The effect of Ce doping and pretreatment of Pt/Al2O3 on its catalysis of propane oxidation was investigated after aging the catalysts. The Ce amount and pretreatment conditions were varied, and the propane oxidation activity was measured. The properties of the catalysts were investigated by means of XRD, STEM-EDX, FT-IR, and H2-TPR. The size of the Pt nanoparticles (PtNPs) decreased for water-treated catalysts doped with a small amount of Ce, suggesting that water treatment of Ce-doped catalysts inhibits Pt sintering. The minimum PtNP size was obtained with ca. 3.6 wt% of Ce. The Ce species with less than 3.6 wt% existed in a dispersed state, whereas above this value, CeO2 particulates co-existed. The propane oxidation temperature of the water-treated catalysts was lowered to an extent that depended on the Ce content. This tendency is consistent with the PtNP size in the catalysts. It is considered that highly dispersed Ce species take a primary role in promoting propane oxidation on PtNPs. The reduction temperature of Ce species on water-treated catalysts was lower than that of untreated catalysts, probably owing to a stronger interaction between Pt and Ce, demonstrated by FT-IR measurements. The increased reducibility of Ce species may be the reason for the improved oxidation activity of the catalysts.
Graphic abstractHighly dispersed Au nanoparticles supported on Ni–Al mixed metal oxides (Au/NiAl-MMO) were prepared by a facile method, which is significantly efficient for the aerobic oxidation of ethyl lactate using authentic air as the oxidant, achieving 72.6% ethyl lactate conversion and 88.3% selectivity to ethyl pyruvate at 240 °C in a continuous fixed-bed reactor. The catalyst retained its catalytic performance during a long-term stability test. Characterization and experimental studies on the kinetic dependence sequence of the reactants and elementary reaction steps confirmed that the Au/NiAl-MMO catalyst followed the Mars–van Krevelen mechanism, with the activation of O2 as the elementary step. The quasi in situ X-ray photoelectron spectroscopy spectra demonstrated that the active sites in the Au/NiAl-MMO catalyst were Au nanoparticles. This work may provide a novel technique for developing more efficient supported metal catalysts for the aerobic oxidation of ethyl lactate using authentic air as the oxidant.
Graphical abstractHighly dispersed Au nanoparticle catalyst was facilely prepared for the efficient catalytic oxidation of ethyl lactate with authentic air.
The one-pot catalytic conversion of cellulose into ethylene glycol (EG) is an attractive way of biomass utilization. However, low-cost, efficient, and stable catalysts are the premise and research challenges of industrial application. Herein, the magnetic recyclable W–Ni@C catalyst was synthesized by in-situ pyrolysis of Ni-MOFs impregnated with ammonium metatungstate. Compared with the Ni-W bimetallic catalysts prepared by the impregnation method and the sol–gel method, the W–Ni@C catalyst for cellulose hydrogenolysis reaction can achieve a higher ethylene glycol yield (67.1% vs 43.3% and 42.6%) and 100% of cellulose conversion rate. The uniformly dispersed Ni nanoparticles and abundant defective WOx were formed in a reductive atmosphere generated in pyrolysis of Ni-MOFs, which was indispensable for the hydrogenolysis of cellulose into EG. Besides, the hierarchical porous carbon derived from organic ligands in Ni-MOFs reduces the mass transfer resistance while confining Ni nanoparticles and WOx to prevent their leaching, effectively enhancing the stability of the W–Ni@C catalyst. Therefore, the remarkable catalytic performance, the simple and effective recovery method as well as satisfying stability would make W–Ni@C become a promising catalyst for the conversion of cellulose to EG.
Graphical abstractProtonation of the molecularly rigid polymer of intrinsic microporosity PIM-EA-TB can be coupled to immobilisation of Fe(CN)63−/4− (as well as immobilisation of Prussian blue) into 1–2 nm diameter channels. The resulting films provide redox-active coatings on glassy carbon electrodes. Uptake, transport, and retention of Fe(CN)63−/4− in the microporous polymer are strongly pH dependent requiring protonation of the PIM-EA-TB (pKA ≈ 4). Both Fe(CN)64− and Fe(CN)63− can be immobilised, but Fe(CN)64− appears to bind tighter to the polymer backbone presumably via bridging protons. Loss of Fe(CN)63−/4− by leaching into the aqueous solution phase becomes significant only at pH > 9 and is likely to be associated with hydroxide anions directly entering the microporous structure to combine with protons. This and the interaction of Fe(CN)63−/4− and protons within the molecularly rigid PIM-EA-TB host are suggested to be responsible for retention and relatively slow leaching processes. Electrocatalysis with immobilised Fe(CN)63−/4− is demonstrated for the oxidation of ascorbic acid.
Graphical abstract
In this study, the Co-based catalyst was prepared by cobalt immobilization on the surface of functionalized silica-coated magnetic NPs (Fe3O4@SiO2-CT-Co) as a magnetically core–shell nanocatalyst and characterized by FT-IR, TGA, XRD, VSM, SEM, TEM, EDX, EDX mapping, and ICP techniques and appraised in the Suzuki–Miyaura cross-coupling reaction under mild reaction conditions. The results displayed the superparamagnetic behavior of the Fe3O4 NPs core encapsulated by SiO2 shell, and the size of the particles was estimated about 30 nm. Compared with the previously reported catalysts, the engineered Fe3O4@SiO2-CT-Co catalyst provided perfect catalytic performance for the Suzuki–Miyaura cross-coupling reaction in water as a green solvent and it was much cheaper in the comparison with the traditional Pd-based catalysts. Importantly, the durability of magnetic nanocatalyst was studied and observed that it is stable under the reaction conditions and could be easily reused for at least six successive cycles without any significant decrease in its catalytic activity.
Graphic abstractWater, as a byproduct in esterification, tends to adsorb on solid acid catalysts, causing loss of active components or decomposition of framework and thereby decreasing their reactivity and durability, while the development of water-tolerant solid acids is expected to solve these problems. In this review, the recent developments of major kinds of water-tolerant solid acids including zeolite, mesoporous silica, metal organic framework-based catalyst, magnetic nanoparticles, and polymeric catalyst are discussed in detail. Special attention has been paid to understand the role of hydrophobicity, acid strength, and structure of water-tolerant solid acids in catalytic performance and their stability. From the literature survey, it is found that despite the modified zeolites have a water contact angle as large as 160°, but their acid strength need to be improved and their small micropore sizes restrict their use in catalyzing the esterification of bulky molecules. In contrast, solid acids with abundant acid sites, suitable hydrophobicity, and abundant mesopores or macropores usually exhibit high activity and reusability. Among all the known solid acids, polystyrene-supported acidic ionic liquid catalysts (PS-CH2-[SO3H-pIM] [HSO4]) show a high yield of n-butyl acetate with 99.1% and high reusability of 13 times, which is a breakthrough over the traditional. This review aims to offer a comprehensive understanding for the water-tolerant solid acid catalysts in esterification.
Graphic AbstractHigh pollution, low-productivity, formation of by-products, and costly recovery of the vitamin are the challenges in common vitamin K3 synthesis methods on the industrial scale. These have encouraged us to design and characterize novel magnetic dendrimer nanoparticles based on silica-coated iron oxide (SCIO-(l5/l8)-G2.0) for nano-encapsulation of Pd, Mn, and Co to highly efficiently selectively synthesize vitamin K3. The CHN, BET, ICP, AAS, TEM, FESEM, TGA, DLS, EDS and XPS techniques were employed to intensively identify the obtained dendritic catalysts. Furthermore, the chemical stability of dendritic catalysts and influence of four various experimental factors were assessed by long-term study and response surface methodology analysis, respectively. The characterization results confirmed that all dendritic catalysts have a quasi-spherical morphology with mean size 20–30 nm, which could provide abundant active sites, high specific surface area and also increase the contact efficiency between the active sites and reactants. These results illustrated that the catalytic efficiency (TOF) depend strongly on the chemical structures as well as Lewis sites and natures (SCIO-l8-G2.0-Pd(II)?>?SCIO-l8-G2.0-Co(II)?>?SCIO-l8-G2.0-Mn(II)?>?SCIO-l5-G2.0-Pd(II)).
Graphical abstractAn electrochemical cycle for the grid energy storage in the redox potential of Fe involves the electrolysis of a highly concentrated aqueous FeCl2 solution yielding solid iron deposits. For the high overall energy efficiency of the cycle, it is crucial to maximize the energy efficiency of the electrolysis process. Here we present a study of the influence of electrolysis parameters on the energy efficiency of such electrolysis, performed in an industrial-type electrolyzer. We studied the conductivity of the FeCl2 solution as a function of concentration and temperature and correlated it with the electrolysis energy efficiency. The deviation from the correlation indicated an important contribution from the conductivity of the ion-exchange membrane. Another important studied parameter was the applied current density. We quantitatively showed how the contribution of the resistance polarization increases with the current density, causing a decrease in overall energy efficiency. The highest energy efficiency of 89 ± 3% was achieved using 2.5 mol L−1 FeCl2 solution at 70 °C and a current density of 0.1 kA m−2. In terms of the energy input per Fe mass, this means 1.88 Wh g−1. The limiting energy input per mass of the Fe deposit was found to be 1.76 Wh g−1.
Graphical abstractBendamustine or Treanda? is used as an anti-cancer drug, especially in treatment of hematologic malignancies. In view of the immense importance of drug/sensor issues, here we report adsorption behavior of this drug in presence of six nanosensors including aluminum nitride (AlN), carbon, and Si-doped carbon nanocones and nanosheets, at B3LYP/6-31G* level of theory. Electrical conductivity of these nanoadsorbents is probed against that of bendamustine for assessing their abilities of drug sensing with possible implications in drug delivery. The adsorption energy (Ead), doping energy (Edop), HOMO energy (EH), LUMO energy (EL), HOMO-LUMO band gap (Eg), change of band gaps in percent (%?Eg), change of natural bond orbital (NBO) charges (?Q), conduction electron population (N), and density of state (DOS) plots are calculated. More Ead, ?Q, and N values imply more interaction between bendamustine and nanosensor which lead to a strong recognition of the drug. The interaction of AlN nanosheet and bendamustine shows the highest Ead, %?Eg, and ?Q (??28.8 kcal/mol, ??33.6%, and 0.4 e, respectively) which make AlN nanosheet as the most promising among our scrutinized nanosensors. A negative Edop indicates an exothermic doping process, where Si atom improves the electronic sensitivity of C nanocone and nanosheet. All calculated Ead and %?Eg turn out as negative values which reveal that electrical conductivity of our scrutinized nanostructures are increased upon adsorbing process which makes them efficient sensors for bendamustine.
Graphical abstract
A cellulosic material has been synthesized that could efficiently and selectively adsorb organic and inorganic contaminants from aqueous solutions without interference from competing adsorption sites. Cellulose-graft-tetraethylenepentamine molecular imprinted polymer (C-TEPA-MIP) was synthesized by using 4-nitrophenol (4-NP) as the template. The C-TEPA-MIP adsorbent could adsorb 4-NP and Cr(VI) simultaneously and selectively, without being affected by the competitive adsorption sites of each of these pollutants. The adsorption of 4-NP was predominantly due to the imprinted sites of 4-NP in C-TEPA-MIP that were located inside of the adsorbent, whereas that of Cr(VI) was primarily due to the amine groups of TEPA found on the surface of the adsorbent. Compared with the non-imprint polymer synthesized without the template, C-TEPA-MIP showed higher selectivity for both 4-NP and Cr(VI) in unitary and binary systems. In addition, C-TEPA-MIP exhibited good stability and recyclability for 4-NP, which makes it a promising candidate material for applications concerning wastewater treatment.
Graphical abstractA novel 3D porous reduced graphene oxide/montmorillonite composite hydrogel (rGO–MMT) was prepared by solvent method, where the MMT nanosheets were homogenously dispersed in 3D rGO hydrogel. The porous 3D structure and the high dispersion of MMT nanosheets can promote the adsorption capacity. The effects of MMT content (wt%), the initial concentration of Cr(VI) solution (C0), pH value (pH0), the adsorption dose and temperatures on the adsorption capacity of rGO–MMT for Cr(VI) ions have been investigated. The optimum pH value for Cr(VI) adsorption is 2, and the adsorption capacity increases with MMT content and adsorption temperature. The rGO–MMT composite hydrogel displays the excellent adsorption property for both the heavy metal and organic pollutants. The adsorption capacity of rGO–MMT composite hydrogel is obviously higher than those of single rGO hydrogel and MMT due to the synergistic adsorption of rGO hydrogel and MMT. The adsorption of Cr(VI) ions on the rGO–MMT composite hydrogel follows linear pseudo-second-order kinetics, and the Langmuir model describes the adsorption process much better. Thermodynamic parameters indicate that adsorption is spontaneous, favorable and endothermic in nature.
Graphic abstractIn this work, a separation and purification process of U(VI), Zr(IV) and I2 from various fission products in nitric acid solution by 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide ([C4mim][NTf2]) and dibutyl-3-(3-methylimidazolium)propylphosphoramide bis(trifluoromethanesulfonyl)imide-task specific ionic liquid (phosphoramide-TSIL) was investigated. The phosphoramide-TSIL was found to reduce ligand loss compared to dibutyl propylphosphoramidate by total organic carbon testing (TOC). The stripping of U(VI), Zr(IV) and I2 could be achieved by guanidine carbonate solution, oxalic acid solution and sodium hydroxide solution, respectively. The phosphoramide-TSIL/[C4mim][NTf2] showed good irradiation stability and recyclability. Phosphoramide-TSIL has the potential to be applied for separation and purification in the actual radioactive environment.
Graphical abstractA simple, efficient and green approach to the synthesis of 1H-pyrazolo[1,2-b]phthalazine-5,10-diones has been developed via one-pot three-component reaction of aromatic aldehyde, malononitrile and phthalhydrazide catalyzed by zinc–proline complex (Zn[L-proline]2) using H2O: PEG400?=?6: 4 as solvent. Atom economy, good to excellent yield, operational simplicity and easy workup are important features of this method.
Graphical abstractLife-threatening diseases, especially those caused by pathogens and harmful ultraviolet radiation (UV-R), have triggered increasing demands for comfortable, antimicrobial, and UV-R protective clothing with a long service life. However, developing such textiles with exceptional wash durability is still challenging. Herein, we demonstrate how to fabricate wash durable multifunctional cotton textiles by growing in situ ZnO-TiO2 hybrid nanocrystals (NCs) on the surface of cellulosic fabrics. The ZnO-TiO2 hybrid NCs presented high functional efficiency, owing to their high charge transfer/separation. Ultrafine fiber surface pores, utilized as nucleating sites, endowed the uniform growth of NCs and their physical locking. The resulting fabrics presented excellent UV protection factors up to 54, displayed bactericidal efficiency of 100% against Staphylococcus aureus and Escherichia coli, and optimum self-cleaning efficacy. Moreover, the functionalized textiles exhibited robust washing durability, maintaining antibacterial and anti-UV-R efficiency even after 30 extensive washing cycles.
Graphical abstractIn the present research, magnesium aluminate spinel was prepared as catalyst support using a novel, facile, and efficient mechanochemical method. The Co-promoted catalysts with 20 wt.% of Ni were fabricated using an impregnation route and the samples were analyzed by the X-ray diffraction (XRD), N2 adsorption/desorption (BET), temperature-programmed reduction and desorption (H2-TPR and O2-TPD), and field emission scanning electron microscopy (FESEM) tests. The results confirmed that all samples have a mesoporous structure with a high specific surface area and the presence of cobalt caused complete CH4 oxidation at low temperatures, and no side reactions were observed. The results indicated that the 3%Co-20%Ni/MgAl2O4 catalyst was the optimal sample among the prepared catalysts, owing to the improvement of reduction features and oxygen mobility. The 50 and 90% of methane conversion was obtained at 530 and 600 °C, respectively. Also, the influence of calcination temperature, GHSV, and feed ratio was determined on the catalytic activity. The obtained outcomes revealed that the calcination temperature has a significant effect on the textural properties and catalytic efficiency. The sample calcined at 700 °C showed the weakest performance, which was related to the sintering of particles at high temperatures. The catalytic stability showed that the 3%Co-20%Ni/MgAl2O4 has acceptable stability during 600 min time of reaction.
Graphical abstractIn this paper, we have described a novel route to produce 5-hydroxymethylfurfural (HMF), a valuable platform molecule obtained from biomass. Metal-exchanged Keggin heteropolyacid salts were used as catalysts, in microwave-assisted reactions carried out in a water-ethyl acetate biphasic system. To avoid the use of homogenous Brønsted acid catalysts, which are corrosive and difficult to be reused, we have exchanged the protons of the Keggin heteropolyacids with transition metal cations. These salts were evaluated in the fructose dehydration, being the Cu3/2PW12O40 the most active and selective catalyst, achieving 81% of HMF yield, after 15 min reaction at 413 K under microwave irradiation. The effects of metal cation, anion or heteropolyanion present in the catalyst were evaluated. The greatest efficiency of the Cu3/2PW12O40 was attributed to its high Lewis acidic strength which allows its coordinates with the water molecules, consequently generating H3O+ ions in the reaction medium. In addition, after assessing reactions of fructose dehydration in the presence of other Copper salts [i.e., CuCl2 or Cu(NO3)2], we conclude the anion plays too a key role. The higher softness of phosphotungstic anion should stabilize protonate intermediates better than chloride or nitrate anions, favouring this way the reaction. Finally, although the catalyst has been soluble, it was easily reused by removing the aqueous phase and adding a new load of the substrate dissolved in ethyl acetate. The runs were successfully repeated without the loss of activity of the catalyst.
Graphical abstractActivated carbon paper-based materials were prepared from softwood pulp, activated carbon powder, and polyester fiber through wet forming process. Then polyethyleneimine was loaded on the activated carbon paper-based materials using physical impregnation method to fabricate green, low cost, and degradable PEI/activated carbon composite paper-based adsorbent materials (PPCA) for the removal of Cr(VI) from drinking water. The surface characteristics of the adsorbent were analyzed by SEM, EDX, BET, FT-IR, and XPS. It was found that the maximum adsorption capacity of Cr(VI) could reach up to 1.58 mg g?1 when the PEI immersion concentration is 1%, the contact time is 180 min, the temperature is 30 °C and pH?=?2. The adsorption of Cr(VI) on PPCA conformed to both the freundlich isotherm model and the quasi-second-order kinetic model, indicating that the adsorption was multi-molecular layer adsorption controlled by chemical reaction process. The adsorption mechanism of Cr(VI) on PPCA included electrostatic attraction, redox and chelation. Overall, this study provides a green, large-scalable production way for the preparation of biodegradable adsorption materials for the efficient removal of Cr(VI) from drinking water aiding the safe management of aqueous system.
Graphical abstractIn CO2 transformation catalysis, the synthesis of cyclic carbonates using two classes of MOF catalysts viz., zeolitic imidazolate frameworks (ZIF) and MOFs with carboxylate-capped SBUs have gained large attention. Herein we propose the strategy of employing a unified multifunctional framework formed in the metal-centered assembly of imidazole and amino-carboxylates for CO2 transformation, such as propylene carbonate (PC) by the cycloaddition of CO2 with propylene oxide. The framework {[Cu(L-asp)(1,4-bix)0.5]·3H2O}n (CuAspBix) comprises of the amino acid building units, L-aspartic acid (L-Asp) and the flexible ligand, 1,4-bis(imidazole-1-yl methyl)benzene [1,4-Bix]. The 1,4-Bix ligand with imidazole terminals renders elongated M-M distances and flexibility in comparison with pristine ZIF materials. The cumbersome synthesis procedure poor phase purity of the bulk catalyst in solvothermal conditions were improved by a microwave-assisted synthesis, preserving the structural and physicochemical properties. Minimal energy input or room temperatures for the catalysis occurred via the synergistic participation of CuAspBix and quaternary ammonium bromide salt, demonstrated by density-functional theory computational studies to propose mechanistic pathway of the reaction. Reaction conditions were optimized by altering the parameters. The heterogeneous catalyst was reused four times without a significant change in activity.
Graphic abstractA simple and efficient method for the synthesis of pyrazolopyranopyrimidines under solvent-free has been developed. The one-pot multicomponent condensation of arylaldehydes with hydrazine hydrate, ethyl acetoacetate and barbituric acid in the vicinity of a mesoporous basic nanomagnetic catalyst, namely DBU immobilized on Fe3O4@nSiO2@mSiO2 was synthesized in remarkably high yields and in short reaction times. Significantly, this catalyst can be easily separated from the reaction media by applying an external magnet, and can be reused for several cycles.
Graphical abstractThe triethylamine-based nanomagnetic ionic liquid, [(Et)3 N-H]FeCl4, was synthesized, and its structural and chemical characteristics were detected. The thermogravimetric analysis indicated its high thermal stability with a decomposition temperature higher than 300 °C. Additionally, [(Et)3 N-H]FeCl4 was used to efficiently catalyze the synthesis of xanthene derivatives under solvent-free conditions at 120 °C. [(Et)3 N-H]FeCl4 was recycled and reused at least five times.
Graphical abstract