层状LiNi0.5Mn0.5O2正极材料的优化合成及电化学性能

采用沉淀法首先得到了Ni0.5Mn0.5(OH)2沉淀物,以其为原料与LiOH反应制备了LiNi0.5Mn0.5O2正极材料。采用XRD、SEM、充放电测试等研究了其结构与电化学性能,同时研究了Li过量时对材料电化学性能和结构的影响。SEM分析表明,Ni0.5Mn0.5(OH)2与LiNi0.5Mn0.5O2产物均为微小晶粒团聚成的颗粒。LiNi0.5Mn0.5O2材料在2.5~4.4V电位区间内,首次放电容量为130mAh/g,0.2C倍率下,50次循环后的容量保持率为87.8%。锂过量有助于形成良好的层状结构材料,并能显著提高材料的比容量和循环性能,Li1.1Ni0.5Mn0.5O2的首次放电容量为149mAh/g,0.2C倍率下,50次循环后的容量保持率为92.6%。     

正极材料LiNi0.5Mn0.5-xCrxO2的低温燃烧合成

以LiNO3、Ni(NO3)2.6H2O、50%Mn(NO3)2溶液、Cr(NO3)3.9H2O和尿素为原料,采用低温燃烧法合成了LiNi0.5Mn0.5-xCrxO2,研究了回火温度、回火时间、锂过量和掺铬量对正极材料电化学性能的影响。结果表明,采用低温燃烧法合成LiNi0.5Mn0.5-xCrxO2的优化条件为:回火温度850℃、回火时间16h、锂过量15%,适宜掺铬量x=0.02。在优化条件下合成的正极材料具有α-NaFeO2型层状结构、球状形貌和良好的电化学性能,以0.1C速率在2.5～4.6V之间充放电,首次放电容量为179.9mAh/g,第50次循环放电容量仍保有171.0mAh/g,容量保持率达到95.1%。     

锂离子正极材料Li(Ni_(1/3)Co_(1/3)Mn_(1/3))_(1-x)Al_xO_2的制备及电化学性能

以化学法合成Li(Ni1/3Co1/3Mn1/3)1-xAlxO2系列正极材料(0≤x≤0.1);用X射线衍射仪、扫描电子显微镜和充放电仪研究系列产物的晶体微观结构、表面形貌以及电化学性能,研究不同Al含量参杂对材料性能的影响。结果表明,合成的材料均属于六方晶系,R3m空间群,保持α-NaFeO2层状结构相;Li(Ni1/3Co1/3Mn1/3)0.95Al0.05O2的首次放电容量166.30 mA·h/g,在2.5~4.5 V区间60次循环后比容量衰竭率为4.43%。通过对比Li(Ni1/3Co1/3Mn1/3)0.95Al0.05O2和Li(Ni1/3Co1/3Mn1/3)O2的电极阻抗,分析它们的电化学循环机理,可知掺杂Al后的正极材料适合大倍率放电。     

草酸盐共沉淀法制备锂离子电池正极材料LiNi_(0.5)Mn_(0.5)O_2及其电化学性能

使用草酸盐共沉淀法合成了LiNi0.5Mn0.5O2,并研究了共沉淀时的pH条件对终产物的结构、形貌及电化学性能的影响.采用X射线衍射(XRD)和扫描电镜(SEM)表征了在pH值为4.0、5.5、7.0和8.5时得到的共沉淀和终产物LiNi0.5Mn0.5O2的结构和形貌.使用充放电实验研究了不同pH条件下得到的LiNi0.5Mn0.5O2的电化学性能.结果表明,pH为7.0时,合成的材料颗粒更小、分布最均匀,材料具有良好的层状特征,且材料中锂镍的混排程度最小.电化学测试结果印证了pH为7.0时合成的材料具有更好的电化学性能,在0.1C的倍率下,材料的首次放电比容量达到了185 mAh.g-1,在循环20周后,放电比容量仍然保持在160 mAh.g-1.X射线光电子能谱(XPS)测试结果表明,pH为7.0时合成的LiNi0.5Mn0.5O2中Ni为+2价,Mn为+4价.     

草酸盐共沉淀法制备锂离子电池正极材料LiNi0.5Mn0.5O2及其电化学性能

使用草酸盐共沉淀法合成了LiNi0.5Mn0.5O2, 并研究了共沉淀时的pH条件对终产物的结构、形貌及电化学性能的影响. 采用X射线衍射(XRD)和扫描电镜(SEM)表征了在pH值为4.0、5.5、7.0和8.5时得到的共沉淀和终产物LiNi0.5Mn0.5O2的结构和形貌. 使用充放电实验研究了不同pH条件下得到的LiNi0.5Mn0.5O2的电化学性能. 结果表明, pH为7.0时, 合成的材料颗粒更小、分布最均匀, 材料具有良好的层状特征, 且材料中锂镍的混排程度最小. 电化学测试结果印证了pH为7.0时合成的材料具有更好的电化学性能, 在0.1C的倍率下, 材料的首次放电比容量达到了185 mAh·g-1, 在循环20周后, 放电比容量仍然保持在160 mAh·g-1. X射线光电子能谱(XPS)测试结果表明, pH为7.0时合成的LiNi0.5Mn0.5O2中Ni为+2价, Mn为+4价.     

锰源对燃烧法制备5V级正极材料LiNi0.5Mn1.5O4的影响

以硝酸锰和醋酸锰,采用蔗糖燃烧法制备锂离子电池正极材料LiNi0.5Mn1.5O4通过XRD、SEM、粒径分布测试、循环伏安、恒流充放电测试以及交流阻抗等方法,研究了醋酸锰和硝酸锰对产物的结构、形貌、粒径及电化学性能的影响。XRD测试结果表明样品的结构都为立方尖晶石型,属于Fd3m空间群。不同的锰源对材料的粒径及粒径分布有很大的影响。以醋酸锰为原料制得的材料的粒径较小并且分布更均匀,有利于锂离子的脱出和嵌入从而提高电化学性能。以醋酸锰为锰源制得的LiNi0.5Mn1.5O4在3.6~5.2 V的充放电电压范围内的电化学性能更好,1C(1C=140.0 mA.g-1)倍率的首次放电容量为144.5 mAh.g-1,循环100周后容量保持率为96%,在3C,5C,10C以及20C的放电容量分别为136.3,132.0,124.7以及96.6 mAh.g-1。     

锂离子电池正极材料LiNi_0.5Mn_1.5O_4表面包覆CuO的研究

本文首先通过共沉淀法和固相球磨法制备了纳米级的LiNi0.5Mn1.5O4高电压正极材料,然后通过溶胶-凝胶法制备了表面包覆CuO的CuO-LiNi0.5Mn1.5O4复合材料.通过对CuO包覆量为1%,3%和5%的复合材料的电化学性能对比,发现当包覆量为1%时,材料的性能最佳.在1 C下,材料的放电比容量高达126.1 mA h g?1,循环100次后容量保持率在99.5%.CuO包覆在纳米LiNi0.5Mn1.5O4材料表面,阻止电解液与活性颗粒的直接接触,削弱了电解液与LiNi0.5Mn1.5O4的相互作用,进而在一定程度上减缓了电解液的分解;CuO的包覆同时还缓解了电解液中HF对材料的攻击,阻止了锰的溶解和由此带来的结构改变,进而提高了材料的循环稳定性.     

LiNi0.49Mn1.49Y0.02O4的合成及其电化学性能研究

应用柠檬酸辅助溶胶-凝胶法.合成了Y3+掺杂的尖晶石LiNi0.49Mn1.49Y0.02O4材料.XRD、循环伏安、恒流充放电和交流阻抗测试结果表明,Y3+的掺杂能提高LiNi0.5Mn1.5O4的倍率和循环性能.在电压区间3.5～4.9V,1C倍率下,其初始放电比容量为114.9 mAh.g-1,100次循环后放电比容量仍可达113.0 mAh.g-1,容量保持率为98.3%.掺杂Y3+能减小材料界面阻抗.     

凝胶燃烧法合成Li1.07Mn1.93O4纳米片及其高倍率放电和循环稳定性

利用聚乙烯吡咯烷酮(PVP)作为聚合物配位剂和燃料,通过凝胶-燃烧法合成了Li1.07Mn1.93O4纳米片.采用热重/差热分析(TG/DTA)研究了凝胶的燃烧过程.采用X射线多晶衍射(XRD)分析了材料的结构,结果表明合成的Li1.07Mn1.93O4结晶完整,无杂质相.扫描电镜(SEM)结果显示材料的二次形貌为厚度约100nm的片状,由大小约100nm的一次颗粒构成.充放电测试表明Li1.07Mn1.93O4纳米片具备极佳的倍率放电性能和优秀的循环性能.0.5C(1C=120mA.g-1)倍率的初始放电容量为115.4mAh.g-1,即使倍率增大到40C,放电容量仍有105.3mAh.g-1.在10C倍率的放电条件下,循环850次容量保持率为81%.电化学阻抗谱(EIS)测试表明Li1.07Mn1.93O4纳米片的界面电荷转移电阻(Rct)远小于同类商业材料.     

微波-固相复合加热技术合成LiNi0.5Co0.5O2及其性能研究

用高分子分散及微波-固相复合加热技术合成了层状锂离子电池正极材料LiNi0.5Co0.5O2. 采用循环伏安、充放电循环、扫描电子显微镜(SEM)以及X射线粉末衍射(XRD)等测试技术, 研究了煅烧条件对材料微观形貌、相结构以及电化学性能的影响规律. 研究结果表明: 在750 ℃煅烧4 h即可得到形状为类球形的纯相层状LiNi0.5Co0.5O2正极材料, 该材料的最大放电容量达到154 mA·h/g, 循环10周后放电容量仍保持在148 mA·h/g以上.     

Li2CO3、NiO和电解MnO2合成高容量LiNi0.5Mn1.5O4及其表征

Well-developed crystalline LiNi_0.5Mn_1.5O₄ was prepared by solid-state reaction using Li₂CO₃, NiO and electrolytic MnO₂ at high heating and cooling rate. X-ray diffraction (XRD) patterns and scanning electron microscopic (SEM) images showed that LiNi_0.5Mn_1.5O₄ synthesized at 900 ℃ and 950 ℃ had cubic spinel structure with clearly defined shape. LiNi_0.5Mn_1.5O₄ spinel phase decomposed at 1 000 ℃ accompanying with structural and morphological degradation. TG measurement revealed that the weight loss during heating process could be mostly gained in cooling process, and the upward tendency of weight loss during heating process decreased, while that of irreversible weight loss rapidly increased with the increase of temperature. LiNi_0.5Mn_1.5O₄ powders prepared at 900 ℃ for 12 h delivered the maximum discharge capacity of 134 mAh·g^-1 with good cyclic performance at 2/7 C. In addition, by adjusting the calcination time at 900 ℃, the capacity and cycling performance of LiNi_0.5Mn_1.5O₄ were further enhanced.     

高容量锂离子电池正极材料LiNi0.9Co0.05Mn0.025Mg0.025O2的合成及电化学性能

以β-Ni0.9Co0.05Mn0.025Mg0.025(OH)2和LiOH.H2O为原料通过高温固相法合成了球形LiNi0.9Co0.05Mn0.025Mg0.025O2。采用热重-差热分析了反应过程,采用X射线衍射和扫描电镜对粉末的结构和形貌进行了表征。采用充放电测试和循环伏安测试对材料电化学性能进行了研究。结果表明:750℃煅烧12 h合成的LiNi0.9Co0.05Mn0.025Mg0.025O2为Li原子混排较少的良好层状结构,二次颗粒尺寸在15μm左右,且具有最高的放电比容量和良好的循环性能,在0.2C,2.8~4.3 V的条件下,首次放电比容量达207 mAh.g-1,40次循环后容量保持率为92.5%。     

脉冲激光沉积LiNi0.5Mn0.5O2薄膜正极性能

高能量密度、功率密度和高温度稳定性的全固态薄膜锂离子电池是微电子器件的理想电源.开发新型的大比容量正极薄膜材料是解决问题的关键之一.与LiCoO2正极相比,层状结构的LiNi0.5Mn0.5O2有更高的可逆比容量和结构稳定性.本文应用脉冲激光沉积法制备LiNi0.5Mn0.5O2沉积薄膜,研究了衬底材料、温度对薄膜的微观结构、表面形貌及组分的影响.由LiNi0.5Mn0.5O2电极组装半电池,研究了薄膜的电化学性能与晶体结构、表面形貌及组分间的关系,表征了LiNi0.5Mn0.5O2沉积薄膜于不同充电截止电压的循环稳定性及倍率性能,并讨论了LiNi0.5Mn0.5O2薄膜的结构特点.     

Electrochemical properties of nano-crystalline LiNi<Subscript>0.5</Subscript>Mn<Subscript>1.5</Subscript>O<Subscript>4</Subscript> synthesized by polymer-pyrolysis method

LiNi_0.5Mn_1.5O₄ powders were prepared through polymer-pyrolysis method. XRD and TEM analysis indicated that the pure spinel structure was formed at around 450 °C due to the very homogeneous intermixing of cations at the atomic scale in the starting precursor in this method, while the well-defined octahedral crystals appeared at a relatively high calcination temperature of 900 °C with a uniform particle size of about 100 nm. When cycled between 3.5 and 4.9 V at a current density of 50 mA/g, the as prepared LiNi_0.5Mn_1.5O₄ delivered an initial discharge capacity of 112.9 mAh/g and demonstrated an excellent cyclability with 97.3% capacity retentive after 50 cycles.     

添加Al2O3对Ni0.5Zn0.5Fe2O4纳米纤维结构和磁性能的影响

采用静电纺丝技术制备了添加0～20wt%Al2O3的Ni0.5Zn0.5Fe2O4纳米纤维。通过XRD、FESEM、TEM和VSM对样品的物相结构、形貌和磁性能进行了表征。结果表明,所合成的复合纳米纤维的直径都分布在40～150 nm之间,添加到纤维中的Al2O3主要以非晶态形式分布于铁氧体晶粒边界;随着Al2O3添加量的增加,可观察到γ-Fe2O3相逐渐析出,Ni-Zn铁氧体的晶格常数单调减小,说明有一些Al2O3进入到尖晶石晶格中取代了B位的Fe3+离子,Ni-Zn铁氧体的平均晶粒尺寸先增大后减小,在Al2O3添加量为8wt%时达到最大值39.2 nm;比饱和磁化强度和矫顽力随Al2O3添加量的增加呈现出相同的变化规律,先减小后增大,当Al2O3添加量超过5wt%时又开始变小。     

锂离子电池正极材料层状LiNi1/2Mn1/2O2的制备与表征

用一种简单的共沉淀法制备出了层状LiNi_1/2Mn_1/2O₂材料，并且用XRD、SEM、循环充放电、循环伏安(CV)和电化学阻抗谱(EIS)等方法对材料进行了表征测试。首先，用共沉淀法制备氢氧化镍和氢氧化锰的混合物;然后，对共沉淀溶液进行预氧化来制备前驱体;最后，用预氧化的前驱体合成了LiNi_1/2Mn_1/2O₂材料。SEM和XRD测试结果分别表明:LiNi_1/2Mn_1/2O₂材料是粒径范围在100～200 nm之间的球形粒子，并且具有非常好的层状结构。循环充放电表明:在空气中900 ℃下合成时间为9 h的材料，在充放电截止电压为2.8～4.6 V的情况下，经过40次循环，材料的容量可以稳定地保持在140 mAh·g^-1左右。循环伏安曲线表明:在锂的初始脱嵌和入嵌过程中存在不可逆相变。电化学阻抗谱测试表明LiNi_1/2Mn_1/2O₂具有很好的锂离子扩散能力。     

正极材料Li(Ni0.5Mn0.5)1-xMxO2 (M=Ti，Al；x=0，0.02)电化学行为的比较研究

0IntroductionMany efforts have been made to develop newmaterials as an alternative to LiCoO2due to the rela-tively high cost and toxicity of Co.Much attention hasbeen paid to layered structure cathode materials suchas LiMnO2and LiNiO2due to their lower co…