纳米SnO_2@TiO_2的制备及其光催化性能

SnCl4和 Ti(OBu)4为原料,采用活性层包覆法制备了 SnO2@TiO2包覆型复合光催化剂,并用 XPS、 IR、 XRD、 TEM和 BET等手段进行了表征,以二甲基二氯乙烯基磷酸酯（简称 DDVP）稀释液为模拟废水,考察了 SnO2@TiO2的光催化活性及降解液初始浓度对反应动力学的影响 .结果表明：包覆粒子由锐钛矿型 TiO2和金红石型 SnO2组成;与纯 SnO2、 TiO2相比, SnO2@TiO2包覆粒子的光催化活性明显提高, DDVP稀释液被光催化降解属于零级反应,但反应表观速率常数与降解液初始浓度成正比 .     

纳米SnO2@TiO2的制备及其光催化性能

以SnCl4和Ti(OBu)4为原料,采用活性层包覆法制备了SnO2@TiO2包覆型复合光催化剂,并用XPS、IR、XRD、TEM和BET等手段进行了表征,以二甲基二氯乙烯基磷酸酯（简称DDVP）稀释液为模拟废水,考察了SnO2@TiO2的光催化活性及降解液初始浓度对反应动力学的影响.结果表明：包覆粒子由锐钛矿型TiO2和金红石型SnO2组成;与纯SnO2、TiO2相比,SnO2@TiO2包覆粒子的光催化活性明显提高,DDVP稀释液被光催化降解属于零级反应,但反应表观速率常数与降解液初始浓度成正比.     

核-壳式纳米SnO2/TiO2光催化剂的制备和性能

 以纳米SnO2·nH2O胶体粒子为基质,采用活性层包覆法制备了纳米SnO2/TiO2复合光催化剂,并用R,TEM,XPS和XRD等手段进行了表征. 采用敌敌畏的光催化降解反应对所制催化剂的活性进行了评价. 结果表明,SnO2/TiO2为核-壳结构,粒径约为12 nm. SnO2/TiO2的光催化活性受TiO2含量及SnO2·nH2O乙醇溶液含水量的影响. 最佳条件为SnO2/TiO2中TiO2含量为56.45%,SnO2·nH2O乙醇溶液含水量为20%. 所制SnO2/TiO2光催化活性比纯TiO2显著提高,且光催化活性稳定,可重复使用.     

SnO2-TiO2复合光催化剂的制备和性能

采用均匀沉淀法在超细TiO2表面包覆SnO2,制备出SnO2-TiO2复合光催化剂,并用EDS,XRD,TEM和BET比表面积测定等手段进行了表征.以活性艳红X-3B溶液为模拟废水,考察了SnO2-TiO2的光催化活性.结果表明,复合粒子由锐钛矿型TiO2和金红石型SnO2组成;与纯TiO2相比,SnO2-TiO2的光催化活性有较大提高,SnO2最佳包覆量为18.4%.复合光催化剂活性的提高归因于不同能级半导体之间光生载流子的输运和分离.     

控制胶体合成法制备掺铁TiO_2粉末及光催化降解甲基橙

分别采用控制胶体合成法和溶胶-凝胶法制备了2种不同掺铁方式的TiO2粉末,并用XRD、TEM、BET、UV-Vis、FS等技术对样品进行了表征。在紫外光照射下,以甲基橙溶液的光催化降解反应为探针,研究了掺Fe离子浓度、包覆的次数、不同掺杂方式对样品光催化活性的影响。结果表明,以均匀掺铁TiO2(铁含量大于0.02mol%)干凝胶粉末为载体,采用控制胶体合成法制备了具有P-N结型结构的非均匀掺铁TiO2粉末,其光催化活性较均匀掺杂TiO2粉末明显提高,并且随着包覆次数(≤3次)的增加而增强,以0.04mol%掺铁TiO2粉末包覆3次后制备的样品具有最佳光催化活性,其表观速率常数是未掺杂的TiO2粉末的5.32倍,是具有相同Fe含量的均匀掺杂TiO2粉末的4.58倍。     

SnO2-TiO2复合颗粒的形态结构及其光催化活性

在气溶胶反应器中,利用TiCl4高温氧化反应制备超细TiO2,采用均匀沉淀法在TiO2表面沉积SnO2,制备SnO2-TiO2复合颗粒,应用TEM、EDS、XRD、BET比表面积测试等手段对粒子进行表征。以活性艳红X-3B溶液为处理对象,考察复合颗粒的光催化活性。结果表明SnO2-TiO2复合颗粒的光催化活性较纯气相合成超细TiO2有较大提高,SnO2最佳含量为15.3%,SnO2-TiO2复合颗粒光催化活性的提高归因于不同能级半导体之间光生载流子的输运和分离。     

TiO2/SnO2复合光催化剂的制备及光催化降解敌敌畏

包覆型催化剂;TiO2/SnO2复合光催化剂的制备及光催化降解敌敌畏     

水洗处理对Au/TiO2催化剂光催化活性的影响

以Au(S2O3)3-2为金前驱体, 分别采用水洗(W)和旋蒸(E)工艺制备了Au/TiO2催化剂. 用UV-Vis漫反射光谱(DRS)、X 射线衍射(XRD)、透射电子显微镜(TEM)和原子吸收光谱(AAS)对制备的催化剂样品进行了表征, 通过光催化降解甲基橙对催化剂光催化活性进行了评价. 结果表明, 通过水洗处理, 催化剂样品表面形成了具有较好分散性的金纳米粒子(2-5 nm), 而旋蒸工艺制备的样品表面形成一层金的包覆结构. Au/TiO2催化剂的光催化活性与制备工艺密切相关. 在相似的金负载量下, 水洗法制备的样品比旋蒸法制备的样品具有更高的光催化活性.     

SnO2/TiO2复合纳米纤维的制备及光催化性能

采用静电纺丝技术,以聚乙烯吡咯烷酮和钛酸正丁酯为前驱体,制得锐钛矿相TiO2纳米纤维。以TiO2纳米纤维为模板,通过水热合成法,制备了具有异质结构的SnO2/TiO2复合纳米纤维。利用扫描电镜(SEM)、X射线能量色散光谱（EDS）、透射电镜(TEM)和X射线衍射(XRD)等分析测试手段对其形貌和结构进行了表征,结果表明,SnO2纳米粒子均匀地生长在TiO2纳米纤维表面,形成了异质结构的SnO2/TiO2复合纳米纤维材料。通过改变反应物浓度,能有效地实现SnO2/TiO2复合纳米纤维的可控合成。以罗丹明B为模拟污染物,考察了SnO2/TiO2复合纳米纤维的光催化性能,与纯TiO2纳米纤维相比光催化活性明显提高,初步探讨了光催化反应机理。     

TiO_2/SnO_2复合光催化剂的制备及光催化降解敌敌畏

以 Sn Cl4· Ti( OBu) 4、氨水、乙醇为原料 ,采用活性层包覆法 ,制备出 Ti O2 / Sn O2 复合光催化剂 ,并用IR、XRD、TEM和 BET等手段对样品进行了表征 .研究其对有机磷农药敌敌畏的光催化降解效果 ,与单一半导体催化剂 Sn O2 、Ti O2 做了简单对比 .结果表明 :所制 Ti O2 / Sn O2 样品为包覆型结构 ,由锐钛矿型 Ti O2 金红石型 Sn O2 组成 ,与 Sn O2 及 Ti O2 晶体粉末相比所制 Ti O2 / Sn O2 包覆粒子光催化活性得到明显提高 .     

TiO2纳米管的光催化作用

光催化降解;十二烷基苯磺酸钠;紫外可见光谱;TiO2纳米管的光催化作用     

NiO@SnO2@Zn2TiO4@TiO2同轴四层纳米电缆的制备、表征及形成机理研究

采用静电纺丝技术, 通过改进实验装置, 在最佳的纺丝条件下制备了[Ni(CH₃COO)₂＋PVP]@[SnCl₄＋PVP]@[Zn(CH₃COO)₂＋PVP]@[Ti(OC₄H₉)₄＋CH₃COOH＋PVP]前驱体复合电缆, 将其进行热处理, 制备出NiO@ SnO₂@Zn₂TiO₄@TiO₂同轴四层纳米电缆. 采用热重-差热(TG-DTA)、X射线衍射(XRD)、傅立叶变换红外光谱(FTIR)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等分析技术对样品进行了表征. 结果表明, 所得产物为同轴四层纳米电缆, 芯层为NiO, 直径为35～55 nm|第二层为SnO₂, 厚度为30～50 nm|第三层为Zn₂TiO₄, 厚度为25～40 nm|壳层为TiO₂, 厚度为40～90 nm. 对同轴四层纳米电缆的形成机理进行了探讨.     

静电纺丝技术制备NiO@Al2O3@TiO2同轴三层亚微米电缆及其形成机理

采用静电纺丝技术,通过改进实验装置,采用同轴三喷嘴实验装置代替传统的单喷嘴实验装置,在最佳的纺丝条件下制备了[Ni(CH3COO)2+PVP]@[Al(NO3)3+PVP]@[Ti(OC4H9)4+CH3COOH+PVP]前驱体复合电缆,将其进行热处理,制备出了NiO@Al2O3@TiO2同轴三层纳米电缆. 采用差热-热重(TG-DTA)、X射线衍射(XRD)、傅立叶变换红外光谱(FTIR)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等分析技术对样品进行了表征. 结果表明,所得产物为NiO@Al2O3@TiO2同轴三层纳米电缆. 纳米电缆芯层为NiO,直径大约为137.83±8.85 nm;中间层为Al2O3,厚度大约为215.11±8.66 nm;壳层为TiO2,厚度大约为156.26±16.50 nm. 对NiO@Al2O3@TiO2同轴三层纳米电缆的形成机理进行了讨论.     

Preparation and enhanced visible-light photocatalytic H2-production activity of CdS-sensitized Pt/TiO2 nanosheets with exposed (001) facets

CdS-sensitized Pt/TiO(2) nanosheets with exposed (001) facets were prepared by hydrothermal treatment of a Ti(OC(4)H(9))(4)-HF-H(2)O mixed solution followed by photochemical reduction deposition of Pt nanoparticles (NPs) on TiO(2) nanosheets (TiO(2) NSs) and chemical bath deposition of CdS NPs on Pt/TiO(2) NSs, successively. The UV and visible-light driven photocatalytic activity of the as-prepared samples was evaluated by photocatalytic H(2) production from lactic acid aqueous solution under UV and visible-light (λ ≥ 420 nm) irradiation. It was shown that no photocatalytic H(2)-production activity was observed on the pure TiO(2) NSs under UV and/or visible-light irradiation. Deposition of CdS NPs on Pt/TiO(2) NSs caused significant enhancement of the UV and visible-light photocatalytic H(2)-production rates. The morphology of TiO(2) particles had also significant influence on the visible-light H(2)-production activity. Among TiO(2) NSs, P25 and the NPs studied, the CdS-sensitized Pt/TiO(2) NSs show the highest photocatalytic activity (13.9% apparent quantum efficiency obtained at 420 nm), exceeding that of CdS-sensitized Pt/P25 by 10.3% and that of Pt/NPs by 1.21%, which can be attributed to the combined effect of several factors including the presence of exposed (001) facets, surface fluorination and high specific surface area. After many replication experiments of the photocatalytic hydrogen production in the presence of lactic acid, the CdS-sensitized Pt/TiO(2) NSs did not show great loss in the photocatalytic activity, confirming that the CdS/Pt/TiO(2) NSs system is stable and not photocorroded.     

氮和碳共掺杂TiO2纳米晶的制备及可见光催化性能

以钛酸四丁酯为钛源, 冰醋酸为抑制剂, 超细铵盐为固体载体, 采用新型溶胶-凝胶法制备了氮和碳共掺杂TiO2纳米晶(N-C-TiO2) 光催化剂. 透射电子显微镜(TEM)结果表明, N-C-TiO2样品颗粒均匀, 尺寸细小, 且分散性好; 热失重分析(TGA)、 X射线粉末衍射(XRD)和X射线光电子能谱(XPS)研究结果表明, 复合干凝胶经低温热处理, 使铵盐载体分解、 挥发去除, 样品为单一的锐钛矿相, N和C原子扩散进入晶格结点或间隙位置, 与TiO2化学键结合; 氮气等温吸附-脱附结果表明, 样品比表面积高达356 m2/g, 孔体积为0.27 mL/g. 以氙灯为可见光光源, 罗丹明B水溶液为模拟污染物, P25为参比催化剂, 在辐射强度为100 mW/cm2的可见光照射条件下, N-C-TiO2具有很高的光催化活性, 其可见光催化活性明显高于P25.     

核壳结构p-n异质结复合光催化剂BiFeO3@TiO2的制备及其在可见光催化降解中的应用

化石燃料的迅速消耗导致环境污染与能源危机日益加剧.太阳能高效利用与转换是解决该难题的有效途径之一.在众多光催化剂中,TiO2因其高催化活性、高稳定性、低毒性以及低成本等优势而普遍受到关注,但TiO2存在着带隙过宽而无法利用可见光的缺陷,严重制约了其在光催化方向的实际应用.核壳型复合纳米材料具有较大的比表面积、较高的光吸收能力以及所吸附的污染物分子易于从吸附面扩散到光致降解面等特点,而表现出较强的有机污染物吸附性能以及良好的光催化活性.以磁体材料为核将TiO2包覆于磁体表面,可以制备具有磁分离特性的磁载光催化剂.而铁酸铋作为一种在室温下同时具有铁电性和铁磁性的钙钛矿型材料,由于其较窄的带宽(2.1 eV)在可见光催化氧化方面也受到了极大的关注.本文首先通过柠檬酸自燃烧法制备了可磁性分离的BiFeO3粉体,再以水解沉淀法将TiO2包裹在BiFeO3前驱体上形成了不同质量比(1:1,1:2,2:1)的核壳结构的BiFeO3@TiO2复合粉体,并以甲基紫为例,对其在紫外光和可见光照射下的光催化性能分别展开了研究.结果表明,BiFeO3@TiO2复合粉体的光催化性能较单独的BiFeO3或TiO2均有所提升.其中质量比为1:1的BiFeO3@TiO2复合粉体(TiO2壳层厚度为50–100 nm)展现出最强的光催化氧化活性,且在可见光下有更高的光催化效率.经表征分析,该复合粉体光催化性能高的原因可能归结于BiFeO3与TiO2两者之间形成了p-n异质结界面,有效地提高了电荷载流子的传输分离效率,同时BiFeO3较窄的禁带宽度拓展了纳米TiO2的光谱吸收范围,增强其光吸收能力.光电化学Mott-Schottky测试结果进一步证实:BiFeO3粉体在与TiO2复合之后,其电荷载流子传输与供体密度均有显著提升.自由基猝灭实验表明,在甲基紫光催化降解中起主要作用的为羟基自由基与光生电子,并结合能带理论与自建电场理论对降解机理进行了阐述.进一步研究表明,甲基紫降解效果最优条件为:复合粉体的投加量为1 g/L,甲基紫初始浓度为10 mg/L,初始pH为5.另外,质量比1:1的BiFeO3@TiO2对甲基橙和刚果红染料废水也具有较好的降解效果,表现出良好的工业应用前景.     

AgBr/TiO_2异质结型复合可见光催化剂的制备及其光催化活性

以钛酸四丁酯、KBr、AgNO3为前体,合成了具有异质结结构的纳米AgBr/Ti O2复合可见光催化剂.利用XRD、TEM、HRTEM和UV-Vis等方法对催化剂的晶相组成、形貌、粒度、微观结构、吸光性能等进行了表征.光催化降解亚甲基蓝活性结果表明,复合与单组分催化剂的光催化活性顺序为:AgBr/Ti O2AgBrAg-Br/P25P25Ti O2.含光敏剂AgBr的复合及单组份催化剂由于具有对可见光的良好吸收性能而具有较高的光催化活性.对于AgBr/Ti O2光催化剂,随mAgNO3/mTi O2比的增加,光催化活性先增强后减弱,当mAgNO3/mTi O2=3.35时光催化活性最高,分析结果表明,该复合催化剂粒径约15 nm,分散均匀且形成了紧密接触的AgBr/Ti O2异质结微结构,在紫外可见区(250～800 nm)都具有最强的光吸收.     

Preparation of Ce-TiO2 catalysts by controlled hydrolysis of titanium alkoxide based on esterification reaction and study on its photocatalytic activity

The Ce-TiO2 catalysts were prepared by controlled hydrolysis of Ti(OC(4)H(9))(4) with water generated "in situ" via an esterification reaction between acetic acid and ethanol, followed by hydrothermal treatment. The samples were characterized by X-ray diffraction (XRD), UV-vis diffuse reflectance spectroscopy (DRS), scanning electron microscopy (SEM), atomic absorption flame emission spectroscopy (AAS), and nitrogen adsorption-desorption methods. Both of undoped TiO2 and Ce-TiO2 samples exclusively consist of primary anatase crystallites, which further form spherical aggregates with diameters ranging from 100 to 500 nm. The photocatalytic activity of Ce-TiO2 was investigated for the photocatalytic degradation of Rhodamine B (RB) aqueous solution both under UV and visible light irradiation. Doping of Ce(4+) effectively improves the photocatalytic activity under both UV light irradiation and visible light irradiation with an optimal doping concentration of 0.2 and 0.4%, respectively. The photocatalytic mechanisms of Ce-TiO2 catalysts were tentatively discussed.