六羟基化合物为骨架的高分子固-固相变材料的合成与性能

分别使用三种含6个羟基的化合物(山梨醇、双季戊四醇和肌醇)作为分子骨架,聚乙二醇(PEG)作为相变功能链,4,4'-二苯基甲烷二异氰酸酯(MDI)为交联剂,合成了3种具有不同交联结构的新型固-固相变储能材料。通过傅里叶变换红外光谱(FT IR)、X-射线衍射(XRD)、偏光显微镜(POM)、示差扫描量热法(DSC)和热重量分析法(TG)分别对合成材料的分子结构、结晶性能、相变行为和热稳定性进行了研究。结果显示,所制备的材料在30~70℃温度范围内具有典型的固-固相变特性,其升温和冷却过程的相变焓最高可达107.5J/g和102.9J/g。此外,通过热重分析发现所合成材料具有较好的可重复使用性和热稳定性。因此,合成的新型固-固相变材料在热能储存和控温领域具有巨大的应用潜力。     

Polyethylene glycol grafted cotton as phase change polymer

Thermal storage cotton possessing solid–solid phase change properties was prepared by direct grafting of polyethylene glycol (PEG) on cotton fiber/cloth. Attempt has been made to characterize intermediates so that desired grafting could be obtained. The grafting was done by using urethane linkage and the grafted cotton was found to undergo solid–solid phase transition. The modified cotton was characterized by using Fourier transform infrared spectroscopy (FT-IR), ¹³C CPMAS, polarizing optical microscopy, differential scanning calorimetry (DSC) and thermogravimetry respectively. The DSC study revealed quite good storage effect of grafted cotton and the enthalpy of melting was found to be 55–59 J/g with a peak appearing at around 60 °C. During cooling scan, the crystallization peak appeared at around 38 °C. Further, thermogravimetric analysis confirmed good thermal stability up to 300 °C. Appreciable improvement of mechanical properties of cotton has been observed after grafting. The polarizing optical micrograph clearly showed change of morphology after grafting, i.e., the grafted PEG adhering to fiber surface.     

Preparation and characterization of pentaerythritol/butane tetracarboxylic acid/polyethylene glycol crosslinking copolymers as solid-solid phase change materials

Pentaerythritol/butane tetracarboxylic acid/polyethylene glycol (PBPEG) crosslinking copolymers as a novel solid-solid phase change material (SSPCM) were successfully synthesized through the reaction mechanism and conditions of hydroxyl-carboxyl condensation reaction. The composition and chemical structure, crystalline properties, phase change behaviors, thermal reliability and chemical stability of PBPEG crosslinking copolymers were investigated by Fourier transform infrared spectroscopy (FT-IR), wide-angle X-ray diffraction (WAXD), polarization optical microscopy (POM), differential scanning calorimetry (DSC), and thermogravimetry (TGA), respectively. The results show that PBPEG crosslinking copolymers have typical solid-solid phase transition temperatures in the range of 10.31～53.27°C and high latent heat enthalpy in the range of 89.6～102.8 J/g, the synthesized SSPCMs have good thermal reliability and chemical stability after 300 thermal cycles, and PBPEG crosslinking copolymers have good thermal stability before 364°C. In summary, the synthesized PBPEG crosslinking copolymers could be potentially used for thermal energy storage.     

Synthesis and thermal energy storage properties of the polyurethane solid–solid phase change materials with a novel tetrahydroxy compound

Based on the phase change theory, a novel tetrahydroxy compound (THCD) was designed and prepared. Depending on the spatial structure of the tetrahydroxy compound, a form-stable thermoplastic polyurethane solid–solid phase change material (TPUPCM) was synthesized via employing PEG as soft segments, while multi-benzene ring structure made by 4,4′-diphenylmethane diisocyanate and tetrahydroxy compound as hard segments. The composition and structure of THCD and TPUPCM, the TPUPCM’s the weight average molecular weight and number average molecular weight, dissolving and melting abilities, phase change behaviors, thermal performances and crystalline morphology were investigated by Fourier transform infrared spectrometer, ¹H nuclear magnetic resonance spectrometer, multiangle laser light scattering apparatus, differential scanning calorimentry, dynamic mechanical thermal analysis, thermogravimetry analysis system, wide-angle X-ray diffraction, polarizing optical microscopy. The results show that the solid–solid phase change material owns excellent phase change properties and a broad processing temperature range. The heating cycle phase change enthalpy is 137.4 J/g, and the cooling cycle phase change enthalpy is 127.6 J/g. The started decomposition temperature and the maximum decomposition temperature are at 323.5 and 396.2 °C, respectively. Furthermore, the solid–solid phase change material is dissolvable, meltable and can be processed directly, and has great potential applications in thermal energy storage.     

Evaluation of PCM/diatomite composites using exfoliated graphite nanoplatelets (xGnP) to improve thermal properties

This paper deals with the thermal performances of shape-stabilized phase change materials (SSPCM) for energy saving in various fields. This study enhanced thermal properties of SSPCM using exfoliated graphite nanoplatelets (xGnP). SSPCM, which contains the xGnP, was prepared by mixing and melting techniques for high dispersibility, thermal conductivity, and latent heat storage. In the experiment, we used hexadecane, octadecane, and paraffin as phase change materials (PCMs), and they have 254.7, 247.6, and 144.6 J g^?1 of latent heat capacity, and melting points of 20.84, 30.4, and 57.09 °C, respectively. The characteristics of SSPCMs were determined using SEM, DSC, FTIR, TG, TCi, and Energy simulation. SEM morphology showed homogenous dispersion of PCM and xGnP in the porous diatomite. DSC analysis results showed the latent heat capacity of SSPCM and SSPCM/xGnP composites, and TG analysis results showed the thermal reliability of the samples. Also, we checked the thermal conductivity of the SSPCM that contains xGnP, by TCi analysis.     

Synthesis and characterization of cellulose-g-polyoxyethylene (2) hexadecyl ether solid–solid phase change materials

A series of novel solid–solid phase change materials, namely, cellulose-g-polyoxyethylene (2) hexadecyl ether (Cellulose-g-E₂C₁₆) copolymers, were synthesized using toluene 2,4-diisocyanate (TDI) as a coupling reagent in the ionic liquid 1-allyl-3-methylimidazolium chloride (AmimCl). The optimum prepolymerization conditions were determined to be 25 °C and 75 min without catalyst, and the optimum reaction conditions of the grafting step were 90 °C, 6 h and 0.1 wt% dibutyltin dilaurate (DBTDL, weight percent of TDI). The successful grafting was confirmed by FTIR and ¹H-NMR. The properties of the Cellulose-g-E₂C₁₆ copolymers were investigated by DSC, TG and XRD. It is shown that the heat storage ability and phase change temperature of Cellulose-g-E₂C₁₆ copolymers depended on the degree of substitution. The crystalline type of the grafted E₂C₁₆ was not affected by the cellulosic backbone. Compared with E₂C₁₆, Cellulose-g-E₂C₁₆ copolymers showed better thermal stability. They are expected to be widely applied in the area of thermal energy storage.     

Synthesis and thermal properties of poly(styrene-co-acrylonitrile)-graft-polyethylene glycol copolymers as novel solid–solid phase change materials for thermal energy storage

A novel poly(styrene-co-acrylonitrile)-graft-polyethylene glycol(SAN-g-PEG) copolymer was synthesized as new solid–solid phase change materials(SSPCMs) by grafting PEG to the main chain of poly(styrene-co-acrylonitrile). The chemical structure of the SAN-g-PEG was confirmed by the Fourier transform infrared(FT-IR) and proton nuclear magnetic resonance(1H NMR) spectroscopy techniques. The thermal energy storage properties and the storage durability of the SAN-g-PEG were investigated by differential scanning calorimetry(DSC). The SAN-g-PEG was endowed with the solid–solid phase transition temperatures within the range of 23–36 8C and the latent heat enthalpy ranged from 66.8 k J/kg to 68.3 k J/kg. Thermal cycling tests revealed that the SAN-g-PEG kept great heat storage durability after 1000 thermal cycles. The thermal stability was evaluated by a thermal gravity analysis(TGA), and the initial decomposition temperature(Td) of SAN-g-PEG is 350 8C, which proves that the SAN-g-PEG possessed good thermal stability.     

Crystallization study of SrSnO3:Fe

Alkaline earth stannates have recently become important materials in ceramic technology due to its application as humidity sensor. In this work, alkaline earth stannates doped with Fe³⁺ were synthesized by the polymeric precursor method, with calcination at 300 °C/7 h and between 400 and 1100 °C/4 h. The powder precursors were characterized by TG/DTA after partial elimination of carbon. Characterization after the second calcination step was done by X-ray diffraction, infrared spectroscopy, and UV?Cvis spectroscopy. Results confirmed the formation of the SrSnO₃:Fe with orthorhombic perovskite structure, besides SrCO₃ as secondary phase. Crystallization occurred at 600 °C, being much lower than the crystallization temperature of perovskites synthesized by solid state reaction. The analysis of TG curves indicated that the phase crystallization was preceded by two thermal decomposition steps. Carbonate elimination occurred at two different temperatures, around 800 °C and above 1000 °C.     

A Novel Solid-Solid Phase Change Material Based on Poly(styrene-co-acrylonitrile) Grafting With Palmitic Acid Copolymers

(SAN-g-PA) as new solid-solid phase change materials (SSPCMs) were synthesized starting from poly(styrene-co- acrylonitrile) (SAN) and palmitic acid (PA). The chemical structure of the synthesized SAN-g-PA were characterized with Fourier transform infrared (FTIR), and Nuclear Magnetic Resonance (¹H-NMR), their thermal energy storage properties and thermal stability were investigated with differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), respectively. Moreover, the crystalline morphology and crystal structures were also measured with polarized optical microscopy (POM) and X-Ray Diffraction (XRD). The result shows that the PA molecule was grafted onto the SAN, SAN-g-PA were obtained successfully. The crystalline morphology and crystal structures of the synthesized SAN-g-PA are different from palmitic acid and SAN. As novel SSPCMs, SAN-g-PA possess suitable phase transition temperature, the higher enthalpy value, and good heat stability.     

Thermal decomposition kinetic evaluation and its thermal hazards prediction of AIBN

AIBN (2,2′-azobis (isobutyronitrile)), widely used for blowing agent and initiator, is a typical self-reactive material, being capable of undergoing runaway reaction due to its self-heating during storage or transportation. In this study, the thermal decomposition process of AIBN was studied by differential scanning calorimetry at different heating rates. The kinetic parameters including the activation energy and pre-exponential factor at different stages were calculated, and the laws of parameter variation were analyzed using the software, named as Advanced Kinetics and Technology Solutions, which can also predict the thermal stability of decomposition process at actual situations, such as ton and kg scale. The results show that heating rate can influence evidently the thermal behavior of AIBN, which can decompose in liquid phase or in liquid–solid co-existing phase, or, even decomposes in solid phase; according to Friedman method, the value of the calculated activation energy is 122 kJ mol^?1; according to Ozawa method, the value decreases gradually with the reaction process, and the smallest one is 124 kJ mol^?1. By mg-scale prediction under isothermal condition, it is known that AIBN decomposes at 30 °C (room temperature), very slowly; by ton-scale prediction under adiabatic condition, the safety diagram of AIBN is acquired, which shows how the time to the maximum rate changes with the initial temperature under ideal adiabatic condition (Φ = 1), for example, for TMR_ad = 24 h, the corresponding mean temperature (i.e., TD₂₄) is 71.23 °C, and for the initial temperature 71.23 °C, the lower and upper limits of the confidence intervals (95 % probability) are 18.5 and 31 h; by kg-scale prediction, it is obtained that the self-accelerating decomposition temperature of 50 kg AIBN with standard package is 63 °C, which is close to that of ARC.     

Thermal study of calcium silicate material synthesized with solid wastes

This work focuses on the thermal characterization of a calcium silicate-based material synthesized with different solid wastes (chamotte and marble) for use as thermal insulation material. Thermal and structural changes occurring during heating were accompanied by differential thermal analysis, thermogravimetric analysis, dilatometric analysis, open photoacoustic cell technique, X-ray diffraction (XRD), and scanning electron microscopy. An endothermic event at 823.2 °C was interpreted as decomposition of carbonates. An exothermic event around 900 °C is associated with the crystallization of calcium silicate phases mainly wollastonite. The themophysical properties of the calcium silicate-based material (thermal diffusivity, thermal conductivity, specific thermal capacity, and thermal effusivity) are influenced by the synthesis temperature. The thermal analysis results agree well with the XRD. The calcium silicate pieces presented low thermal conductivity values (0.227?0.376 W m^?1 K^?1). These results suggest that the calcium silicate-based materials produced essentially with chamotte and marble wastes has high potential to be used as thermal insulation construction material.     

Synthesis and characterization of an environmentally friendly PHBV/PEG copolymer network as a phase change material

Novel environmentally friendly poly(hydroxybutyrate-co-hydroxyvalerate) and poly(ethylene glycol) (PHBV/PEG) copolymer networks were synthesized through free-radical solution polymerization with PHBV diacrylate (PHBVDA) and polyethylene glycol diacrylate (PEGDA) as macromers. The molecular structure of PHBV/PEG copolymer network was characterized by Fourier transform infrared (FT-IR) and ¹H nuclear magnetic resonance (¹H NMR). The morphology of the PHBV/PEG copolymer network was characterized by polarization optical microscopy. Thermal energy storage properties, thermal reliability and thermal stability were investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis. The results indicated that the PHBV/PEG copolymer network hindered the growth of PEG crystalline segments or PHBV segments. PHBV/PEG copolymer network had a higher latent heat enthalpy, which didn’t reduce with the components of PHBV increased. Moreover, PHBV/PEG copolymer network still had good thermal stability even at 300 °C. These results suggested that such environmentally friendly copolymer network would have wide applications in phase change energy storage materials.     

Preparation and thermal reliability of <Emphasis Type="Italic">N</Emphasis>-butyl stearate/methyl palmitate composite phase change material

In this study, a series of binary mixtures of N-butyl stearate (nBS) and methyl palmitate (MP) were used to produce a novel composite phase change material (CPCM) for potential application in the eastern China, and their thermal properties were investigated by differential scanning calorimetry (DSC). The results of DSC indicated that the mixture consisting of 10 mass% nBS and 90 mass% MP is optimum as the CPCM in terms of the phase change temperature ranges (T _f = 19.74–5.59 °C; T _m = 18.34–33.80 °C) and latent heats (ΔH _f = 176.8 J g^?1; ΔH _m = 189.3 J g^?1). On the other hand, the thermal reliability and chemical stability of the CPCM after 120, 180, 240, 300, 360 and 500 accelerated thermal cycling tests were studied by DSC and fourier transform infrared (FTIR) analysis. The results demonstrated that the CPCM had good thermal reliability and chemical stability.     

Thermal and spectroscopic characterization of nanostructured zirconia–scandia–dysprosia

Zirconia containing 10 mol% scandia and x mol% dysprosia (0 ≤ x ≤ 1.5) gels was synthesized by simultaneous precipitation at room temperature. The aim of this work is to verify the effect of dysprosium on the cubic phase stabilization of the zirconia–scandia solid electrolyte. The gel was characterized by thermogravimetry, differential scanning calorimetry, and differential thermal analyses. The thermally treated powders were analyzed by Fourier transform infrared spectroscopy, thermal analyses, and X-ray diffraction techniques. For comparison purpose, a commercial zirconia–10 mol% scandia powder was subjected to some characterization techniques. The infrared spectrum shows characteristic absorption bands due to residual material from the synthesis on the surface of the powder particles. Nanostructured powders were obtained after thermal treatments at 500 °C for 2 h. Infrared spectroscopy and X-ray diffraction results evidence the stabilization of the cubic phase in zirconia–scandia containing dysprosium. The thermal stability of the cubic phase during thermal cycling was ascertained by thermal analysis.     

Influence of synthesis route on physicochemical properties of nanostructured electrolyte material La0.9Sr0.1Ga0.8Mg0.2O3−δ for IT-SOFCs

Nanosized La_0.9Sr_0.1Ga_0.8Mg_0.2O_3?δ (LSGM) has been synthesized by both gel-combustion method and solid state reaction method as an electrolyte material for IT-SOFCs. The effect of synthesis route on phase purity of the samples has been studied by X-ray diffraction technique. In the gel-combustion method, perovskite structure was formed at 1,200 °C with only trace amount of impurity and has an average crystallite size of 27 nm obtained by Scherrer’s equation. In solid state route, phase pure product was obtained only at the calcination temperature of 1,500 °C. The characteristics of the samples were also studied using FTIR, TG/DTA, Small angle X-ray scattering, BET surface area, thermal expansion measurements, and electrochemical impedance spectroscopy. The activation energy for oxide ion conduction of LSGM samples derived from Arrhenius plot is ~1.01 and 1.09 eV for gel-combustion and ceramic route, respectively. Linear increment of thermal expansion obtained by Dilatometry shows that there is no phase change at higher temperature in the sample. Sintered densities and microstructural features of the samples were also studied. The chemical compatibility of this electrolyte material has been studied with the perovskite oxide-based cathode material La_0.6Sr_0.4Co_0.2Fe_0.8O_3?δ and NiO.     

Calcination temperature-dependent morphology of photocatalytic ZnO nanoparticles prepared by an electrochemical–thermal method

ZnO nanoparticles (NPs) with tunable morphologies were synthesized by a hybrid electrochemical–thermal method at different calcination temperatures without the use of any surfactant or template. The NPs were characterized by Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction, dynamic light scattering, thermogravimetry–differential thermal analysis, scanning electron microscope and N₂ gas adsorption–desorption studies. The FT-IR spectra of ZnO NPs showed a band at 450 cm^?1, a characteristic of ZnO, which remained fairly unchanged at calcination temperatures even above 300 °C, indicating complete conversion of the precursor to ZnO. The products were thermally stable above 300 °C. The ZnO NPs were present in a hexagonal wurtzite phase and the crystallinity of ZnO increased with an increasing calcination temperature. The ZnO NPs calcined at lower temperature were mesoporous in nature. The surface areas of ZnO NPs calcined at 300 and 400 °C were 51.10 and 40.60 m² g^?1, respectively, which are significantly larger than commercial ZnO nanopowder. Surface diffusion has been found to be the key mechanism of sintering during heating from 300 to 700 °C with the activation energy of sintering as 8.33 kJ mol^?1. The photocatalytic activity of ZnO NPs calcined at different temperatures evaluated by photocatalytic degradation of methylene blue under sunlight showed strong dependence on the surface area of ZnO NPs. The ZnO NPs with high surface area showed enhanced photocatalytic activity.     

Thermo-physical characterization of some paraffins used as phase change materials for thermal energy storage

Three phase change paraffinic materials (PCMs) were thermophysically (phase-transition temperatures, latent heat, heat capacity at constant pressure, density, and thermal conductivity) investigated in order to be used as latent heat storage media in a pilot plant developed in Plovdiv Bulgaria. Raman structural investigation probes aliphatic character of the E53 sample, while the E46 and ECP samples contain also unsaturated components due to their Raman features within 1,500–1,700 cm^?1 range. Orthorhombic structure of the three PCMs was evidenced by the Raman modes at the 1,417 cm^?1. The highest latent heat value, ΔH, of phase transitions among the three materials was represented by summation of a solid order–disorder, and melting latent heat was encountered by the E53 paraffin, i.e., 194.32 J g^?1 during a μ-DSC scan of 1 °C min^?1. Conversely, the ECP composite containing ceresin component shows the lowest latent heat value of 143.89 J g^?1 and the highest thermal conductivity of 0.46 W m^?1 K^?1 among the three phase change materials (PCMs). More facile melt-disordered solid transition with the activation energy of 525.45 kJ mol^?1 than the lower temperature transition of disorder–order (E _a of 631.73 kJ mol^?1) during the two-step process of solidification for the E53 melt are discussed in terms of structural and molecular motion changes.     

Effect of the thermal treatment conditions on the formation of zinc ferrite nanocomposite, ZnFe2O4, by sol–gel method

Zinc ferrite nanocomposite was synthesized via thermal decomposition of zinc acetate and iron nitrate at three different temperatures (350, 450, and 550 °C). The influence of the thermal decomposition of precursors on the formation zinc ferrites was studied by differential thermal gravimetry and thermogravimetry (TG). The TG curve shows two steps for the thermal decomposition with mass loss of 17.3 % at 78 °C and 63.3 % at 315 °C. The prepared zinc ferrites nanocomposite was characterized by X-ray diffraction and scanning electron microscopy. The X-ray diffractograms of ZnFe₂O₄ shows that a crystalline phase, spinel system is formed. SEM micrograph of the zinc ferrite nanocomposite indicates the formation of uniformly spherical 48-nm nanograins. The properties of the zinc ferrite phase were strongly dependent on their calcinations temperature and molar ratio of precursors.     

Thermal study of NaP zeolite with different morphologies

NaP zeolites samples with different morphologies were successfully synthesized and their thermal behaviors were fully characterized by in situ HT-XRD, IR spectrum, and TG-DSC techniques. It was found that the cubic zeolite NaP phase underwent the same phase transitions, despite their different morphologies. During the whole heating process, they first underwent a minor phase transition into the tetragonal phase at 200 °C. Then they were gradually converted into the phillipsite phase between 400 and 700 °C. Finally, a very stable NaAlSiO₄ nepheline phase formed when the calcination temperature reached 800 °C, which would be kept even after the sample was cooled to room temperature. Although samples with different morphologies had similar phase transitions, they did have different thermal stability as proved by the TG-DSC study.     

Modification of acrylic bone cements by poly(ethylene glycol) with different molecular weight

The high polymerization temperature of acrylic bone cements can cause arthroplasty failure because of the thermal necrosis of surrounding bone tissue. To reduce this undesired effect we have developed novel acrylic bone cement composites containing a phase change material (PCM). As PCM poly(ethylene glycol) (PEG) of different molecular weight was applied and the effect of its incorporation on curing parameters, mechanical and morphological properties of acrylic bone cement was investigated. A significant decrease in maximum temperature from 65.8°C to 47.4°C and slight increase of setting time were observed. PEG introduction also contributed to the thermal stability of acrylic bone cement increase. SEM investigation of modified bone cement confirmed that the microstructure does not alter considerably because of PEG content. It was found that both PEG addition and incubation test contribute to an inconsiderable decrease in mechanical strength of bone cement. However, the mechanical strength increase can be caused by the fresh bone tissue incorporation into the pores appearing in bone cement. Copyright © 2016 John Wiley & Sons, Ltd.