膨胀阻燃硬质聚氨酯泡沫塑料热降解及燃烧产烟研究

采用热失重、X-射线光电子能谱分析、氧指数及烟密度测试等方法研究了可膨胀石墨(EG)与聚磷酸铵(APP)复配膨胀阻燃硬质聚氨酯泡沫塑料(RPUF)的热降解、燃烧性能及产烟行为.在此基础上利用锥形量热仪考察了EG/APP对磷酸三(β-氯异丙基)酯(TCPP)阻燃RPUF体系燃烧性能的影响.研究表明,EG与APP间的相互作用导致了EG/APP体系高温阶段失重速率下降、残炭量显著上升;EG/APP与RPUF之间的成炭作用以APP的化学成炭为主.与RPUF比较,RPUF/EG/APP的氧指数由19.8%提高至35.4%的同时,烟密度没有显著上升.对比EG、APP及EG/APP阻燃RPUF,体系残炭量越高、炭层耐热氧化能力越强,氧指数就越大;残炭表面越致密,产烟量就越少.添加EG/APP可显著降低含卤体系RPUF/TCPP的热释放、烟释放及CO释放速率,体现了EG与APP复合体系物理与化学膨胀结合的优势.     

The investigation of intumescent flame-retarded polypropylene using poly(hexamethylene terephthalamide) as carbonization agent

A novel intumescent flame retardant, containing ammonium polyphosphate (APP), and poly(hexamethylene terephthalamide) (PA6T), was prepared for flame retarding polypropylene (PP). The flame retardation of the PP composites was characterized by limiting oxygen index (LOI). The thermal degradation of the composites was investigated by means of thermogravimetric analysis (TG) and TG coupled with Fourier transform infrared spectroscopy (TG-FTIR). The morphology of the char obtained after combustion of the composites was studied by scanning electron microscopy. It has been found the intumescent flame retardant showed good flame retardancy, with the LOI value of the PA6T/APP/PP (5/25/70) system increasing from 17.5 to 32. Meanwhile, the TG and TG-FTIR work indicated that PA6T could be effective as a carbonization agent and there was a synergistic reaction between PA6T and APP, which effectively promoted the char formation of the PP composites. Moreover, it was revealed that uniform and compact intumescent char layer was formed after combustion of the intumescent flame retarded PP composites.     

Effect of aluminum diethylphosphinate on flame retardant and thermal properties of rigid polyurethane foam composites

Rigid polyurethane foam/aluminum diethylphosphinate (RUPF/ADP) composites were prepared by one-step water-blown method. Furthermore, scanning electron microscope (SEM), thermal conductivity meter, thermogravimetric analysis (TGA), limiting oxygen index, Underwriters Laboratories vertical burning test (UL-94) and microsacle combustion calorimetry were applied to investigate thermal conductivity, thermal stability, flame retardancy and combustion behavior of RPUF/ADP composites. Thermogravimetric analysis–Fourier transform infrared spectroscopy (TG–FTIR) was introduced to investigate gaseous products in degradation process of RPUF/ADP composites, while SEM and X-ray photoelectron spectroscopy were used to research char residue of the composites. It was confirmed that RPUF/ADP composites presented well cell structure with density of 53.1–59.0 kg m^?3 and thermal conductivity of 0.0425–0.0468 W m^?1 K^?1, indicating excellent insulation performance of the composites. Flame retardant test showed that ADP significantly enhanced flame retardancy of RPUF/ADP composites, RPUF/ADP30 passed UL-94 V-1 rating with LOI of 23.0 vol%. MCC test showed that ADP could significantly decrease peak of heat release rate (PHPR) of RPUF/ADP composites. PHPR value of RPUF/ADP20 was decreased to 158 W g^?1, which was 21.8% reduced compared with that of pure RPUF. TG–FTIR test revealed that the addition of ADP promoted the release of CO₂, hydrocarbons and isocyanate compound in first-step degradation of RPUF matrix while inhibited the release of CO in second step degradation. Char residue analysis showed that the addition of ADP promoted polyurethane molecular chain to form aromatic and aromatic heterocyclic structure, enhancing strength and compactness of the char. This work associated a gas–solid flame retardancy mechanism with the incorporation of ADP, which presented an effective strategy for preparation of flame retardant RPUF composites.

     

Supramolecular self‐assembly modification of ammonium polyphosphate and its flame retardant application in polypropylene

In order to improve its water resistance and compatibility with polymer matrix, ammonium polyphosphate (APP) is modified with melamine‐trimesic acid (MEL‐TA) aggregates by supramolecular self‐assembly technology. Chemical structure and morphology of APP@MEL‐TA are investigated by Fourier transform infrared spectroscopy and scanning electron microscopy (SEM), respectively. Intumescent flame retardant system of APP@MEL‐TA and charring‐foaming agent is introduced into polypropylene (PP) matrix. The flammability and combustion behavior of PP composites are investigated by limiting oxygen index (LOI), UL‐94 vertical burning, and cone calorimetry tests. In terms of LOI values and cone combustion results, APP@MEL‐TA performs better than pristine APP. Char residue of PP composites is investigated by SEM and Raman spectra. Flame retardant mechanisms are proposed based on thermal decomposition, combustion results, and analysis on char residue.     

Flame retardant properties and mechanism of an efficient intumescent flame retardant PLA composites

The charring agent (CNCA‐DA) containing triazine and benzene rings was combined with ammonium polyphosphate (APP) to form intumescent flame retardant (IFR), and it was occupied to modify polylactide (PLA). The flame retardant properties and mechanism of flame retardant PLA composites were investigated by the limited oxygen index (LOI), vertical burning test (UL‐94), thermogravimetric analysis, microscale combustion calorimetry, scanning electron microscopy, laser Raman spectroscopy analysis and X‐ray photoelectron spectroscopy. The analysis from LOI and UL‐94 presented that the IFR was very effective in flame retardancy of PLA. When the weight ratio of APP to CNCA‐DA was 3:1, and the IFR loading was 30%, the IFR showed the best effect, and the LOI value reached 45.6%. It was found that when 20 wt% IFR was loaded, the flame retardancy of PLA/IFR still passed UL‐94 V‐0 rating, and its LOI value reached 32.8%. The microscale combustion calorimetry results showed that PLA/IFR had lower heat release rate, total heat release, and heat release capacity than other composites, and there was an obvious synergistic effect between APP and CNCA‐DA for PLA. IFR containing APP/CNCA‐DA had good thermal stability and char‐forming ability with the char residue 29.3% at 800°C under N₂ atmosphere. Scanning electron microscopy observation further indicated that IFR could promote forming continuous and compact intumescent char layer. The laser Raman spectroscopy analysis and X‐ray photoelectron spectroscopy analysis results indicated that an appropriate graphitization degree of the residue char was formed, and more O and N were remained to form more cross‐linking structure. Copyright © 2016 John Wiley & Sons, Ltd.     

改性可膨胀石墨的制备及在硬质聚氨酯泡沫中的阻燃性能

采用表面接枝硅烷偶联剂法将硼酸负载在可膨胀石墨(EG)表面制得了改性EG(MEG), 并考察了MEG在硬质聚氨酯泡沫(RPUF)中的阻燃性能. 利用扫描电子显微镜、 X射线光电子能谱、 傅里叶变换红外光谱、 膨胀试验及热失重分析对MEG进行了形貌、 元素组成及结构性能表征, 通过热失重分析、 极限氧指数(LOI)及锥形量热仪考察了RPUF/MEG的热稳定性及燃烧性能. 结果表明, 硼硅化合物作为硅硼陶瓷前驱体已负载在EG表面; MEG及RPUF/MEG体系膨胀炭层更为致密, 800 ℃时的残余量分别较EG和RPUF/EG提高了8.7%和3.7%; RPUF/MEG体系的LOI较RPUF/EG有所提高, 热释放速率峰值降低了10%, 产烟速率及CO生成速率均显著降低. RPUF/MEG阻燃性能的提高与MEG负载的硅硼陶瓷前驱体促进了阻燃RPUF各组分间的相互作用及增强了炭层的阻隔性有关.     

Flame retardancy mechanisms of poly(1,4‐butylene terephthalate) containing microencapsulated ammonium polyphosphate and melamine cyanurate

The flame retardancy mechanisms of poly(1,4‐butylene terephthalate) (PBT) containing microencapsulated ammonium polyphosphate (MAPP) and melamine cyanurate (MC) were investigated via pyrolysis analysis (thermogravimetric analysis (TGA), real‐time Fourier transform infrared (FTIR), TG‐IR), cone calorimeter test, combustion tests (limited oxygen index (LOI), UL‐94), and residue analysis (scanning electron microscopy (SEM)). A loading of 20 wt% MC to PBT gave the PBT composites an LOI of 26%, V‐2 classification in UL‐94 test and a high peak heat release rate (HRR) in cone calorimeter test. Adding APP to PBT/MC composites did not improve their flame retardancy. In comparison with the addition of ammonium polyphosphate (APP) to PBT, MAPP with silica gel shell and MAPP with polyurethane shell both promoted the intumescent char‐forming and improved the flame retardancy of PBT through different mechanisms in the presence of MC. These two halogen‐free PBT composites with V‐0 classification according to UL‐94 test were obtained; their LOI were 32 and 33%, respectively. Copyright © 2010 John Wiley & Sons, Ltd.     

Thermal degradation and intumescent flame retardation of cellulose whisker/epoxy resin composite

The morphology, thermal degradation, and flame retardancy of epoxy (EP) composites containing microcrystalline cellulose whisker (MCW) and microencapsulated ammonium polyphosphate (MFAPP) were investigated using optical microscopy, limiting oxygen index (LOI), UL-94, thermogravimetry (TG), microscale combustion calorimeter, and TG-FTIR. EP/MFAPP/MCW composites can pass V-0 in UL-94 test at 6 wt% loading, and its peak heat release rate decreases when compared with EP and EP/MFAPP. The reason is that the presence of MCW strengthens the charring capacity of EP composites in a fire. The results of TG and TG-FTIR show that at low temperature, MFAPP stimulates the dehydration of MCW and EP, and produces gas which is helpful for the formation of an intumescent char. Moreover, the residue at high temperature does not release any flammable gas and is a good insulation layer on the surface of the sample, which protects the underlying material in a fire.     

聚磷酸酯阻燃剂复配聚磷酸铵对环氧树脂阻燃性能的影响

合成了一种9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)的衍生物——聚苯氧基磷酸-2-10-氢-9-氧杂-磷杂菲基对苯二酚酯(POPP), 以间苯二胺(m-PDA)为固化剂, 环氧树脂(EP)为基料, POPP为阻燃剂, 复配聚磷酸铵(APP), 制备了不同磷含量的阻燃环氧树脂. 利用极限氧指数(LOI)和垂直燃烧(UL94)实验表征了环氧树脂的阻燃性能; 以热重分析、 锥型量热和扫描电镜分析了阻燃环氧树脂的热性能和表面形态. 研究结果表明, 阻燃剂总加入量(质量分数)为5%时即可达到UL94 V-0级, 同时LOI值为27.7%; 当总加入量为15%, 即w_POPP=5%, w_APP=10 %时, 其LOI值可达到33.8%. 随着磷含量的增加, 阻燃环氧树脂的初始降解温度略有降低, 但高温下的残炭率明显增加. POPP/APP的加入在很大程度上降低了环氧树脂的热释放速率、 有效燃烧热、 烟释放量和有毒气体释放量. 阻燃环氧树脂在高温下形成比较稳定的致密膨胀炭层, 为底层的环氧树脂主体隔绝了分解产物及热量和氧气交换, 增强了高温下的热稳定性.     

The investigation of intumescent flame-retarded ABS using zinc borate as synergist

The influence of zinc borate (ZB) on the flammability and thermal properties of acrylonitrile–butadiene–styrene copolymer (ABS)/ammonium polyphosphate (APP)/poly(p-ethylene terephthalamide) (PETA) system was investigated. When the loadings of ABS, APP, PETA, and ZB were 70, 20.8, 6.9, and 2.3 %, respectively, the LOI value reached 36 and UL-94 vertical burning test was V-0. Even when 1.5 % ZB was added into ABS/APP/PETA (80/13.9/4.6) system, the LOI value was also 27. The thermal degradation of the composites was investigated by means of thermogravimetric analysis (TG) and Fourier transform infrared spectroscopy (FTIR). The TG indicated that the addition of ZB improved the thermal stability and the char residue of the ABS/APP/PETA system. What’s more, the mechanism was investigated by FTIR. The spectrum of flame retardant residue suggested that ZB reacted with APP/PETA physically. Additionally, scanning electron microscopy showed that the surface of intumescent charred layer obtained after combustion of ABS/APP/PETA/ZB (70/20.8/6.9/2.3) was compact and thick.     

Synergistic effect of zeolite 4A on thermal,mechanical and flame retardant properties of intumescent flame retardant HDPE composites

The combination of synergistic agent with intumescent flame retardant (IFR) systems provides a promising way to prepare high performance IFR composites. In this study, the effects of the synthetic zeolite 4 A in combination with the IFR system consisting of ammonium polyphosphate (APP) and tris (2-hydroxyethyl) isocynurate (THEIC) on thermal degradation, mechanical properties, flame retardancy and char formation of high-density polyethylene composites were investigated by limiting oxygen index (LOI) measurement, cone calorimetry, scanning electron microscopy and laser Raman spectroscopy. The LOI value of HD/FR/Z-0.5 composite with an optimum content of 0.5 wt. % zeolite 4 A and 25 wt. % of total flame retardant reaches 26.3 %. A low loading of zeolite 4 A can improve the bench-scale combustion performance as determined by cone calorimetry, and promote the formation of more compact char residue with a highly graphitic structure. However, a low loading of zeolite in combination with the IFR system consisting of APP and THEIC produces no significant changes in mechanical performance.     

Water resistance,thermal stability,and flame retardation of polypropylene composites containing a novel ammonium polyphosphate microencapsulated by UV‐curable epoxy acrylate resin

In this work, ammonium polyphosphate (APP) was microencapsulated by UV‐curable epoxy acrylate (EA) resin. The resulting novel EA‐microencapsulated APP (EA‐APP) was characterized by Fourier transform infrared spectra, X‐ray photoelectron spectroscopy, X‐ray diffraction, scanning electron microscopy, granulometry, and thermogravimetric (TG) analysis. EA‐APP was used to flame retard polypropylene (PP). The water solubility of EA‐APP and the water resistance of PP/EA‐APP systems were investigated. The thermal stability and combustion behaviors of PP/EA‐APP composites were studied through TG and cone calorimeter (CC) tests, respectively. The water resistance test showed that the EA shell could significantly improve the water resistance of PP/APP. TG data illustrated that the char residue of EA‐APP greatly increased by 149% compared with uncoated APP, and the thermal stability of PP/EA‐APP composite was improved because of the microencapsulation of APP, with an increment of 248% for the char residue compared with PP/APP. CC test results indicated that the peak value of heat release rate, the total heat release, and the peak of smoke production rate of PP/EA‐APP decreased in comparison with PP/APP. The mechanism for the improvement of flame retardancy in CC test was discussed based on the experimental results. EA resin containing a large number of hydroxyl groups might promote the dehydration reaction in EA‐APP, which facilitated the formation of char residue and the stabilization of APP. Consequently, the flame‐retardant efficiency for APP was improved because of the presence of EA shell. Copyright © 2014 John Wiley & Sons, Ltd.     

Monitoring thermal,structural properties,methotrexate release and biological activity from biocompatible spray-dried microparticles

Boron phosphates (BPs) with different acidities were prepared by regulating the calcination temperatures for the reaction products of boric acid and phosphoric acid. The crystal structure, morphology, surface acidity, and thermal stability were characterized by X-ray diffraction, scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), chemical absorbed apparatus, and thermogravimetric analysis (TG). The effects of BPs on the combustion behavior and catalyzing the carbonization of bisphenol-A epoxy resin (EP) were investigated by the limiting oxygen index (LOI) and cone calorimetry test. Upon loading 5 mass% BP prepared at 300 °C, the LOI value of the EP/BP composites increased to 29.6%, and moreover, the peak heat release rate and average specific extinction area decreased by 43 and 25%, respectively. A possible catalyzing carbonization mechanism was explored by TG coupled with Fourier transform infrared spectroscopy (TG–FTIR), TG, FTIR, SEM, Raman spectroscopy (Raman), and XPS. The results demonstrated that BP catalyzed EP to degrade at relatively low temperature, and the yield, compactness, and graphitization degree of the char residue were obviously enhanced with an increase in the ratio of Brønsted and Lewis acid sites (B/L value) and the total surface acid sites on the BP surface. Therefore, the catalyzing carbonization flame retardancy of the EP/BP composites can be improved through regulating the surface acidity of BP.     

Synergistic effects of 4A zeolite on the flame retardant properties and thermal stability of a novel halogen‐free PP/IFR composite

The synergistic effects of 4A zeolite (4A) on the thermal degradation, flame retardancy and char formation of a novel halogen‐free intumescent flame retardant polypropylene composites (PP/IFR) were investigated by the means of limiting oxygen index (LOI), vertical burning test (UL‐94), digital photos, scanning electron microscopy (SEM), thermogravimetric analysis (TGA), cone calorimeter test (CCT), laser Raman spectroscopy (LRS) and X‐ray photoelectron spectroscopy (XPS). It was found that a small amount of 4A could dramatically enhance the LOI value of the PP/IFR systems and the materials could pass the UL‐94 V‐0 rating test. Also, it could enhance the fire retardant performance with a great reduction in combustion parameters of PP/IFR system from CCT test. The morphological structures observed by digital and SEM photos revealed that 4A could promote PP/IFR to form more continuous and compact intumescent char layer. The LRS measurement, XPS and TGA analysis demonstrated that the compactness and strength of the outer char surface of the PP/IFR/4A system was enhanced, and more graphite structure was formed to remain more char residue and increase the crosslinking degree. Copyright © 2013 John Wiley & Sons, Ltd.     

磷化淀粉的合成及其与聚磷酸铵协效阻燃聚乳酸的性能研究

利用9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)和马来酸酐(MA)对淀粉进行改性得到磷化淀粉(DOPOMASt),通过红外光谱(FTIR)、核磁共振谱(1H-NMR)和X射线光电子能谱(XPS)确定其结构.利用DOPOMASt作为碳源,与聚磷酸铵(APP)复配后通过熔融共混制备了阻燃聚乳酸(PLA)...     

Aluminum hypophosphite in combination with expandable graphite as a novel flame retardant system for rigid polyurethane foams

The main aim of this work was to investigate the synergistic effect of expandable graphite (EG) and aluminum hypophosphite (AHP) on the flame retardancy of rigid polyurethane foams (RPUFs). A series of flame retardant RPUF containing EG and AHP were prepared by one‐shot and free‐rise method. The flame retardant, thermal degradation, and combustion properties of RPUF hybrids were characterized through limiting oxygen index (LOI) test, vertical burning (UL‐94) test, thermogravimetric analysis and microscale combustion calorimeter. The LOI and UL‐94 results showed that the RPUF sample with 10 wt% EG and 5 wt% AHP passed UL‐94 V‐0 rating and reached a relatively high LOI value of 28.5%, which is superior over other EG/AHP ratios in RPUF at the equivalent filler loading. Microscale combustion calorimeter results revealed that the incorporation of EG and AHP into RPUF reduced the peak heat release rate and total heat release, thus decrease the fire risk of RPUF significantly. Incorporation of EG and AHP improved the thermal stability of RPUF as observed from the thermogravimetric analysis results and also enhanced the thermal resistance of char layer at high temperature from scanning electron microscopy and Raman spectroscopy. Moreover, it could be seen from thermogravimetric analysis/infrared spectrometry spectra that the addition of EG and AHP significantly decreased the combustible gaseous products such as hydrocarbons and ethers. Finally, the synergistic mechanism in flame retardancy was discussed and speculated. Copyright © 2014 John Wiley & Sons, Ltd.     

Synergistic effects of aluminum hypophosphite on intumescent flame retardant polypropylene system

The effects of aluminum hypophosphite(AHP) as a synergistic agent on the flame retardancy and thermal degradation behavior of intumescent flame retardant polypropylene composites(PP/IFR) containing ammonium polyphosphate(APP) and triazine charring-foaming agent(CFA) were investigated by limiting oxygen index(LOI), UL-94 measurement, thermogravimetric analysis(TGA), cone calorimeter test(CONE), scanning electron microscopy(SEM) and X-ray photoelectron spectroscopy(XPS). It was found that the combination of IFR with AHP exhibited an evident synergistic effect and enhanced the flame retardant efficiency for PP matrix. The specimens with the thickness of 0.8 mm can pass UL-94 V-0 rating and the LOI value reaches 33.5% based on the total loading of flame retardant of 24 wt%, and the optimum mass fraction of AHP/IFR is 1:6. The TGA data revealed that AHP could change the degradation behavior of IFR and PP/IFR system, enhance the thermal stability of the IFR and PP/IFR systems at high temperatures and promote the char residue formation. The CONE results revealed that IFR/AHP blends can efficiently reduce the combustion parameters of PP, such as heat release rate(HRR), total heat release(THR), smoke production rate(SPR) and so on. The morphological structures of char residue demonstrated that AHP is of benefit to the formation of a more compact and homogeneous char layer on the materials surface during burning. The analysis of XPS indicates that AHP may promote the formation of sufficient char on the materials surface and improve the flame retardant properties.     

AN S- AND P-CONTAINING FLAME RETARDANT FOR POLYPROPYLENE

A novel charring agent,bis(1-oxo-4-hydroxymethyl-2,6,7-trioxa-1-phosphabicyclo[2.2.2]octane) phenylphosphine sulfide (BCPPS),has been synthesized,and it is combined with ammonium polyphosphate (APP) and melamine phosphate (MP) to impart flame retardance and dripping resistance for polypropylene (PP).The fire performance of the treated PP is investigated by limiting oxygen index (LOI),vertical burning test (UL-94) and cone calorimeter,and the thermal stability and thermal oxidative stability of the compos...     

磷杂菲类阻燃剂的合成及其与聚磷酸铵复合膨胀体系对环氧树脂的阻燃性能研究

以9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)、五硫化二磷(P2S5)为原料合成9,10-二氢-9-氧杂-10-磷杂菲-10-硫化物(DOPS),并将DOPS与聚磷酸铵(APP)组成复合阻燃剂,用于环氧树脂(EP)的阻燃改性.通过氧指数(LOI)、垂直燃烧(UL-94)、热失重(TGA)、锥形量热(CONE)和扫描电镜(SEM)等方法对改性后的环氧树脂的阻燃性能和阻燃机理进行了测试和分析.实验结果表明,DOPS/APP阻燃体系对EP具有很好的阻燃性能,且复配阻燃剂的阻燃效果比单一的阻燃剂阻燃效果好;其中,当阻燃剂的总添加量达到30%时即W_(DOPS)=10%、W_(APP)=20%时,阻燃EP复合材料的LOI值可达到29.2%,垂直燃烧等级达到UL-94 V-0级,残炭量可达49.3%.     

磷腈类衍生物改性磷酸锆的合成及其复配聚磷酸铵对硅橡胶阻燃性能和力学性能的影响

利用原位插层反应制得磷腈类衍生物修饰的改性磷酸锆(F-ZrP),并用机械共混工艺制得阻燃硅橡胶复合材料(FRSR).采用X射线衍射(XRD)、透射电子显微镜(TEM)、傅立叶红外光谱(FTIR)、热重(TG)、扫描电子显微镜(SEM)分别对磷酸锆的结构及其在硅橡胶基体的分散进行表征,并结合FRSR的垂直燃烧(UL-94)、极限氧指数(LOI)、锥形量热测试及残渣表面形貌的观察,研究了不同份数的F-ZrP复配聚磷酸铵对FRSR阻燃性能的影响并和添加未改性磷酸锆的样品性能对比,并对阻燃机理进行初步探讨;最后分析FRSR的力学性能.结果表明:F-ZrP拥有更大的层间距,而且在FRSR中分散的更好;当1 phr F-ZrP和19 phr APP复配使用时,UL-94达V-0级且LOI值为31.4,热释放速率峰值为265.3 kW/m~2,拉伸强度达8.11 MPa,FRSR的阻燃性能和力学性能得到明显的改善.适量的F-ZrP和APP复配使用能在气相和固相发挥协效阻燃作用,F-ZrP与APP的并用能提高残渣质量并且使阻隔层更加紧实,致密.