Electrospinning synthesis and luminescence properties of one-dimensional La(9.33)(SiO4)6O2: Ln3+ (Ln = Ce, Eu, Tb) microfibers

One-dimensional La(9.33)(SiO(4))(6)O(2): Ln(3+) (Ln = Ce, Eu, Tb) microfibers were fabricated by a simple and cost-effective electrospinning method. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), photoluminescence (PL) and low voltage cathodoluminescence (CL) as well as kinetic decay were used to characterize the resulting samples. SEM and TEM results indicated that the diameter of the microfibers annealed at 1000 °C for 3 h was 200-245 nm. The microfibers were further composed of fine and closely linked nanoparticles. La(9.33)(SiO(4))(6)O(2): Ln(3+) (Ln = Ce, Eu, Tb) phosphors showed the characteristic emission of Ce(3+) (5d → 4f), Eu(3+) ((5)D(0)→(7)F(J)) and Tb(3+) ((5)D(3,4)→(7)F(J)) under ultraviolet excitation and low-voltage electron beams (3-5 kV) excitation. An energy transfer from Ce(3+) to Tb(3+) was observed in the La(9.33)(SiO(4))(6)O(2): Ce(3+), Tb(3+) phosphor under ultraviolet excitation and low-voltage electron beam excitation. Luminescence mechanisms were proposed to explain the observed phenomena. Blue, red and green emission can be realized in La(9.33)(SiO(4))(6)O(2): Ln(3+) (Ln = Ce, Eu, Tb) microfibers by changing the doping ions. So the La(9.33)(SiO(4))(6)O(2): Ln(3+) (Ln = Ce, Eu, Tb) phosphors have potential applications in full-color field emission displays.     

A red-emitting Ca8MgLa(PO4)7:Ce3+,Mn2+ phosphor for UV-based white LEDs application

Ca(8)MgLa(PO(4))(7):Ce(3+),Mn(2+) phosphors have been prepared by a conventional solid state reaction under a weak reductive atmosphere. The crystal structure and photoluminescent properties were investigated. It was found that the red emission at 640nm originated from the (4)T(1)((4)G)→(6)A(1)((6)S) transition of Mn(2+) increases dramatically by a factor of 6.4 with the optimum Ce(3+) co-doping. The energy transfer from Ce(3+) to Mn(2+) was proposed to be resonance-type via an electric dipole-dipole mechanism and the energy transfer efficiency was also calculated by the relative emission intensity. With the broadband ultraviolet (UV) absorption of Ce(3+) and the suitable color coordinates, Ca(8)MgLa(PO(4))(7):Ce(3+),Mn(2+) phosphors might be a promising candidate as red phosphors in the field of UV-based white light-emitting diodes.     

Luminescence investigation on ultraviolet-emitting rare-earth-doped phosphors using synchrotron radiation

Three series of new ultraviolet-emitting Ca(9)Y(PO(4))(7):Ln(3+) (Ln = Ce, Gd, Pr) phosphors were synthesized, and their luminescence was investigated. Under vacuum ultraviolet excitation Ca(9)Y(PO(4))(7):Ce(3+) phosphors emit UVA light with one broad emission centered at 346 nm, on account of the 5d(1) → 4f(1) transition of Ce(3+) ions; the optimal doping concentration of these phosphors is 0.2 mol. Ca(9)Y(PO(4))(7):Gd(3+) phosphors show a strong 4f(7) → 4f(7) transition and a sharp UVB emission band at 312 nm; the optimal doping concentration of these phosphors is 0.7 mol. The PL spectra of Ca(9)Y(PO(4))(7):Pr(3+) show two broad UVC emission bands centered between 230 and 340 nm, owing to the 4f(1)5d(1) → 4f(2) transition of Pr(3+) ions; the optimal doping concentration of these phosphors is 0.2 mol. Under 172 nm excitation, we found that the luminescence intensity of the UVA-emitting Ca(9)Y(PO(4))(7):0.2Ce(3+) is 0.3675 times that of BaSi(2)O(5):0.05Pb(2+), that of the UVB-emitting Ca(9)Y(PO(4))(7):0.7Gd(3+) is 1.7 times that of YAl(3)(BO(3))(4):0.25Gd(3+), and that of the UVC-emitting Ca(9)Y(PO(4))(7):0.2Pr(3+) is 1.5 times that of LaPO(4):0.1Pr(3+). The thermal stability investigation indicated that the luminescence decay was only 9.2%, 18.2%, and 10.3% for Ca(9)Y(PO(4))(7):0.2Ce(3+), Ca(9)Y(PO(4))(7):0.7Gd(3+), and Ca(9)Y(PO(4))(7):0.2Pr(3+) at 250 °C relative to that at ambient temperature, respectively. The Ca(9)Y(PO(4))(7):Ln(3+) (Ln = Ce, Gd, Pr) phosphors exhibit high emission efficiency and excellent thermal stability.     

Novel yellow-emitting Sr8MgLn(PO4)7:Eu2+ (Ln=Y, La) phosphors for applications in white LEDs with excellent color rendering index

Eu(2+)-activated Sr(8)MgY(PO(4))(7) and Sr(8)MgLa(PO(4))(7) yellow-emitting phosphors were successfully synthesized by solid-state reactions for applications in excellent color rendering index white light-emitting diodes (LEDs). The excitation and reflectance spectra of these phosphors show broad band excitation and absorption in the 250-450 nm near-ultraviolet region, which is ascribed to the 4f(7) → 4f(6)5d(1) transitions of Eu(2+). Therefore, these phosphors meet the application requirements for near-UV LED chips. Upon excitation at 400 nm, the Sr(8)MgY(PO(4))(7):Eu(2+) and Sr(8)MgLa(PO(4))(7):Eu(2+) phosphors exhibit strong yellow emissions centered at 518, 610, and 611 nm with better thermal stability than (Ba,Sr)(2)SiO(4) (570 nm) commodity phosphors. The composition-optimized concentrations of Eu(2+) in Sr(8)MgLa(PO(4))(7):Eu(2+) and Sr(8)MgY(PO(4))(7):Eu(2+) phosphors were determined to be 0.01 and 0.03 mol, respectively. A warm white-light near-UV LED was fabricated using a near-UV 400 nm chip pumped by a phosphor blend of blue-emitting BaMgAl(10)O(17):Eu(2+) and yellow-emitting Sr(8)MgY(PO(4))(7):0.01Eu(2+) or Sr(8)MgLa(PO(4))(7):0.03Eu(2+), driven by a 350 mA current. The Sr(8)MgY(PO(4))(7):0.01Eu(2+) and Sr(8)MgLa(PO(4))(7):0.03Eu(2+) containing LEDs produced a white light with Commission International de I'Eclairage (CIE) chromaticity coordinates of (0.348, 0.357) and (0.365, 0.328), warm correlated color temperatures of 4705 and 4100 K, and excellent color rendering indices of 95.375 and 91.75, respectively.     

Nanocrystalline CaYAlO4:Tb3+/Eu3+ as promising phosphors for full-color field emission displays

Eu(3+) and/or Tb(3+)-doped CaYAlO(4) phosphor samples were synthesized by Pechini-type sol-gel method. X-Ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), photoluminescence (PL) and cathodoluminescence (CL) spectra were used to characterize the samples. For CaYAlO(4):Tb(3+), it is shown that the Tb(3+)-doping concentration has a significant effect on the (5)D(3)/(5)D(4) emission intensity of Tb(3+), which is attributed to the cross relaxation from (5)D(3) to (5)D(4). Under the 4f(8)→ 4f(7)5d excitation of Tb(3+) or low-voltage electron beams excitation, the CaYAlO(4):Tb(3+) phosphors show tunable luminescence from blue to cyan, and then to green with the change of Tb(3+)-doping concentration. The CaYAlO(4):Eu(3+) samples exhibit a reddish-orange emission of Eu(3+) corresponding to (5)D(0,1)→(7)F(0,1,2,3) transitions. Furthermore, a white emission can be realized in the single phase CaYAlO(4) host by reasonably adjusting the doping concentrations of Tb(3+) and Eu(3+) under low-voltage electron beams excitation. Compared with the commercial blue (Y(2)SiO(5):Ce(3+)) and green (ZnO:Zn) phosphors, CaYAlO(4):0.1%Tb(3+) and CaYAlO(4):5%Tb(3+) phosphors have higher CL intensity and stability under continuous electron bombardment. Due to the excellent CL properties and good CIE chromaticity coordinates, the as-prepared Tb(3+)/Eu(3+)-doped CaYAlO(4) nanocrystalline phosphors have potential application in FEDs devices.     

Ca(9)Lu(PO(4))(7):Eu(2+),Mn(2+): a potential single-phased white-light-emitting phosphor suitable for white-light-emitting diodes

A novel white-light-emitting phosphor Ca(9)Lu(PO(4))(7):Eu(2+),Mn(2+) has been prepared by solid-state reaction. The photoluminescence properties indicate that there is an efficient energy transfer from the Eu(2+) to Mn(2+) ions via a dipole-quadrupole reaction. The obtained phosphor exhibits a strong excitation band between 250 and 430 nm, matching well with the dominant emission band of a UV light-emitting-diode (LED) chip. Upon excitation of UV light, white light is realized by combining a broad blue-green emission band at 480 nm and a red emission band at 645 nm attributed to the Eu(2+) and Mn(2+) ions. The energy-transfer efficiency and critical distance were also calculated. Furthermore, the phosphors can generate lights from blue-green through white and eventually to red by properly tuning the relative ratio of the Eu(2+) to Mn(2+) ions through the principle of energy transfer. Preliminary studies showed that the phosphor might be promising as a single-phased white-light-emitting phosphor for a UV white-light LED.     

Luminescence and microstructures of Eu(3+)-doped Ca9LiGd(2/3)(PO4)7

A red-emitting phosphor, Eu(3+)-doped Ca(9)LiGd(2/3)(PO(4))(7), was synthesized by the conventional high-temperature solid-state reaction. X-ray powder diffraction (XRD) analyses confirmed the pure crystalline phase of Whitlockite-type structure. The excitation spectra of Eu(3+) doped Ca(9)LiGd(2/3)(PO(4))(7) were measured in the VUV and UV region indicating an efficient energy transfer process from the host and Gd(3+) to Eu(3+) ions. Upon excitation with VUV and UV radiation, the phosphor showed strong red emission around 611 nm corresponding to the forced electric dipole (5)D(0)→(7)F(2) transition of Eu(3+) ions. The VUV- and UV-excited luminescence spectra of Ca(9)LiGd(2/3)(PO(4))(7):Eu(3+) together with the dependence of the integrated emission intensities on the doping levels were investigated. The Eu(3+) ions were investigated by a tunable laser as an excitation source. The excitation spectra of (7)F(0)→(5)D(0) transitions suggest that there are two families of inequivalent sites for Eu(3+) in this host. The concentration quenching and crystallographic site-occupancy of Eu(3+) ions in Ca(9)LiGd(2/3)(PO(4))(7) host were discussed on the basis of the site selective excitation and emission spectra, the luminescence decay and its crystal structure.     

The fabrication of one-dimensional Ca4Y6(SiO4)6O: Ln3+ (Ln=Eu, Tb) phosphors by electrospinning method and their luminescence properties

One-dimensional Ca(4)Y(6)(SiO(4))(6)O: Ln(3+) (Ln=Eu, Tb) microfibers were fabricated by a simple and cost-effective electrospinning method. X-ray diffraction (XRD) pattern and high-resolution transmission electron microscopy (HRTEM) confirmed that the fibers were composed of hexagonal Ca(4)Y(6)(SiO4)(6)O phase. Thermogravimetric and differential scanning calorimetry (TG-DSC) results showed that the Ca(4)Y(6)(SiO4)(6)O phase began to crystallize at 740°C. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results indicated that the diameter of as-prepared microfibers ranged from 390 to 900 nm and the diameter of the microfibers annealed at 1000°C ranged from to 120 to 260 nm. Under ultraviolet and low-voltage electron beams (3-5 kV) excitation, the Ca(4)Y(6)(SiO(4))(6)O: Ln(3+) (Ln=Eu, Tb) samples showed the red and green emission, corresponding to (5)D(0)→(7)F(2) transition of Eu(3+) and (5)D(4)→(7)F(5) transition of Tb(3+), respectively.     

A tunable single-component warm white-light Sr3Y(PO4)3:Eu2+,Mn2+ phosphor for white-light emitting diodes

The photoluminescence properties and energy transfer of the Eu(2+) and Mn(2+) co-doped Sr(3)Y(PO(4))(3) phosphors are investigated in detail. Two main emission bands attributed to the Eu(2+) and Mn(2+) ions are observed under UV light excitation via an efficient energy transfer process. When the Eu(2+) doping content is fixed, the emission chromaticity can be varied by simply adjusting the content of Mn(2+). The study of the behavior as a function of doping concentration indicates that the warm white-light can be obtained in a single host lattice. Furthermore, the analysis of the fluorescence decay curves based on the Inokuti-Hirayama theoretical model reveals that the dipole-quadrupole interaction is mainly responsible for the energy transfer mechanism from the Eu(2+) to Mn(2+) ions in the Sr(3)Y(PO(4))(3) phosphor. The developed phosphor exhibits a strong absorption in UV spectral region and white-light emission which may find utility as a single-component white-light-emitting UV-convertible phosphor in white LED devices.     

Novel red-emitting Ba2Tb(BO3)2Cl:Eu phosphor with efficient energy transfer for potential application in white light-emitting diodes

A novel red-emitting Ba(2)Tb(BO(3))(2)Cl:Eu phosphor possessing a broad excitation band in the near-ultraviolet (n-UV) region was synthesized by the solid-state reaction. Versatile Ba(2)Tb(BO(3))(2)Cl compound has a rigid open framework, which can offer two types of sites for various valence's cations to occupy, and the coexistence of Eu(2+)/Eu(3+) and the red-emitting luminescence from Eu(3+) with the aid of efficient energy transfer of Eu(2+)-Eu(3+)(Tb(3+)) and Tb(3+)-Eu(3+) have been investigated. Ba(2)Tb(BO(3))(2)Cl emits green emission with the main peak around 543 nm, which originates from (5)D(4) → (7)F(5) transition of Tb(3+). Ba(2)Tb(BO(3))(2)Cl:Eu shows bright red emission from Eu(3+) with peaks around 594, 612, and 624 nm under n-UV excitation (350-420 nm). The existence of Eu(2+) can be testified by the broad-band excitation spectrum, UV-vis reflectance spectrum, X-ray photoelectron spectrum, and Eu L(3)-edge X-ray absorption spectrum. Decay time and time-resolved luminescence measurements indicated that the interesting luminescence behavior should be ascribed to efficient energy transfer of Eu(2+)-Eu(3+)(Tb(3+)) and Tb(3+)-Eu(3+) in Ba(2)Tb(BO(3))(2)Cl:Eu phosphors.     

Patterning of Gd2(WO4)3:Ln3+ (Ln=Eu, Tb) luminescent films by microcontact printing route

Gd(2)(WO(4))(3) doped with Eu(3+) or Tb(3+) thin phosphor films with dot patterns have been prepared by a combinational method of sol-gel process and microcontact printing. This process utilizes a PDMS elastomeric mold as the stamp to create heterogeneous pattern on quartz substrates firstly and then combined with a Pechini-type sol-gel process to selectively deposit the luminescent phosphors on hydrophilic regions, in which a Gd(2)(WO(4))(3):Ln(3+) (Ln=Eu, Tb) precursor solutions were employed as ink. X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) spectra, as well as low voltage cathodoluminescence (CL) spectra were carried out to characterize the obtained samples. Under ultraviolet excitation and low-voltage electron beams excitation, the Gd(2)(WO(4))(3):Eu(3+) samples exhibit a strong red emission arising from Eu(3+)(5)D(0,1,2)-(7)F(1,2) transitions, while the Gd(2)(WO(4))(3):Tb(3+) samples show the green emission coming from the characteristic emission of Tb(3+) corresponding to (5)D(4)-(7)F(6,5,4,3) transitions. The results show that the patterning of rare earth-doped phosphors through combining microcontact printing with a Pechini-type sol-gel route has potential for field emission displays (FEDs) applications.     

Spectroscopic properties and intense red-light emission of (Ca, Eu, M)WO4 (M=Mg, Zn, Li)

The red-emitting phosphors of (Ca, Eu, M)WO4 (M=Mg, Zn, Li) were prepared through solid-state reactions, and their spectroscopic properties were studied. After the addition of a small amount of Mg2+, Zn2+ or Li+ in (Ca, Eu)WO4, the red-light emission intensity of Eu3+ increases obviously. In the luminescence spectra of the phosphors, the predominant transition emission is 5D0-->7F2 (616nm), whereas the other emissions are very weak. The excitation spectra are composed of interweaved ligand-to-metal charge-transfer bands (CTB) of W6+-O(2-) and Eu3+-O(2-), and a few 4f excitation transitions of Eu3+. Among the 4f excitation transitions of Eu3+, there are three strong excitation lines corresponding to 7F0-->5L6, 7F0-->5D2 and 7F0-->5D1 transitions, whose relative excitation intensity ratio is seriously affected when Li+ doped in the host. The new phosphors may be applied as red-emitting phosphors for white light emitting diodes.     

A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO(4))(2):Eu(2+),Mn(2+) Phosphor for Application in White-Light LEDs

Novel single-phased white light-emitting KCaY(PO(4))(2):Eu(2+),Mn(2+) phosphors for light-emitting diode (LED) applications were synthesized by conventional solid-state reaction. The emission hue could be controlled by tuning the Eu(2+)/Mn(2+) ratio via the energy transfer; the the emission hue of KCaY(PO(4))(2):Eu(2+),Mn(2+) varied from blue (0.1853, 0.2627) to white-light (0.3350, 0.3203) and eventually to purple (0.3919, 0.2867). The mechanism of energy transfer from a sensitizer Eu(2+) to an activator Mn(2+) in KCaY(PO(4))(2):Eu(2+),Mn(2+) phosphors was demonstrated to be an electric dipole-quadrupole interaction. Combining a NUV 405-nm chip and a white-emitting KCaY(PO(4))(2):1%Eu(2+),4%Mn(2+) phosphor produced a white-light NUV LED, demonstrating CIE chromaticity coordinates of (0.314, 0.329) and a color temperature of 6507 K.     

A new emission band of Eu2+ and its efficient energy transfer to Mn2+ in Sr2Mg3P4O15:Mn2+, Eu2+

Eu(2+) singly and Eu(2+), Mn(2+) co-doped Sr(2)Mg(3)P(4)O(15) exhibit not only the well known blue emission band of Eu(2+) peaking at 448 nm but also a new band at 399 nm in violet. They are attributed to Eu(2+) on different Sr(2+) sites. The Eu(2+) for the violet band can transfer energy to the red emitting Mn(2+) more efficiently than Eu(2+) for the blue band. The new Eu(2+) band could enable Sr(2)Mg(3)P(4)O(15):Mn(2+), Eu(2+) to be a promising phosphor for enriching the red component of white LEDs.     

Ce3+,Tb3+,Eu3+共掺杂Sr2MgSi2O7体系的白色发光和能量传递机理

通过正交试验,采用高温固相法制备了Sr2-x-y-zMgSi2O7∶xCe3+,yTb3+,zEu3+系列样品.使用X射线衍射仪和荧光光谱仪表征了样品的物相和发光性质,并讨论了Ce3+-Tb3+-Eu3+共掺杂Sr2MgSi2O7体系中的能量传递过程.实验结果表明,在327 nm波长激发下,所合成荧光粉的发射峰主要位于387 nm(蓝紫)、542nm(绿)和611 nm(红)处;分别以387,542和611 nm为监控波长,所得激发光谱显示荧光粉在327 nm处有最好的激发.在327 nm光激发下,系列样品发光进入白光区.最优化的荧光粉为Sr1.91MgSi2O7∶0.01Ce3+,0.05Tb3+,0.03Eu3+,其色坐标为(0.337,0.313),是一种潜在的发光二极管(LED)用白色荧光粉.     

Promising oxonitridosilicate phosphor host Sr3Si2O4N2: synthesis, structure, and luminescence properties activated by Eu2+ and Ce3+/Li+ for pc-LEDs

A novel oxonitridosilicate phosphor host Sr(3)Si(2)O(4)N(2) was synthesized in N(2)/H(2) (6%) atmosphere by solid state reaction at high temperature using SrCO(3), SiO(2), and Si(3)N(4) as starting materials. The crystal structure was determined by a Rietveld analysis on powder X-ray and neutron diffraction data. Sr(3)Si(2)O(4)N(2) crystallizes in cubic symmetry with space group Pa ?3, Z = 24, and cell parameter a = 15.6593(1) ?. The structure of Sr(3)Si(2)O(4)N(2) is constructed by isolated and highly corrugated 12 rings which are composed of 12 vertex-sharing [SiO(2)N(2)] tetrahedra with bridging N and terminal O to form three-dimensional tunnels to accommodate the Sr(2+) ions. The calculated band structure shows that Sr(3)Si(2)O(4)N(2) is an indirect semiconductor with a band gap ≈ 2.84 eV, which is close to the experimental value ≈ 2.71 eV from linear extrapolation of the diffuse reflection spectrum. Sr(3-x)Si(2)O(4)N(2):xEu(2+) shows a typical emission band peaking at ~600 nm under 460 nm excitation, which perfectly matches the emission of blue InGaN light-emitting diodes. For Ce(3+)/Li(+)-codoped Sr(3)Si(2)O(4)N(2), one excitation band is in the UV range (280-350 nm) and the other in the UV blue range (380-420 nm), which matches emission of near-UV light-emitting diodes. Emission of Sr(3-2x)Si(2)O(4)N(2):xCe(3+),xLi(+) shows a asymmetric broad band peaking at ~520 nm. The long-wavelength excitation and emission of Eu(2+) and Ce(3+)/Li(+)-doped Sr(3)Si(2)O(4)N(2) make them attractive for applications in phosphor-converted white light-emitting diodes.     

The quantum cutting of Tb(3+) in Ca(6)Ln(2)Na(2)(PO(4))(6)F(2) (Ln = Gd, La) under VUV-UV excitation: with and without Gd(3+)

The VUV-vis spectroscopic properties of Tb(3+) activated fluoro-apatite phosphors Ca(6)Ln(2-x)Tb(x)Na(2)(PO(4))(6)F(2) (Ln = Gd, La) were studied. The results show that phosphors Ca(6)Gd(2-x)Tb(x)Na(2)(PO(4))(6)F(2) with Gd(3+) ions as sensitizers have intense absorption in the VUV range. The emission color of both phosphors can be tuned from blue to green by changing the doping concentration of Tb(3+) under 172 nm excitation. The visible quantum cutting (QC) via cross relaxation between Tb(3+) ions was observed in cases with and without Gd(3+). Though QC can be realized in phosphors Ca(6)La(2-x)Tb(x)Na(2)(PO(4))(6)F(2), we found that Gd(3+)-containg phosphors have a higher QC efficiency, confirming that the Gd(3+) ion indeed plays an important role during the quantum cutting process. In addition, the energy transfer process from Gd(3+) to Tb(3+) as well as (5)D(3)-(5)D(4) cross relaxation was investigated and discussed in terms of luminescence spectra and decay curves.     

Sr2SiO4:Eu3+发光材料的制备及其光谱特性

采用溶胶-凝胶法制备了Sr2SiO4:Eu3+发光材料. 测量了Sr2SiO4:Eu3+材料的激发与发射光谱, 发射光谱主峰位于618 nm处;监测618 nm发射峰时, 所得激发光谱主峰分别为320、397、464 和518 nm. 研究了Sr2SiO4:Eu3+材料在618 nm的主发射峰强度随Eu3+浓度的变化情况. 结果显示, 随Eu3+浓度的增大, 发射峰强度先增大; 当Eu3+浓度为7%时(x), 峰值强度最大; 而后随Eu3+浓度的增大, 峰值强度减小. 在Eu3+浓度为7%的情况下, 研究了电荷补偿剂Li+的掺杂浓度(x(Li+))对Sr2SiO4:Eu3+材料发射光谱强度的影响. 结果显示, 随x(Li+)的增大, 材料发射光谱强度先增大后减小, 当x(Li+)为8%时, 峰值强度最大.     

Structure Refinement and Two-Center Luminescence of Ca(3)La(3)(BO(3))(5):Ce(3+) under VUV-UV Excitation

A series of Ca(3)La(3(1-x))Ce(3x)(BO(3))(5) phosphors were prepared by a high-temperature solid-state reaction technique. Rietveld refinement was performed using the powder X-ray diffraction (XRD) data, which shows occupation of Ce(3+) on both Ca(2+) and La(3+) sites with a preferred location on the La(3+) site over the Ca(2+) site. The prepared samples contain minor second phase LaBO(3) with contents of ～0.64-3.27 wt % from the Rietveld analysis. LaBO(3):1%Ce(3+) was prepared as a single phase material and its excitation and emission bands were determined for identifying the influence of impurity LaBO(3):Ce(3+) luminescence on the spectra of the Ca(3)La(3(1-x))Ce(3x)(BO(3))(5) samples. The luminescence properties of Ca(3)La(3(1-x))Ce(3x)(BO(3))(5) samples under vacuum ultraviolet (VUV) and UV excitation were investigated, which exhibited two-center luminescence of Ce(3+), assigned to the Ce(1)(3+) center in the La(3+) site and Ce(2)(3+) center in the Ca(2+) site, taking into account the spectroscopic properties and the Rietveld refinement results. The influences of the doping concentration and the excitation wavelength on the luminescence of Ce(3+) in Ca(3)La(3(1-x))Ce(3x)(BO(3))(5) are discussed together with the decay characteristics.     

Combinatorial search for green and blue phosphors of high thermal stabilities under UV excitation based on the K(Sr1-x-y)PO4:Tb3+ xEu2+y system

The present investigation aims at the synthesis of KSr 1-x-y PO 4:Tb(3+) x Eu(2+) y phosphors using the combinatorial chemistry method. We have developed square-type arrays consisting of 121 compositions to investigate the optimum composition and luminescence properties of KSrPO 4 host matrix under 365 nm ultraviolet (UV) light. The optimized compositions of phosphors were found to be KSr 0.93PO 4:Tb(3+) 0.07 (green) and KSr 0.995PO 4:Eu(2+) 0.005 (blue). These phosphors showed good thermal luminescence stability better than commercially available YAG:Ce at temperature above 200 degrees C. The result indicates that the KSr 1-x-y PO 4:Tb(3+) x Eu (2+)y can be potentially useful as a UV radiation-converting phosphor for light-emitting diodes.