At 950 °C, J_H2 of the 50 μm SCY asymmetrical membrane towards a mixture of 80% H₂/He was as high as 7.6 × 10⁻⁸ mol/cm² s, which was about 7 times higher than that of the symmetrical membranes with a thickness of about 620 μm. The hydrogen permeation properties of SCY asymmetrical membranes were investigated and activation energies for hydrogen permeation fluxes were calculated. The slope of the relationship between the hydrogen permeation fluxes and the thickness of the membranes was −0.72, indicating that permeation in SCY asymmetric membranes was controlled by both bulk diffusion and surface reaction in the range investigated.     

固-溶法制备中温固体氧化物燃料电池高性能La0.8Sr0.2MnO3-Ba0.5Sr0.5Co0.8Fe0.2O3阴极

研究了新型固溶法合成La_0.8Sr_0.2MnO₃（LSM）包覆Ba_0.5Sr_0.5Co_0.8Fe_0.2O₃（BSCF）复合粉体（LSM-BSCF）,并探讨了其作为中温固体氧化物燃料电池阴极材料的电化学性能。LSM-BSCF阴极结合了LSM和BSCF阴极的优点,不仅增大了三相界面,而且稳定了微观结构。当温度为600-750℃时,其极化阻抗为0.61-0.09 Ω·cm²。与溶液注入法制备的高性能电极相比,极大地提高了性能稳定性。     

Sr2NiMoO6−δ as anode material for LaGaO3-based solid oxide fuel cell

The double-perovskite Sr₂NiMoO_6−δ (SNMO) was investigated as an anode material of a solid oxide fuel cell (SOFC). With a 300 μm thick La_0.9Sr_0.1Ga_0.8Mg_0.2O_3−σ (LSGM) disk as electrolyte and Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3−δ as the cathode, the SNMO anode showed power densities of 819 mW cm⁻² in hydrogen at 1123 K. Moreover, there was no buffer layer between anode and electrolyte, which would reduce design techniques and save design cost. After test no chemical reaction was discovered between anode and electrolyte. The anode exhibited good conductivity and the value was around 60 S cm⁻¹ in H₂. Also it had almost linear thermal expansion from room temperature to 1253 K and the average thermal expansion coefficient was about 12.14 × 10⁻⁶ K⁻¹, which was quite close to that of La_0.9Sr_0.lGa_0.8Mg_0.2O₃ (12.17 × 10⁻⁶ K⁻¹) electrolyte.     

Synthesis and ac susceptibility of YCa2Cu3O7−δ

The bulk superconducting YCa₂Cu₃O_7−δ compounds are prepared at an ordinary pressure of oxygen by conventional solid-state reaction method. The formation of sample is tested by means of XRD and is studied for their ac susceptibility below room temperature up to 77.5 K. The samples are found single-phase orthorhombic structure and found superconducting at 83.5 K. It is shown that the analysis is consistent with published data on YBa₂Cu₃O_7−δ oxide superconductor.     

Pressure Dependence of the Lattice Distortion in Perovskite La0.5−xBixCa0.5MnO3 (x=0.1, 0.15, 0.2)

The in situ behavior of distorted perovskite La_0.5−xBi_xCa_0.5MnO₃ (x=0.1, 0.15, 0.2) under high pressure has been studied by energy-dispersive X-ray diffraction in a diamond anvil cell. An abnormal change of the 202–040 d-spacing ascribed to the disappearance of the distortion mode Q₂ in the MnO₆ octahedra is observed at 1.2, 1.4, and 1.6 GPa, respectively, and it results in a reduction of the Jahn–Teller distortion commonly existing in the manganites. Effect of the unique 6s² long-pair character of the Bi³⁺ ion on the pressure dependence of the lattice distortion is discussed.     

Ternary [Al2O3–electrolyte–Cu] species: EPR spectroscopy and surface complexation modeling

Cu²⁺ binding on γ-Al₂O₃ is modulated by common electrolyte ions such as Mg²⁺, , and in a complex manner: (a) At high concentrations of electrolyte ions, Cu²⁺ uptake by γ-Al₂O₃ is inhibited. This is partially due to bulk ionic strength effects and, mostly, due to direct competition between Mg²⁺ and Cu²⁺ ions for the SO⁻ surface sites of γ-Al₂O₃. (b) At low concentrations of electrolyte ions, Cu²⁺ uptake by γ-Al₂O₃ can be enhanced. This is due to synergistic coadsorption of Cu²⁺ and electrolyte anions, and _. This results in the formation of ternary surface species (SOH₂SO₄Cu)⁺, (SOH₂PO₄Cu), and (SOH₂HPO₄Cu)⁺ which enhance Cu²⁺ uptake at pH < 6. The effect of phosphate ions may be particularly strong resulting in a 100% Cu uptake by the oxide surface. (c) EPR spectroscopy shows that at pH  pH_PZC, Cu²⁺ coordinates to one SO⁻ group. Phosphate anions form stronger, binary or ternary, surface species than sulfate anions. At pH  pH_PZC Cu²⁺ may coordinate to two SO⁻ groups. At pH  pH_PZC electrolyte ions and are bridging one O-atom from the γ-Al₂O₃ surface and one Cu²⁺ ion forming ternary [γ-Al₂O₃/elecrolyte/Cu²⁺] species.     

X-ray diffraction and Mössbauer spectroscopy studies of LiFe0.5Ti1.5O4 – A new primitive cubic ordered spinel

LiFe_0.5Ti_1.5O₄ was synthesized by solid-state reaction carried out at 900 °C in flowing argon atmosphere, followed by rapid quenching of the reaction product to room temperature. The compound has been characterized by X-ray powder diffraction (XRD) and ⁵⁷Fe Mössbauer effect spectroscopy (MES). It crystallizes in the space group P4₃32, a = 8.4048(1) Å. Results from Rietveld structural refinement indicated 1:3 cation ordering on the octahedral sites: Li occupies the octahedral (4b) sites, Ti occupies the octahedral (12d) sites, while the tetrahedral (8c) sites have mixed (Fe/Li) occupancy. A small, about 5%, inversion of Fe on the (4b) sites has been detected. The MES data is consistent with cation distribution and oxidation state of Fe, determined from the structural data.The title compound is thermally unstable in air atmosphere. At 800 °C it transforms to a mixture of two Fe³⁺ containing phases – a face centred cubic spinel Li_(1+y)/2Fe_(5−3y)/2Ti_yO₄ and a Li_(z−1)/2Fe_(7−3z)/2Ti_zO₅ – pseudobrookite. The major product of thermal treatment at 1000 °C is a ramsdellite type lithium titanium iron(III) oxide, accompanied by traces of rutile and pseudobrookite.     

La0.6Sr1.4MnO4 layered perovskite anode material for intermediate temperature solid oxide fuel cells

La_0.6Sr_1.4MnO₄ (LSMO₄) layered perovskite with K₂NiF₄ structure was prepared and evaluated as anode material for La_0.8Sr_0.2Ga_0.83Mg_0.17O_3 − δ (LSGM) electrolyte supported intermediate temperature solid oxide fuel cells (IT-SOFCs). X-ray diffraction results show that LSMO₄ is redox stability. Thermal expansion coefficient of LSMO₄ is close to that of LSGM electrolyte. By adopting LSMO₄ as anode and La_0.6Sr_0.4Co_0.8Fe_0.2O₃ (LSCF) as cathode, maxium power densities of 146.6, 110.9 mW cm^− 2 with H₂ fuel at 850, 800 °C and 47.3 mW cm^− 2 with CH₄ fuel at 800 °C were obtained, respectively. Further, the cell demonstrated a reasonably stable performance under 180 mA cm^− 2 for over 40 h with H₂ fuel at 800 °C.     

High performance anode-supported intermediate temperature solid oxide fuel cells (IT-SOFCs) with La0.8Sr0.2Ga0.8Mg0.2O3−δ electrolyte films prepared by electrophoretic deposition

Remarkable power density was obtained for anode-supported solid oxide fuel cells (SOFCs) based on La_0.8Sr_0.2Ga_0.8Mg_0.2O_3−δ (LSGM) electrolyte films, fabricated following an original procedure that allowed avoiding undesired reactions between LSGM and electrode materials, especially Ni. Electrophoretic deposition (EPD) was used for the fabrication of 30 μm-thick electrolyte films. Anode supports were made of La_0.4Ce_0.6O_2−x (LDC). The LSGM powder was deposited by EPD on an LDC green tape-cast membrane added with carbon powder, both as pore former and substrate conductivity booster. A subsequent co-firing step at 1490 °C produced dense electrolyte films on porous LDC skeletons. Then, a La_0.8Sr_0.2Fe_0.8Co_0.2O_3−δ (LSFC) cathode was applied by slurry-coating and calcined at 1100 °C. Finally, the porous LDC layer was impregnated with molten Ni nitrate to obtain, after calcination at 900 °C, a composite NiO–LDC anode. Maximum power densities of 780, 450, 275, 175, and 100 mW/cm² at 700, 650, 600, 550, and 500 °C, respectively, were obtained using H₂ as fuel and air as oxidant, demonstrating the success of the processing strategy. As a comparison, electrolyte-supported SOFCs made of the same materials were tested, showing a maximum power density of 150 mW/cm² at 700 °C, more than 5 times smaller than the anode-supported counterpart.     

EDTA-甘氨酸法制备SmBaCo2O5+δ阴极材料及其性能

采用EDTA-甘氨酸法(EGP)合成了中温固体氧化物燃料电池(IT-SOFC)的阴极材料SmBaCo2O5+δ(SBCO).通过热重-差热分析(TG-DTA),X射线衍射(XRD),透射电镜(TEM),扫描电镜(SEM),直流四极法及交流阻抗技术分析材料的性能.结果表明,初始粉体在850°C煅烧5 h形成钙钛矿结构单相.EGP制备的SBCO粉体颗粒细小、分散性好、粒径分布均匀,其与Sm0.2Ce0.8O1.9(SDC)电解质材料具有良好的高温化学相容性.SBCO的电导率在500-800°C时达到668-382 S cm-1.以SDC为电解质,SBCO为阴极制备对称半电池,其界面结合良好,颗粒连接充分,形成好的三相界面,具有高的阴极催化活性,750°C时阴极极化电阻为0.0688Ωcm2,远低于固相法(SSR)的值,活化能(Ea)为122.21 kJ mol-1.     

Pulsed laser-induced oxygen deficiency at TiO2 surface: Anomalous structure and electrical transport properties

We have studied pulsed laser-induced oxygen deficiencies at rutile TiO₂ surfaces. The crystal surface was successfully reduced by excimer laser irradiation, and an oxygen-deficient TiO_2−δ layer with 160 nm thickness was formed by means of ArF laser irradiation at 140 mJ/cm² for 2000 pulses. The TiO_2−δ layer fundamentally maintained a rutile structure, though this structure was distorted by many stacking faults caused by the large oxygen deficiency. The electrical resistivity of the obtained TiO_2−δ layer exhibited unconventional metallic behavior with hysteresis. A metal–insulator transition occurred at 42 K, and the electrical resistivity exceeded 10⁴ Ω cm below 42 K. This metal–insulator transition could be caused by bipolaronic ordering derived from Ti–Ti pairings that formed along the stacking faults. The constant magnetization behavior observed below 42 K is consistent with the bipolaronic scenario that has been observed previously for Ti₄O₇. These peculiar electrical properties are strongly linked to the oxygen-deficient crystal structure, which contains many stacking faults formed by instantaneous heating during excimer laser irradiation.     

Energetics of copper diphosphates – Cu2P2O7 and Cu3(P2O6OH)2

Differential scanning calorimetry and high temperature oxide melt solution calorimetry are used to study enthalpy of phase transition and enthalpies of formation of Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂. α-Cu₂P₂O₇ is reversibly transformed to β-Cu₂P₂O₇ at 338–363 K with an enthalpy of phase transition of 0.15 ± 0.03 kJ mol⁻¹. Enthalpies of formation from oxides of α-Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂ are −279.0 ± 1.4 kJ mol⁻¹ and −538.8 ± 2.7 kJ mol⁻¹, and their standard enthalpies of formation (enthalpy of formation from elements) are −2096.1 ± 4.3 kJ mol⁻¹ and −4302.7 ± 6.7 kJ mol⁻¹, respectively. The presence of hydrogen in diphosphate groups changes the geometry of Cu(II) and decreases acid–base interaction between oxide components in Cu₃(P₂O₆OH)₂, thus decreasing its thermodynamic stability.     

A novel single phase cathode material for a proton-conducting SOFC

A novel single phase BaCe_0.5Bi_0.5O_3 ? δ (BCB) was employed as a cathode material for a proton-conducting solid oxide fuel cell (SOFC). The single cell, consisting of a BaZr_0.1Ce_0.7Y_0.2O_3 ? δ (BZCY7)-NiO anode substrate, a BZCY7 anode functional layer, a BZCY7 electrolyte membrane and a BCB cathode layer, was assembled and tested from 600 to 700 °C with humidified hydrogen (～3% H₂O) as the fuel and the static air as the oxidant. An open-circuit potential of 0.96 V and a maximum power density of 321 mW cm^?2 were obtained for the single cell. A relatively low interfacial polarization resistance of 0.28Ω cm² at 700 °C indicated that the BCB was a promising cathode material for proton-conducting SOFCs.     

Mechanosynthesis of nanopowders of the proton-conducting electrolyte material Ba(Zr, Y)O3−δ

The formation of perovskite nanopowders of the common proton-conducting, electrolyte material Ba(Zr_1−xY_x)O_3−δ is demonstrated by room temperature mechanosynthesis for the compositional range x=0, 0.058 and 0.148. This is achieved with a planetary ball mill at 650 rpm in zirconia vials, starting from BaO₂ with ZrO₂, (ZrO₂)_0.97(Y₂O₃)_0.03 or (ZrO₂)_0.92(Y₂O₃)_0.08 precursors, respectively. Powder X-ray diffraction (XRD) reveals the formation of the perovskite phase in the early stages of milling with phase purity being achieved after milling times of 240 min for composition x=0.058 whereas 420 min is necessary for composition x=0.148. In contrast, traces of ZrO₂ are apparent in composition x=0 even after milling times of 420 min. The use of BaCO₃ as precursor does not allow the formation of the perovskite phase for any composition. The perovskite crystallites are spherical in shape with an average size determined from XRD of ca. 30 nm in agreement with transmission electron microscopy observations. FTIR spectra demonstrate that contamination levels of BaCO₃ in the mechanosynthesized powders are very low. The spherical shape and nanoscale of the crystallites allow densification levels that are highly competitive when compared to BaZrO₃-based materials formed by alternative synthesis techniques documented in the literature.     

Ionic Conduction and Application of Ba1.03Ce0.8Tm0.2O3−α Ceramic

Ba_1.03Ce_0.8Tm_0.2O_3?α ceramic with orthorhombic perovskite structure was prepared by conventional solid‐state reaction. The conductivity and ionic transport number of Ba_1.03Ce_0.8Tm_0.2O_3?α were measured by ac impedance spectroscopy and gas concentration cell methods in the temperature range of 500–900°C in wet hydrogen and wet air. Using the ceramic as solid electrolyte and porous platinum as electrodes, the hydrogen‐air fuel cell was constructed, and the cell performance was examined at 500–900°C. The results indicate that the specimen is a pure ionic conductor with the ionic transport number of 1 at 500–900°C in wet hydrogen. In wet air, the specimen is a mixed conductor of proton, oxide ion and electron hole. The protonic transport numbers are 0.071–0.018, and the oxide ionic transport numbers are 0.273–0.365. The conductivities of Ba_1.03Ce_0.8Tm_0.2O_3?α under wet hydrogen, wet air or fuel cell atmosphere are higher than those of Ba_1.03Ce_0.8RE_0.2O_3?α (RE?Y, Eu, Ho) reported previously by us. The fuel cell can work stably. At 900°C, the maximum power output density is 122.7 mW·cm^?2, which is higher than that of our previous cell using Ba_1.03Ce_0.8RE_0.2O_3?α (RE?Y, Eu, Ho) as electrolyte.     

Preparation of “pore-fill” type Pd–YSZ–γ-Al2O3 composite membrane supported on α-Al2O3 tube for hydrogen separation

Mesoporous YSZ–γ-Al₂O₃ membranes were coated on α-Al₂O₃ (Ø2 mm) tube by dipping the α-Al₂O₃ support tube into mixed sol consists of nano-size YSZ and bohemite particles followed by drying and calcination at 600 °C. Addition of bohemite in YSZ sol helped a good adhesion and uniform coating of the membrane film onto α-Al₂O₃ support. The quality of the mesoporous YSZ–γ-Al₂O₃ membranes was evaluated by the gas permeability experiments. The number of defects was minimized when the γ-Al₂O₃ content became more than 40%. Addition of γ-Al₂O₃ inhibited the crystal growth of YSZ, sintering shrinkage and distortion stress. Increase of calcination temperature and time results in the increase of pore size and N₂ permeance. A hydrogen perm-selective membrane was prepared by filling palladium into the nano-pores of YSZ–γ-Al₂O₃ layer by vacuum-assisted electroless plating. Crystal growth of palladium was observed by thermal annealing of the membrane at 600 °C for 40 h. The Pd–YSZ–γ-Al₂O₃ composite membrane revealed improved thermal stability allowing long-term operation at elevated temperature (>500 °C). This has been attributed to the improved fracture toughness of YSZ–γ-Al₂O₃ layer and matching of thermal expansion coefficient between palladium and YSZ. Although fracture of the membrane did not occur, decline of H₂ flux was observed when the membrane was exposed in 600 °C. This has been attributed to the agglomeration of palladium particles by crystal growth and dense packing into the pore networks of YSZ–γ-Al₂O₃ by elevation of temperature.     

Fabrication and characterization of γ-Al2O3–clay composite ultrafiltration membrane for the separation of electrolytes from its aqueous solution

In this paper, we have reported the preparation of low cost γ-Al₂O₃ membrane on a macroporous clay support by dip-coating method. For the synthesis of γ-Al₂O₃ top layer on the support, a stable boehmite sol is prepared using aluminium chloride salt as a starting material by sol–gel route. The structural properties of the composite membrane as well as γ-Al₂O₃ powder is carried out using scanning electron microscopy (SEM), X-ray diffraction (XRD), nitrogen adsorption–desorption isotherm data, Fourier transform infrared analysis (FTIR) and dynamic light scattering (DLS) analysis. The mean particle size of the boehmite sol used for coating is found to be 30.9 nm. The pore size distribution of the γ-Al₂O₃–clay composite membrane is found to be in the range of 5.4–13.6 nm. Separation performance of the membrane in terms of flux and rejection of single salts solution such as MgCl₂ and AlCl₃ as a function of pH, salt concentration and applied pressure is also studied. The rejection and flux behavior are found to be strongly dependent on electrostatic interaction between the charged molecules and γ-Al₂O₃–clay composite membrane. The intrinsic rejection has been determined by calculating the concentration at membrane surface (C_m) using Speigler–Kedem model. It is found that the observed rejection shows anomalous trend with increase in applied pressure and the intrinsic rejection increases with increase in applied pressure, a trend typical of the separation of electrolyte through charged membranes. At acidic pH, both the salt solution shows higher rejection. With increase in the salt concentration, observed rejection of salt decreases due to the enhanced concentration polarization. The maximum rejection of MgCl₂ and AlCl₃ is found to be 72% and 88%, respectively for salt concentration of 3000 ppm.     

Preparation and characterization of lithium ion-conducting glass-ceramics in the Li1 + xCrxGe2 − x(PO4)3 system

Li₂O–Cr₂O₃–GeO₂–P₂O₅ based glasses were synthesized by a conventional melt-quenching method and successfully converted into glass-ceramics through heat treatment. Experimental results of DTA, XRD, ac impedance techniques and FESEM indicated that Li_1.4Cr_0.4Ge_1.6(PO₄)₃ glass-ceramics treated at 900 °C for 12 h in the Li_1 + xCr_xGe_2 − x(PO₄)₃ (x = 0–0.8) system exhibited the best glass stability against crystallization and the highest ambient conductivity value of 6.81 × 10⁻⁴ S/cm with an activation energy as low as 26.9 kJ/mol. In addition, the Li_1.4Cr_0.4Ge_1.6(PO₄)₃ glass-ceramics displayed good chemical stability against lithium metal at room temperature. The good thermal and chemical stability, excellent conducting property, easy preparation and low cost make it promising to be used as solid-state electrolytes for all-solid-state lithium batteries.